CN108342130A - A kind of diatom Fender formaldehyde indoor coating preparation process - Google Patents
A kind of diatom Fender formaldehyde indoor coating preparation process Download PDFInfo
- Publication number
- CN108342130A CN108342130A CN201810075545.7A CN201810075545A CN108342130A CN 108342130 A CN108342130 A CN 108342130A CN 201810075545 A CN201810075545 A CN 201810075545A CN 108342130 A CN108342130 A CN 108342130A
- Authority
- CN
- China
- Prior art keywords
- agent
- diatom
- preparation process
- fender
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of diatom Fender formaldehyde indoor coating preparation process, the coating mainly includes the ingredient of following mass fraction：Diatomite 15 35%, dispersant 0.2 1%, surfactant 0.1 2%, modified starch 15 25%, synthetic emulsion 10 17%, Nano titanium dioxide 6 13%, talcum powder 5 12%, filler 0 30%, silver ion antimicrobial agent 0.5 2%, auxiliary agent 1 5% moistens and shows agent 0.3 0.5%, antifoaming agent 0.2 0.5%, 10 15 parts of activated carbon, the water of surplus, in short, the present invention has the advantages that extensive raw material sources, cheap, safety and environmental protection, formaldehyde adsorption ability are strong.
Description
Technical field
The invention belongs to decoration technology fields, and in particular to a kind of decorative paint preparation process more particularly to a kind of diatom
Fender formaldehyde indoor coating preparation process.
Background technology
Formaldehyde is a kind of clear, colorless, volatilization gas excitatory.It hangs up one's hat in the environment of formaldehyde, can go out
The serious stimulation of existing respiratory tract and oedema, eye shouting pain, headache, can also occur bronchial asthma.Direct skin contact formaldehyde can draw
Play dermatitis, color spot, necrosis.It is also possible to causing slow poisoning, there is mucous hyperemia, skin irritatin disease, allergic dermatitis.Seriously
Directly cause leukaemia and lymph cancer, cause life greatly to be threatened.Formaldehyde, as a kind of to the most harmful gas of the mankind
Body is known as indoor " taking life killer by force ", especially in China, seriously endangers new finishing family, especially children, pregnant woman, old man
Health.Existing coatings contain a large amount of formaldehyde components, there is larger harm to human body.
The main raw material(s) of diatom ooze is diatom mineral --- the diatomite formed after 1 years, and diatom is a kind of life
Algae in ocean, lake.The aquatic class biology that swims that diatom ooze is taken before living in millions of years --- diatom deposit and
At natural materials, main component is opal, be rich in multiple beneficial minerals, quality is light and soft, and electron microscope shows its grain
Sublist face has countless small holes, and for porosity up to 90% or more, specific surface area is up to 65 ㎡/g.It is outstanding point exactly this
Sub- sieve structure determines its unique function --- there is extremely strong physical adsorption property and ion-exchange performance, it is big in metope
Area is sprayed water, and can be absorbed a large amount of water, be illustrated that adsorptivity is extremely strong, and slowly sustained release negative oxygen ion, energy effectively decomposing formaldehyde,
Harmful carcinogen such as benzene, radon gas.
Invention content
There is provided it is an object of the invention to overcome the deficiencies in the prior art a kind of raw material sources it is extensive, it is cheap, peace
The diatom Fender formaldehyde indoor coating preparation process that loopful is protected, formaldehyde adsorption ability is strong.
The technical scheme is that：A kind of diatom Fender formaldehyde indoor coating preparation process, the coating include as follows
The raw material of proportioning forms：
Diatomite 15-35%, dispersant 0.2-1%, surfactant 0.1-2%, modified starch 15-25%, synthetic emulsion 10-
17%, Nano titanium dioxide 6-13%, talcum powder 5-12%, filler 0-30%, silver ion antimicrobial agent 0.5-2%, auxiliary agent 1-5%,
Profit shows agent 0.3-0.5%, and the preparation process of antifoaming agent 0.2-0.5%, 10-15 parts of activated carbon, the water of surplus, the coating include such as
Lower step：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Water is poured into container, and starts to stir, sequentially added during stirring modified starch, synthetic emulsion,
Talcum powder, and be sufficiently stirred；
Step 3：The mixed liquor that step 2 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add mixed-powder；
Step 4：Diatomite powder heating will be added in step 3 after twenty minutes, continue into mixed liquor successively filler, auxiliary agent, point
Powder, profit show agent and surfactant, and continue to stir；
Step 5：The mixed liquor obtained into step continues to add antifoaming agent, silver ion antimicrobial agent, Nano titanium dioxide successively,
And it stirs to raw material and is mixed thoroughly.
The synthetic emulsion is phenylpropyl alcohol compound emulsion and propyl alcohol lotion, the phenylpropyl alcohol compound emulsion and propyl alcohol lotion matter
Amount is than being 2-3:1.
The dispersant is SN-5040.
The profit shows agent AP-680.
The invention is realized in this way：The present invention use primary raw material of the diatom ooze as coating, diatom ooze it is main at
Divide diatomaceous pyroconductivity very low, be ideal heat preserving and insulating material in itself, there is extraordinary thermal and insulating performance, every
Thermal effect is 6 times of condition of equivalent thickness cement mortar, unique " molecular sieve " structure of diatom ooze, after the moisture in touching air
" water fall effect " is will produce, to constantly release the negative oxygen ion beneficial to human body, any heavy metal is free of, does not generate quiet
Electricity, floating dust are not easy to adhere to, and metope is permanently pure and fresh, and diatom ooze is not likely to produce electrostatic, and metope surface is not easy dust fall, and diatom ooze selects nothing
Machine coloring earth is mixed colours, and color is soft.When people lives in the room of coating diatom ooze, metope reflection light is naturally soft,
People does not allow to be also easy to produce visual fatigue, the eyesight of effective protection you and household, especially to protecting children's vision significant effect.Silicon simultaneously
Algal gel wall color is lasting, colour-fast using high temperature dye technology, and metope as newly, increases the service life of metope for a long time, reduces wall
Number is decorated in face, has saved room cost.
Specific implementation mode
With reference to embodiment, the present invention is further illustrated.
Embodiment
A kind of diatom Fender formaldehyde indoor coating preparation process, the coating include the raw material composition matched as follows：
Diatomite 15-35%, dispersant 0.2-1%, surfactant 0.1-2%, modified starch 15-25%, synthetic emulsion 10-
17%, Nano titanium dioxide 6-13%, talcum powder 5-12%, filler 0-30%, silver ion antimicrobial agent 0.5-2%, auxiliary agent 1-5%,
Profit shows agent 0.3-0.5%, and the preparation process of antifoaming agent 0.2-0.5%, 10-15 parts of activated carbon, the water of surplus, the coating include such as
Lower step：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Water is poured into container, and starts to stir, sequentially added during stirring modified starch, synthetic emulsion,
Talcum powder, and be sufficiently stirred；
Step 3：The mixed liquor that step 2 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add mixed-powder；
Step 4：Diatomite powder heating will be added in step 3 after twenty minutes, continue into mixed liquor successively filler, auxiliary agent, point
Powder, profit show agent and surfactant, and continue to stir；
Step 5：The mixed liquor obtained into step continues to add antifoaming agent, silver ion antimicrobial agent, Nano titanium dioxide successively,
And it stirs to raw material and is mixed thoroughly.
The synthetic emulsion is phenylpropyl alcohol compound emulsion and propyl alcohol lotion, the phenylpropyl alcohol compound emulsion and propyl alcohol lotion matter
Amount is than being 2-3:1.
The dispersant is SN-5040.
The profit shows agent AP-680.
The present invention uses primary raw material of the diatom ooze as coating, and the diatomaceous pyroconductivity of main component of diatom ooze is very
It is low, it is ideal heat preserving and insulating material in itself, there is extraordinary thermal and insulating performance, heat insulation is condition of equivalent thickness cement
6 times of mortar, unique " molecular sieve " structure of diatom ooze, will produce " water fall effect " after the moisture in touching air, from
And the negative oxygen ion beneficial to human body is constantly released, any heavy metal is free of, does not generate electrostatic, floating dust is not easy to adhere to, wall
Face is permanently pure and fresh, and diatom ooze is not likely to produce electrostatic, and metope surface is not easy dust fall, and diatom ooze selects inorganic mineral pigments toning, color
It is color soft.When people lives in the room of coating diatom ooze, metope reflection light is naturally soft, and people does not allow to be also easy to produce vision tired
Labor, the eyesight of effective protection you and household, especially to protecting children's vision significant effect.Diatom ooze wall color is lasting simultaneously,
Colour-fast using high temperature dye technology, metope as newly, increases the service life of metope for a long time, reduces wall decoration number, saves
Room cost.
Claims (4)
1. a kind of diatom Fender formaldehyde indoor coating preparation process, it is characterised in that：The coating includes the original matched as follows
Material composition：
Diatomite 15-35%, dispersant 0.2-1%, surfactant 0.1-2%, modified starch 15-25%, synthetic emulsion 10-
17%, Nano titanium dioxide 6-13%, talcum powder 5-12%, filler 0-30%, silver ion antimicrobial agent 0.5-2%, auxiliary agent 1-5%,
Profit shows agent 0.3-0.5%, and the preparation process of antifoaming agent 0.2-0.5%, 10-15 parts of activated carbon, the water of surplus, the coating include such as
Lower step：
Step 1：Activated carbon, diatomite are put into ball mill ball milling 1-1.5 hours, 300-450 mesh sieve is crossed after ball milling, is obtained
It is for use to mixed-powder；
Step 2：Water is poured into container, and starts to stir, sequentially added during stirring modified starch, synthetic emulsion,
Talcum powder, and be sufficiently stirred；
Step 3：The mixed liquor that step 2 obtains is heated and stirred, when being heated to 55-60 DEG C, continues to add into mixed liquor
Add mixed-powder；
Step 4：Diatomite powder heating will be added in step 3 after twenty minutes, continue into mixed liquor successively filler, auxiliary agent, point
Powder, profit show agent and surfactant, and continue to stir；
Step 5：The mixed liquor obtained into step continues to add antifoaming agent, silver ion antimicrobial agent, Nano titanium dioxide successively,
And it stirs to raw material and is mixed thoroughly.
2. a kind of diatom Fender formaldehyde indoor coating preparation process as described in claim 1, it is characterised in that：The synthesis
Lotion is phenylpropyl alcohol compound emulsion and propyl alcohol lotion, and the phenylpropyl alcohol compound emulsion and propyl alcohol quality of the emulsion ratio are 2-3:1.
3. a kind of diatom Fender formaldehyde indoor coating preparation process as described in claim 1, it is characterised in that：The dispersion
Agent is SN-5040.
4. a kind of diatom Fender formaldehyde indoor coating preparation process as described in claim 1, it is characterised in that：The profit is aobvious
Agent AP-680.