CN106497205A - A kind of powder of lacquer putty for use on and preparation method thereof - Google Patents
A kind of powder of lacquer putty for use on and preparation method thereof Download PDFInfo
- Publication number
- CN106497205A CN106497205A CN201611100910.2A CN201611100910A CN106497205A CN 106497205 A CN106497205 A CN 106497205A CN 201611100910 A CN201611100910 A CN 201611100910A CN 106497205 A CN106497205 A CN 106497205A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- trioxide
- lacquer putty
- terbia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of powder of lacquer putty for use on and preparation method thereof, is made up of following mass fraction formula components:68 parts of attapulgite, 46 parts of starch alkenyl succinate ester, 13 parts of pigment, 57 parts of cerium oxide, 24 parts of Dineodymium trioxide, 6 10 parts of bagasse fibre, 5 15 parts of silica flour, 6 10 parts of terbia. Diterbium trioxide, 12 14 parts of white cement, 68 parts of palygorskite clay, 13 parts of lanthana, 10 20 parts of sierozem power, 68 parts of heavy calcium carbonate, 60 100 parts of pure water, the present invention improves the living environment of people in larger scope, simultaneously allow people to stay indoor the sensation that just can be experienced in the Nature, improve the physical condition of people.The problems such as solving low common putty adhesion strength, water-fast flexible difference, again can effective anion releasing, meet people for the serious hope of shower the Nature breath, also fundamentally improve existing living environment, with preferably developing meaning.
Description
Technical field
The present invention relates to wall plastering field, in particular to a kind of powder of lacquer putty for use on and preparation method thereof.
Background technology
Anion is negatively charged oxonium ion, and it is present in air.In the indoor environment of people's life at ordinary times just
Containing anion, simply content is low cannot perceive.And by the sea, forest, waterfall, grassland you can feel that air is very pure and fresh, breathe
Especially happy, it is because the high reason of anion concentration.
The effect that anion is medically showed:
1st, the impact to nervous system:
Strengthen cerebral cortex function and mental activity, in high spirits, working efficiency is improved, and is changed can sleep quality
Kind.Anion strengthens can also the oxidizing process dynamics of cerebral tissue, make cerebral tissue obtain more oxygen.
2nd, the impact to cardiovascular system:
Observe according to scholar, anion plays the role of obvious expansion of blood vessels, can release arteries spasm, reduce blood pressure
Purpose, anion is conducive to hypertension and cardiovascular and cerebrovascular vessel for improving cardiac function and improving myocardial nutrition and be also of great benefit to
The state of an illness of illness patient is recovered.
3rd, the impact to blood system:
Research confirm, anion make blood pool flow velocity slack-off, extend clotting time, oxygen content in blood can be made
Increase, be conducive to blood oxygen conveying, absorb and utilize.
4th, impact of the anion to respiratory system:
Impact to respiratory system is most obvious.This is because anion is to enter human body by respiratory tract, it can carry
The vital capacity of high people.Someone once tested, and in glass mask, suction negative aeroion 30 minutes, can make pulmonary absorption amount of oxygen
Increase by 2%, and discharging amount of carbon dioxide can increase by 14.5%, therefore anion plays the role of to improve and increases pulmonary function.
World Health Organization (WHO) confirms in fresh air anion concentration in 1000-1500/cm3, countryside, seashore, forest,
Waterfall, grassland anion reach 3000/more than cm3, and content is less than 600/cm3 in general family room.Anion contains
Amount is too low to induce numerous disease.Weather scientist thinks that big city as Beijing belongs to continental climate, bears in air
Oxonium ion is fewer than marine climate area, and air pollution is than more serious in addition, in air negative oxygen ion easily by smog, dust,
The pollutant such as pathogenic bacteria, vehicle exhaust adsorb and disappear, and room ventilation is bad and pollutes, and negative oxygen ion just more lacks.For this purpose, long
The resident for occupying business district often to suburb field, beach, Forest Park etc. should particularly arrive the landscape of waterfall natural flow splashing
Area is carried out " air bath ", so can just be more beneficial for the physical and mental health of human body.
There is presently no can produce and releasing negative oxygen ion house decorative material.
Content of the invention
The invention provides a kind of powder of lacquer putty for use on and preparation method thereof, the inhabitation ring for improving people in larger scope of the invention
Border, while allowing people to stay indoor the sensation that just can be experienced in the Nature, improves the physical condition of people.Solve general
Logical putty adhesion strength is low, water-fast flexible difference the problems such as, again can effective anion releasing, meet people for shower the Nature
The serious hope of breath, also fundamentally improves existing living environment, with preferably development meaning.
For achieving the above object, the present invention provides following technical scheme:
A kind of powder of lacquer putty for use on and preparation method thereof, is made up of following mass fraction formula components:Attapulgite 6-8 parts, thiazolinyl
Succinic acid starch ester 4-6 parts, pigment 1-3 parts, cerium oxide 5-7 parts, Dineodymium trioxide 2-4 parts, bagasse fibre 6-10 parts, silica flour 5-
15 parts, terbia. Diterbium trioxide 6-10 parts, white cement 12-14 parts, palygorskite clay 6-8 parts, lanthana 1-3 parts, sierozem power 10-20 parts, weight
Matter Paris white 6-8 parts, pure water 60-100 parts.
Further:It is made up of following mass fraction formula components:6 parts of attapulgite, 4 parts of starch alkenyl succinate ester, face
1 part of material, 5 parts of cerium oxide, 2 parts of Dineodymium trioxide, 6 parts of bagasse fibre, 5 parts of silica flour, 6 parts of terbia. Diterbium trioxide, 12 parts of white cement, Paligorskite
6 parts of clay, 1 part of lanthana, 10 parts of sierozem power, 6 parts of heavy calcium carbonate, 60 parts of pure water.
Further:It is made up of following mass fraction formula components:7 parts of attapulgite, 5 parts of starch alkenyl succinate ester, face
2 parts of material, 6 parts of cerium oxide, 3 parts of Dineodymium trioxide, 8 parts of bagasse fibre, 10 parts of silica flour, 8 parts of terbia. Diterbium trioxide, 13 parts of white cement, slope thread
7 parts of stone clay, 2 parts of lanthana, 15 parts of sierozem power, 7 parts of heavy calcium carbonate, 80 parts of pure water.
Further:It is made up of following mass fraction formula components:8 parts of attapulgite, 6 parts of starch alkenyl succinate ester, face
3 parts of material, 7 parts of cerium oxide, 4 parts of Dineodymium trioxide, 10 parts of bagasse fibre, 15 parts of silica flour, 10 parts of terbia. Diterbium trioxide, 14 parts of white cement, slope
8 parts of thread stone clay, 3 parts of lanthana, 20 parts of sierozem power, 8 parts of heavy calcium carbonate, 100 parts of pure water.
Further:Preparation method of the present invention has following steps:
Step one, above-mentioned raw materials are allocated in proportion, standby;
Step 2, above-mentioned raw material is sequentially added in horizontal or vertical mixer in order, mixing time is 1-2h, so
Discharging can obtain nagative ion inner wall waterproof putty powder afterwards;
Step 3, sampling observation, then it is assumed that detection is qualified, filter, pack, get product.
The invention has the beneficial effects as follows:
1st, the present invention improves the living environment of people in larger scope, while allow people to stay indoor just can experience in big
Sensation in nature, improves the physical condition of people;
2nd, the problems such as solving low common putty adhesion strength, water-fast flexible difference, again can effective anion releasing, meet people
For the serious hope of shower the Nature breath;
3rd, existing living environment is fundamentally improved, with preferably development meaning.
Specific embodiment
Below in conjunction with the embodiment of the present invention, to the embodiment of the present invention in technical scheme be clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiment.In based on the present invention
Embodiment, the every other embodiment obtained under the premise of creative work is not made by those of ordinary skill in the art, all
Belong to the scope of protection of the invention.
Embodiment one:
A kind of powder of lacquer putty for use on is made up of following mass fraction formula components:Attapulgite 6-8 parts, starch alkenyl succinate ester 4-
6 parts, pigment 1-3 parts, cerium oxide 5-7 parts, Dineodymium trioxide 2-4 parts, bagasse fibre 6-10 parts, silica flour 5-15 parts, terbia. Diterbium trioxide 6-
10 parts, white cement 12-14 parts, palygorskite clay 6-8 parts, lanthana 1-3 parts, sierozem power 10-20 parts, heavy calcium carbonate 6-8
Part, pure water 60-100 parts.
Embodiment two:
A kind of powder of lacquer putty for use on is made up of following mass fraction formula components:6 parts of attapulgite, 4 parts of starch alkenyl succinate ester,
1 part of pigment, 5 parts of cerium oxide, 2 parts of Dineodymium trioxide, 6 parts of bagasse fibre, 5 parts of silica flour, 6 parts of terbia. Diterbium trioxide, 12 parts of white cement, slope thread
6 parts of stone clay, 1 part of lanthana, 10 parts of sierozem power, 6 parts of heavy calcium carbonate, 60 parts of pure water.
Embodiment three:
A kind of powder of lacquer putty for use on is made up of following mass fraction formula components:7 parts of attapulgite, 5 parts of starch alkenyl succinate ester,
2 parts of pigment, 6 parts of cerium oxide, 3 parts of Dineodymium trioxide, 8 parts of bagasse fibre, 10 parts of silica flour, 8 parts of terbia. Diterbium trioxide, 13 parts of white cement, slope
7 parts of thread stone clay, 2 parts of lanthana, 15 parts of sierozem power, 7 parts of heavy calcium carbonate, 80 parts of pure water.
Example IV:
A kind of powder of lacquer putty for use on is made up of following mass fraction formula components:8 parts of attapulgite, 6 parts of starch alkenyl succinate ester,
3 parts of pigment, 7 parts of cerium oxide, 4 parts of Dineodymium trioxide, 10 parts of bagasse fibre, 15 parts of silica flour, 10 parts of terbia. Diterbium trioxide, 14 parts of white cement,
8 parts of palygorskite clay, 3 parts of lanthana, 20 parts of sierozem power, 8 parts of heavy calcium carbonate, 100 parts of pure water.
Embodiment five:
A kind of preparation method preparation method of powder of lacquer putty for use on comprises the steps:
Step one, by chemical fibre powder, butyl ester, monooctyl ester, alpha-cyanoacrylate second fat add stainless steel cauldron in, stirring
Lower addition surplus stock, stirring make its mix homogeneously, and are uniformly heating to 45-55 DEG C, and the heating-up time is 30-50min;
Step 2, by step one and surplus stock input blender, the speed of agitator of 100-300r/min is dispersed
5-30min, disperses at a high speed and is ground to below 35um fineness;
Step 3, sampling observation, then it is assumed that detection is qualified, filter, pack, get product.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Contain an independent technical scheme, this narrating mode of description is only that those skilled in the art should for clarity
Using description as an entirety, the technical scheme in each embodiment can also form those skilled in the art through appropriately combined
Understandable other embodiment.
Claims (5)
1. a kind of powder of lacquer putty for use on, it is characterised in that:It is made up of following mass fraction formula components:
Attapulgite 6-8 parts, starch alkenyl succinate ester 4-6 parts, pigment 1-3 parts, cerium oxide 5-7 parts, Dineodymium trioxide 2-4 parts, sweet
Sugarcane fiber 6-10 parts, silica flour 5-15 parts, terbia. Diterbium trioxide 6-10 parts, white cement 12-14 parts, palygorskite clay 6-8 parts, lanthana
1-3 parts, sierozem power 10-20 parts, heavy calcium carbonate 6-8 parts, pure water 60-100 parts.
2. a kind of powder of lacquer putty for use on according to claim 1, it is characterised in that:It is made up of following mass fraction formula components:
6 parts of attapulgite, 4 parts of starch alkenyl succinate ester, 1 part of pigment, 5 parts of cerium oxide, 2 parts of Dineodymium trioxide, bagasse fibre 6
Part, 5 parts of silica flour, 6 parts of terbia. Diterbium trioxide, 12 parts of white cement, 6 parts of palygorskite clay, 1 part of lanthana, 10 parts of sierozem power, heavy carbonic acid
6 parts of calcium powder, 60 parts of pure water.
3. a kind of powder of lacquer putty for use on according to claim 1, it is characterised in that:It is made up of following mass fraction formula components:
7 parts of attapulgite, 5 parts of starch alkenyl succinate ester, 2 parts of pigment, 6 parts of cerium oxide, 3 parts of Dineodymium trioxide, bagasse fibre 8
Part, 10 parts of silica flour, 8 parts of terbia. Diterbium trioxide, 13 parts of white cement, 7 parts of palygorskite clay, 2 parts of lanthana, 15 parts of sierozem power, heavy carbon
7 parts of sour calcium powder, 80 parts of pure water.
4. a kind of powder of lacquer putty for use on according to claim 1, it is characterised in that:It is made up of following mass fraction formula components:
8 parts of attapulgite, 6 parts of starch alkenyl succinate ester, 3 parts of pigment, 7 parts of cerium oxide, 4 parts of Dineodymium trioxide, bagasse fibre 10
Part, 15 parts of silica flour, 10 parts of terbia. Diterbium trioxide, 14 parts of white cement, 8 parts of palygorskite clay, 3 parts of lanthana, 20 parts of sierozem power, heavy carbon
8 parts of sour calcium powder, 100 parts of pure water.
5. a kind of a kind of preparation method of powder of lacquer putty for use on according to claim 1, it is characterised in that:Comprise the steps:
Step one, above-mentioned raw materials are allocated in proportion, standby;
Step 2, above-mentioned raw material is sequentially added in horizontal or vertical mixer in order, mixing time is 1-2h, then goes out
Material can obtain nagative ion inner wall waterproof putty powder;
Step 3, sampling observation, then it is assumed that detection is qualified, filter, pack, get product.