Ceramic tile adhesive mortar and preparation method thereof
Technical field
The present invention relates to building fields, and in particular to a kind of ceramic tile adhesive mortar and preparation method thereof.
Background technology
Mortar is common construction material, is generally used for building by laying bricks or stones and plastering engineering.Mortar is by cementitious material (cement, stone
Ash, clay etc.) and fine aggregate (sand) plus water mix form.According to composition material, can be divided into:1. lime mortar:By lime paste, sand
Be made according to a certain ratio with water, be generally used for intensity requirement it is not high, from moist masonry and coat of plaster;2. cement mortar:By
Cement, Sha Heshui are made according to a certain ratio, masonry, metope or the ground etc. being generally used in wet environment or water;3. mixed sand
Slurry:Appropriate admixture such as flyash, diatomite etc. are filled in cement or lime mortar to be made, and are used with saving cement or lime
Amount, and improve the workability of mortar, common mixed mortar has cement-lime mortar, cement clay mortar and lime clay mortar
Deng.It is divided by purposes difference:Masonry mortar, decorative mortar (including decoration mortar, waterproof mortar), adhesive mortar etc..It is and ceramic
Brick adhesive mortar is high for caking property requirement, and particularly exterior wall Ceramic Tiles adhesive mortar caking property is extremely good, and
Current Ceramic Tiles are poor with adhesive mortar caking property persistence, come off so as to cause ceramic tile.
The content of the invention
It is an object of the invention in view of the above-mentioned problems, providing a kind of ceramic tile adhesive mortar, caking property of the present invention is held
Long property is good, prevents ceramic tile from coming off.
Technical solution provided by the invention is:
A kind of ceramic tile adhesive mortar, the ceramic tile adhesive mortar are made by weight of following material:Modified ring
50-100 parts of oxygen resin, 50-100 parts of nano zine oxide, 30-55 parts of hydroxylated cellulose, 20-50 parts of sodium methyl silicate, dodecane
10-20 parts of base benzene sulfonic acid sodium salt, 20-50 parts of xanthans, 15-30 parts of vitamin C, 35-55 parts of castor oil polyoxyethylene ether, second two
100-200 parts of alcohol, 50-100 parts of nano ceramics grain, wooden sodium sulfonate 22-38 parts, 100-150 parts of fine sand, portland cement 400-
800 parts, 200-400 parts of water.
Preferably, the ceramic tile adhesive mortar is made by weight of following material:85 parts of modified epoxy,
65 parts of nano zine oxide, 45 parts of hydroxylated cellulose, 35 parts of sodium methyl silicate, 13 parts of neopelex, 35 parts of xanthans,
22 parts of vitamin C, 45 parts of castor oil polyoxyethylene ether, 165 parts of ethylene glycol, 78 parts of nano ceramics grain, 32 parts of wooden sodium sulfonate,
128 parts of fine sand, 655 parts of portland cement, 300 parts of water.
Preferably, the nano ceramics grain is made of following parts by weight material:100-200 parts of kaolin, montmorillonite 50-
100 parts, 45-55 parts of aluminium oxide, 30-50 parts of attapulgite, 8-15 parts of neopelex, polyethylene glycol 400 100-200
Part, 150-300 parts of water;The nano ceramics grain is made of following methods:By kaolin, montmorillonite, aluminium oxide, attapulgite powder
After when broken 500 mesh sieve of mistake, obtained powder and neopelex, polyethylene glycol 400, water mixing 1-2 small, spraying
Be dried to obtain solid particle, solid particle is sintered at 800-1000 DEG C 4-6 it is small when, after cooling, be crushed to less than 100 nanometers
Obtain the nano ceramics grain.
Preferably, the nano ceramics grain is made of following parts by weight material:150 parts of kaolin, 60 parts of montmorillonite, oxygen
Change 48 parts of aluminium, 38 parts of attapulgite, 12 parts of neopelex, 160 parts of polyethylene glycol 400,220 parts of water.
Preferably, the grain size of the fine sand is 300-500 mesh.
A kind of preparation method of the ceramic tile adhesive mortar, the preparation method of the ceramic tile adhesive mortar include
The following steps:
I heats water to 60 DEG C of constant temperature, adds in xanthans and vitamin C, and stirring obtains solution A to after dissolving;
II disperses modified epoxy, castor oil polyoxyethylene ether, ethylene glycol using emulsion dispersion machine, until solution is transparent
Until, obtain solution B;
III by solution A, solution B, nano zine oxide, hydroxylated cellulose, sodium methyl silicate, neopelex with
Wooden sodium sulfonate using emulsion dispersion machine disperse 0.5-1 it is small when, vacuumize to obtain mixing liquid C;
IV is uniformly mixed mixing liquid C with nano ceramics grain, fine sand, portland cement up to the Ceramic Tiles binding sand
Slurry.
Preferably, emulsion dispersion machine rate of dispersion is 2000-3000rmp in step II, when jitter time 0.5 is small.
Preferably, emulsion dispersion machine rate of dispersion is 500-1000rmp in step III, and the vacuum degree vacuumized is
0.8-0.9Mpa。
Beneficial effects of the present invention are as follows:
Modified epoxy, nano zine oxide, xanthans, vitamin C can be penetrated by solvent interaction in the present invention
The other materials of Ceramic Tiles veneer surface layer and the present invention form one layer of fine and close net structure, and intensity is high, and caking property is lasting so that
Ceramic Tiles are not easy to fall off, and wherein sodium methyl silicate, which plays waterproof action, can improve the water resistance of mortar so as to play mortar not
It is corroded, improves the service life of mortar, nano-ceramic particle is by materials such as kaolin, montmorillonite, aluminium oxide, attapulgites in the present invention
Material is made, and can significantly improve the tensile strength and compression strength of mortar of the present invention;Caking property of the present invention is good in summary, intensity
Height, waterproof ability is strong, prevents Ceramic Tiles from coming off.
Specific embodiment
With reference to specific embodiment, the present invention is described in further detail, those skilled in the art's reference to be made to say
Bright book word can be implemented according to this.
Embodiment 1:
A kind of ceramic tile adhesive mortar is made by weight of following material:It is 50 parts of modified epoxy, nano oxidized
50 parts of zinc, 30 parts of hydroxylated cellulose, 20 parts of sodium methyl silicate, 10 parts of neopelex, 20 parts of xanthans, vitamin C
15 parts, 35 parts of castor oil polyoxyethylene ether, 100 parts of ethylene glycol, 50 parts of nano ceramics grain, 22 parts of wooden sodium sulfonate, fine sand 100
Part, 400 parts of portland cement, 200 parts of water.
The preparation method of the ceramic tile adhesive mortar, comprises the following steps:
I heats water to 60 DEG C of constant temperature, adds in xanthans and vitamin, and stirring obtains solution A to after dissolving;
II disperses modified epoxy, castor oil polyoxyethylene ether, ethylene glycol using emulsion dispersion machine, until solution is transparent
Until, obtain solution B;
III by solution A, solution B, nano zine oxide, hydroxylated cellulose, sodium methyl silicate, neopelex with
Wooden sodium sulfonate using emulsion dispersion machine disperse 0.5 it is small when, vacuumize to obtain mixing liquid C;
IV is uniformly mixed mixing liquid C with nano ceramics grain, fine sand, portland cement up to the Ceramic Tiles binding sand
Slurry.
Embodiment 2
A kind of ceramic tile adhesive mortar is made by weight of following material:100 parts of modified epoxy, nano oxygen
Change 100 parts of zinc, 55 parts of hydroxylated cellulose, 50 parts of sodium methyl silicate, 20 parts of neopelex, 50 parts of xanthans, dimension life
Plain 30 parts of C, 55 parts of castor oil polyoxyethylene ether, 200 parts of ethylene glycol, 100 parts of nano ceramics grain, 38 parts of wooden sodium sulfonate, fine sand
150 parts, 800 parts of portland cement, 400 parts of water;The nano ceramics grain is made of following parts by weight material:100 parts of kaolin,
50 parts of montmorillonite, 45 parts of aluminium oxide, 30 parts of attapulgite, 8 parts of neopelex, 100 parts of polyethylene glycol 400, water 150
Part;The nano ceramics grain is made of following methods:Kaolin, montmorillonite, aluminium oxide, attapulgite were crushed into 500 mesh sieves,
After when obtained powder and small neopelex, polyethylene glycol 400, water mixing 1, spray drying obtains solid
Grain, solid particle is sintered at 800 DEG C 4 it is small when, after cooling, be crushed to less than 100 nanometers and obtain the nano ceramics grain.
The preparation method of the ceramic tile adhesive mortar, comprises the following steps:
I heats water to 60 DEG C of constant temperature, adds in xanthans and vitamin, and stirring obtains solution A to after dissolving;
II disperses modified epoxy, castor oil polyoxyethylene ether, ethylene glycol using emulsion dispersion machine, until solution is transparent
Until, solution B is obtained, emulsion dispersion machine rate of dispersion is 2000rmp, when jitter time 0.5 is small;
III by solution A, solution B, nano zine oxide, hydroxylated cellulose, sodium methyl silicate, neopelex with
Wooden sodium sulfonate using emulsion dispersion machine disperse 1 it is small when, vacuumize to obtain mixing liquid C, emulsion dispersion machine rate of dispersion is
500rmp, the vacuum degree vacuumized are 0.8Mpa;
IV is uniformly mixed mixing liquid C with nano ceramics grain, fine sand, portland cement up to the Ceramic Tiles binding sand
Slurry.
Embodiment 3
A kind of ceramic tile adhesive mortar is made by weight of following material:It is 85 parts of modified epoxy, nano oxidized
65 parts of zinc, 45 parts of hydroxylated cellulose, 35 parts of sodium methyl silicate, 13 parts of neopelex, 35 parts of xanthans, vitamin C
22 parts, 45 parts of castor oil polyoxyethylene ether, 165 parts of ethylene glycol, 78 parts of nano ceramics grain, 32 parts of wooden sodium sulfonate, fine sand 128
Part, 655 parts of portland cement, 300 parts of water;The nano ceramics grain is made of following parts by weight material:200 parts of kaolin covers
De- 100 parts of stone, 55 parts of aluminium oxide, 50 parts of attapulgite, 15 parts of neopelex, 200 parts of polyethylene glycol 400, water 300
Part;The nano ceramics grain is made of following methods:Kaolin, montmorillonite, aluminium oxide, attapulgite were crushed into 500 mesh sieves,
After when obtained powder and small neopelex, polyethylene glycol 400, water mixing 2, spray drying obtains solid
Grain, solid particle is sintered at 1000 DEG C 6 it is small when, after cooling, be crushed to less than 100 nanometers and obtain the nano ceramics grain;
The grain size of the fine sand is 300-500 mesh.
The preparation method of the ceramic tile adhesive mortar, comprises the following steps:
I heats water to 60 DEG C of constant temperature, adds in xanthans and vitamin, and stirring obtains solution A to after dissolving;
II disperses modified epoxy, castor oil polyoxyethylene ether, ethylene glycol using emulsion dispersion machine, until solution is transparent
Until, solution B is obtained, emulsion dispersion machine rate of dispersion is 3000rmp, when jitter time 0.5 is small;
III by solution A, solution B, nano zine oxide, hydroxylated cellulose, sodium methyl silicate, neopelex with
Wooden sodium sulfonate using emulsion dispersion machine disperse 1 it is small when, vacuumize to obtain mixing liquid c, emulsion dispersion machine rate of dispersion is
1000rmp, the vacuum degree vacuumized are 0.9Mpa;
IV is uniformly mixed mixing liquid C with nano ceramics grain, fine sand, portland cement up to the Ceramic Tiles binding sand
Slurry.
Embodiment 4
A kind of ceramic tile adhesive mortar is made by weight of following material:It is 85 parts of modified epoxy, nano oxidized
65 parts of zinc, 45 parts of hydroxylated cellulose, 35 parts of sodium methyl silicate, 13 parts of neopelex, 35 parts of xanthans, vitamin C
22 parts, 45 parts of castor oil polyoxyethylene ether, 165 parts of ethylene glycol, 78 parts of nano ceramics grain, 32 parts of wooden sodium sulfonate, fine sand 128
Part, 655 parts of portland cement, 300 parts of water;The nano ceramics grain is made of following parts by weight material:The nano ceramics grain
It is made of following parts by weight material:150 parts of kaolin, 60 parts of montmorillonite, 48 parts of aluminium oxide, 38 parts of attapulgite, dodecyl
12 parts of benzene sulfonic acid sodium salt, 160 parts of polyethylene glycol 400,220 parts of water;The nano ceramics grain is made of following methods:By kaolin,
Montmorillonite, aluminium oxide, attapulgite crushed 500 mesh sieves, obtained powder and neopelex, polyethylene glycol 400,
Water be mixed 2 it is small when after, spray drying obtains solid particle, solid particle is sintered at 900 DEG C 5 it is small when, after cooling, powder
It is broken to less than 100 nanometers and obtains the nano ceramics grain;The grain size of the fine sand is 300-500 mesh.
The preparation method of the ceramic tile adhesive mortar, comprises the following steps:
I heats water to 60 DEG C of constant temperature, adds in xanthans and vitamin, and stirring obtains solution A to after dissolving;
II disperses modified epoxy, castor oil polyoxyethylene ether, ethylene glycol using emulsion dispersion machine, until solution is transparent
Until, solution B is obtained, emulsion dispersion machine rate of dispersion is 3000rmp, when jitter time 0.5 is small;
III by solution A, solution B, nano zine oxide, hydroxylated cellulose, sodium methyl silicate, neopelex with
Wooden sodium sulfonate using emulsion dispersion machine disperse 0.5 it is small when, vacuumize to obtain mixing liquid C, emulsion dispersion machine rate of dispersion is
800rmp, the vacuum degree vacuumized are 0.9Mpa;
IV is uniformly mixed mixing liquid C with nano ceramics grain, fine sand, portland cement up to the Ceramic Tiles binding sand
Slurry.
Although the embodiments of the present invention have been disclosed as above, but its be not restricted in specification and embodiment it is listed
With it can be fully applied to various fields suitable for the present invention, for those skilled in the art, can be easily
Realize other modification, therefore without departing from the general concept defined in the claims and the equivalent scope, it is of the invention and unlimited
In specific details and shown here as the embodiment with description.