CN103351699A - Water resistance anti-cracking putty and production method thereof - Google Patents
Water resistance anti-cracking putty and production method thereof Download PDFInfo
- Publication number
- CN103351699A CN103351699A CN 201310330821 CN201310330821A CN103351699A CN 103351699 A CN103351699 A CN 103351699A CN 201310330821 CN201310330821 CN 201310330821 CN 201310330821 A CN201310330821 A CN 201310330821A CN 103351699 A CN103351699 A CN 103351699A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- vermiculite
- titanium dioxide
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a water resistance anti-cracking putty and a production method thereof. The water resistance anti-cracking putty comprises, by weight, 20-30 parts of ash calcium powder, 10-15 parts of heavy calcium, 8-15 parts of vermiculite, 5-10 parts of plant fibers, 3-5 parts of a silicone-acrylic resin, 3-5 parts of a vinyl acetate-acrylate emulsion, 2-3 parts of polyvinyl alcohol, 10-20 parts of titanium dioxide powder, 20-40 parts of lime powder, and 1-3 parts of a diluent. According to the present invention, the organic materials such as the silicone-acrylic resin, the vinyl acetate-acrylate emulsion and the polyvinyl alcohol are added, such that the produced putty can resist fine cracks of buildings due to subsidence and other causes, does not contain toxic substances, does not release toxic gases, and has characteristics of green environmental protection, good water resistance, and good moisture resistance.
Description
Technical field:
The present invention relates to a kind of water-fast anti-crack mastic and preparation method thereof, belong to the construction material technical field.
Background technology:
Putty is a kind of decoration gel material of smooth surface of wall, is a kind of thick slurry coating material, is that coating whitewashes front requisite a kind of product.Be coated with to impose on the priming paint or directly be coated with and impose on the object, in order to remove rugged defective on the coated article surface.Adopt a small amount of lacquer base, mass filler and an amount of tinting pigment formulated, used pigment mainly is iron oxide red, carbon black, chrome yellow etc.Filler mainly is calcium bicarbonate, talcum powder etc.Can fill up the part has the working-surface of depression, also can strike off at all surfaces, normally after prime coat parches, is applied over the prime coat surface.Require that tack is good, do not crack in the bake process.Putty is as the basic unit of metope emulsion paint, so must possess water-repellancy, contacts with the direct of emulsion paint with isolated metope, prevent that metope from making moist and together emulsion paint come off.
Buildings is being because the problem such as structure sediment is using an end more tiny crackle can occur after the time, if putty elasticity not crackle immediately can highlight, affect the overall aesthetics of buildings use.
Summary of the invention:
The purpose of this invention is to provide a kind of water-fast anti-crack mastic and preparation method thereof, the putty water-tolerant of production, and can resist buildings because the fine cracks that the reasons such as sedimentation cause.
Above-mentioned purpose realizes by following technical scheme:
Water-fast anti-crack mastic, comprise grey calcium powder, coarse whiting, vermiculite, vegetable fibre, organosilicon acrylic resin, acrylate and vinyl acetate emulsion, polyvinyl alcohol, titanium dioxide, lime powder, thinner, the parts by weight of each component are grey calcium powder 20-30 part, coarse whiting 10-15 part, vermiculite 8-15 part, vegetable fibre 5-10 part, organosilicon acrylic resin 3-5 part, acrylate and vinyl acetate emulsion 3-5 part, polyvinyl alcohol 2-3 part, titanium dioxide 10-20 part, lime powder 20-40 part, thinner 1-3 part.
Described water-fast anti-crack mastic, described thinner is comprised of butylacetate, ethyl acetate, propylene dichloride and the pimelinketone of equivalent.
The preparation method of above-mentioned water-fast anti-crack mastic, the method comprises the steps:
(1) gets the raw materials ready, grey calcium powder, coarse whiting, vermiculite, vegetable fibre, titanium dioxide, lime powder are crushed to the 200-300 order for subsequent use;
(2) material loading, mixing: the raw material that crushes is got grey calcium powder 20-30 part, coarse whiting 10-15 part, vermiculite 8-15 part, vegetable fibre 5-10 part, titanium dioxide 10-20 part, lime powder 20-40 part according to parts by weight, add thinner 1-3 part, organosilicon acrylic resin 3-5 part, acrylate and vinyl acetate emulsion 3-5 part, polyvinyl alcohol 2-3 part, 5-10 minute mixing of water 80-100 part stirring;
(3) measure and pack.
Beneficial effect:
1. proportioning of the present invention is superior, organosilicon acrylic resin, acrylate and vinyl acetate emulsion, these organism of polyvinyl alcohol have been added, the fine cracks that the reasons such as sedimentation cause so that the putty of producing can be resisted buildings, and do not contain poisonous objectionable impurities, do not distribute toxic gas, environmental protection also has good waterproof, humidity resistance.
2. production technique of the present invention is simple, and production cost is low, is applicable to mass industrialized production.
Embodiment:
Embodiment 1:
Water-fast anti-crack mastic, comprise grey calcium powder, coarse whiting, vermiculite, vegetable fibre, organosilicon acrylic resin, acrylate and vinyl acetate emulsion, polyvinyl alcohol, titanium dioxide, lime powder, thinner, the parts by weight of each component are grey calcium powder 20-30 part, coarse whiting 10-15 part, vermiculite 8-15 part, vegetable fibre 5-10 part, organosilicon acrylic resin 3-5 part, acrylate and vinyl acetate emulsion 3-5 part, polyvinyl alcohol 2-3 part, titanium dioxide 10-20 part, lime powder 20-40 part, thinner 1-3 part.
Embodiment 2:
Embodiment 1 described water-fast anti-crack mastic, described thinner is comprised of butylacetate, ethyl acetate, propylene dichloride and the pimelinketone of equivalent.
The preparation method of above-mentioned water-fast anti-crack mastic, the method comprises the steps:
(1) gets the raw materials ready, grey calcium powder, coarse whiting, vermiculite, vegetable fibre, titanium dioxide, lime powder are crushed to the 200-300 order for subsequent use;
(2) material loading, mixing: the raw material that crushes is got grey calcium powder 20-30 part, coarse whiting 10-15 part, vermiculite 8-15 part, vegetable fibre 5-10 part, titanium dioxide 10-20 part, lime powder 20-40 part according to parts by weight, add thinner 1-3 part, organosilicon acrylic resin 3-5 part, acrylate and vinyl acetate emulsion 3-5 part, polyvinyl alcohol 2-3 part, 5-10 minute mixing of water 80-100 part stirring;
(3) measure and pack.
The disclosed technical scheme of the present invention program is not limited only to the disclosed technique means of above-mentioned technical characterictic, also comprises by above technical characterictic being equal to the technical scheme that replacement forms.Unaccomplished matter of the present invention belongs to those skilled in the art's common practise.
Claims (3)
1. water-fast anti-crack mastic, it is characterized in that: comprise grey calcium powder, coarse whiting, vermiculite, vegetable fibre, organosilicon acrylic resin, acrylate and vinyl acetate emulsion, polyvinyl alcohol, titanium dioxide, lime powder, thinner, the parts by weight of each component are grey calcium powder 20-30 part, coarse whiting 10-15 part, vermiculite 8-15 part, vegetable fibre 5-10 part, organosilicon acrylic resin 3-5 part, acrylate and vinyl acetate emulsion 3-5 part, polyvinyl alcohol 2-3 part, titanium dioxide 10-20 part, lime powder 20-40 part, thinner 1-3 part.
2. water-fast anti-crack mastic according to claim 1, it is characterized in that: described thinner is comprised of butylacetate, ethyl acetate, propylene dichloride and the pimelinketone of equivalent.
3. the preparation method of one kind water-fast anti-crack mastic, it is characterized in that: the method comprises the steps:
(1) gets the raw materials ready, grey calcium powder, coarse whiting, vermiculite, vegetable fibre, titanium dioxide, lime powder are crushed to the 200-300 order for subsequent use;
(2) material loading, mixing: the raw material that crushes is got grey calcium powder 20-30 part, coarse whiting 10-15 part, vermiculite 8-15 part, vegetable fibre 5-10 part, titanium dioxide 10-20 part, lime powder 20-40 part according to parts by weight, add thinner 1-3 part, organosilicon acrylic resin 3-5 part, acrylate and vinyl acetate emulsion 3-5 part, polyvinyl alcohol 2-3 part, 5-10 minute mixing of water 80-100 part stirring;
(3) measure and pack.