CN107311595A - A kind of waterproof high viscosity tile grout and preparation method thereof - Google Patents
A kind of waterproof high viscosity tile grout and preparation method thereof Download PDFInfo
- Publication number
- CN107311595A CN107311595A CN201710649466.8A CN201710649466A CN107311595A CN 107311595 A CN107311595 A CN 107311595A CN 201710649466 A CN201710649466 A CN 201710649466A CN 107311595 A CN107311595 A CN 107311595A
- Authority
- CN
- China
- Prior art keywords
- parts
- high viscosity
- cellulose
- tile grout
- waterproof high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of waterproof high viscosity tile grout, the waterproof high viscosity tile grout includes following raw material according to parts by weight：30 ~ 60 parts of adhesive, extraordinary 20 ~ 40 parts of white cement, 10 ~ 30 parts of waterproofing agent, 15 ~ 30 parts of Ludox, dispersed 10 ~ 30 parts of latex powder, 5 ~ 20 parts of acrylic resin, 6 ~ 18 parts of cellulose ether, 6 ~ 9 parts of organic silica gel, 4 ~ 8 parts of aluminium-magnesium silicate, 6 ~ 24 parts of thickener, 5 ~ 10 parts of retarder, 8 ~ 16 parts of mould inhibitor, 9 ~ 12 parts of antibacterial surface agent and water.The waterproof high viscosity tile grout that the present invention is prepared has adhesive strength height after low-shrinkage, high solidity, high intensity, hardening, does not have the phenomenon of cracking, percolating water after joint filling.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of waterproof high viscosity tile grout and preparation method thereof.
Background technology
Gap filler has the spies such as strong stickiness, the small, Anti-cracking of contraction, compressive resistance, wear-resistant, antifungi, good water proofing property
Point.
Ceramic tile has turned into one of building and ornament materials that Modern Heavy is wanted, is widely used for interior and exterior wall and the ground of building
Decorations, needed between ceramic tile and ceramic tile reserve certain gap can so avoid expanding with heat and contract with cold and producing hollowing, so
The gap is accomplished by tile grout to fill, and the gap filler of most ceramic tile is that ordinary cement, building fine sand, inorganic pigment etc. add
Water reconciles the packing material stitched as ceramic tile, this filler easily occur under the natural environment contraction fissure, go mouldy, even porcelain
Brick such as comes off at the quality problems, so it is significant to prepare a kind of high-quality tile grout.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of waterproof high viscosity tile grout and its
Preparation method.
To achieve the above object, the technical scheme is that：A kind of waterproof high viscosity tile grout, waterproof height is viscous
Spend tile grout includes following raw material according to parts by weight：30 ~ 60 parts of adhesive, extraordinary 20 ~ 40 parts of white cement, waterproofing agent 10
~ 30 parts, it is 15 ~ 30 parts of Ludox, dispersed 10 ~ 30 parts of latex powder, 5 ~ 20 parts of acrylic resin, 6 ~ 18 parts of cellulose ether, organic
6 ~ 9 parts of silica gel, 4 ~ 8 parts of aluminium-magnesium silicate, 6 ~ 24 parts of thickener, 5 ~ 10 parts of retarder, 8 ~ 16 parts of mould inhibitor, antibacterial surface agent 9 ~ 12
Part and water.
Preferably, be somebody's turn to do the heat-preservation building paint containing nanoparticle includes following raw material according to parts by weight：30 parts of adhesive,
Extraordinary 20 parts of white cement, 10 parts of waterproofing agent, 15 parts of Ludox, dispersed 10 parts of latex powder, 5 parts of acrylic resin, cellulose
6 parts of ether, 6 parts of organic silica gel, 4 parts of aluminium-magnesium silicate, 6 parts of thickener, 5 parts of retarder, 8 parts of mould inhibitor, 9 parts of antibacterial surface agent and
Water.
Preferably, described adhesive by weight percentage by 25% ~ 30% amino resins, 20% ~ 30% organic siliconresin, 15% ~
25% acrylic acid modified resin is constituted.
Preferably, the dispersed latex powder be vinylacetate and ethylene copolymer rubber powder, vinylacetate and ethene and
Higher aliphatic vinyl acetate ternary polymerization rubber powder, vinylacetate and acrylate and higher aliphatic vinyl acetate ternary polymerization glue
Powder, ethene and vinyl chloride and moon silicic acid vinyl acetate ternary polymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization glue
One or more in powder.
Preferably, the cellulose ether is methylcellulose, benzylcellulose, hydroxypropyl methyl cellulose, cyanoethyl fibre
Tie up element, hydroxyethyl cellulose, benzyl hydroxyethylmethylcellulose, carboxymethyl cellulose, base cyanethyl cellulose, ethyl cellulose,
One or more in benzyl cellulose and carboxymethyl hydroxyethyl cellulose.
A kind of preparation method of waterproof high viscosity tile grout, is mainly included the following steps that：
Step 1：Adhesive, extraordinary white cement, waterproofing agent are added to the water 1 ~ 3h of stirring, mixture is obtained；
Step 2：By Ludox, dispersed latex powder, acrylic resin, cellulose ether, organic silica gel, aluminium-magnesium silicate, thickener
Add step 1 in gained mixture in, be placed in mixer, with 800 ~ 1000r/min of rotating speed carry out uniform stirring 20 ~
40min, obtains mixture；
Step 3：Retarder, mould inhibitor, antibacterial surface agent are added in step 2 gained mixture, are placed in reactor, is heated
To 40 ~ 60 DEG C, 2 ~ 4h is kept, the waterproof high viscosity tile grout is obtained.
Preferably, the waterproofing agent inorganic aluminate water-proof agent in the step 1.
Preferably, need to be heated to 40 ~ 50 DEG C before mixture stirring in the step 2.
The beneficial effects of the present invention are：A kind of waterproof high viscosity tile grout and its preparation side that the present invention is provided
The adhesive added in method, present invention sheet has the viscosity of high intensity, can effectively strengthen the degree of adhesion between ceramic tile, it is ensured that
The using effect of gap filler；The inorganic aluminate water-proof agent of addition can effectively improve the water proofing property after gap filler use；Present invention system
Standby obtained waterproof high viscosity tile grout has adhesive strength height after low-shrinkage, high solidity, high intensity, hardening, fills out
The phenomenon of cracking, percolating water is not had after seam.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is described in further detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, do not limit
The fixed present invention.
Embodiment 1
A kind of waterproof high viscosity tile grout, the waterproof high viscosity tile grout includes following raw material according to parts by weight：It is viscous
30 parts of mixture, extraordinary 20 parts of white cement, 10 parts of waterproofing agent, 15 parts of Ludox, dispersed 10 parts of latex powder, acrylic resin 5
Part, 6 parts of cellulose ether, 6 parts of organic silica gel, 4 parts of aluminium-magnesium silicate, 6 parts of thickener, 5 parts of retarder, 8 parts of mould inhibitor, antibacterial surface
9 parts of agent and water.
Preferably, described adhesive is changed by 25% amino resins, 20% organic siliconresin, 15% acrylic acid by weight percentage
Property resin constitute.
Preferably, the dispersed latex powder be vinylacetate and ethylene copolymer rubber powder, vinylacetate and ethene and
Higher aliphatic vinyl acetate ternary polymerization rubber powder, vinylacetate and acrylate and higher aliphatic vinyl acetate ternary polymerization glue
Powder, ethene and vinyl chloride and moon silicic acid vinyl acetate ternary polymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization glue
One or more in powder.
Preferably, the cellulose ether is methylcellulose, benzylcellulose, hydroxypropyl methyl cellulose, cyanoethyl fibre
Tie up element, hydroxyethyl cellulose, benzyl hydroxyethylmethylcellulose, carboxymethyl cellulose, base cyanethyl cellulose, ethyl cellulose,
One or more in benzyl cellulose and carboxymethyl hydroxyethyl cellulose.
A kind of preparation method of waterproof high viscosity tile grout, is mainly included the following steps that：
Step 1：Adhesive, extraordinary white cement, waterproofing agent are added to the water stirring 1h, mixture is obtained；
Step 2：By Ludox, dispersed latex powder, acrylic resin, cellulose ether, organic silica gel, aluminium-magnesium silicate, thickener
Add in mixture obtained by step 1, be placed in mixer, uniform stirring 20min is carried out with rotating speed 800r/min, mixed
Compound；
Step 3：Retarder, mould inhibitor, antibacterial surface agent are added in step 2 gained mixture, are placed in reactor, is heated
To 40 DEG C, 2h is kept, the waterproof high viscosity tile grout is obtained.
Preferably, the waterproofing agent inorganic aluminate water-proof agent in the step 1.
Preferably, need to be heated to 40 DEG C before mixture stirring in the step 2.
Embodiment 2
A kind of waterproof high viscosity tile grout, the waterproof high viscosity tile grout includes following raw material according to parts by weight：It is viscous
45 parts of mixture, extraordinary 30 parts of white cement, 20 parts of waterproofing agent, 23 parts of Ludox, dispersed 20 parts of latex powder, acrylic resin 13
Part, 12 parts of cellulose ether, 8 parts of organic silica gel, 6 parts of aluminium-magnesium silicate, 15 parts of thickener, 7 parts of retarder, 12 parts of mould inhibitor, surface
10 parts of antiseptic and water.
Preferably, described adhesive is changed by 27% amino resins, 25% organic siliconresin, 20% acrylic acid by weight percentage
Property resin constitute.
Preferably, the dispersed latex powder be vinylacetate and ethylene copolymer rubber powder, vinylacetate and ethene and
Higher aliphatic vinyl acetate ternary polymerization rubber powder, vinylacetate and acrylate and higher aliphatic vinyl acetate ternary polymerization glue
Powder, ethene and vinyl chloride and moon silicic acid vinyl acetate ternary polymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization glue
One or more in powder.
Preferably, the cellulose ether is methylcellulose, benzylcellulose, hydroxypropyl methyl cellulose, cyanoethyl fibre
Tie up element, hydroxyethyl cellulose, benzyl hydroxyethylmethylcellulose, carboxymethyl cellulose, base cyanethyl cellulose, ethyl cellulose,
One or more in benzyl cellulose and carboxymethyl hydroxyethyl cellulose.
A kind of preparation method of waterproof high viscosity tile grout, is mainly included the following steps that：
Step 1：Adhesive, extraordinary white cement, waterproofing agent are added to the water stirring 2h, mixture is obtained；
Step 2：By Ludox, dispersed latex powder, acrylic resin, cellulose ether, organic silica gel, aluminium-magnesium silicate, thickener
Add in mixture obtained by step 1, be placed in mixer, uniform stirring 30min is carried out with rotating speed 900r/min, mixed
Compound；
Step 3：Retarder, mould inhibitor, antibacterial surface agent are added in step 2 gained mixture, are placed in reactor, is heated
To 50 DEG C, 3h is kept, the waterproof high viscosity tile grout is obtained.
Preferably, the waterproofing agent inorganic aluminate water-proof agent in the step 1.
Preferably, need to be heated to 45 DEG C before mixture stirring in the step 2.
Embodiment 3
A kind of waterproof high viscosity tile grout, the waterproof high viscosity tile grout includes following raw material according to parts by weight：It is viscous
60 parts of mixture, extraordinary 40 parts of white cement, 30 parts of waterproofing agent, 30 parts of Ludox, dispersed 30 parts of latex powder, acrylic resin 20
Part, 18 parts of cellulose ether, 9 parts of organic silica gel, 8 parts of aluminium-magnesium silicate, 24 parts of thickener, 10 parts of retarder, 16 parts of mould inhibitor, surface
12 parts of antiseptic and water.
Preferably, described adhesive is changed by 30% amino resins, 30% organic siliconresin, 25% acrylic acid by weight percentage
Property resin constitute.
Preferably, the dispersed latex powder be vinylacetate and ethylene copolymer rubber powder, vinylacetate and ethene and
Higher aliphatic vinyl acetate ternary polymerization rubber powder, vinylacetate and acrylate and higher aliphatic vinyl acetate ternary polymerization glue
Powder, ethene and vinyl chloride and moon silicic acid vinyl acetate ternary polymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization glue
One or more in powder.
Preferably, the cellulose ether is methylcellulose, benzylcellulose, hydroxypropyl methyl cellulose, cyanoethyl fibre
Tie up element, hydroxyethyl cellulose, benzyl hydroxyethylmethylcellulose, carboxymethyl cellulose, base cyanethyl cellulose, ethyl cellulose,
One or more in benzyl cellulose and carboxymethyl hydroxyethyl cellulose.
A kind of preparation method of waterproof high viscosity tile grout, is mainly included the following steps that：
Step 1：Adhesive, extraordinary white cement, waterproofing agent are added to the water stirring 3h, mixture is obtained；
Step 2：By Ludox, dispersed latex powder, acrylic resin, cellulose ether, organic silica gel, aluminium-magnesium silicate, thickener
Add in mixture obtained by step 1, be placed in mixer, uniform stirring 40min is carried out with rotating speed 1000r/min, obtained
Mixture；
Step 3：Retarder, mould inhibitor, antibacterial surface agent are added in step 2 gained mixture, are placed in reactor, is heated
To 60 DEG C, 4h is kept, the waterproof high viscosity tile grout is obtained.
Preferably, the waterproofing agent inorganic aluminate water-proof agent in the step 1.
Preferably, need to be heated to 50 DEG C before mixture stirring in the step 2.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, although with reference to foregoing reality
Apply example the present invention is described in detail, for those skilled in the art, it still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic.All essences in the present invention
God is with principle, and any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (8)
1. a kind of waterproof high viscosity tile grout, it is characterised in that the waterproof high viscosity tile grout is according to parts by weight bag
Include following raw material：It is 30 ~ 60 parts of adhesive, extraordinary 20 ~ 40 parts of white cement, 10 ~ 30 parts of waterproofing agent, 15 ~ 30 parts of Ludox, scattered
10 ~ 30 parts of latex powder of property, 5 ~ 20 parts of acrylic resin, 6 ~ 18 parts of cellulose ether, 6 ~ 9 parts of organic silica gel, 4 ~ 8 parts of aluminium-magnesium silicate,
6 ~ 24 parts of thickener, 5 ~ 10 parts of retarder, 8 ~ 16 parts of mould inhibitor, 9 ~ 12 parts of antibacterial surface agent and water.
2. a kind of waterproof high viscosity tile grout according to claim 1, it is characterised in that nanoparticle should be contained
Heat-preservation building paint includes following raw material according to parts by weight：30 parts of adhesive, extraordinary 20 parts of white cement, 10 parts of waterproofing agent, silicon
15 parts of colloidal sol, dispersed 10 parts of latex powder, 5 parts of acrylic resin, 6 parts of cellulose ether, 6 parts of organic silica gel, 4 parts of aluminium-magnesium silicate,
6 parts of thickener, 5 parts of retarder, 8 parts of mould inhibitor, 9 parts of antibacterial surface agent and water.
3. a kind of waterproof high viscosity tile grout according to claim 1, it is characterised in that described adhesive is by weight
Percentage is made up of 25% ~ 30% amino resins, 20% ~ 30% organic siliconresin, 15% ~ 25% acrylic acid modified resin.
4. a kind of waterproof high viscosity tile grout according to claim 1, it is characterised in that the dispersed latex powder
For vinylacetate and ethylene copolymer rubber powder, vinylacetate and ethene and higher aliphatic vinyl acetate ternary polymerization rubber powder, vinegar
Vinyl acetate and acrylate and higher aliphatic vinyl acetate ternary polymerization rubber powder, ethene and vinyl chloride and moon silicic acid vinyl acetate three
One or more in first copolymerization rubber powder, vinylacetate and higher aliphatic vinyl acetate copolymerization rubber powder.
5. a kind of waterproof high viscosity tile grout according to claim 1, it is characterised in that the cellulose ether is first
Base cellulose, benzylcellulose, hydroxypropyl methyl cellulose, cyanethyl cellulose, hydroxyethyl cellulose, benzyl hydroxyethyl methyl are fine
Tie up in element, carboxymethyl cellulose, base cyanethyl cellulose, ethyl cellulose, benzyl cellulose and carboxymethyl hydroxyethyl cellulose
One or more.
6. a kind of preparation method of waterproof high viscosity tile grout, it is characterised in that mainly include the following steps that：
Step 1：Adhesive, extraordinary white cement, waterproofing agent are added to the water 1 ~ 3h of stirring, mixture is obtained；
Step 2：By Ludox, dispersed latex powder, acrylic resin, cellulose ether, organic silica gel, aluminium-magnesium silicate, thickener
Add step 1 in gained mixture in, be placed in mixer, with 800 ~ 1000r/min of rotating speed carry out uniform stirring 20 ~
40min, obtains mixture；
Step 3：Retarder, mould inhibitor, antibacterial surface agent are added in step 2 gained mixture, are placed in reactor, is heated
To 40 ~ 60 DEG C, 2 ~ 4h is kept, the waterproof high viscosity tile grout is obtained.
7. a kind of preparation method of waterproof high viscosity tile grout according to claim 6, it is characterised in that the step
Waterproofing agent inorganic aluminate water-proof agent in rapid 1.
8. a kind of preparation method of waterproof high viscosity tile grout according to claim 6, it is characterised in that the step
Need to be heated to 40 ~ 50 DEG C before mixture stirring in rapid 2.