CN104559405A - Damp-proof anti-cracking putty powder - Google Patents
Damp-proof anti-cracking putty powder Download PDFInfo
- Publication number
- CN104559405A CN104559405A CN201410759211.3A CN201410759211A CN104559405A CN 104559405 A CN104559405 A CN 104559405A CN 201410759211 A CN201410759211 A CN 201410759211A CN 104559405 A CN104559405 A CN 104559405A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- putty
- moistureproof anti
- lignocellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a damp-proof anti-cracking putty powder. The putty powder is prepared from the following raw materials in parts by weight: 70-100 parts of ground calcium carbonate powder, 30-50 parts of ash-calcium-powder, 2-10 parts of hydroxypropyl methyl cellulose, 1-5 parts of lignocellulose, 8-15 parts of a dampproof anti-cracking agent, 0.5-2 parts of phthalocyanine blue and 5-10 parts of probiotic powder. The raw materials are prepared according to the weight portion, are stirred in a stirrer, and are packaged and sealed after being uniformly stirred. The anti-freeze putty powder is mixed with water when being used. According to the anti-freeze putty powder, hydroxypropyl methyl cellulose and lignocellulose have the effect of a frame, and the using strength of putty can be improved; and diatom ooze and sodium bentonite have excellent damp prevention and chemical resistance. After the putty is applied to an inner wall, the wall surface does not peel, blister or separate, and has excellent abrasion resistance and washing durability.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of moistureproof anti-crack mastic powder, belong to technical field of chemical paint.
Background technology
Putty is the one decoration gel material of smooth surface of wall, and being a kind of thick slurry coating material, is that coating whitewashes front requisite a kind of product.Painting imposes on priming paint or is directly coated with and imposes on object, in order to remove coated article rugged defect on the surface.It is formulated that base, mass filler and appropriate tinting pigment are painted in employing on a small quantity, and pigment used is iron oxide red, carbon black, chrome yellow etc. mainly.Filler is calcium bicarbonate, talcum powder etc. mainly.The working-surface that there is depression local can be filled up, also can strike off at all surfaces, normally after prime coat parches, be applied over primer coat surface.Require not crack in good, the bake process of tack.
Currently make a general survey of domestic whole elastic coating market, most product is only limited to and possesses elastomeric feature, its water tolerance and water-repellancy poor, tensile strength is low, and sticking power is general.Because it is not water-fast, non-watertight, after rain drop erosion its
Paint film will entirety peel off, or causes cracking due to the difference of water ratio or peel off, and rainwater just infiltrates metope, corrosion metope.With
Time due to the contamination resistance of elastic coating poor, the dirt of the dust in an atmosphere of being easily subject to after construction suspending, oily matter
Dye makes coating surface be polluted.
Summary of the invention
Technical problem to be solved by this invention is for the deficiencies in the prior art, there is provided that high, the resistance to viscosity of a kind of highly versatile, intensity is strong, wear resistance good, laundry-resistant putty powder, there is excellent protection against the tide, resistance to cleavage, do not rise rouse, do not come off, do not hinder hand, to human body without any harm.
In order to achieve the above object, the technical solution used in the present invention is:
A kind of moistureproof anti-crack mastic powder, comprises the raw material of following weight part: heavy calcium carbonate 70-100 part, sierozem power, 30-50 part, Vltra tears 2-10 part, lignocellulose 1-5 part, moistureproof anti-fissuring agent 6-15 part, the blue 0.5-2 part of phenol cyanines, probiotic powder 5-10 part.
Preferably, described moistureproof anti-fissuring agent is the mixture of sodium bentonite and diatom ooze, and its weight ratio is 1-3:2-5.
Preferably, described sodium bentonite and the weight ratio of diatom ooze are 1:2.
Preferably, described probiotic powder is the mixture of yeast powder and lactobacillus powder, and its weight ratio is 1-3:2-5.
Preferably, described yeast powder and the weight ratio of lactobacillus powder are 2:3.
Preferably, the viscosity of described Vltra tears is 80,000-10 ten thousand bold and unconstrained handkerchiefs. second.
Above-mentioned raw materials is prepared according to above-mentioned formula, is placed in stirrer and stirs, splitting sealing after stirring; During use and water routinely proportioning stir.
Vltra tears of the present invention and lignocellulose play the effect of skeleton, increase the working strength of putty; Diatom ooze and sodium bentonite have excellent protection against the tide, chemical resistance, and putty brush, after interior wall, metope non-scale, does not play drum, do not come off, and the wear resistance of excellence and water-fastness.
Embodiment
Embodiment 1:
A kind of moistureproof anti-crack mastic powder, comprises the raw material of following weight part: blue 0.5 part of heavy calcium carbonate 70 parts, sierozem power 30 parts, Vltra tears 2 parts, lignocellulose 1 part, sodium bentonite 2 parts, diatom ooze 4 parts, phenol cyanines, 2 parts, yeast powder, lactobacillus powder 3 parts.
Embodiment 2:
A kind of moistureproof anti-crack mastic powder, comprises the raw material of following weight part: blue 2 parts of heavy calcium carbonate 100 parts, sierozem power 50 parts, Vltra tears 10 parts, lignocellulose 5 parts, sodium bentonite 5 parts, diatom ooze 10 parts, phenol cyanines, 4 parts, yeast powder, lactobacillus powder 6 parts.
Embodiment 3:
A kind of moistureproof anti-crack mastic powder, comprises the raw material of following weight part: blue 1 part of heavy calcium carbonate 80 parts, sierozem power 35 parts, Vltra tears 4 parts, lignocellulose 2 parts, sodium bentonite 3 parts, diatom ooze 6 parts, phenol cyanines, 4 parts, yeast powder, lactobacillus powder 6 parts.
Embodiment 4:
A kind of moistureproof anti-crack mastic powder, comprises the raw material of following weight part: blue 1 part of heavy calcium carbonate 90 parts, sierozem power 40 parts, Vltra tears 6 parts, lignocellulose 3 parts, sodium bentonite 3 parts, diatom ooze 6 parts, phenol cyanines, 4 parts, yeast powder, lactobacillus powder 6 parts.
Embodiment 5:
A kind of moistureproof anti-crack mastic powder, comprises the raw material of following weight part: blue 1 part of heavy calcium carbonate 90 parts, sierozem power 45 parts, Vltra tears 8 parts, lignocellulose 4 parts, sodium bentonite 3 parts, diatom ooze 6 parts, phenol cyanines, 4 parts, yeast powder, lactobacillus powder 6 parts.
By the recipe configuration putty powder of embodiment of the present invention 1-5, raw material is good according to weight, be placed in stirrer and stir, stir, with water conveniently proportioning stir brush metope after detect a putty powder performance: result is as shown in table 1:
Table 1: embodiment 1-5 gained putty powder performance index
Above-mentioned example just for technical conceive of the present invention and technical characterstic are described, can not limit the scope of the invention with this.The equivalent transformation that all essence according to the present invention is done or modification, all should be encompassed within protection scope of the present invention.
Claims (6)
1. a moistureproof anti-crack mastic powder, it is characterized in that, comprise the raw material of following weight part: heavy calcium carbonate 70-100 part, sierozem power, 30-50 part, Vltra tears 2-10 part, lignocellulose 1-5 part, moistureproof anti-fissuring agent 6-15 part, the blue 0.5-2 part of phenol cyanines, probiotic powder 5-10 part.
2. moistureproof anti-crack mastic powder according to claim 1, is characterized in that, described moistureproof anti-fissuring agent is the mixture of sodium bentonite and diatom ooze, and its weight ratio is 1-3:2-5.
3. moistureproof anti-crack mastic powder according to claim 2, is characterized in that, described sodium bentonite and the weight ratio of diatom ooze are 1:2.
4. moistureproof anti-crack mastic powder according to claim 1, is characterized in that, described probiotic powder is the mixture of yeast powder and lactobacillus powder, and its weight ratio is 1-3:2-5.
5. moistureproof anti-crack mastic powder according to claim 4, is characterized in that, described yeast powder and the weight ratio of lactobacillus powder are 2:3.
6. moistureproof anti-crack mastic powder according to claim 1, is characterized in that, the viscosity of described Vltra tears is 80,000-10 ten thousand bold and unconstrained handkerchiefs. second.