CN105524576A - Mildewproof and waterproof tile joint filling agent - Google Patents

Mildewproof and waterproof tile joint filling agent Download PDF

Info

Publication number
CN105524576A
CN105524576A CN201610039240.1A CN201610039240A CN105524576A CN 105524576 A CN105524576 A CN 105524576A CN 201610039240 A CN201610039240 A CN 201610039240A CN 105524576 A CN105524576 A CN 105524576A
Authority
CN
China
Prior art keywords
parts
agent
mildew
emulsion
joint filling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610039240.1A
Other languages
Chinese (zh)
Inventor
张玉华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi University
Original Assignee
Guangxi University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi University filed Critical Guangxi University
Priority to CN201610039240.1A priority Critical patent/CN105524576A/en
Publication of CN105524576A publication Critical patent/CN105524576A/en
Pending legal-status Critical Current

Abstract

The invention discloses a mildewproof and waterproof tile joint filling agent, prepared from the following components in terms of parts by mass: 5 to 15 parts of water, 0.3 to 1.0 part of potassium methane-siliconic alkoxide, 0.2 to 0.3 part of dispersant, 0.06 to 0.1 part of wetting agent, 16 to 35 parts of high-activity quartz powder, 25 to 45 parts of precipitated barium sulphate, 0.1 to 0.4 part of filling agent, 12 to 28 parts of elastic emulsion, 2 to 9 parts of silica sol, 1 to 4 parts of silicon dioxide and 0.15 to 0.5 part of surface antibacterial agent. The mildewproof and waterproof tile joint filling agent disclosed by the invention has the advantages that the agent is used for building joint treatment, so that the long filling and fixation effects are achieved, and the shrinkage crack is prevented again.

Description

A kind of tile grout of anti-mildew waterproof
Technical field
The invention belongs to building field, particularly relate to a kind of tile grout of anti-mildew waterproof.
Background technology
Spackling tackiness is strong, it is little to shrink, color pull-out capacity strong, has the flexibility of Anti-cracking, and decoration texture is good, compressive resistance is wear-resistant, antimycotic feature, makes it perfectly can repair cracking or the breakage of floor surface, can also paint in its surface, have good water-repellancy.Spackling rich color, also can prepare color voluntarily, thus more and more favor by guest, for reaching good result, must be noted that during use.
In the buildings of China, ceramic tile has become one of important architectural coating finishing material, is widely used in
In the Decorating Project at the positions such as the inner-outer wall of buildings and ground.At present, tile decorative surface spackling used is adopt Portland cement, building fine sand, mineral dye through hybrid packed mostly, temper as the packing material of ceramic tile seam during use, apply this tile grout constructed after not long time through wind, Exposure to Sunlight, drench with rain, under the impact of the factor of natural environment of freeze thawing etc., just there will be the whiting of large-area ceramic tile the metope accumulation of salt in the surface soil, shrinkage crack, go mouldy, even ceramic tile quality problems and the potential safety hazard such as to come off.In order to the design effect obtained and embody buildings effectively reduces potential safety hazard, the high-quality tile grout of the accumulation of salt in the surface soil is just particularly unimportant for preparation one.
Summary of the invention
For solving above-mentioned Problems existing, the invention provides a kind of tile grout of anti-mildew waterproof.
Technical scheme of the present invention is as follows:
A tile grout for anti-mildew waterproof, the mass fraction proportion of each component and component is: water 5-15 part, methyl silanol potassium 0.3-1.0 part, dispersion agent 0.2-0.3 part, wetting agent 0.06-0.1 part, high reactivity silica powder 16-35 part, process white 25-45 part, weighting agent 0.1-0.4 part, elastic emulsion 12-28 part, silicon sol 2-9 part, silica 1-4 parts, antibacterial surface agent 0.15-0.5 part.
Further illustrate, described ceramic tile joint filling cream also comprises mill base.
Further illustrate, described weighting agent adopts one or more combinations in heavy calcium carbonate, talcum powder, kaolin, barium sulfate and mica powder.
Further illustrate, described emulsion adopts pure-acrylic emulsion or benzene emulsion or VAE emulsion.
Further illustrate, described ceramic tile joint filling cream also comprises Vltra tears: 0.1-0.3 part, titanium dioxide 3-5 part, wood fibre 0.1-0.3 part, film coalescence aid 0.3-1.2 part, frostproofer 1-2 part, sanitas 0.1-0.3 part.
Further illustrate, described high reactivity silica powder is non-crystal structure, and through organism surface modification, D10≤2.5 μm in size distribution, particle shape is ball-type, dioxide-containing silica >=99%.
Wetting agent has emulsifying property, and elastic emulsion has adhesive effect.
The invention has the beneficial effects as follows:
Methyl silanol potassium in the ceramic tile joint filling cream of invention, in ceramic tile joint filling cream drying process, can infiltrate matrix, forms siloxane bond, increase the bonding force of same basic unit with substrate surface; Have good cohesive force to base material, and a talcum powder tool sheet structure, can intercept steam through with enhancing tensile property, strongthener resistance to cleavage.Ceramic tile joint filling cream of the present invention, for building gap process, provides permanent filling and fixes, preventing shrinkage cracking again.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, exercising ordinary skill, not making the every other embodiment obtained under creative work prerequisite, belongs to the scope of protection of the invention.
Embodiment 1
A tile grout for anti-mildew waterproof, the mass fraction proportion of each component and component is: 5 parts, water, methyl silanol potassium 0.3 part, dispersion agent 0.2 part, wetting agent 0.06 part, high reactivity silica powder 16 parts, process white 25 parts, weighting agent 0.1 part, elastic emulsion 12 parts, silicon sol 2 parts, silica 1 part, antibacterial surface agent 0.15 part.
Ceramic tile joint filling cream also comprises mill base.Weighting agent adopts heavy calcium carbonate.Emulsion adopts pure-acrylic emulsion or benzene emulsion.Ceramic tile joint filling cream also comprises Vltra tears: 0.1 part, titanium dioxide 3 parts, wood fibre 0.1 part, film coalescence aid 0.3 part, frostproofer 1 part, sanitas 0.1 part.High reactivity silica powder is non-crystal structure, and through organism surface modification, D10≤2.5 μm in size distribution, particle shape is ball-type, dioxide-containing silica >=99%.
Embodiment 2
A tile grout for anti-mildew waterproof, the mass fraction proportion of each component and component is: 15 parts, water, methyl silanol potassium 1.0 parts, dispersion agent 0.3 part, wetting agent 0.1 part, high reactivity silica powder 35 parts, process white 45 parts, weighting agent 0.4 part, elastic emulsion 28 parts, silicon sol 9 parts, silicon-dioxide 4 parts, antibacterial surface agent 0.5 part.
Ceramic tile joint filling cream also comprises mill base.Weighting agent adopts heavy calcium carbonate.Emulsion adopts pure-acrylic emulsion or benzene emulsion.Ceramic tile joint filling cream also comprises Vltra tears: 0.3 part, titanium dioxide 5 parts, wood fibre 0.3 part, film coalescence aid 1.2 parts, frostproofer 2 parts, sanitas 0.3 part.High reactivity silica powder is non-crystal structure, and through organism surface modification, D10≤2.5 μm in size distribution, particle shape is ball-type, dioxide-containing silica >=99%.
Embodiment 3
A tile grout for anti-mildew waterproof, the mass fraction proportion of each component and component is: 10 parts, water, methyl silanol potassium 0.9 part, dispersion agent 0.25 part, wetting agent 0.07 part, high reactivity silica powder 20 parts, process white 30 parts, weighting agent 0.2 part, elastic emulsion 20 parts, silicon sol 7 parts, silicon-dioxide 2 parts, antibacterial surface agent 0.2 part.
Ceramic tile joint filling cream also comprises mill base.Weighting agent adopts heavy calcium carbonate.Emulsion adopts pure-acrylic emulsion or benzene emulsion.Ceramic tile joint filling cream also comprises Vltra tears: 0.2 part, titanium dioxide 4 parts, wood fibre 0.2 part, film coalescence aid 0.6 part, frostproofer 2 parts, sanitas 0.2 part.High reactivity silica powder is non-crystal structure, and through organism surface modification, D10≤2.5 μm in size distribution, particle shape is ball-type, dioxide-containing silica >=99%.
Above-described embodiment is the present invention's preferably embodiment; but embodiments of the present invention are not restricted to the described embodiments; change, the modification done under other any does not deviate from spirit of the present invention and principle, substitute, combine, simplify; all should be the substitute mode of equivalence, be included within protection scope of the present invention.

Claims (6)

1. the tile grout of an anti-mildew waterproof, it is characterized in that, the mass fraction proportion of each component and component is: water 5-15 part, methyl silanol potassium 0.3-1.0 part, dispersion agent 0.2-0.3 part, wetting agent 0.06-0.1 part, high reactivity silica powder 16-35 part, process white 25-45 part, weighting agent 0.1-0.4 part, elastic emulsion 12-28 part, silicon sol 2-9 part, silica 1-4 parts, antibacterial surface agent 0.15-0.5 part.
2. the tile grout of anti-mildew waterproof according to claim 1, is characterized in that, described ceramic tile joint filling cream also comprises mill base.
3. the tile grout of anti-mildew waterproof according to claim 1, is characterized in that, described weighting agent adopts one or more combinations in heavy calcium carbonate, talcum powder, kaolin, barium sulfate and mica powder.
4. the tile grout of anti-mildew waterproof according to claim 1, is characterized in that, described emulsion adopts pure-acrylic emulsion or benzene emulsion or VAE emulsion.
5. the tile grout of anti-mildew waterproof according to claim 1, it is characterized in that, described ceramic tile joint filling cream also comprises Vltra tears: 0.1-0.3 part, titanium dioxide 3-5 part, wood fibre 0.1-0.3 part, film coalescence aid 0.3-1.2 part, frostproofer 1-2 part, sanitas 0.1-0.3 part.
6. the tile grout of anti-mildew waterproof according to claim 1, is characterized in that, described high reactivity silica powder is non-crystal structure, and through organism surface modification, D10≤2.5 μm in size distribution, particle shape is ball-type, dioxide-containing silica >=99%.
CN201610039240.1A 2016-01-21 2016-01-21 Mildewproof and waterproof tile joint filling agent Pending CN105524576A (en)