CN104513527A - Vintage texture coating - Google Patents
Vintage texture coating Download PDFInfo
- Publication number
- CN104513527A CN104513527A CN201310455792.7A CN201310455792A CN104513527A CN 104513527 A CN104513527 A CN 104513527A CN 201310455792 A CN201310455792 A CN 201310455792A CN 104513527 A CN104513527 A CN 104513527A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- parts
- water
- slurry
- texture coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A vintage texture coating comprises, by weight, 12-15 parts of a special emulsion for real stone paints, 10-15 parts of cellulose, 3-5 parts of water, 1 part of a dispersant, 2.5 parts of heavy calcium, 5 parts of 200 mesh quartz sand, 0.5 parts of a titanium dioxide slurry, 20-30 parts of 40-80 mesh river sand, and 30-40 parts of 80-120 mesh river sand. The special emulsion for real stone paints is a novel emulsion developed for overcoming the water absorption whitening phenomenon of emulsions in the film formation process. The emulsion is prepared by adopting a foreign high-quality emulsifier and a monomer and polymerizing through a core shell cladding technology. The emulsion has moderate viscosity and uniform granule, and the real stone paints prepared by using the emulsion have the advantages of strong adhesion, ageing resistance, outdoor durability, pollution resistance, no color fading, water washing resistance and the like. The cellulose is hydroxypropyl methylcellulose, and the excellent water retention performance of the hydroxypropyl methylcellulose makes the slurry not cracked due to too fast drying after the slurry is smeared and enhances the strength after hardening.
Description
Technical field
The present invention relates to a kind of coating, particularly a kind of texture coating.Belong to chemical field.
Background technology
Along with the requirement of raising to environment of living standards of the people is more and more higher, and gradually to natural stype future development, for addressing this problem, invent this coating.
Summary of the invention
A kind of concrete component of pseudo-classic type texture coating and part by weight are: true mineral varnish special emulsion 12-15; Mierocrystalline cellulose 10-15; Water 3-5; Dispersion agent 1; Coarse whiting 2.5; 200 order quartz sands 5; Titanium dioxide slurry 0.5; 40-80 order river sand 20-30; 80-120 order river sand 30-40. true mineral varnish special emulsion used there is a kind of New Emulsion that water suction whiting basis is developed overcoming emulsion film forming.Adopt external quality milk agent and monomer, be polymerized through nucleocapsid cladding process.This emulsion viscosity is moderate, uniform particle, has strong, the anti-aging and outside durabitity of cohesive force, anti-pollution, the advantage such as colour-fast, water-fastness with the true mineral varnish of its preparation.Mierocrystalline cellulose used is Vltra tears, and the water retention property of its excellence makes slurry because of so dry that to chap too soon, can not strengthen the rear intensity of sclerosis after smearing.
Embodiment:
Production stage of the present invention is: according to formula quantity, various measuring raw materials is accurately for subsequent use, use cantilever double-spiral conical mixer, the order of starting material according to formula is added successively, in room temperature, under relative air humidity is less than the environment of 60%, stir 15-20 minute, after stirring after testing, detect discharging packaging.
Claims (3)
1. the concrete component of pseudo-classic type texture coating and part by weight are: true mineral varnish special emulsion 12-15; Mierocrystalline cellulose 10-15; Water 3-5; Dispersion agent 1; Coarse whiting 2.5; 200 order quartz sands 5; Titanium dioxide slurry 0.5; 40-80 order river sand 20-30; 80-120 order river sand 30-40.
2. the pseudo-classic type texture coating of one according to claim 1, it is characterized in that true mineral varnish special emulsion used is overcoming a kind of New Emulsion that emulsion film forming existence water suction whiting basis is developed, adopt external quality milk agent and monomer, be polymerized through nucleocapsid cladding process, this emulsion viscosity is moderate, uniform particle, has strong, the anti-aging and outside durabitity of cohesive force, anti-pollution, the advantage such as colour-fast, water-fastness with the true mineral varnish of its preparation.
3. the pseudo-classic type texture coating of one according to claim 1, is characterized in that Mierocrystalline cellulose used is Vltra tears, and the water retention property of its excellence makes slurry because of so dry that to chap too soon, can not strengthen the rear intensity of sclerosis after smearing.