CN109233458A - A kind of aqueousance artificial granite coating and preparation method thereof - Google Patents
A kind of aqueousance artificial granite coating and preparation method thereof Download PDFInfo
- Publication number
- CN109233458A CN109233458A CN201710290872.XA CN201710290872A CN109233458A CN 109233458 A CN109233458 A CN 109233458A CN 201710290872 A CN201710290872 A CN 201710290872A CN 109233458 A CN109233458 A CN 109233458A
- Authority
- CN
- China
- Prior art keywords
- base
- water
- color spot
- preservative
- mass ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueousance artificial granite coating and preparation method thereof, which is characterized in that the configuration including color spot base paint, protective glue, base-material: the configuration raw material of color spot base paint is in mass ratio are as follows: water 800; rubber powder 40, mould inhibitor 3, preservative 4; ethylene glycol 6, elastic emulsion 90, defoaming agent 5；The configuration raw material of protective glue is in mass ratio are as follows: hydroxypropyl methyl cellulose 1.2, water 200, preservative 0.8, defoaming agent 0.4；The configuration raw material of base-material is in mass ratio are as follows: water 10, preservative 8, defoaming agent 12, propylene glycol 25, coalescing agent 40, styrene-acrylic emulsion 700-900, thickener 12-18.Coating of the invention has excellent complete aqueous, free from extraneous odour, and loopful is protected, and waterproof is mould proof, and resistance to soiling is good, alternative natural granite, construction is simple, has many advantages, such as good and cheap, energy conservation and environmental protection, maintenance is simple, superior performance.
Description
Technical field
The present invention relates to building material technical fields more particularly to a kind of aqueousance artificial granite coating and preparation method thereof.
Background technique
Water granite paint --- also having it is referred to as granite-simulating paint, granite mineral varnish, granite paint etc., belongs to true stone
Major class is painted, is the colorful building coating of sand wall-like that water-basedization is free of any solvent type substance.Granite coating is rich in natural flowers
The strength of character intension of hilllock stone, the noble grade of quite aobvious granite, is the novel upgrading kind of traditional natural real stone paint.Through spraying and decorating
Big-pattern, big idea, good-looking, secured afterwards, effect exactly likes the abundant texture of stone material, give as natural granite it is dignified,
Rough, atmosphere visual enjoyment.Single uninteresting sand wall-like lacquer or other building coatings lack the skill of granite texture
Art makings can not also compare favourably with the effect of granite coating.And water granite paint is on this basis, and perfect in the past
Other thick coatings defect, more perfectly show water-borne granite imitate stone system superiority.
Water granite paint breaks through painting scientific principle, exploitation, the special resin substrate for producing system, with the production of innovation
Technology, and the product formula of uniqueness produce water-based list and apply colorful main material, and single main material can have more than 10 kinds or more face
The distribution of color, and the granularity color lump of large and small difference can be formed on demand, can height imitate various granite appearances.Primary coat uses high
It permeates, the sealing emulsion of high intensity and high associativity, then apply resistance to scrub to have color bottom paint.Upper painting then uses high durable and resistant is resistance to
The finish of scrub is arranged in pairs or groups, and is formed resistance to high-intensitive, the high associativity in face, high extension crack resistance, high-dirt-resistance and height the bottom of by
The perfect combination of time property: and material is all water-based coating layer by layer, actually the High-performance green environment-friendly building materials in tunnel.
Summary of the invention
In view of the above drawbacks of the prior art, technical problem to be solved by the invention is to provide a kind of aqueous hilllocks Fang Hua
Rock coating and preparation method thereof, coating of the invention have excellent complete aqueous, free from extraneous odour, and loopful is protected, and waterproof is mould proof, resistance to soiling
Good, alternative natural granite, construction is simple has good and cheap, energy conservation and environmental protection, and maintenance is simple, and superior performance etc. is many excellent
Point.
To achieve the above object, the present invention provides a kind of aqueousance artificial granite coating, which is characterized in that including color spot base
The configuration of plinth paint, protective glue, base-material:
The configuration raw material of color spot base paint is in mass ratio are as follows: water 800, rubber powder 40, mould inhibitor 3, preservative 4, ethylene glycol 6, elasticity
Lotion 90, defoaming agent 5；
The configuration raw material of protective glue is in mass ratio are as follows: hydroxypropyl methyl cellulose 1.2, water 200, preservative 0.8, defoaming agent 0.4；
The configuration raw material of base-material is in mass ratio are as follows: water 10, preservative 8, defoaming agent 12, propylene glycol 25, coalescing agent 40, phenylpropyl alcohol cream
Liquid 700-900, thickener 12-18.
A kind of aqueousance artificial granite preparation method for coating as described in claim 1, it is characterised in that: including following step
It is rapid:
(1) preparation of base paint is equipped with according to the formula, and 1%- is added according to institute's imitation stone color spot shade, actual situation
4% prefabricated titanium dioxide slurry is mixed colours, and mill base and titanium dioxide slurry total amount are no more than 8%, and it is left that 25-45% is added in the base paint for mixing up color
It is stand-by to be adjusted to 75KU or so by right water for viscosity；
(2) it is granulated, water is added in agitator tank, adds 2/3rds of granulating agent solution formula amount, blender dispersion impeller changes into
Agitating paddle, revolving speed are adjusted to 100-300 revs/min, and the water surface forms circinate turbulent flow, and the color spot base paint that injection mixes up viscosity is more than half
When, add remaining granulation agent solution, reinject it is remaining mix up viscosity color spot base paint, be eventually adding PH regulator tune
For whole pH value to 8-9, net particle can be filtered out after twenty minutes by standing；
(3) color spot makes, and protective glue is added in net particle, and cut with dispersion machine according to the size of required color spot, stirred
Uniformly color spot；
(4) base-material is prepared, and by formula by water, preservative, defoaming agent, propylene glycol, coalescing agent successively input cylinder, opens dispersion
Machine stirs evenly, then is stirred evenly to 110-135KU as base-material with styrene-acrylic emulsion, thickener adjustment viscosity；
(5) base-material and color spot are subjected to mixed preparing according to the mass ratio of 1:3, obtain required colored paint.
The beneficial effects of the present invention are:
Coating of the invention has excellent complete aqueous, free from extraneous odour, and loopful is protected, and waterproof is mould proof, and resistance to soiling is good, alternative natural flowers
Gang Yan, construction is simple have many advantages, such as good and cheap, energy conservation and environmental protection, maintenance is simple, superior performance.
Specific embodiment
A kind of aqueousance artificial granite coating, which is characterized in that the configuration including color spot base paint, protective glue, base-material:
The configuration raw material of color spot base paint is in mass ratio are as follows: water 800, rubber powder 40, mould inhibitor 3, preservative 4, ethylene glycol 6, elasticity
Lotion 90, defoaming agent 5；
The configuration raw material of protective glue is in mass ratio are as follows: hydroxypropyl methyl cellulose 1.2, water 200, preservative 0.8, defoaming agent 0.4；
The configuration raw material of base-material is in mass ratio are as follows: water 10, preservative 8, defoaming agent 12, propylene glycol 25, coalescing agent 40, phenylpropyl alcohol cream
Liquid 700-900, thickener 12-18.
A kind of aqueousance artificial granite preparation method for coating as described in claim 1, it is characterised in that: including following step
It is rapid:
(1) preparation of base paint is equipped with according to the formula, and 1%- is added according to institute's imitation stone color spot shade, actual situation
4% prefabricated titanium dioxide slurry is mixed colours, and mill base and titanium dioxide slurry total amount are no more than 8%, and it is left that 25-45% is added in the base paint for mixing up color
It is stand-by to be adjusted to 75KU or so by right water for viscosity；
(2) it is granulated, water is added in agitator tank, adds 2/3rds of granulating agent solution formula amount, blender dispersion impeller changes into
Agitating paddle, revolving speed are adjusted to 100-300 revs/min, and the water surface forms circinate turbulent flow, and the color spot base paint that injection mixes up viscosity is more than half
When, add remaining granulation agent solution, reinject it is remaining mix up viscosity color spot base paint, be eventually adding PH regulator tune
For whole pH value to 8-9, net particle can be filtered out after twenty minutes by standing；
(3) color spot makes, and protective glue is added in net particle, and cut with dispersion machine according to the size of required color spot, stirred
Uniformly color spot；
(4) base-material is prepared, and by formula by water, preservative, defoaming agent, propylene glycol, coalescing agent successively input cylinder, opens dispersion
Machine stirs evenly, then is stirred evenly to 110-135KU as base-material with styrene-acrylic emulsion, thickener adjustment viscosity；
(5) base-material and color spot are subjected to mixed preparing according to the mass ratio of 1:3, obtain required colored paint.
Characteristic of the invention is as follows:
1. complete Water-borne modification: complete aqueous, free from extraneous odour, loopful are protected.
2. high simulation quality: coating is uneven, color is various, decorative pattern is uniform, can imitate naturally, wonderful workmanship excelling nature surpasses day
So.
3. decorative effect is peculiar: plasticity is strong, cooperates the different middle layer property made is plastic to produce different sensorial effects.
4. crack resistance: there is good ductility, metope fine cracks can be covered.
5. coating is excellent: washability, waterproof is mould proof, and resistance to soiling is excellent, persistently keeps cleaner appearance.
6. construction is fast: construction is simple, single spraying apply, one-pass molding.
7. cost performance is high: compared with natural granite, cost is its 30-40% or so.
8. light material: no matter comparing natural granite or lacquer, all greatly lighten the burden to wall, meet development
Direction.
9. renovating fast: the part renovation and repairing of wall are safe and easy, can mix the spurious with the genuine completely.
Mainly it is used as wall body decoration use, applicable basal plane has: cement sand pulp, concrete surface, cement fibrolite plate, various guarantors
Warm layer surface, aluminium sheet, timber, heavy metal plate etc., be widely used in all types of buildings for example villa, commercial and residential building, company, hotel,
The external and internal wall surface decoration of the public places such as bar, the packet Room, leisure center, building hall.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be within the scope of protection determined by the claims.
Claims (2)
1. a kind of aqueousance artificial granite coating, which is characterized in that the configuration including color spot base paint, protective glue, base-material:
The configuration raw material of color spot base paint is in mass ratio are as follows: water 800, rubber powder 40, mould inhibitor 3, preservative 4, ethylene glycol 6, elasticity
Lotion 90, defoaming agent 5；
The configuration raw material of protective glue is in mass ratio are as follows: hydroxypropyl methyl cellulose 1.2, water 200, preservative 0.8, defoaming agent 0.4；
The configuration raw material of base-material is in mass ratio are as follows: water 10, preservative 8, defoaming agent 12, propylene glycol 25, coalescing agent 40, phenylpropyl alcohol cream
Liquid 700-900, thickener 12-18.
2. a kind of aqueousance artificial granite preparation method for coating as described in claim 1, it is characterised in that: the following steps are included:
(1) preparation of base paint is equipped with according to the formula, and 1%- is added according to institute's imitation stone color spot shade, actual situation
4% prefabricated titanium dioxide slurry is mixed colours, and mill base and titanium dioxide slurry total amount are no more than 8%, and it is left that 25-45% is added in the base paint for mixing up color
It is stand-by to be adjusted to 75KU or so by right water for viscosity；
(2) it is granulated, water is added in agitator tank, adds 2/3rds of granulating agent solution formula amount, blender dispersion impeller changes into
Agitating paddle, revolving speed are adjusted to 100-300 revs/min, and the water surface forms circinate turbulent flow, and the color spot base paint that injection mixes up viscosity is more than half
When, add remaining granulation agent solution, reinject it is remaining mix up viscosity color spot base paint, be eventually adding PH regulator tune
For whole pH value to 8-9, net particle can be filtered out after twenty minutes by standing；
(3) color spot makes, and protective glue is added in net particle, and cut with dispersion machine according to the size of required color spot, stirred
Uniformly color spot；
(4) base-material is prepared, and by formula by water, preservative, defoaming agent, propylene glycol, coalescing agent successively input cylinder, opens dispersion
Machine stirs evenly, then is stirred evenly to 110-135KU as base-material with styrene-acrylic emulsion, thickener adjustment viscosity；
(5) base-material and color spot are subjected to mixed preparing according to the mass ratio of 1:3, obtain required colored paint.