CN107652745A - A kind of waterproof inner wall putty powder and preparation method thereof - Google Patents
A kind of waterproof inner wall putty powder and preparation method thereof Download PDFInfo
- Publication number
- CN107652745A CN107652745A CN201711134640.1A CN201711134640A CN107652745A CN 107652745 A CN107652745 A CN 107652745A CN 201711134640 A CN201711134640 A CN 201711134640A CN 107652745 A CN107652745 A CN 107652745A
- Authority
- CN
- China
- Prior art keywords
- parts
- alkenyl succinate
- waterproof inner
- succinate ester
- wall putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of waterproof inner wall putty powder and preparation method thereof, belong to building material technical field.It is made up of the raw material of following parts by weight：3~9 parts of 5~15 parts of starch alkenyl succinate ester, 3~9 parts of nano zine oxide, 5~9 parts of hydroxypropyl methyl cellulose, 4~12 parts of bagasse fibre, 4~12 parts of Sodium Polyacrylate, 4~8 parts of talcum powder, 4~10 parts of aluminium-magnesium silicate, 4~10 parts of palygorskite clay and starch alkenyl succinate ester.The powder of lacquer putty for use on of the present invention, water-fastness, easy construction, hardness is high, film forming is fast, and the holding time is long, easy to use, stable performance, and preparation method is simple, easy to use, cost is low, wide market, is adapted to large-scale production.
Description
Technical field
The present invention relates to a kind of waterproof inner wall putty powder and preparation method thereof, belong to building material technical field.
Background technology
Powder of lacquer putty for use on is a kind of ornament materials of smooth surface of wall, is using inorganic coagulation material as base-material, is equipped with and coheres material
Material and other auxiliary agent retrofits form, and are a kind of products essential before coating paints, and painting imposes on priming paint or directly painting
Impose on object, to remove the defects of being uneven on coated article surface.Powder of lacquer putty for use on is extensive as interior wall packing material
Use.But existing interiro wall latex paint powder of lacquer putty for use on causes subsequent construction efflorescence occur there is the shortcomings that water-wash resistance difference
Phenomenon.
The content of the invention
The purpose of the present invention is to make up the deficiencies in the prior art, there is provided a kind of waterproof inner wall putty powder and preparation method thereof.
The powder of lacquer putty for use on of the present invention, water-fastness, easy construction, hardness is high, film forming is fast, and the holding time is long, easy to use, stable performance.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of waterproof inner wall putty powder, by following parts by weight
Several raw materials are made：5~15 parts of starch alkenyl succinate ester, 3~9 parts of nano zine oxide, 5~9 parts of hydroxypropyl methyl cellulose,
4~12 parts of bagasse fibre, 4~12 parts of Sodium Polyacrylate, 4~8 parts of talcum powder, 4~10 parts of aluminium-magnesium silicate, palygorskite clay 4
~10 parts and 3~9 parts of starch alkenyl succinate ester.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight：10 parts of starch alkenyl succinate ester, 6 parts of nano zine oxide, hydroxyl
7 parts of propyl methocel, 8 parts of bagasse fibre, 8 parts of Sodium Polyacrylate, 6 parts of talcum powder, 7 parts of aluminium-magnesium silicate, palygorskite glue
6 parts of 7 parts of soil and starch alkenyl succinate ester.
Further, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000 mpas.
A kind of preparation method of waterproof inner wall putty powder, comprises the following steps：Weigh the raw material of following parts by weight：Alkenyl
5~15 parts of succinic acid starch ester, 3~9 parts of nano zine oxide, 5~9 parts of hydroxypropyl methyl cellulose, bagasse fibre 4~12
Part, 4~12 parts of Sodium Polyacrylate, 4~8 parts of talcum powder, 4~10 parts of aluminium-magnesium silicate, 4~10 parts of palygorskite clay and alkenyl succinate
3~9 parts of acid-starch ester, after being well mixed, produce the waterproof inner wall putty powder.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the parts by weight of the raw material are：10 parts of starch alkenyl succinate ester, 6 parts of nano zine oxide, hydroxypropyl
7 parts of methylcellulose, 8 parts of bagasse fibre, 8 parts of Sodium Polyacrylate, 6 parts of talcum powder, 7 parts of aluminium-magnesium silicate, 7 parts of palygorskite clay
With 6 parts of starch alkenyl succinate ester.
Further, the viscosity of the hydroxypropyl methyl cellulose is not less than 50,000 mpas.
A kind of application method of waterproof inner wall putty powder as described above, by powder of lacquer putty for use on：Water=1：0.4~0.6 weight ratio,
After well mixed.
The beneficial effects of the invention are as follows：
(1) powder of lacquer putty for use on of the invention, water-fastness, easy construction, hardness is high, film forming is fast, and the holding time it is long, it is easy to use,
Stable performance.
(2) preparation method of the invention is simple, easy to use, cost is low, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1：
The waterproof inner wall putty powder of the present embodiment, is made up of the raw material of following weight：Starch alkenyl succinate ester 5kg, receive
Rice zinc oxide 9kg, hydroxypropyl methyl cellulose 5kg, bagasse fibre 12kg, Sodium Polyacrylate 4kg, talcum powder 8kg, magnesium silicate
Aluminium 4kg, palygorskite clay 10kg and starch alkenyl succinate ester 3kg.
The preparation method of the waterproof inner wall putty powder of above-described embodiment, comprises the following steps：Weigh the raw material of following weight：
Starch alkenyl succinate ester 5kg, nano zine oxide 9kg, hydroxypropyl methyl cellulose 5kg, bagasse fibre 12kg, polyacrylic acid
Sodium 4kg, talcum powder 8kg, aluminium-magnesium silicate 4kg, palygorskite clay 10kg and starch alkenyl succinate ester 3kg, wherein, the hydroxypropyl
The viscosity of ylmethyl cellulose is not less than 50,000 mpas, after being well mixed, produces the waterproof inner wall putty powder.
The application method of above-mentioned waterproof inner wall putty powder, by powder of lacquer putty for use on：Water=1：0.4 weight ratio, after being well mixed i.e.
Can.
Embodiment 2：
The waterproof inner wall putty powder of the present embodiment, is made up of the raw material of following parts by weight：Starch alkenyl succinate ester
10kg, nano zine oxide 6kg, hydroxypropyl methyl cellulose 7kg, bagasse fibre 8kg, Sodium Polyacrylate 8kg, talcum powder 6kg,
Aluminium-magnesium silicate 7kg, palygorskite clay 7kg and starch alkenyl succinate ester 6kg, wherein, the hydroxypropyl methyl cellulose is glued
Degree is not less than 50,000 mpas.
The preparation method of the waterproof inner wall putty powder of above-described embodiment, comprises the following steps：Weigh the raw material of following weight：
Starch alkenyl succinate ester 10kg, nano zine oxide 6kg, hydroxypropyl methyl cellulose 7kg, bagasse fibre 8kg, polyacrylic acid
Sodium 8kg, talcum powder 6kg, aluminium-magnesium silicate 7kg, palygorskite clay 7kg and starch alkenyl succinate ester 6kg, wherein, the hydroxypropyl
The viscosity of ylmethyl cellulose is not less than 50,000 mpas, after being well mixed, produces the waterproof inner wall putty powder.
The application method of above-mentioned waterproof inner wall putty powder, by powder of lacquer putty for use on：Water=1：0.5 weight ratio, after being well mixed i.e.
Can.
Embodiment 3：
The waterproof inner wall putty powder of the present embodiment, is made up of the raw material of following parts by weight：Starch alkenyl succinate ester
15kg, nano zine oxide 3kg, hydroxypropyl methyl cellulose 9kg, bagasse fibre 4kg, Sodium Polyacrylate 12kg, talcum powder
4kg, aluminium-magnesium silicate 10kg, palygorskite clay 4kg and starch alkenyl succinate ester 9kg, wherein, the hydroxypropyl methyl cellulose
Viscosity be not less than 50,000 mpas.
The preparation method of the waterproof inner wall putty powder of above-described embodiment, comprises the following steps：Weigh the raw material of following weight：
Starch alkenyl succinate ester 15kg, nano zine oxide 3kg, hydroxypropyl methyl cellulose 9kg, bagasse fibre 4kg, polyacrylic acid
Sodium 12kg, talcum powder 4kg, aluminium-magnesium silicate 10kg, palygorskite clay 4kg and starch alkenyl succinate ester 9kg, wherein, the hydroxyl
The viscosity of propyl methocel is not less than 50,000 mpas, after being well mixed, produces the waterproof inner wall putty powder.
The application method of above-mentioned waterproof inner wall putty powder, by powder of lacquer putty for use on：Water=1：0.6 weight ratio, after being well mixed i.e.
Can.
The performance detection of embodiment 1-3 waterproof inner wall putty powder is as shown in table 1.
The performance detection of table 1
As can be seen here, waterproof inner wall putty powder of the invention, water-fastness, easy construction, hardness is high, film forming is fast, and during preservation
Between long, easy to use, stable performance.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of waterproof inner wall putty powder, it is characterised in that be made up of the raw material of following parts by weight：Starch alkenyl succinate ester
5~15 parts, 3~9 parts of nano zine oxide, 5~9 parts of hydroxypropyl methyl cellulose, 4~12 parts of bagasse fibre, Sodium Polyacrylate 4
~12 parts, 4~8 parts of talcum powder, 4~10 parts of aluminium-magnesium silicate, 4~10 parts of palygorskite clay and starch alkenyl succinate ester 3~9
Part.
2. a kind of waterproof inner wall putty powder according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into：10 parts of starch alkenyl succinate ester, 6 parts of nano zine oxide, 7 parts of hydroxypropyl methyl cellulose, 8 parts of bagasse fibre, poly- third
6 parts of 8 parts of olefin(e) acid sodium, 6 parts of talcum powder, 7 parts of aluminium-magnesium silicate, 7 parts of palygorskite clay and starch alkenyl succinate ester.
A kind of 3. waterproof inner wall putty powder according to claim 1 or 2, it is characterised in that the hydroxypropyl methyl fiber
The viscosity of element is not less than 50,000 mpas.
4. a kind of preparation method of waterproof inner wall putty powder, it is characterised in that comprise the following steps：Weigh following parts by weight
Raw material：5~15 parts of starch alkenyl succinate ester, 3~9 parts of nano zine oxide, 5~9 parts of hydroxypropyl methyl cellulose, bagasse are fine
Dimension 4~12 parts, 4~12 parts of Sodium Polyacrylate, 4~8 parts of talcum powder, 4~10 parts of aluminium-magnesium silicate, 4~10 parts of palygorskite clay and
3~9 parts of starch alkenyl succinate ester, after being well mixed, produce the waterproof inner wall putty powder.
A kind of 5. preparation method of waterproof inner wall putty powder according to claim 4, it is characterised in that the weight of the raw material
Measuring number is：10 parts of starch alkenyl succinate ester, 6 parts of nano zine oxide, 7 parts of hydroxypropyl methyl cellulose, bagasse fibre 8
Part, 8 parts of Sodium Polyacrylate, 6 parts of talcum powder, 7 parts of aluminium-magnesium silicate, 7 parts of palygorskite clay and 6 parts of starch alkenyl succinate ester.
A kind of 6. preparation method of waterproof inner wall putty powder according to claim 4 or 5, it is characterised in that the hydroxypropyl
The viscosity of ylmethyl cellulose is not less than 50,000 mpas.