CN109881854A - A kind of flexible compound coating patch material of color spot and its manufacture and construction method - Google Patents
A kind of flexible compound coating patch material of color spot and its manufacture and construction method Download PDFInfo
- Publication number
- CN109881854A CN109881854A CN201910148938.0A CN201910148938A CN109881854A CN 109881854 A CN109881854 A CN 109881854A CN 201910148938 A CN201910148938 A CN 201910148938A CN 109881854 A CN109881854 A CN 109881854A
- Authority
- CN
- China
- Prior art keywords
- layer
- color spot
- coating
- flexible
- forms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of manufacturing methods of the flexible compound coating of color spot patch material, include the following steps: that (a) provides a kind of carrier layer, carrier layer is flexible material;(b) bottom coating is processed in the carrier layer, forms prime coat;(c) flexible texture filling paint is sprayed on the prime coat, forms flexible texture filled layer;(d) flexible texture pigmented finiss is sprayed on the flexible texture filled layer, forms flexible texture coloring layer;(e) common pigmented finiss is sprayed on the flexible texture coloring layer, forms common coloring layer;(f) color spot coating is sprayed on the common coloring layer, forms color spot layer;(g) aqueous finishing varnish is sprayed on the color spot layer, forms aqueous finishing varnish layer.By above-mentioned technique be prepared it is a kind of it is counter-bending it is good, be easy bonding, easily, the flexible compound coating of color spot of construction color spot that certain density, one or more different colours are readily rendered as with flexible coating surface paste material.
Description
Technical field
The present invention relates to a kind of flexible compound coating of color spot patch material and its manufacture and construction methods.
Background technique
The exterior wall surface decoration construction of building trade at present, if wanting to make the flexible texture dress with color spot in construction surface
Facing usually has following methods:
One, for leveling putty construction, closing (sealing) priming paint construction, main material (such as multicolor finish, lacquer, texture coating,
Plucking or tangerine line coating etc.) construction, finishing varnish construction.Coating is transported as a kind of liquid semi-finished product to building site, is pressed by worker
Process sequence from putty to finishing coat is successively constructed into finished product coating in the exterior wall outer surface of building.This exterior coating is applied
The shortcomings that work mode, is that physical strength is heavy, long in time limit, and construction environment is severe, and construction quality is more difficult to control.
Two, by the way of integral decorative plate, plate is pacified by the way of steel extension or fastener in plant produced in exterior wall
Dress.The weight bearing load of the costs rather expensive of this mode, exterior wall is very big, just in case falling from high building, there are generation significant damages
A possibility that (similar with the harm that high building ceramic tile falls off).
Three, the hardness porcelain tendre paste block made of sintering, thick and heavy, it is inconvenient to paste, and stickiness is bad.
Four, more convenient using hard coating patch material, but patch material integral hardness is larger, it is disconnected to be easy, and cannot when construction
Using a large amount of glue, otherwise glue is not easy solid, the better glue of cohesive force need to be used, so that construction cost is higher.
Summary of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide a kind of flexible compound coating of color spot paste material, one
The flexible compound coating patch material manufacturing method of the kind color spot and a kind of flexible compound coating patch material manufacture suitable for the color spot
The patch material construction method of method.
The scheme of the invention is be achieved:
A kind of manufacturing method of the flexible compound coating patch material of color spot, includes the following steps:
(a) a kind of carrier layer is provided, the carrier layer is flexible material layer;
(b) bottom coating is processed in the carrier layer, forms prime coat;
(C) flexible texture filling paint is sprayed on the prime coat, forms flexible texture filled layer;
(d) flexible texture pigmented finiss is sprayed on the flexible texture filled layer, forms flexible texture coloring layer;
(e) common pigmented finiss is sprayed on the flexible texture coloring layer, forms common coloring layer;
(f) color spot coating is sprayed on the common coloring layer, forms color spot layer;
(g) aqueous finishing varnish is sprayed on the color spot layer, forms aqueous finishing varnish layer.
As present invention further optimization mode, the carrier layer is glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock
One of cotton, rock wool blanket, silicate fiber cloth or silicate fiber blanket.
As present invention further optimization mode, the color spot coating includes the component of following proportion:
As present invention further optimization mode, the acrylic emulsion includes styrene-acrylic emulsion, pure-acrylic emulsion, the third cream of silicon
One of liquid, polyurethane-modified acrylic acid and elastomeric propylene yogurt liquid are a variety of.
As present invention further optimization mode, the step (f) include: the color spot coating is let down into it is suitable
Viscosity trickles down the color spot coating sprayed on common coloring layer in dotted by color spot coating described in spray gun spraying, after dry
Form color spot layer.
A kind of flexible compound coating patch material of color spot, by the manufacturer of the flexible compound coating patch material of color spot described above
Method is prepared.
A kind of patch material construction method, by way of roller coating by alite paste roller coating on basal plane to be onstructed, described viscous
Agent is tied in the state of moistening, patch material is attached on the basal plane for being coated with the binder.
As present invention further optimization mode, the thickness of dry film that the binder is formed is less than 0.5mm.
As present invention further optimization mode, the binder includes the component of following proportion:
The beneficial effects of the present invention are:
The flexible compound coating patch material of the color spot is provided with the carrier layer as base, wherein the material of carrier layer is soft
Property material, compound common coloring layer and color spot layer are made that a kind of that there is surface effect to be that flexible coating surface is rendered as is certain close
The patch material of degree, one or more different colours color spot, and the decorative pattern on surface can through the invention in color spot coating
Each color point painting effect of different densities, different color spot granular sizes is made in formula, toning.Wherein, using flexible material
The characteristic that carrier layer has good flexibility, bend-resistance good, even if on the work face of surface irregularity, patch material of the invention
Can closely attach to it is in connection on its surface, not will cause with work face formed gap the problems such as.And by using flexibility
The carrier layer of material makes the flexibility for pasting material entirety splendid, is not easily broken, tension failure.Patch material of the invention is slim and graceful, it is soft,
Easy to attach, the cleavable paste block at certain size carries out sticking construction, installs simple, quick and easy.
Detailed description of the invention
The invention will be further described with embodiment with reference to the accompanying drawing.
Fig. 1 is the flow diagram that the flexible compound coating of color spot in one embodiment of the invention pastes the manufacturing method of material.
Fig. 2 is that the flexible compound coating of color spot in one embodiment of the invention pastes the structural schematic diagram of material.
Specific embodiment
It should be noted that in the absence of conflict, the feature in embodiment and embodiment in the present invention can phase
Mutually combination.Below with reference to the attached drawing of the embodiment of the present invention, technical solution of the present invention is described further, the present invention is not only
It is limited to following specific embodiments.
It is to be appreciated that in the attached drawing of embodiment, the same or similar label correspond to the same or similar components.At this
In the description of invention, it is to be understood that if having term " upper ", " under ", " preceding ", " rear ", " left side ", " right side ", " top ", " bottom " etc. refer to
The orientation or positional relationship shown is to be based on the orientation or positional relationship shown in the drawings, and is merely for convenience of the description present invention and simplifies
Description, rather than the equipment of indication or suggestion meaning or element must have a particular orientation, constructed and grasped with specific orientation
Make, therefore the terms describing the positional relationship in the drawings are only for illustration, should not be understood as the limitation to this patent, for
For those skilled in the art, the concrete meaning of above-mentioned term can be understood as the case may be.
The invention discloses the flexible compound coatings of a kind of flexible compound coating of color spot patch material and the color spot to paste material
Manufacturing method, as shown in Figure 1, its manufacturing method that material is pasted for the flexible compound coating of the color spot of one embodiment of the invention, including
Following steps:
(a) a kind of carrier layer is provided, the carrier layer is flexible material layer;
(b) bottom coating is processed in the carrier layer, forms prime coat;
(c) flexible texture filling paint is sprayed on the prime coat, forms flexible texture filled layer;
(d) flexible texture pigmented finiss is sprayed on the flexible texture filled layer, forms flexible texture coloring layer;
(e) common pigmented finiss is sprayed on the flexible texture coloring layer, forms common coloring layer;
(f) color spot coating is sprayed on the common coloring layer, forms color spot layer;
(g) aqueous finishing varnish is sprayed on the color spot layer, forms aqueous finishing varnish layer.
The present invention provides a kind of flexible compound coating patch material of color spot, is pasted by the flexible compound coating of color spot described above
The manufacturing method of material is prepared, specifically, as shown in Fig. 2, the structure of the flexible compound coating patch material of the color spot are as follows: including
Carrier layer 106, prime coat 105, flexible texture filled layer 104, flexible texture coloring layer 103, common coloring layer 102, color spot layer
101 and aqueous finishing varnish layer 107, it is the carrier layer 106, the prime coat 105, the flexible texture filled layer 104, described
Flexible texture coloring layer 103, the common coloring layer 102, the color spot layer 101 and the aqueous finishing varnish layer 107 are successively
Attach setting, that is to say, that in the one side of the carrier layer by be attached at its surface lamination layer structure (i.e. prime coat,
Flexible texture filled layer, flexible texture coloring layer, common coloring layer, color spot layer and aqueous finishing varnish layer) combination, realize carry
The combination of body layer and Building material layer.Wherein, the another side of carrier layer is for being attached at construction surface.
As disclosure of the invention, wherein in the beneath setting carrier layer of the material layer of MULTILAYER COMPOSITE, applied as first
The carrier of layer (i.e. prime coat), carrier layer ensure that first of coating will not be revealed, also, hard coating pastes material in traditional handicraft
Quality is harder, if the problem that construction surface out-of-flatness can not then construct and this patch material is easily broken off etc., lacks to improve these
Point, the carrier layer are flexible material layer, and in one embodiment, the carrier layer is glass-fiber-fabric, glass blanket, asbestos cloth, stone
One of cotton blanket, rock wool cloth, rock wool blanket, silicate fiber cloth or silicate fiber blanket.Wherein, glass-fiber-fabric is that glass fibre is spun
Cloth made of knitting, asbestos cloth are the cloth that asbestos fibre is formed by weaving, and rock wool cloth is the cloth that rock wool fibers are formed by weaving, and glass blanket is
Fiber filament is squeezed to the loose coma of slabbing.Wherein, the glass-fiber-fabric of above-mentioned selection and glass blanket are compared in fishnet shape
Glass fiber reticular cloth have the function of there is better fireproof partition so that patch material be provided with better fireproof partition function.Wherein, on
The cloth silk gap of the materials such as glass-fiber-fabric, the asbestos cloth is stated less than 1 millimeter.Each carrier layer materials described above have strong
The characteristics such as degree is high, pull resistance is strong, by with remaining remaining construction material layer mixed binding, corresponding Building wood can be prepared
Material patch material, facilitates construction, and the patch material has good intensity, is not easy tension failure, and glass-fiber-fabric, glass blanket etc. have well
Flexibility, can resist bending so that patch material entirety have flexible, anti-crack.Also, as first of coating (i.e. priming paint
Layer) carrier, count ensure that first of coating will not be revealed, meanwhile, this glass-fiber-fabric or glass blanket or asbestos cloth
The flexible compound coating patch material of color spot in the present invention is improved in shearing packaging and intensity needed for construction paste process, and
Promote the solidification of adhesive in sticking state.
Wherein, in the flexible compound coating patch material of color spot disclosed by the invention, there is flexible texture filled layer, flexible texture
Coloring layer, common coloring layer and color spot layer, by complex carrier layer, it is that flexible coating surface is rendered as that surface effect, which is prepared,
The patch material of the color spot of certain density, one or more different colours, the patch material is soft, flexible, easy to attach.
Specifically, as a kind of disclosure of the invention, a kind of manufacture of the flexible compound coating patch material of color spot presented below
Method:
(a) a kind of carrier layer is provided, the carrier layer is flexible material layer.
There is provided the carrier layer of 100~600g, wherein the thickness of carrier layer is less than 1.8mm.
Wherein, the carrier layer is glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock wool cloth, rock wool blanket, silicate fiber
One of cloth or silicate fiber blanket.Material braiding described above is closely knit, and average cloth silk gap is less than 1mm, after ensure that
Continuous coating will not be revealed.
(b) bottom coating is processed in the carrier layer, forms prime coat.
Bottom coating is processed on a carrier layer, after dry, forms the priming paint that coating layer thickness is 20-50 μm on a carrier layer
Layer.
Wherein, prime coat is used for closed base, penetrates into substrate internal structure, blocks the pore in substrate, reduces
Open hole number, increases closing hole count, inhibits the infiltration of water content of coating in substrate, and infiltration is made to become uniformly, to make substrate to upper layer
The absorption of coating becomes the intensity that substrate uniformly can be improved, and improves carrier layer and remaining by the good ply adhesion of priming paint
The binding force of coating.
Wherein, as a kind of disclosure of the invention, specific embodiment is provided:
The process (2) includes: to provide a kind of carrier layer, and the carrier layer is glass-fiber-fabric, asbestos cloth, rock wool cloth or silicic acid
One of salt fiber cloth sprays seal coat on a carrier layer, and after dry, forming coating layer thickness on a carrier layer is 20-50 μ
The prime coat of m.
As a kind of disclosure of the invention, a kind of component formula of seal coat is provided, including the component matched as follows:
Wherein, acrylic emulsion is styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion, polyurethane-modified acrylic acid lotion, epoxy
One of resin modified acrylic emulsion and elastic emulsion are a variety of, for example, the acrylic emulsion is styrene-acrylic emulsion, example
Such as, the acrylic emulsion is pure-acrylic emulsion, for example, the acrylic emulsion is silicone acrylic emulsion, for example, the acrylic emulsion
For polyurethane-modified acrylic acid lotion, for example, the acrylic emulsion is epoxy resin modification acrylic emulsion, for example, described
Acrylic emulsion is elastic emulsion, for example, the acrylic emulsion is the mixture of styrene-acrylic emulsion and pure-acrylic emulsion, for example, institute
State the mixture that acrylic emulsion is styrene-acrylic emulsion, pure-acrylic emulsion and silicone acrylic emulsion, in the present embodiment, not burdensome description.
Wherein, open as another kind of the invention, specific embodiment is provided:
The process (b) includes: to provide a kind of carrier layer, and the carrier layer is glass blanket, asbestos mat, rock wool blanket or silicic acid
Carrier layer is put into dip-coating in the lotion after dilution by one of salt tapetum fibrosum, and after dry, forming coating layer thickness is 20-50 μm
Prime coat.
Wherein, for example, lotion described in above-mentioned operation (b) be acrylic emulsion, for example, the lotion be styrene-acrylic emulsion,
One of pure-acrylic emulsion, polyaminoester emulsion or acrylate and vinyl acetate emulsion are a variety of.
(C) flexible texture filling paint is sprayed on the prime coat, forms flexible texture filled layer.
Flexible texture filling paint is sprayed on prime coat, after dry, it is 0.1- that coating layer thickness is formed on prime coat
The flexible texture filled layer of 6.0mm.
Wherein, flexible texture filling paint is formed flexible texture filled layer resilience with higher and is stretched at flexibility
Long property can be attached to after dry and form uniform continuous and tough and tensile elastic protective film, elasticity by the surface of painting base
The elasticity of texture filling paint is established on certain film thickness, and the coating formed is thicker, and elasticity is stronger, therefore elasticity applies
The thickness of material is thicker than common coating, in the present invention, the flexible texture filled layer coating which forms
With a thickness of 0.1-0.6mm, this thickness can make the patch material being prepared have good elasticity and tensile strength, and will not make
It must paste that material integral thickness is blocked up, Specific construction thickness can be according to production needs depending on the requirement to elasticity.Therefore, by priming paint
Flexible texture filled layer is done on layer, then by subsequent other coatings of constructing on flexible texture filled layer, so that flexible texture is filled out
It fills the coating tensile strength of layer and extends the logy problem of follow-up coating that can make up, make up crack, improve the soft of color spot
Property the composite coating patch integral, flexible of material, resistance to bend(ing) can etc..
As a kind of disclosure of the invention, a kind of component formula of flexible texture filling paint is provided, including is matched as follows
Component:
Wherein, ordinary portland cement is at least one of ash concrete and white cement, for example, the ordinary portland cement
For ash concrete, for example, the ordinary portland cement is white cement, for example, the ordinary portland cement is ash concrete and white
The mixture of cement, wherein ordinary portland cement can mix colours according to actual needs, that is, be adjusted to the gray scale needed.Wherein,
Mill base is assorted mill base, to adjust the color of elastic filling paint.Wherein, the mesh number of quartz sand or silica flour is 5-200 mesh, 5-
Various quartz sands, silica flour between 200 mesh.
Wherein, in order to improve the reflective insulation function of flexible texture filling paint, for example, the mill base in formula can be used
There are the mill base or pigment of reflective insulation function, for example, the filler or auxiliary agent for having reflective insulation function is added.
(d) flexible texture pigmented finiss is sprayed on the flexible texture filled layer, forms flexible texture coloring layer.
Flexible texture pigmented finiss is sprayed on flexible texture filled layer to be formed on flexible texture filled layer after dry
Coating layer thickness is 0.1-6.0mm flexible texture coloring layer.
Wherein, flexible texture pigmented finiss is formed flexible texture coloring layer resilience with higher and is stretched at flexibility
Long property can be attached to after dry and form uniform continuous and tough and tensile elastic protective film, elasticity by the surface of painting base
The elasticity of texture pigmented finiss is established on certain film thickness, and the coating formed is thicker, and elasticity is stronger, therefore elasticity applies
The thickness of material is thicker than common coating, and in preferred embodiment, which need to be greater than 100 μm, in this hair
In bright, the elastic packed layer coating layer thickness which forms is 0.1-0.6mm, this thickness can to prepare
Obtained patch material has good elasticity and tensile strength, and patch material integral thickness will not be made blocked up, and Specific construction thickness can
According to production needs depending on the requirement to elasticity.Therefore, by doing flexible texture coloring layer in elastic packed layer, make two bullets
Property layer it is mutually compound, then by subsequent other coatings of constructing on flexible texture coloring layer, so that the painting of flexible texture coloring layer
Material tensile strength and the flexible compound painting for extending the logy problem of follow-up coating that can make up, making up crack, improving color spot
Integral, flexible, resistance to bend(ing) energy of layer patch material etc..
Wherein, flexible texture coloring layer is different from flexible texture filled layer in this step: the flexible texture in this step
Coloring layer is added without cement, but joined the elastic emulsion for making it have elasticity, meanwhile, being added to can make coating form decorative pattern
Particle decorative pattern is made, so that the flexible compound coating of color spot pastes for example, quartz sand or color sand, and by assorted color paste toning
The surface effect of material is particle texture coating effect.
As a kind of disclosure of the invention, a kind of component formula of flexible texture pigmented finiss is provided, including is matched as follows
Component:
Wherein, mill base is assorted mill base, to adjust the color of flexible texture pigmented finiss, while by addition quartz sand or
Color sand forms decorative pattern.
Wherein, in order to improve the reflective insulation function of flexible texture pigmented finiss, for example, the mill base in formula can be used
There are the mill base or pigment of reflective insulation function, for example, the filler or auxiliary agent for having reflective insulation function is added.
(e) common pigmented finiss is sprayed on the flexible texture coloring layer, forms common coloring layer.
Common pigmented finiss is sprayed on flexible texture coloring layer forms coating on flexible texture coloring layer after dry
Thickness is greater than 20 μm of common coloring layer.
Wherein, common coloring layer is used to adjust the color of whole patch material, forms the complexion of a patch material.
As a kind of disclosure of the invention, a kind of component formula of common pigmented finiss is provided, including the group matched as follows
Point:
Wherein, the acrylic emulsion include styrene-acrylic emulsion, pure-acrylic emulsion, silicon third or polyurethane-modified acrylic acid lotion and
One of elastomeric propylene yogurt liquid is a variety of.
Wherein, mill base is assorted mill base, to adjust the color of flexible texture pigmented finiss.
Wherein, in order to improve the reflective insulation function of common pigmented finiss, for example, the mill base in formula can be used instead
The mill base or pigment of heat insulating function are penetrated, for example, the filler or auxiliary agent for having reflective insulation function is added.
(f) color spot coating is sprayed on the common coloring layer, forms color spot layer.
Color spot coating is sprayed on common coloring layer, can be sprayed several times, sprays a color every time, after dry,
Color spot layer is formed on common coloring layer.
Specifically, in one embodiment, the step (f) includes: that the color spot coating is let down into suitable viscosity,
It by color spot coating described in spray gun spraying, trickles down the color spot coating sprayed on common coloring layer in dotted, is formed after dry
Color spot layer.
Wherein, assorted mill base is added according to demand to recall the color of needs.Color spot coating is let down into suitable viscosity
Afterwards, when being sprayed in construction surface with paint sprayer, control oil pump capacity and tolerance be should be noted, make the coating sprayed should not abundant mist
Change, so that coating is diametrically on the coating of 0.5-5 millimeter of the unrestrained road previous process of dot.Alternatively, pulp spraying can also be used
Rifle (such as lacquer spray gun) sprays big color spot.The spraying of this process can spray several times, spray a color every time, color
The density of point controls as needed, to make the color spot layer of multicolour, lines.
As a kind of disclosure of the invention, a kind of component formula of color spot coating is provided, including the component matched as follows:
Wherein, the acrylic emulsion include styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion, polyurethane-modified acrylic acid and
One of elastomeric propylene yogurt liquid is a variety of.
Wherein, in order to improve the reflective insulation function of colour-wash, for example, the mill base in formula can be used reflection every
The mill base or pigment of heat function, for example, the filler or auxiliary agent for having reflective insulation function is added.
(g) aqueous finishing varnish is sprayed on the color spot layer, forms aqueous finishing varnish layer.
Aqueous finishing varnish is sprayed on color spot layer, after dry, it is 20-100 μm that coating layer thickness is formed on color spot layer
Aqueous finishing varnish layer.
As a kind of disclosure of the invention, a kind of component formula of aqueous finishing varnish is provided, including the group matched as follows
Point:
Wherein, the cover lotion includes one of pure-acrylic emulsion, silicone acrylic emulsion or fluorine carbon emulsion or a variety of.Wherein,
Other described auxiliary agents include thickener and levelling agent, that is to say, that the total amount of adding of the thickener and levelling agent accounts for formula and matches
The 0-2.O% of ratio.
As another embodiment of the invention, the cover lotion in aqueous finishing varnish can also use weather-proof, water-fast
The dumb light lotion of albefaction, increases the matte effect of aqueous finishing varnish.
Wherein, in order to improve the reflective insulation function of aqueous finishing varnish, for example, reflective insulation can also be added in formula
The filler or auxiliary agent of function.
(h) overlay film on the aqueous finishing varnish layer.
Surface covering is protected using film mulching method.
By various processes described above, the present invention is prepared, a kind of flexible compound coating patch material of color spot is provided,
Its surface effect is the color spot that flexible coating surface is rendered as certain density, one or more different colours, decorative strong.And
The decorative pattern on surface can through the invention in color spot formulation for coating material, different densities, different color spot granular size are made in toning
Each color point painting effect, it is practical.
Wherein, the overall thickness of the flexible compound coating patch material for the color spot being prepared is between 0.2-7mm.It can pass through
Production requirement adjusts its thickness, especially by each coating layer thickness of adjustment to adjust overall thickness.
By using glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock wool cloth, rock wool blanket, silicate fiber cloth or silicic acid
One of salt tapetum fibrosum is used as substrate (carrier layer), and each layer coating is fabricated on the surface of carrier layer, formed it is a kind of it is light,
It is flexible, can anti-crack, have the color spot patch material of water-proof function, surface can be modulated into the effect of various color spot decorative patterns, can also be with
The color spot effect of decorative patterns for designing and producing various different densities, different color spot granular sizes is arranged by the substrate of carrier layer, makes it
Very easily paste on exterior wall or work face that other are to be onstructed on.Patch material of the invention is slim and graceful, soft, easy to attach, cleavable
At the paste block at certain size, sticking construction is carried out, is installed simple, quick and easy.
Wherein, the material described above that carrier layer is selected, all has the good characteristic of good flexibility, bend-resistance,
Even if on the work face of surface irregularity, patch material of the invention can also closely attach to it is in connection on its surface, will not
Cause the problems such as forming gap with work face.And pass through this characteristic of carrier layer, so that the flexibility of patch material entirety is splendid, it is not easy
It fractures, tension failure.
Also, traditional patch material is easy to cause solid difficulty because of poor air permeability, using a large amount of binders, therefore is being bonded to
It is not usually available a large amount of binder when on work face, causes that its cohesive force is not strong, is easy to fall off, or needs using cohesive force more
Strong binder improves cost, glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock wool cloth, rock wool used in the present invention
Blanket, silicate fiber cloth and silicate fiber blanket have hygroscopicity when not being coated with by resin, and have splendid gas permeability, can make
With a large amount of cheap binders, and it is quickly solid, keep it strong with the cohesive force in work face.
Also, the flexible compound coating patch material of color spot provided by the invention meets following technical indicator:
It pastes material stain resistant (white or light-colored)≤15, GB/T9755-2014;
Paste material temperature-change resistance: 3 without exception, JG/T172-2014 of circulation;
Paste material water penetration :≤0.6, GB/T9755-2014
Paste material water resistance: 96h is without exception, GB/T1733-1993;
Paste material alkali resistance: 48h is without exception, GB/T9265
Paste the resistance to artificial weathering aging of material: 600h is not blistering, does not peel off, flawless;GB/T9755-2014
Dusting: 1 grade;GB/T9755-2014
Discoloration: 2 grades;GB/T9755-2014
As a kind of disclosure of the invention, a kind of construction method for pasting material is provided, comprising: will paste by way of roller coating
Agent roller coating is on basal plane to be onstructed, in the state that the binder is in wet, patch material is attached at and is coated with described glue
On the basal plane for tying agent.
Wherein, the thickness of dry film that the binder is formed is less than 0.5mm.
Further, as a kind of disclosure of the invention, a kind of component formula of binder is provided, including following proportion
Component:
Wherein, transparent color can be made in the adhesive, can also by be added mill base be made it is identical as plane materiel or
Close color avoids edge of the solid adhesive in patch material and before pasting material from forming crack or cause heterochromia, destroy
It is beautiful.
Wherein, epoxy glue or anaerobic adhesive or MS glue can also be used and constructed with construction method described above to patch material.
Wherein, carrier layer not only acts as humidification, more has ventilative and hygroscopicity, adhesive described above can be promoted fast
Speed dehydration and drying, quickly forms cohesive force.Meanwhile the non-ignitable, high temperature resistant such as glass-fiber-fabric, glass blanket, it in process of production can be real
Existing assembly line high-temperature baking, improves production efficiency.
Modern architecture exterior coating is in terms of construction, and main coating decoration mode, batch production degree is not high, mainly by applying
Work worker carries out the multilayer construction from putty to finishing coat in building site, and basic reason is that the industry does not find one kind and inexpensively may be used
Capable technology pattern.Glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock wool cloth, rock wool blanket, the silicate used in carrier layer is fine
The application of Wei Bu and silicate fiber blanket in this patent had both solved the problems, such as that coating was quickly produced in the assembly line of factory
(as substrate and can high temperature drying, such as glass-fiber-fabric or the resistance to 500 DEG C of high temperature of glass blanket), so that may be implemented in process of production
Assembly line high-temperature baking improves production efficiency.The packed and transported for pasting material is set to become simple (glass-fiber-fabric, glass blanket, asbestos cloth, stone
Cotton blanket, rock wool cloth, rock wool blanket, silicate fiber cloth and silicate fiber blanket itself have non-stick), but also honest and clean in this patent
The bonding method of valence become it is feasible (glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock wool cloth, rock wool blanket, silicate fiber cloth and
Silicate fiber blanket has hygroscopicity when not being coated with by resin).Compared with the construction of conventional exterior coating, this product is completed in factory
Coating constructing operation;The outdoor construction time substantially shortens, two kinds of the processing operations only pasted and stitched.The labor of outdoor construction personnel
Fatigue resistance is greatly reduced, and construction speed is obviously accelerated, and greatly reduces human cost.
Each technical characteristic of embodiment described above can be combined arbitrarily, for simplicity of description, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all should be considered as described in this specification.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (9)
1. a kind of manufacturing method of the flexible compound coating patch material of color spot, which comprises the steps of:
(a) a kind of carrier layer is provided, the carrier layer is flexible material layer;
(b) bottom coating is processed in the carrier layer, forms prime coat;
(c) flexible texture filling paint is sprayed on the prime coat, forms flexible texture filled layer;
(d) flexible texture pigmented finiss is sprayed on the flexible texture filled layer, forms flexible texture coloring layer;
(e) common pigmented finiss is sprayed on the flexible texture coloring layer, forms common coloring layer;
(f) color spot coating is sprayed on the common coloring layer, forms color spot layer;
(g) aqueous finishing varnish is sprayed on the color spot layer, forms aqueous finishing varnish layer.
2. the manufacturing method of the flexible compound coating patch material of color spot according to claim 1, which is characterized in that the carrier
Layer is in glass-fiber-fabric, glass blanket, asbestos cloth, asbestos mat, rock wool cloth, rock wool blanket, silicate fiber cloth or silicate fiber blanket
It is a kind of.
3. the manufacturing method of the flexible compound coating patch material of color spot according to claim 1, which is characterized in that the color spot
Coating includes the component of following proportion:
4. the manufacturing method of the flexible compound coating patch material of color spot according to claim 3, which is characterized in that the propylene
Yogurt liquid includes one of styrene-acrylic emulsion, pure-acrylic emulsion, silicone acrylic emulsion, polyurethane-modified acrylic acid and elastomeric propylene yogurt liquid
Or it is a variety of.
5. the manufacturing method of the flexible compound coating patch material of color spot according to claim 1, which is characterized in that the step
(f) include: that the color spot coating is let down into suitable viscosity, by color spot coating described in spray gun spraying, make the color spot sprayed
Coating is trickled down on common coloring layer in dotted, forms color spot layer after dry.
6. a kind of flexible compound coating of color spot pastes material, which is characterized in that the flexible compound of the color spot as described in claim 1-5
The manufacturing method of coating patch material is prepared.
7. a kind of patch material construction method, which is characterized in that by way of roller coating by alite paste roller coating on basal plane to be onstructed,
In the state that the binder is in wet, patch material is attached on the basal plane for being coated with the binder.
8. patch material construction method according to claim 7, which is characterized in that the thickness of dry film that the binder is formed is less than
0.5mm。
9. patch material construction method according to claim 7, which is characterized in that the binder includes the group of following proportion
Point: