CN104119750A - Indoor decorative waterproof paint - Google Patents
Indoor decorative waterproof paint Download PDFInfo
- Publication number
- CN104119750A CN104119750A CN201410293399.7A CN201410293399A CN104119750A CN 104119750 A CN104119750 A CN 104119750A CN 201410293399 A CN201410293399 A CN 201410293399A CN 104119750 A CN104119750 A CN 104119750A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- add
- waterproof paint
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an indoor decorative waterproof paint which is prepared from the following raw materials in parts by weight: 63-70.2 parts of a water-based acrylic emulsion, 1.4-2 parts of chamomile essential oil, 2-3 parts of calcium aluminate, 1-2 parts of sodium methylene bisnaphthalene sulphonate, 1.2-2 parts of 2-dithienyl methyl glycolate, 2.3-4 parts of hexagonal boron nitride, 0.3-1 parts of beta-hydroxyalkyl amide, 0.1-0.2 part of sebacic dihydrazide, 7-11.2 parts of calcite in powder, 0.8-1.2 parts of acrylic acid, 0.6-1 part of aluminum stearate, 5-7 parts of coalescing agents and 10-15 parts of deionized water. The waterproof paint disclosed by the invention does not pollute the environment and is harmless to human body, and the added chamomile essential oil can improve the indoor environment to maintain indoor freshness, so that the waterproof paint is particularly suitable for being used as a paint for an exterior wall and has the effects of insulating and preserving heat, preventing water and decorating.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of indoor decoration type waterproof paint.
Background technology
Traditional water-proof material mainly contains the flexible waterproof materials such as waterproof roll, waterproof paint, sealing cement, and take cement matrix as main, adds the rigidity water-proofing material of liquid medicine agent and other auxiliary agent.The most of waterproofing work of China all adopts conventional waterproof material, conventional waterproof material exist loss of properties on aging, tensile strength low, to shortcomings such as temperature sensitives.Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, be out of shape, fracture, the phenomenon such as layering, for indoor waterproof, for complex-shaped place, constructional difficulties, and to Seepage, quality is more difficult to guarantee, people will spend a large amount of funds every several years and labor force reprocesses, and have not only confused people's orthobiosis, work and the production order, and affect the work-ing life of the indoor decoration type thing in whole building.In order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of indoor decoration type waterproof paint.
The present invention is achieved by the following technical solutions:
An indoor decoration type waterproof paint, it is comprised of the raw material of following weight parts:
Aqueous acrylic emulsion 63-70.2, Flos Matricariae chamomillae essential oil 1.4-2, calcium aluminate 2-3, sodium metnylene bis-naphthalene sulfonate 1-2,2,2-dithienyl methyl glycolate 1.2-2, hexagonal boron nitride 2.3-4, β-hydroxyalkyl amide 0.3-1, sebacic dihydrazide 0.1-0.2, calcite in powder 7-11.2, vinylformic acid 0.8-1.2, aluminum stearate 0.6-1, film coalescence aid 5-7, deionized water 10-15;
Described film coalescence aid is comprised of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 20-26, pyrrolidone hydroxy acid sodium 1-2, alkenyl succinic anhydride 0.5-1, glyceryl monostearate 0.3-1, kaempferol 0.1-0.2, sodium tetraborate 2-3, polyvinyl alcohol 3-4, gum arabic 1-2, calcium lactate 2-3, deionized water 60-70;
By calcium lactate and kaempferol mixing and stirring, add the 20-30% of above-mentioned deionized water weight, at 70-75 ℃, be uniformly mixed 5-7 minute, add gum arabic, be stirred to normal temperature, obtain gel;
Sodium tetraborate is mixed with alkenyl succinic anhydride, after stirring, add polyvinyl alcohol, at 60-70 ℃, be uniformly mixed 3-5 minute, join in remaining deionized water, be stirred to normal temperature, add each raw material of residue, 400-500 rev/min of dispersed with stirring 10-16 minute, obtains described film coalescence aid.
A preparation method for indoor decoration type waterproof paint, comprises the following steps:
By calcite in powder, calcium aluminate mixing and ball milling, add 2,2-dithienyl methyl glycolate, be uniformly mixed 2-4 minute at 50-60 ℃, join in deionized water, 40-60 rev/min is uniformly mixed 2-3 minute, adds β-hydroxyalkyl amide, stirs;
Hexagonal boron nitride is joined in aqueous acrylic emulsion, after stirring, add aluminum stearate, sebacic dihydrazide, be uniformly mixed 10-15 minute at 50-60 ℃;
Each raw material after above-mentioned processing is mixed with each raw material of residue, and 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described indoor decoration type waterproof paint.
Advantage of the present invention is:
Waterproof paint of the present invention is free from environmental pollution, and to human body, without injury, the Flos Matricariae chamomillae essential oil adding can improve indoor environment, pure and fresh in holding chamber, is specially applicable to doing interior wall coating, has heat-insulation and heat-preservation, waterproof, U.S. decorations effect.
Embodiment
Embodiment 1
An indoor decoration type waterproof paint, it by following weight parts (kilogram) raw material form:
Aqueous acrylic emulsion 70.2, Flos Matricariae chamomillae essential oil 1.4, calcium aluminate 2, sodium metnylene bis-naphthalene sulfonate 1-2,2,2-dithienyl methyl glycolate 1.2, hexagonal boron nitride 2.3, β-hydroxyalkyl amide 0.3, sebacic dihydrazide 0.2, calcite in powder 11.2, vinylformic acid 1.2, aluminum stearate 0.6, film coalescence aid 7, deionized water 15;
Described film coalescence aid is comprised of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 26, pyrrolidone hydroxy acid sodium 2, alkenyl succinic anhydride 0.5, glyceryl monostearate 0.3, kaempferol 0.2, sodium tetraborate 3, polyvinyl alcohol 3, gum arabic 2, calcium lactate 3, deionized water 70;
By calcium lactate and kaempferol mixing and stirring, add 30% of above-mentioned deionized water weight, at 75 ℃, be uniformly mixed 5 minutes, add gum arabic, be stirred to normal temperature, obtain gel;
Sodium tetraborate is mixed with alkenyl succinic anhydride, after stirring, add polyvinyl alcohol, at 60 ℃, be uniformly mixed 3 minutes, join in remaining deionized water, be stirred to normal temperature, add each raw material of residue, 500 revs/min of dispersed with stirring 16 minutes, obtain described film coalescence aid.
A preparation method for indoor decoration type waterproof paint, comprises the following steps:
By calcite in powder, calcium aluminate mixing and ball milling, add 2,2-dithienyl methyl glycolate, be uniformly mixed 2 minutes at 60 ℃, join in deionized water, 60 revs/min are uniformly mixed 2 minutes, add β-hydroxyalkyl amide, stir;
Hexagonal boron nitride is joined in aqueous acrylic emulsion, after stirring, add aluminum stearate, sebacic dihydrazide, be uniformly mixed 15 minutes at 60 ℃;
Each raw material after above-mentioned processing is mixed with each raw material of residue, and 500 revs/min of dispersed with stirring 30 minutes, obtain described indoor decoration type waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an indoor decoration type waterproof paint, is characterized in that what it was comprised of the raw material of following weight parts:
Aqueous acrylic emulsion 63-70.2, Flos Matricariae chamomillae essential oil 1.4-2, calcium aluminate 2-3, sodium metnylene bis-naphthalene sulfonate 1-2,2,2-dithienyl methyl glycolate 1.2-2, hexagonal boron nitride 2.3-4, β-hydroxyalkyl amide 0.3-1, sebacic dihydrazide 0.1-0.2, calcite in powder 7-11.2, vinylformic acid 0.8-1.2, aluminum stearate 0.6-1, film coalescence aid 5-7, deionized water 10-15;
Described film coalescence aid is comprised of the raw material of following weight parts:
Acrylate and vinyl acetate emulsion 20-26, pyrrolidone hydroxy acid sodium 1-2, alkenyl succinic anhydride 0.5-1, glyceryl monostearate 0.3-1, kaempferol 0.1-0.2, sodium tetraborate 2-3, polyvinyl alcohol 3-4, gum arabic 1-2, calcium lactate 2-3, deionized water 60-70;
By calcium lactate and kaempferol mixing and stirring, add the 20-30% of above-mentioned deionized water weight, at 70-75 ℃, be uniformly mixed 5-7 minute, add gum arabic, be stirred to normal temperature, obtain gel;
Sodium tetraborate is mixed with alkenyl succinic anhydride, after stirring, add polyvinyl alcohol, at 60-70 ℃, be uniformly mixed 3-5 minute, join in remaining deionized water, be stirred to normal temperature, add each raw material of residue, 400-500 rev/min of dispersed with stirring 10-16 minute, obtains described film coalescence aid.
2. a preparation method for indoor decoration type waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
By calcite in powder, calcium aluminate mixing and ball milling, add 2,2-dithienyl methyl glycolate, be uniformly mixed 2-4 minute at 50-60 ℃, join in deionized water, 40-60 rev/min is uniformly mixed 2-3 minute, adds β-hydroxyalkyl amide, stirs;
Hexagonal boron nitride is joined in aqueous acrylic emulsion, after stirring, add aluminum stearate, sebacic dihydrazide, be uniformly mixed 10-15 minute at 50-60 ℃;
Each raw material after above-mentioned processing is mixed with each raw material of residue, and 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described indoor decoration type waterproof paint.