CN103254749A - Water-based blackboard paint - Google Patents
Water-based blackboard paint Download PDFInfo
- Publication number
- CN103254749A CN103254749A CN2013101497017A CN201310149701A CN103254749A CN 103254749 A CN103254749 A CN 103254749A CN 2013101497017 A CN2013101497017 A CN 2013101497017A CN 201310149701 A CN201310149701 A CN 201310149701A CN 103254749 A CN103254749 A CN 103254749A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- agent
- good
- agents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to water-based blackboard paint. The water-based blackboard paint is proportioned by the following substances: water, an assistant, a film forming substance, pigment and filler, a macromolecule dispersion agent, inorganic pigment, polymerized powder, a thermal stabilizer, an adhesive force promoter, a viscosity adjusting solvent, a cross-linking agent, cellulose, an anti-foaming agent, a flatting agent, a wetting agent, a paint anticorrosion agent, a surfactant, an anti-blushing agent, a thickening agent and an alkali. The water-based blackboard paint has the beneficial effects of no toxicity, no pollution, difficulty in burning, good thermal stability, convenience in storage and transportation, energy conservation, environmental protection and no pungent smell, and has high crosslink density, good solvent resistance, good chemicals resistances, good temperature changing resistance, good after-back resistance, good scratching resistance, good weather resistance, difficulty in color changing and good attaching effect after forming a paint film.
Description
Technical field
The invention belongs to a kind of coating, especially a kind of water-based chalkboard paint coating.
Background technology
Along with the steady-state growth of world economy, the consumers demand of water-based chalkboard paint and toy product day by day enlarges.As the whole world maximum water-based chalkboard paint and toy production base, China has international water-based chalkboard paint and the market share of toy product more than 70%, water-based chalkboard paint and toy industry are bearing the export market depression, the dual-pressure that production cost and technical threshold improve, meanwhile, based on health, environmental protection, the original intention of safety and economy Sustainable development, strict control test and rules have been set up in countries in the world or area, and constantly upgraded, refinement, the contentious matter that industry causes rises one after another, the sanction of relevant laws and regulations is also severe day by day, the particularly restriction of VOC, give manufacturers, importor and retailer have brought great challenge, at this moment, water-based chalkboard paint and toy coating arise.
At present, woodenware chalkboard paint and the toy coating major part used on the market are based on pyroxylin(e)finish, part is water-based, PU, because pyroxylin(e)finish has the advantage of himself: fast drying, easy construction, no restriction duration of service, cheap etc., but pyroxylin(e)finish also has the shortcoming of self: admittedly divide low, fullness ratio is poor, anti-solvent, chemically-resistant material difference etc., environmental pollution is greatly its main shortcoming, because it is solvent based coating, mainly lean on solvent evaporates and film forming, therefore, pyroxylin(e)finish can be replaced by other environment-friendly type coating eventually, and that water-based chalkboard paint and toy coating have is nontoxic, pollution-free, difficult combustion, store convenient transportation, advantage such as energy-conservation, and along with various countries' environmental protection law, rules are sound gradually, and it is trend of the times that water-borne coatings substitutes conventional solvent type coating, also will become the important development direction of following coating.
Summary of the invention
The present invention is directed to the shortcoming of above-mentioned prior art, a kind of water-based chalkboard paint coating is provided, can replace woodenware chalkboard paint commonly used in the market, and have the not available advantage of woodenware chalkboard paint.
The present invention solves the technical scheme that its technical problem adopts:
A kind of water-based chalkboard paint coating, it is that mass fraction according to following material carries out proportioning: 100 parts～140 parts in water, 40 parts～60 parts of auxiliary agents, 60 parts～90 parts of filmogens, 40 parts～70 parts of color stuffings, 20 parts～35 parts of macromolecule dispersing agents, 10 parts～15 parts of inorganic pigments, 15 parts～30 parts of aggretion type powders, 10 parts～30 parts of thermo-stabilizers, 20 parts～30 parts of adhesion promoters, viscosity is adjusted 5 parts～10 parts of solvents, 20 parts～40 parts of linking agents, 10 parts～20 parts of Mierocrystalline celluloses, 10 parts～20 parts of defoamers, 8 parts～15 parts of flow agents, 9 parts～18 parts of wetting agents, 12 parts～24 parts of coating antiseptics, 4 parts～8 parts in tensio-active agent, 9 parts～16 parts of non-blushing thinners, 10 parts～15 parts of thickening materials, 4 parts～8 parts in alkali.
As preferably, above-mentioned water-based chalkboard paint coating, it is that mass fraction according to following material carries out proportioning: 120 parts in water, 50 parts of auxiliary agents, 80 parts of filmogens, 60 parts of color stuffings, macromolecule dispersing agent 28,13 parts of inorganic pigments, 18 parts of aggretion type powders, 20 parts of thermo-stabilizers, 25 parts of adhesion promoters, viscosity are adjusted 8 parts of solvents, 24 parts of linking agents, 16 parts of Mierocrystalline celluloses, 16 parts of defoamers, 14 parts of flow agents, 15 parts of wetting agents, 20 parts of coating antiseptics, 6 parts in tensio-active agent, 12 parts of non-blushing thinners, 12 parts of thickening materials, 7 parts in alkali.
Filmogen is aqueous polyurethane dispersion.
The aggretion type powder is carbon black.
Adopt aqueous polyurethane dispersion as filmogen, form the cross-linking density height of filming after filming, anti-solvent, chemicals-resistant, temp. variation resistant, anti-ly after-tack, the effect of weathering resistance is better, is particularly useful for colored paint.Linking agent is used for improving cross-linking density, thereby improves paint film property, and the hydrophilic radical generation crosslinking reaction in linking agent and the coating has improved cross-linking density, thereby has improved performances such as hardness, anti-solvent, water tolerance, chemical resistant properties, sticking power.
The effect that the present invention is useful is: water-based chalkboard paint coating of the present invention, nontoxic pollution-free, nonflammable, Heat stability is good stores convenient transportation, energy-conserving and environment-protective, do not have irritating smell, form the back cross-linking density height of filming, anti-solvent, chemicals-resistant, temp. variation resistant, anti-ly after-tack, the effect of anti scuffing, weathering resistance is better, it is good to form the back light fastness of filming, not easy to change, adhesion effect is good.
Embodiment
The invention will be further described below in conjunction with specific embodiment:
Embodiment one:
The water-based chalkboard paint coating of present embodiment, it is that mass fraction according to following material carries out proportioning:
130 parts in water, 45 parts of auxiliary agents, 90 parts of filmogens, 60 parts of color stuffings, 35 parts of macromolecule dispersing agents, 15 parts of inorganic pigments, 30 parts of aggretion type powders, 18 parts of thermo-stabilizers, 280 parts of adhesion promoters, viscosity are adjusted 9 parts of solvents, 36 parts of linking agents, 16 parts of Mierocrystalline celluloses, 15 parts of defoamers, 12 parts of flow agents, 16 parts of wetting agents, 18 parts of coating antiseptics, 6 parts in tensio-active agent, 14 parts of non-blushing thinners, 13 parts of thickening materials, 7 parts in alkali.
The preparation method of above-mentioned water-based chalkboard paint coating is: with water, auxiliary agent adds in the dispersion cylinder, after stirring, add color stuffing, macromolecule dispersing agent carries out blending dispersion, add filmogen again and fully mix the formation mixture, in mixture, add inorganic pigment successively, the aggretion type powder, thermo-stabilizer, adhesion promoter, linking agent, Mierocrystalline cellulose, flow agent, wetting agent, coating antiseptic, tensio-active agent, non-blushing thinner, alkali fully mixes, add defoamer again, viscosity is adjusted solvent, thickening material fully mixes, again the final mixture of gained is tested, be water-based chalkboard paint coating through the mixture of gained after the assay was approved.
Embodiment two:
The water-based chalkboard paint coating of present embodiment, it is that mass fraction according to following material carries out proportioning:
110 parts in water, 46 parts of auxiliary agents, 70 parts of filmogens, 45 parts of color stuffings, 20 parts of macromolecule dispersing agents, 14 parts of inorganic pigments, 28 parts of aggretion type powders, 28 parts of thermo-stabilizers, 25 parts of adhesion promoters, viscosity are adjusted 9 parts of solvents, 30 parts of linking agents, 15 parts of Mierocrystalline celluloses, 15 parts of defoamers, 12 parts of flow agents, 16 parts of wetting agents, 22 parts of coating antiseptics, 6 parts in tensio-active agent, 14 parts of non-blushing thinners, 14 parts of thickening materials, 6 parts in alkali.
The preparation method of above-mentioned water-based chalkboard paint coating is: with water, auxiliary agent adds in the dispersion cylinder, after stirring, add color stuffing, macromolecule dispersing agent carries out blending dispersion, add filmogen again and fully mix the formation mixture, in mixture, add inorganic pigment successively, the aggretion type powder, thermo-stabilizer, adhesion promoter, linking agent, Mierocrystalline cellulose, flow agent, wetting agent, coating antiseptic, tensio-active agent, non-blushing thinner, alkali fully mixes, add defoamer again, viscosity is adjusted solvent, thickening material fully mixes, again the final mixture of gained is tested, be water-based chalkboard paint coating through the mixture of gained after the assay was approved.
Embodiment three:
The water-based chalkboard paint coating of present embodiment, it is that mass fraction according to following material carries out proportioning:
135 parts in water, 55 parts of auxiliary agents, 78 parts of filmogens, 60 parts of color stuffings, 32 parts of macromolecule dispersing agents, 14 parts of inorganic pigments, 18 parts of aggretion type powders, 22 parts of thermo-stabilizers, 26 parts of adhesion promoters, viscosity are adjusted 8 parts of solvents, 30 parts of linking agents, 18 parts of Mierocrystalline celluloses, 15 parts of defoamers, 12 parts of flow agents, 16 parts of wetting agents, 22 parts of coating antiseptics, 6 parts in tensio-active agent, 15 parts of non-blushing thinners, 12 parts of thickening materials, 5 parts in alkali.
The preparation method of above-mentioned water-based chalkboard paint coating is: with water, auxiliary agent adds in the dispersion cylinder, after stirring, add color stuffing, macromolecule dispersing agent carries out blending dispersion, add filmogen again and fully mix the formation mixture, in mixture, add inorganic pigment successively, the aggretion type powder, thermo-stabilizer, adhesion promoter, linking agent, Mierocrystalline cellulose, flow agent, wetting agent, coating antiseptic, tensio-active agent, non-blushing thinner, alkali fully mixes, add defoamer again, viscosity is adjusted solvent, thickening material fully mixes, again the final mixture of gained is tested, be water-based chalkboard paint coating through the mixture of gained after the assay was approved.
Embodiment four:
The water-based chalkboard paint coating of present embodiment, it is that mass fraction according to following material carries out proportioning:
128 parts in water, 55 parts of auxiliary agents, 76 parts of filmogens, 66 parts of color stuffings, 30 parts of macromolecule dispersing agents, 14 parts of inorganic pigments, 20 parts of aggretion type powders, 28 parts of thermo-stabilizers, 25 parts of adhesion promoters, viscosity are adjusted 9 parts of solvents, 30 parts of linking agents, 14 parts of Mierocrystalline celluloses, 17 parts of defoamers, 14 parts of flow agents, 18 parts of wetting agents, 20 parts of coating antiseptics, 6 parts in tensio-active agent, 14 parts of non-blushing thinners, 12 parts of thickening materials, 4 parts in alkali.
The preparation method of above-mentioned water-based chalkboard paint coating is: with water, auxiliary agent adds in the dispersion cylinder, after stirring, add color stuffing, macromolecule dispersing agent carries out blending dispersion, add filmogen again and fully mix the formation mixture, in mixture, add inorganic pigment successively, the aggretion type powder, thermo-stabilizer, adhesion promoter, linking agent, Mierocrystalline cellulose, flow agent, wetting agent, coating antiseptic, tensio-active agent, non-blushing thinner, alkali fully mixes, add defoamer again, viscosity is adjusted solvent, thickening material fully mixes, again the final mixture of gained is tested, be water-based chalkboard paint coating through the mixture of gained after the assay was approved.
Embodiment five:
The water-based chalkboard paint coating of present embodiment, it is that mass fraction according to following material carries out proportioning:
138 parts in water, 48 parts of auxiliary agents, 68 parts of filmogens, 66 parts of color stuffings, 32 parts of macromolecule dispersing agents, 13 parts of inorganic pigments, 19 parts of aggretion type powders, 28 parts of thermo-stabilizers, 28 parts of adhesion promoters, viscosity are adjusted 8 parts of solvents, 26 parts of linking agents, 16 parts of Mierocrystalline celluloses, 18 parts of defoamers, 14 parts of flow agents, 16 parts of wetting agents, 20 parts of coating antiseptics, 7 parts in tensio-active agent, 12 parts of non-blushing thinners, 12 parts of thickening materials, 7 parts in alkali.
The preparation method of above-mentioned water-based chalkboard paint coating is: with water, auxiliary agent adds in the dispersion cylinder, after stirring, add color stuffing, macromolecule dispersing agent carries out blending dispersion, add filmogen again and fully mix the formation mixture, in mixture, add inorganic pigment successively, the aggretion type powder, thermo-stabilizer, adhesion promoter, linking agent, Mierocrystalline cellulose, flow agent, wetting agent, coating antiseptic, tensio-active agent, non-blushing thinner, alkali fully mixes, add defoamer again, viscosity is adjusted solvent, thickening material fully mixes, again the final mixture of gained is tested, be water-based chalkboard paint coating through the mixture of gained after the assay was approved.
Embodiment six:
The water-based chalkboard paint coating of present embodiment, it is that mass fraction according to following material carries out proportioning:
132 parts in water, 46 parts of auxiliary agents, 88 parts of filmogens, 68 parts of color stuffings, 30 parts of macromolecule dispersing agents, 13 parts of inorganic pigments, 28 parts of aggretion type powders, 28 parts of thermo-stabilizers, 28 parts of adhesion promoters, viscosity are adjusted 6 parts of solvents, 30 parts of linking agents, 15 parts of Mierocrystalline celluloses, 15 parts of defoamers, 14 parts of flow agents, 16 parts of wetting agents, 22 parts of coating antiseptics, 6 parts in tensio-active agent, 15 parts of non-blushing thinners, 12 parts of thickening materials, 6 parts in alkali.
The preparation method of above-mentioned water-based chalkboard paint coating is: with water, auxiliary agent adds in the dispersion cylinder, after stirring, add color stuffing, macromolecule dispersing agent carries out blending dispersion, add filmogen again and fully mix the formation mixture, in mixture, add inorganic pigment successively, the aggretion type powder, thermo-stabilizer, adhesion promoter, linking agent, Mierocrystalline cellulose, flow agent, wetting agent, coating antiseptic, tensio-active agent, non-blushing thinner, alkali fully mixes, add defoamer again, viscosity is adjusted solvent, thickening material fully mixes, again the final mixture of gained is tested, be water-based chalkboard paint coating through the mixture of gained after the assay was approved.
Linking agent is used for linking agent and is used for improving cross-linking density, thereby improves paint film property, and the hydrophilic radical generation crosslinking reaction in linking agent and the coating has improved cross-linking density, thereby has improved performances such as hardness, anti-solvent, water tolerance, chemical resistant properties, sticking power.
Macromolecule dispersing agent adopts impact resistant polystyrene, and macromolecule dispersing agent is used for promoting that pressed powder is scattered in liquid, thereby improves the hardness performance of water-based chalkboard paint coating.
Inorganic pigment adopts colour black, and inorganic pigment can be protected the color of water-based chalkboard paint coating.
The aggretion type powder adopts Degussa carbon black FW200, can make water-based chalkboard paint coating form paint film after light fastness good, not easy to change.
Thermo-stabilizer adopts hot polymerization vinylchlorid, and thermo-stabilizer is used for improving the thermostability of water-based chalkboard paint coating, is convenient to store transportation.
Adhesion promoter adopts solvent type resin, and adhesion promoter is used for improving the adhesion property after the formation of water-based chalkboard paint coating is filmed.
Viscosity is adjusted solvent and is adopted the resene solvent, and viscosity is adjusted the solvent resistance that solvent is used for improving water-based chalkboard paint coating.
Coating antiseptic adopts benzimidazole ester class, and coating antiseptic is used for preventing the mouldy corrosion of coating, improves the work-ing life of water-based chalkboard paint coating.
Tensio-active agent adopts quaternary ammonium compound, and tensio-active agent is convenient to the use of water-based chalkboard paint coating for increasing the surfactivity of water-based chalkboard paint coating.
Non-blushing thinner adopts esters solvent, and non-blushing thinner is used for preventing that water-based chalkboard paint coating from making moist, improves the work-ing life of water-based chalkboard paint coating.
Alkali is used for reducing the irritating smell of water-based chalkboard paint coating.
Other materials adopt common chalkboard paint starting material can satisfy service requirements.
In six above-mentioned embodiment, manufacture craft according to reinforced, dispersion, toning, accent viscosity, detection, filtration is made water-based chalkboard paint coating, the water-based chalkboard paint coating for preparing is carried out sample making, adopt warm air drying that model is carried out forced drying, after finishing the paint film that forms is carried out Performance Detection, detected result is as follows:
From detected result, can draw, water-based chalkboard paint coating of the present invention forms the back cross-linking density height of filming, anti-solvent, chemicals-resistant, temp. variation resistant, anti-ly after-tacks, the effect of anti scuffing, weathering resistance is better, and it is good to form the back light fastness of filming, not easy to change, adhesion effect is good.
The model of getting 100 parts of water-based chalkboard paint coating making of the present invention carries out hardness, anti-solvent, chemicals-resistant, temp. variation resistant, anti-after-tacking, anti scuffing, weathering resistance, photostabilization, tack, the detection of thermostability, 98 increment plate hardness are qualified, 96 increment plate solvent resistances are qualified, 98 increment plate chemical resistant propertiess are qualified, 99 increment plate temp. variation resistants are qualified, 97 parts of anti-performances of after-tacking are qualified, 98 increment plate anti scuffing performances are qualified, 99 increment plate weather resistances are qualified, 96 increment plate light fastness are qualified, 99 increment plate adhesion properties are qualified, 98 increment plate thermostabilitys are qualified, comprehensively draw, the overall qualification rate of water-based chalkboard paint coating property of the present invention is 97.9%, and result of use is good.
Though the present invention is described by the reference preferred embodiment,, those skilled in the art should understand, and in the scope of claims, can do the various variation on form and the details.
Claims (4)
1. water-based chalkboard paint coating, it is characterized in that it is that mass fraction according to following material carries out proportioning: 100 parts～140 parts in water, 40 parts～60 parts of auxiliary agents, 60 parts～90 parts of filmogens, 40 parts～70 parts of color stuffings, 20 parts～35 parts of macromolecule dispersing agents, 10 parts～15 parts of inorganic pigments, 15 parts～30 parts of aggretion type powders, 10 parts～30 parts of thermo-stabilizers, 20 parts～30 parts of adhesion promoters, viscosity is adjusted 5 parts～10 parts of solvents, 20 parts～40 parts of linking agents, 10 parts～20 parts of Mierocrystalline celluloses, 10 parts～20 parts of defoamers, 8 parts～15 parts of flow agents, 9 parts～18 parts of wetting agents, 12 parts～24 parts of coating antiseptics, 4 parts～8 parts in tensio-active agent, 9 parts～16 parts of non-blushing thinners, 10 parts～15 parts of thickening materials, 4 parts～8 parts in alkali.
2. water-based chalkboard paint coating according to claim 1, it is characterized in that it is that mass fraction according to following material carries out proportioning: 120 parts in water, 50 parts of auxiliary agents, 80 parts of filmogens, 60 parts of color stuffings, macromolecule dispersing agent 28,13 parts of inorganic pigments, 18 parts of aggretion type powders, 20 parts of thermo-stabilizers, 25 parts of adhesion promoters, viscosity are adjusted 8 parts of solvents, 24 parts of linking agents, 16 parts of Mierocrystalline celluloses, 16 parts of defoamers, 14 parts of flow agents, 15 parts of wetting agents, 20 parts of coating antiseptics, 6 parts in tensio-active agent, 12 parts of non-blushing thinners, 12 parts of thickening materials, 7 parts in alkali.
3. water-based chalkboard paint coating according to claim 1, it is characterized in that: described filmogen is aqueous polyurethane dispersion.
4. water-based chalkboard paint coating according to claim 1, it is characterized in that: described aggretion type powder is carbon black.