CN107286720A - The inner wall putty powder and its production technology of a kind of environmental protection - Google Patents
The inner wall putty powder and its production technology of a kind of environmental protection Download PDFInfo
- Publication number
- CN107286720A CN107286720A CN201710695279.3A CN201710695279A CN107286720A CN 107286720 A CN107286720 A CN 107286720A CN 201710695279 A CN201710695279 A CN 201710695279A CN 107286720 A CN107286720 A CN 107286720A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- environmental protection
- wall putty
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inner wall putty powder of environmental protection and its production technology, including base-material, filler and auxiliary agent, wherein, the base-material includes the component of following parts by weight：24 parts of 10 15 parts of latex powder and organogel；The filler includes the component of following parts by weight：50 60 parts of 40 50 parts of calcium carbonate, 20 25 parts of diatomite and dry powder；The auxiliary agent includes the component of following parts by weight：5 10 parts of 5 10 parts of nano zine oxide, 5 10 parts of methyl cellulose ether and bamboo charcoal powder.According to the inner wall putty powder obtained by raw material proportioning provided by the present invention and production technology, not only adhesive force is good, and cracking resistance is good, and can adjust indoor humidity, purifies air, environmental protection.
Description
Technical field
The present invention relates to powder of lacquer putty for use on field, the inner wall putty powder and its production technology of specifically a kind of environmental protection.
Background technology
A kind of material of decoration property of smooth surface of wall, is a kind of thick slurry coating material during putty, is that coating is whitewashed a wall money
A kind of essential product.Painting is imposed on priming paint or directly applied and imposes on object, for eliminating on coated article surface height not
Flat defect.
At present, requirement of the internal wall finishing to environmental protection is more and more stricter, the health of the life of this people of this direct relation.And city
Some putty for interior wall powder on field, through after a while when after, be easy for that cracking, the phenomenon such as come off, destroy wall
The overall appearance in face, and the poisonous and harmful substance contained in powder of lacquer putty for use on, can be directly emitted to damage human body in air,
Environment is polluted, is detrimental to health.
The content of the invention
The present invention provides inner wall putty powder and its life of a kind of good adhesive force, environmental protection and the environmental protection of fire protection flame retarding
Production. art.
The present invention solves above-mentioned technical problem and adopted the technical scheme that：A kind of inner wall putty powder of environmental protection, including
Base-material, filler and auxiliary agent, wherein, the base-material includes the component of following parts by weight：10-15 parts of latex powder and organogel 2-4
Part；The filler includes the component of following parts by weight：50-60 parts of 40-50 parts of calcium carbonate, 20-25 parts of diatomite and dry powder；Institute
Stating auxiliary agent includes the component of following parts by weight：5-10 parts of 5-10 parts of nano zine oxide, 5-10 parts of methyl cellulose ether and bamboo charcoal powder.
Further, the diatomaceous particle diameter is 7-10 microns.
Further, the ratio of the inner wall putty powder and water is 1：0.5.
Further, the particle diameter of the Paris white is 300-350 mesh, and the particle diameter of the dry powder is 250-300 mesh.
Further, the organogel is starch or polished rice gel powder.
A kind of production technology of the inner wall putty powder of environmental protection, is mainly included the following steps that：
(1) crush：Calcium carbonate is broken into graininess with disintegrating machine, particle diameter is in 15-20mm；
(2) grind：Granular calcium carbonate is put into grinder, is ground, the particle diameter for making calcium carbonate is 300-350
Mesh；
(3) match：Base-material, filler and auxiliary agent are compared according to weight to be matched；
(4) base-material is mixed：Latex powder and organogel powder are added in batch mixer and mixed, primary mixing is formed
Material；
(5) filler is mixed：Calcium carbonate, diatomite and dry powder are added and mixed in batch mixer, two grades of mixing are formed
Material；
(6) auxiliary agent is mixed：Nano zine oxide, methyl cellulose ether and bamboo charcoal powder are added and mixed in mixer, shape
Into ultimate compound；
(7) drying process：Processing is dried in ultimate compound, finished product is formed；
(8) test package：Finished product is tested, bag is packaged into.
Further, the rotating speed of the base-material mixing is 60-120r/min, and mixing time is 20-40min.
Further, the mixing speed of the filler mixing is 60-120r/min, and mixing time is 40-60min.
Further, the mixing speed of the auxiliary agent mixing is 50-70r/min, and mixing time is 20-30min.
Further, the drying temperature of the drying process is 65-95 DEG C, and drying time is 25-45min.
Above-mentioned material and method are employed, the present invention can obtain a kind of good and environmental protection the inner wall putty powder of adhesive force,
The adhesive force of powder of lacquer putty for use on wherein can be improved due to the addition of polished rice gel powder in the powder of lacquer putty for use on, powder of lacquer putty for use on is not easy from wall
Face is peeled off, so as to improve the stability of powder of lacquer putty for use on；, can be in room air due to the addition of nano zine oxide in powder of lacquer putty for use on
Moisture absorption, storage simultaneously discharge in good time, so as to reach the function of regulation indoor humidity, and ensure that powder of lacquer putty for use on will not occur
The phenomenon of peeling, hollowing and cracking, prevents metope from going mouldy；Due to the addition of diatomite in powder of lacquer putty for use on, elimination can be played
Formaldehyde, purification air and the effect for adjusting humidity, and diatomite can be with releasing negative oxygen ion, and fire protection flame retarding is good, with killing
The function of bacterium deodorization；Due to the addition of bamboo charcoal powder in powder of lacquer putty for use on, can further improve powder of lacquer putty for use on purification air, eliminate peculiar smell,
The effect of the mould proof and antibacterial deinsectization of moisture absorption；Due to the addition of wood fibre in powder of lacquer putty for use on, the water-retaining property of powder of lacquer putty for use on can be improved, is entered
One step prevents the cracking of powder of lacquer putty for use on wall, strengthens adhesive ability.
Embodiment
In order that present disclosure is easier to be clearly understood, below according to specific embodiment, to the green of the present invention
The inner wall putty powder and its production technology that colour circle is protected are described in further detail.
Embodiment one：
A kind of inner wall putty powder of environmental protection, including base-material, filler and auxiliary agent, wherein, the base-material includes following heavy
Measure the component of part：2 parts of 10 parts of latex powder and organogel；The filler includes the component of following parts by weight：40 parts of calcium carbonate, silicon
50 parts of 20 parts of diatomaceous earth and dry powder；The auxiliary agent includes the component of following parts by weight：5 parts of nano zine oxide, methyl cellulose ether 5
5 parts of part and bamboo charcoal powder.
Embodiment 2：
A kind of inner wall putty powder of environmental protection, including base-material, filler and auxiliary agent, wherein, the base-material includes following heavy
Measure the component of part：4 parts of 15 parts of latex powder and organogel；The filler includes the component of following parts by weight：50 parts of calcium carbonate, silicon
60 parts of 25 parts of diatomaceous earth and dry powder；The auxiliary agent includes the component of following parts by weight：10 parts of nano zine oxide, methyl cellulose ether
10 parts and 10 parts of bamboo charcoal powder.
Embodiment three：
A kind of inner wall putty powder of environmental protection, including base-material, filler and auxiliary agent, wherein, the base-material includes following heavy
Measure the component of part：3 parts of 12.5 parts of latex powder and organogel；The filler includes the component of following parts by weight：45 parts of calcium carbonate,
55 parts of 22.5 parts of diatomite and dry powder；The auxiliary agent includes the component of following parts by weight：7.5 parts of nano zine oxide, methyl are fine
7.5 parts of 7.5 parts of the plain ether of dimension and bamboo charcoal powder.
Example IV：
A kind of inner wall putty powder of environmental protection, including base-material, filler and auxiliary agent, wherein, the base-material includes following heavy
Measure the component of part：3.5 parts of 13 parts of latex powder and organogel；The filler includes the component of following parts by weight：47 parts of calcium carbonate,
57 parts of 23 parts of diatomite and dry powder；The auxiliary agent includes the component of following parts by weight：8 parts of nano zine oxide, methylcellulose
8 parts of 8 parts of ether and bamboo charcoal powder.
In embodiment one, two, three and four, diatomaceous particle diameter is 7-10 microns, can increase the exquisiteness of powder of lacquer putty for use on,
Diatomite bare area is added, the efficiency and effect of purification air is improved.
The ratio of inner wall putty powder and water is 1：0.5, adhesive force of the powder of lacquer putty for use in metope can be increased.
The particle diameter of the Paris white is 300-350 mesh, and the particle diameter of the dry powder is 250-300 mesh, can be increased greasy
The exquisiteness and flatness of sub- powder.
The organogel is starch or polished rice gel powder, can increase the adhesive force of powder of lacquer putty for use on, make powder of lacquer putty for use on surface thin
Greasy, stability is good.
Embodiment five：
A kind of production technology of the inner wall putty powder of environmental protection, is mainly included the following steps that：
(1) crush：Calcium carbonate is broken into graininess with disintegrating machine, particle diameter is in 15-20mm；
Block calcium carbonate can be broken into graininess, the convenient grinding for carrying out next step by step (1).
(2) grind：Granular calcium carbonate is put into grinder, is ground, the particle diameter for making calcium carbonate is 300-350
Mesh；
Step further pulverizes granular calcium carbonate in (2), convenient to add in powder of lacquer putty for use on, improves powder of lacquer putty for use on
Exquisiteness, and it is filtered after the completion of grinding, the granular impurity mixed in powder of going out, improve powder of lacquer putty for use on
Quality.
(3) match：Base-material, filler and auxiliary agent are compared according to weight to be matched；
(4) base-material is mixed：Latex powder and organogel powder are added in batch mixer and mixed, primary mixing is formed
Material, rotating speed is 60-120r/min, and mixing time is 20-40min.
Step is first mixed base-material in (4), is easy to base-material to be evenly distributed in powder of lacquer putty for use on, improves its adhesive force,
Avoid the occurrence of the situation of cracking.
(5) filler is mixed：Calcium carbonate, diatomite and dry powder are added and mixed in batch mixer, two grades of mixing are formed
Material, mixing speed is 60-120r/min, and mixing time is 40-60min.
Step (5) is to be mixed filler, makes base-material and filler well mixed.
(6) auxiliary agent is mixed：Nano zine oxide, methyl cellulose ether and bamboo charcoal powder are added and mixed in mixer, shape
Into ultimate compound, the mixing speed of auxiliary agent mixing is 50-70r/min, and mixing time is 20-30min.
Base-material, filler and auxiliary agent can be well mixed by step (6).
(7) drying process：Processing is dried in ultimate compound, the drying temperature of drying process is 65-95 DEG C, is dried
Time is 25-45min, forms finished product；
Step (7) is, for moisture unnecessary in inner wall putty powder of going out, it is kept drying, is easy to preserve, and
Under the drying temperature simultaneously, it is ensured that dry efficiency will not be impacted to powder of lacquer putty for use on.
(8) test package：Finished product is tested, bag is packaged into.
Inspection in step (8) includes composition inspection, mixture homogeneity are examined and aridity is examined etc., wraps after the assay was approved
Bag is dressed up, the quality of inner wall putty powder is further ensured that.
In addition, in step (4), (5) and (6), the setting of mixing speed and mixing time, it is ensured that in the most short time
It is interior, fully component is well mixed, the uniformity and quality of inner wall putty powder is further improved.
Interior wall is made according to the production technology described by embodiment five in raw material proportioning in embodiment one, two, three and four
Powder of lacquer putty for use on, after testing, institute's inspection project meet《Architecture indoor putty》JG/T3049-1998 standards and《Paint film antibacterial and mouldproof is surveyed
Method for testing》The requirement of HG/T3950-2007 standards, it is qualified.
Wherein Detection results are as follows：
The inner wall putty powder that quality proportioning and production technology according to the present invention make, not only adhesive force is good, crack resistance
Can be good, and indoor humidity can be adjusted, purify air, environmental protection.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effect carry out
It is further described, should be understood that the specific embodiment that the foregoing is only the present invention, is not limited to this
Invention, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc. should be included in this hair
Within bright protection domain.
Claims (10)
1. a kind of inner wall putty powder of environmental protection, it is characterised in that：Including base-material, filler and auxiliary agent, wherein,
The base-material includes the component of following parts by weight：2-4 parts of 10-15 parts of latex powder and organogel；
The filler includes the component of following parts by weight：50-60 parts of 40-50 parts of calcium carbonate, 20-25 parts of diatomite and dry powder；
The auxiliary agent includes the component of following parts by weight：5-10 parts of nano zine oxide, 5-10 parts of methyl cellulose ether and bamboo charcoal powder
5-10 parts.
2. the inner wall putty powder of environmental protection according to claim 1, it is characterised in that：The diatomaceous particle diameter is 7-
10 microns.
3. the inner wall putty powder of environmental protection according to claim 1, it is characterised in that：The inner wall putty powder and water
Ratio is 1：0.5.
4. the inner wall putty powder of environmental protection according to claim 1, it is characterised in that：The particle diameter of the Paris white is
300-350 mesh, the particle diameter of the dry powder is 250-300 mesh.
5. the inner wall putty powder of environmental protection according to claim 1, it is characterised in that：The organogel be starch or
Polished rice gel powder.
6. a kind of production technology of the inner wall putty powder of environmental protection, it is characterised in that：Mainly include the following steps that：
（1）It is broken：Calcium carbonate is broken into graininess with disintegrating machine, particle diameter is in 15-20mm；
（2）Grinding：Granular calcium carbonate is put into grinder, is ground, the particle diameter for making calcium carbonate is 300-350 mesh；
（3）Proportioning：Base-material, filler and auxiliary agent are compared according to weight to be matched；
（4）Base-material is mixed：Latex powder and organogel powder are added in batch mixer and mixed, primary compound is formed；
（5）Filler is mixed：Calcium carbonate, diatomite and dry powder are added and mixed in batch mixer, two grades of compounds are formed；
（6）Auxiliary agent is mixed：Nano zine oxide, methyl cellulose ether and bamboo charcoal powder are added and mixed in mixer, is formed eventually
Pole compound；
（7）Drying process：Processing is dried in ultimate compound, finished product is formed；
（8）Test package：Finished product is tested, bag is packaged into.
7. the production technology of the inner wall putty powder of environmental protection according to claim 6, it is characterised in that：The base-material is mixed
The rotating speed of conjunction is 60-120r/min, and mixing time is 20-40min.
8. the production technology of the inner wall putty powder of environmental protection according to claim 6, it is characterised in that：The filler is mixed
The mixing speed of conjunction is 60-120r/min, and mixing time is 40-60min.
9. the production technology of the inner wall putty powder of environmental protection according to claim 6, it is characterised in that：The auxiliary agent is mixed
The mixing speed of conjunction is 50-70r/min, and mixing time is 20-30min.
10. the production technology of the inner wall putty powder of environmental protection according to claim 6, it is characterised in that：The drying
The drying temperature of processing is 65-95 DEG C, and drying time is 25-45min.