CN107325619A - Water-proof putty powder - Google Patents
Water-proof putty powder Download PDFInfo
- Publication number
- CN107325619A CN107325619A CN201710782875.5A CN201710782875A CN107325619A CN 107325619 A CN107325619 A CN 107325619A CN 201710782875 A CN201710782875 A CN 201710782875A CN 107325619 A CN107325619 A CN 107325619A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- powder
- alginate
- proof putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-proof putty powder, it is made of the raw material of following parts by weight：Sierozem power：18 parts to 35 parts；Palygorskite clay：2.5 parts to 3.5 parts；Bagasse fibre：3 parts to 8 parts；Hydroxypropyl methyl cellulose：0.5 part to 1 part；Natural resin：5 parts to 10 parts；Na-alginate：2.5 parts to 3.5 parts；1 part of silica flour 0.5 part.
Description
Technical field
The invention belongs to decoration material field, and in particular to a kind of water-proof putty powder.
Background technology
With the improvement of people's life quality, house decoration increasingly obtains the attention of people, powder of lacquer putty for use on be in finishing not
The material that can lack, uses the raw materials such as talcum powder, PVOH glue existing powder of lacquer putty for use on more and is made, it not only has toxicity
Greatly, seriously polluted the problem of, also exist through the easy efflorescence of coating after a period of time, cracking, hollowing and come off and wet
It is wet to be also easy to produce the problem of going mouldy, therefore it is this area skill to provide a kind of powder of lacquer putty for use on that nontoxic, caking ability is strong and environmental protection is water-fast
The problem of art personnel's urgent need to resolve.
The content of the invention
For above technical deficiency, the invention provides a kind of water-proof putty powder, solve what is be previously mentioned in background technology
The problem of existing powder of lacquer putty for use on is present.
The present invention is achieved in that a kind of water-proof putty powder, is made of the raw material of following parts by weight：Sierozem power：18
Part is to 35 parts；Palygorskite clay：2.5 parts to 3.5 parts；Bagasse fibre：3 parts to 8 parts；Hydroxypropyl methyl cellulose：0.5 part extremely
1 part；Natural resin：5 parts to 10 parts；Na-alginate：2.5 parts to 3.5 parts；0.5 part -1 part of silica flour.
Preferably, water-proof putty powder is made of the raw material of following parts by weight：Sierozem power：20 parts to 30 parts；Palygorskite
Powder：2.7 parts to 3 parts；Bagasse fibre：5 parts to 7 parts；Hydroxypropyl methyl cellulose：0.6 part to 0.9 part；Natural resin：6 parts
To 8 parts；Na-alginate：2.7 parts to 3 parts；0.8 part -1 part of silica flour.
Preferably, water-proof putty powder is made of the raw material of following parts by weight：Sierozem power：25 parts；Palygorskite powder：2.8
Part；Bagasse fibre：6 parts；Hydroxypropyl methyl cellulose：0.7 part；Natural resin：7 parts；Na-alginate：3 parts；Silica flour 0.9
Part.
Due to using above-mentioned technical proposal, the present invention has the advantages that：
1st, due to adding palygorskite powder in sierozem power, its not only add the caking ability and water resistance of powder of lacquer putty for use on and
Palygorskite powder drying shrinkage is small, and cracking is not produced；
2nd, due to adding bagasse fibre, bagasse fibre is as toughener, and it not only adds the crack resistance of putty
And natural environmental-protective；
3rd, due to adding hydroxypropyl methyl cellulose, as dispersant and stabilizer, each raw material is made in water or organic molten
All there is good intermiscibility in agent；
4th, due to adding natural resin, natural environmental-protective and water-fast moisture-proof role is played, the wet putty of wet is not likely to produce mould
Become；
5th, due to adding Na-alginate, Na-alginate natural environmental-protective and improves the viscous of putty as bonding agent, not only
Connecing property；
6th, due to adding silica flour, then the hardness of powder of lacquer putty for use on is more effectively strengthened.
Embodiment
In order that technical problems, technical solutions and advantages to be solved are more clearly understood, tie below
Embodiment is closed, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only to explain
The present invention, is not intended to limit the present invention.
Embodiment 1：The water-proof putty powder that the present invention is provided, is made of the raw material of following weight：
Sierozem power：18 kilograms；Palygorskite clay：2.5 kilogram；Bagasse fibre：3 kilograms；Hydroxypropyl methyl cellulose：
0.5 kilogram；Natural resin：5 kilograms；Na-alginate：2.5 kilogram；0.5 kilogram of silica flour；
It is made as follows：
A. palygorskite clay is placed in earth kiln and be fired, time 2 h, 280 degrees Celsius to 300 degrees Celsius of temperature,
It is stand-by；
B. palygorskite clay and natural resin made from step A are put into pulverizer and crushed, obtain crushed material；
C. crushed material made from step B and hydroxypropyl methyl cellulose, Na-alginate, bagasse fibre, silica flour are put
Enter in mixer, stirred 2 minutes with 6000 revs/min of speed, obtain compound；
D. compound made from step C is put into grinder and be ground, fineness is 500 mesh, is produced.
Embodiment 2：This water-proof putty powder, is made of the raw material of following weight：Sierozem power：35 kilograms；Palygorskite glues
Soil：3.5 kilogram；Bagasse fibre：8 kilograms；Hydroxypropyl methyl cellulose：1 kilogram；Natural resin：10 kilograms；Na-alginate：
3.5 kilograms, 1 kilogram of silica flour；Remaining is identical with embodiment one.
Embodiment 3：This water-proof putty powder, is made of the raw material of following weight：Sierozem power：20 kilograms；Palygorskite powder：
2.7 kilogram；Bagasse fibre：5 kilograms；Hydroxypropyl methyl cellulose：0.6 kilogram；Natural resin：6 kilograms；Na-alginate：2.7
Kilogram；0.9 kilogram of silica flour, remaining is identical with embodiment one.
The water resistance of water-proof putty powder made from three embodiments is detected, the putty of the gained of embodiment 3 is found
The drying shrinkage of powder is minimum, the cementability most strong and hardness of crack resistance most strong, putty is maximum.
By above-described embodiment, the purpose of the present invention is reached by fully effective.One of ordinary skilled in the art
It should be understood that the present invention includes but does not limit the content described in embodiment above.Any modification without departing from the present invention is all
It is included within the scope of claims.
Claims (3)
1. a kind of water-proof putty powder, it is characterised in that：It is made of the raw material of following parts by weight：Sierozem power：18 parts to 35 parts；Slope
Thread stone clay：2.5 parts to 3.5 parts；Bagasse fibre：3 parts to 8 parts；Hydroxypropyl methyl cellulose：0.5 part to 1 part；Natural tree
Fat：5 parts to 10 parts；Na-alginate：2.5 parts to 3.5 parts；0.5 part -1 part of silica flour.
2. water-proof putty powder according to claim 1, it is characterised in that：It is made of the raw material of following parts by weight：Grey calcium
Powder：20 parts to 30 parts；Palygorskite powder：2.7 parts to 3 parts；Bagasse fibre：5 parts to 7 parts；Hydroxypropyl methyl cellulose：0.6 part
To 0.9 part；Natural resin：6 parts to 8 parts；Na-alginate：2.7 parts to 3 parts；0.8 part -1 part of silica flour.
3. water-proof putty powder according to claim 1 or 2, it is characterised in that：It is made of the raw material of following parts by weight：Ash
Calcium powder：25 parts；Palygorskite powder：2.8 part；Bagasse fibre：6 parts；Hydroxypropyl methyl cellulose：0.7 part；Natural resin：7 parts；
Na-alginate：3 parts；0.9 part of silica flour.