CN107325620A - Exterior wall powder of lacquer putty for use on - Google Patents
Exterior wall powder of lacquer putty for use on Download PDFInfo
- Publication number
- CN107325620A CN107325620A CN201710782882.5A CN201710782882A CN107325620A CN 107325620 A CN107325620 A CN 107325620A CN 201710782882 A CN201710782882 A CN 201710782882A CN 107325620 A CN107325620 A CN 107325620A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- lacquer putty
- exterior wall
- zine oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of exterior wall powder of lacquer putty for use on, it is made from the following raw materials in parts by weight：45 60 parts of modified talc powder, 10 40 parts of carbonic acid fine particle calcium carbonate, 20 30 parts of sierozem power, palygorskite clay：25 35 parts；Bagasse fibre：38 parts；Sodium alginate：25 parts to 35 parts；1.5 2.5 parts of hydroxypropyl methyl cellulose, 10 15 parts of nano zine oxide, 5 10 parts of silica flour, 25 parts of starch alkenyl succinate ester, 23 parts of rubber powder, 0.5 1 parts of pigment.
Description
Technical field
The invention belongs to decoration material field, and in particular to a kind of exterior wall powder of lacquer putty for use on.
Background technology
Putty is a kind of decoration gel material of smooth surface of wall, is a kind of thick slurry coating material, and being must not before coating is painted
A kind of product that can lack；The purpose of brushing putty is the curve deviation of the hole for filling construction surface and correction construction surface, to obtain
Smoothly, uniform lacquer painting lay a solid foundation, and traditional powder of lacquer putty for use on so just inevitably exists often using cement as cementitious matter
Cement base material is not in that the phenomenons such as peeling, hollowing and cracking occur under the long-term corrosion of vapor in atmosphere.
The content of the invention
For above technical deficiency, the invention provides a kind of exterior wall powder of lacquer putty for use on, solve in background technology and be previously mentioned
Existing powder of lacquer putty for use on the problem of exist.
The present invention is achieved in that a kind of exterior wall powder of lacquer putty for use on, is made from the following raw materials in parts by weight：Modified talc powder
45-60 parts, 10-40 parts of carbonic acid fine particle calcium carbonate, 20-30 parts of sierozem power, palygorskite clay：25-35 parts；Bagasse fibre：3-8 parts；Sea
Algin：25 parts to 35 parts；1.5-2.5 parts of hydroxypropyl methyl cellulose, 10-15 parts of nano zine oxide, 5-10 parts of silica flour, alkene
2-5 parts of base succinic acid starch ester, 2-3 parts of rubber powder, 0.5-1 parts of pigment.
Further, the particle size range of the nano zine oxide is 2~40 nanometers, specific surface area be 51.5 squares of faces/gram,
The rubber powder is any one in acrylic resin, polyvinyl alcohol rubber powder or two kinds of mixtures；The hydroxypropyl methyl fiber
Plain viscosity is not less than 50,000 mpas.
Further, described parts by weight of raw materials is as follows：45 parts of modified talc powder, 40 parts of carbonic acid fine particle calcium carbonate, 25 parts of sierozem power,
30 parts of palygorskite clay；6 parts of bagasse fibre；30 parts of Na-alginate；1.5 parts of hydroxypropyl methyl cellulose, nano zine oxide 10
Part, 8 parts of silica flour, 2 parts of starch alkenyl succinate ester, 2 parts of rubber powder, 0.5 part of pigment.
Due to using above-mentioned technical proposal, the present invention has the advantages that：
1st, due to adding palygorskite powder, it not only adds the caking ability and water resistance and palygorskite dried bean noodles of powder of lacquer putty for use on
Dry shrinkage factor is small, and cracking is not produced；
2nd, due to adding bagasse fibre, bagasse fibre is as toughener, and it not only adds the crack resistance of putty
And natural environmental-protective；
3rd, due to adding hydroxypropyl methyl cellulose, as dispersant and stabilizer, each raw material is made in water or organic molten
All there is good intermiscibility in agent；
4th, due to adding nano zine oxide, the specific surface area of its super large can be by the moisture absorption in air, storage simultaneously
Discharge in good time, automatically adjust indoor humidity, powder of lacquer putty for use on is not occurred peeling, hollowing and cracking etc. because of humid air existing
As；Various pernicious gases, smoke and peculiar smell can be adsorbed and decompose simultaneously, with purification air, deodorization is dispelled the function of taste.；
5th, due to adding Na-alginate, Na-alginate natural environmental-protective and improves the viscous of putty as bonding agent, not only
Connecing property；
6th, due to adding silica flour, then the hardness of powder of lacquer putty for use on is more effectively strengthened.
Embodiment
In order that technical problems, technical solutions and advantages to be solved are more clearly understood, tie below
Embodiment is closed, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only to explain
The present invention, is not intended to limit the present invention.
Embodiment 1：A kind of exterior wall powder of lacquer putty for use on that the present invention is provided, is made from the following raw materials in parts by weight：Modified talc
45 parts of powder, 40 parts of carbonic acid fine particle calcium carbonate, 25 parts of sierozem power, 30 parts of palygorskite clay；6 parts of bagasse fibre；30 parts of sodium alginate；Hydroxypropyl
1.5 parts of ylmethyl cellulose, 10 parts of nano zine oxide, 8 parts of silica flour, 2 parts of starch alkenyl succinate ester, 2 parts of rubber powder, pigment
0.5 part.
Wherein, the particle size range of the nano zine oxide is 2~40 nanometers, specific surface area be 51.5 squares of faces/gram, it is described
Rubber powder is any one in acrylic resin, polyvinyl alcohol rubber powder or two kinds of mixtures；The hydroxypropyl methyl cellulose glues
Degree is not less than 50,000 mpas.
Preparation method is：Will remodeling talcum powder, carbonic acid fine particle calcium carbonate, sierozem power, palygorskite clay, bagasse fibre, alginic acid
Sodium, nano zine oxide and silica flour are added in mixer, are stirred after being well mixed within 20 minutes, are sequentially added carboxymethyl cellulose
Element, starch alkenyl succinate ester, rubber powder, triclosan, pigment continue to stir 10 minutes, are sufficiently mixed it, i.e., into mixer
.
The powder of lacquer putty for use on as made from the above method, the caking ability and water resistance of powder of lacquer putty for use on is stronger, and drying shrinkage is small, does not produce
Cracking, the crack resistance of putty is also greatly enhanced and natural environmental-protective, due to adding hydroxypropyl methyl cellulose, is used as dispersant
And stabilizer, make each raw material that all there is good intermiscibility, due to adding nano zine oxide, its super large in water or organic solvent
Specific surface area, can by the moisture absorption in air, store and discharge in good time, automatically adjust indoor humidity, make powder of lacquer putty for use on not
Can occur the phenomenons such as peeling, hollowing and cracking because of humid air；It can adsorb and decompose various pernicious gases, smoke simultaneously
And peculiar smell, with purification air, deodorization is dispelled the function of taste.Due to adding Na-alginate, Na-alginate is as bonding agent, not only
Natural environmental-protective and the cementability for improving putty, due to adding silica flour, then more effectively strengthen the hardness of powder of lacquer putty for use on.
By above-described embodiment, the purpose of the present invention is reached by fully effective.One of ordinary skilled in the art
It should be understood that the present invention includes but does not limit the content described in embodiment above.Any modification without departing from the present invention is all
It is included within the scope of claims.
Claims (3)
1. a kind of exterior wall powder of lacquer putty for use on, it is characterised in that be made from the following raw materials in parts by weight：45-60 parts of modified talc powder, carbon
Sour fine particle calcium carbonate 10-40 parts, 20-30 parts of sierozem power, palygorskite clay：25-35 parts；Bagasse fibre：3-8 parts；Sodium alginate：25 parts
To 35 parts；1.5-2.5 parts of hydroxypropyl methyl cellulose, 10-15 parts of nano zine oxide, 5-10 parts of silica flour, alkenyl succinic acid forms sediment
2-5 parts of powder ester, 2-3 parts of rubber powder, 0.5-1 parts of pigment.
2. exterior wall powder of lacquer putty for use on according to claim 1, it is characterised in that：The particle size range of the nano zine oxide is 2
~40 nanometers, specific surface area be 51.5 squares of faces/gram, the rubber powder is any one in acrylic resin, polyvinyl alcohol rubber powder
Plant or two kinds of mixtures；The hydroxypropyl methyl cellulose viscosity is not less than 50,000 mpas.
3. exterior wall powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that described parts by weight of raw materials is as follows：It is modified
45 parts of talcum powder, 40 parts of carbonic acid fine particle calcium carbonate, 25 parts of sierozem power, 30 parts of palygorskite clay；6 parts of bagasse fibre；30 parts of sodium alginate；
1.5 parts of hydroxypropyl methyl cellulose, 10 parts of nano zine oxide, 8 parts of silica flour, 2 parts of starch alkenyl succinate ester, 2 parts of rubber powder, face
0.5 part of material.