CN110317506A - A kind of high tenacity joint trimming agent - Google Patents
A kind of high tenacity joint trimming agent Download PDFInfo
- Publication number
- CN110317506A CN110317506A CN201910635173.3A CN201910635173A CN110317506A CN 110317506 A CN110317506 A CN 110317506A CN 201910635173 A CN201910635173 A CN 201910635173A CN 110317506 A CN110317506 A CN 110317506A
- Authority
- CN
- China
- Prior art keywords
- agent
- joint trimming
- stirring
- high tenacity
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to joint trimming agent technical fields, especially a kind of high tenacity joint trimming agent, including following component: propylene glycol, dispersing agent, defoaming agent, wetting agent, ammonium hydroxide, fungicide, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener and deionized water, then pass through first mixing, pulvis is added, sampling Detection, add lotion, thickening and etc. high tenacity joint trimming agent obtained compare existing joint trimming agent and have toughness high, the advantages of convenient for constructing, surface erosion will not be caused to building materials such as wall bricks, simultaneously added with thickener, so that joint trimming agent is jelly, it will not trickle when in injection brickwork joint, reduce the usage amount of joint trimming agent.
Description
Technical field
The present invention relates to joint trimming agent technical field more particularly to a kind of high tenacity joint trimming agents.
Background technique
It after exterior walls of buildings sticks ceramic tile, needs to be filled the gap between ceramic tile, construction in the past is using white
Cement is embedded in gap, and sometimes for the color of cooperation ceramic tile, construction personnel can deploy some pigment and be mixed into wherein.This joint filling
Mode there are many drawbacks, such as moist season can mouldy influence aesthetics, and after use a period of time, cement toughness
Deficiency is easy to happen cracking, falls off, so that the gap exposure between wall brick, influences its service life.
Summary of the invention
The purpose of the present invention is to solve the shortcomings that traditional gap filler toughness deficiency is easy to fall off exists in the prior art,
And a kind of high tenacity joint trimming agent proposed.
To achieve the goals above, present invention employs following technical solutions:
Design a kind of high tenacity joint trimming agent, including following component: propylene glycol, defoaming agent, wetting agent, ammonium hydroxide, is killed at dispersing agent
It microbial inoculum, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener and goes
Ionized water, each component is according to mass percent are as follows: propylene glycol 1.5-2.0%, dispersing agent 0.2-0.5%, defoaming agent 0.1-
0.2%, wetting agent 0.05-0.1%, ammonium hydroxide 0.1-0.2%, fungicide 0.05-0.1%, titanium dioxide 12-15%, coarse whiting 10-
13%, kaolin 8-11%, coalescing agent 0.1-0.5%, pure acrylate elastic emulsion 25-30%, pure-acrylic emulsion 7-10%, elasticity disappear
Infusion 0.1-0.2%, thickener 1.0-1.5%, surplus are deionized water.
Preferably, the coalescing agent is propylene glycol methyl ether acetate.
Preferably, the mesh number of the titanium dioxide and coarse whiting is 400 mesh.
Preferably, the preparation method of the high tenacity joint trimming agent includes the following steps:
S1, first mixing, suitable deionized water is added into dispersator according to said ratio, dispersion is then added
Agent, defoaming agent and wetting agent, then booting carries out dispersion stirring, and control mixing speed is 30-50r/min, mixing time 2-
5min；
S2, pulvis is added, successively adds titanium dioxide, coarse whiting, kaolinite in the solution after stirring according to said ratio into S1
Soil improves dispersator revolving speed to 800r/min-900r/min progress high-speed stirred, mixing time 30-40min；
S3, sampling Detection take mixed liquor sampling Detection device fineness in S2, and reaching 100-110 μm is qualification, then will be qualified
Mixed liquor be added in dispersion machine and carry out vulgar stirring, control mixing speed is 200-300r/min, while agitating slowly
Propylene glycol and elastic defoaming agent is added to stirring evenly；
S4, addition lotion, in the case where stirring at low speed, slowly by pure acrylate elastic emulsion, pure-acrylic emulsion, the fungicide in formula
It is added to coalescing agent and carries out stirring at low speed dispersion in dispersion machine, added ammonium hydroxide into mixed liquor after stirring to paste, adjust
The pH value of whole system is saved to 8.5-9；
S5, thickening add thickener according to said ratio into S4 neutral and alkali mixed liquor, and then low speed is dispersed to glue,
Dispersion later detection mixed liquor in whether contain excessive bubble, if air bubble content excessively if stand mixed liquor to dissipation of air bubbles after seal
Dress completes the preparation of high tenacity joint trimming agent.
A kind of high tenacity joint trimming agent proposed by the present invention, beneficial effect are: being added to film forming in the high tenacity joint trimming agent
Auxiliary agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener etc., the existing U.S. seam of the comparison of joint trimming agent made of modulation
Agent has the advantages that toughness is high, is convenient for construction, will not cause surface erosion to building materials such as wall bricks, simultaneously added with thickener, make
It obtains joint trimming agent jelly, will not trickle when injecting in brickwork joint, reduce the usage amount of joint trimming agent.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment one
A kind of high tenacity joint trimming agent, including following component: propylene glycol, dispersing agent, defoaming agent, wetting agent, ammonium hydroxide, sterilization
Agent, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener and go from
Sub- water, each component is according to mass percent are as follows: propylene glycol 1.5%, dispersing agent 0.2%, defoaming agent 0.1%, wetting agent 0.05%,
Ammonium hydroxide 0.1%, fungicide 0.05%, titanium dioxide 12%, coarse whiting 10%, kaolin 8%, coalescing agent 0.1%, pure acrylate elastic cream
Liquid 25%, pure-acrylic emulsion 7%, elastic defoaming agent 0.1%, thickener 1.0%, surplus is deionized water.The coalescing agent is
Propylene glycol methyl ether acetate.The mesh number of the titanium dioxide and coarse whiting is 400 mesh.The preparation method of the high tenacity joint trimming agent includes
Following steps:
S1, first mixing, suitable deionized water is added into dispersator according to said ratio, dispersion is then added
Agent, defoaming agent and wetting agent, then booting carries out dispersion stirring, and control mixing speed is 30r/min, mixing time 2min；
S2, pulvis is added, successively adds titanium dioxide, coarse whiting, kaolinite in the solution after stirring according to said ratio into S1
Soil improves dispersator revolving speed to 800r/min progress high-speed stirred, mixing time 30min；
S3, sampling Detection take mixed liquor sampling Detection device fineness in S2, reach 100 μm for qualification, then mix qualified
It closes liquid and is added in dispersion machine and carries out vulgar stirring, control mixing speed is 200r/min, is slowly added to the third two while agitating
Pure and mild elasticity defoaming agent is to stirring evenly；
S4, addition lotion, in the case where stirring at low speed, slowly by pure acrylate elastic emulsion, pure-acrylic emulsion, the fungicide in formula
It is added to coalescing agent and carries out stirring at low speed dispersion in dispersion machine, added ammonium hydroxide into mixed liquor after stirring to paste, adjust
The pH value of whole system is saved to 8.5；
S5, thickening add thickener according to said ratio into S4 neutral and alkali mixed liquor, and then low speed is dispersed to glue,
Dispersion later detection mixed liquor in whether contain excessive bubble, if air bubble content excessively if stand mixed liquor to dissipation of air bubbles after seal
Dress completes the preparation of high tenacity joint trimming agent.
Embodiment two
A kind of high tenacity joint trimming agent, including following component: propylene glycol, dispersing agent, defoaming agent, wetting agent, ammonium hydroxide, sterilization
Agent, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener and go from
Sub- water, each component is according to mass percent are as follows: propylene glycol 1.6%, dispersing agent 0.3%, defoaming agent 0.13%, wetting agent
0.06%, ammonium hydroxide 0.13%, fungicide 0.06%, titanium dioxide 13%, coarse whiting 11%, kaolin 9%, coalescing agent 0.2%, pure
Acrylate elastic emulsion 26%, pure-acrylic emulsion 8%, elastic defoaming agent 0.13%, thickener 1.1%, surplus is deionized water.It is described at
Film auxiliary agent is propylene glycol methyl ether acetate.The mesh number of the titanium dioxide and coarse whiting is 400 mesh.The preparation of the high tenacity joint trimming agent
Method includes the following steps:
S1, first mixing, suitable deionized water is added into dispersator according to said ratio, dispersion is then added
Agent, defoaming agent and wetting agent, then booting carries out dispersion stirring, and control mixing speed is 35r/min, mixing time 3min；
S2, pulvis is added, successively adds titanium dioxide, coarse whiting, kaolinite in the solution after stirring according to said ratio into S1
Soil improves dispersator revolving speed to 830r/min progress high-speed stirred, mixing time 33min；
S3, sampling Detection take mixed liquor sampling Detection device fineness in S2, reach 103 μm for qualification, then mix qualified
It closes liquid and is added in dispersion machine and carries out vulgar stirring, control mixing speed is 230r/min, is slowly added to the third two while agitating
Pure and mild elasticity defoaming agent is to stirring evenly；
S4, addition lotion, in the case where stirring at low speed, slowly by pure acrylate elastic emulsion, pure-acrylic emulsion, the fungicide in formula
It is added to coalescing agent and carries out stirring at low speed dispersion in dispersion machine, added ammonium hydroxide into mixed liquor after stirring to paste, adjust
The pH value of whole system is saved to 8.6；
S5, thickening add thickener according to said ratio into S4 neutral and alkali mixed liquor, and then low speed is dispersed to glue,
Dispersion later detection mixed liquor in whether contain excessive bubble, if air bubble content excessively if stand mixed liquor to dissipation of air bubbles after seal
Dress completes the preparation of high tenacity joint trimming agent.
Embodiment three
A kind of high tenacity joint trimming agent, including following component: propylene glycol, dispersing agent, defoaming agent, wetting agent, ammonium hydroxide, sterilization
Agent, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener and go from
Sub- water, each component is according to mass percent are as follows: propylene glycol 1.7%, dispersing agent 0.4%, defoaming agent 0.16%, wetting agent
0.07%, ammonium hydroxide 0.16%, fungicide 0.07%, titanium dioxide 14%, coarse whiting 12%, kaolin 10%, coalescing agent 0.3%,
Pure acrylate elastic emulsion 27%, pure-acrylic emulsion 9%, elastic defoaming agent 0.16%, thickener 1.2%, surplus is deionized water.It is described
Coalescing agent is propylene glycol methyl ether acetate.The mesh number of the titanium dioxide and coarse whiting is 400 mesh.The system of the high tenacity joint trimming agent
Preparation Method includes the following steps:
S1, first mixing, suitable deionized water is added into dispersator according to said ratio, dispersion is then added
Agent, defoaming agent and wetting agent, then booting carries out dispersion stirring, and control mixing speed is 40r/min, mixing time 4min；
S2, pulvis is added, successively adds titanium dioxide, coarse whiting, kaolinite in the solution after stirring according to said ratio into S1
Soil improves dispersator revolving speed to 860r/min progress high-speed stirred, mixing time 36min；
S3, sampling Detection take mixed liquor sampling Detection device fineness in S2, reach 106 μm for qualification, then mix qualified
It closes liquid and is added in dispersion machine and carries out vulgar stirring, control mixing speed is 260r/min, is slowly added to the third two while agitating
Pure and mild elasticity defoaming agent is to stirring evenly；
S4, addition lotion, in the case where stirring at low speed, slowly by pure acrylate elastic emulsion, pure-acrylic emulsion, the fungicide in formula
It is added to coalescing agent and carries out stirring at low speed dispersion in dispersion machine, added ammonium hydroxide into mixed liquor after stirring to paste, adjust
The pH value of whole system is saved to 8.7；
S5, thickening add thickener according to said ratio into S4 neutral and alkali mixed liquor, and then low speed is dispersed to glue,
Dispersion later detection mixed liquor in whether contain excessive bubble, if air bubble content excessively if stand mixed liquor to dissipation of air bubbles after seal
Dress completes the preparation of high tenacity joint trimming agent.
Example IV
A kind of high tenacity joint trimming agent, including following component: propylene glycol, dispersing agent, defoaming agent, wetting agent, ammonium hydroxide, sterilization
Agent, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener and go from
Sub- water, each component is according to mass percent are as follows: propylene glycol 1.8%, dispersing agent 0.5%, defoaming agent 0.19%, wetting agent
0.09%, ammonium hydroxide 0.19%, fungicide 0.08%, titanium dioxide 15%, coarse whiting 13%, kaolin 11%, coalescing agent 0.4%,
Pure acrylate elastic emulsion 28%, pure-acrylic emulsion 10%, elastic defoaming agent 0.19%, thickener 1.3%, surplus is deionized water.Institute
Stating coalescing agent is propylene glycol methyl ether acetate.The mesh number of the titanium dioxide and coarse whiting is 400 mesh.The high tenacity joint trimming agent
Preparation method includes the following steps:
S1, first mixing, suitable deionized water is added into dispersator according to said ratio, dispersion is then added
Agent, defoaming agent and wetting agent, then booting carries out dispersion stirring, and control mixing speed is 45r/min, mixing time 5min；
S2, pulvis is added, successively adds titanium dioxide, coarse whiting, kaolinite in the solution after stirring according to said ratio into S1
Soil improves dispersator revolving speed to 890r/min progress high-speed stirred, mixing time 39min；
S3, sampling Detection take mixed liquor sampling Detection device fineness in S2, reach 109 μm for qualification, then mix qualified
It closes liquid and is added in dispersion machine and carries out vulgar stirring, control mixing speed is 300r/min, is slowly added to the third two while agitating
Pure and mild elasticity defoaming agent is to stirring evenly；
S4, addition lotion, in the case where stirring at low speed, slowly by pure acrylate elastic emulsion, pure-acrylic emulsion, the fungicide in formula
It is added to coalescing agent and carries out stirring at low speed dispersion in dispersion machine, added ammonium hydroxide into mixed liquor after stirring to paste, adjust
The pH value of whole system is saved to 8.8；
S5, thickening add thickener according to said ratio into S4 neutral and alkali mixed liquor, and then low speed is dispersed to glue,
Dispersion later detection mixed liquor in whether contain excessive bubble, if air bubble content excessively if stand mixed liquor to dissipation of air bubbles after seal
Dress completes the preparation of high tenacity joint trimming agent.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of high tenacity joint trimming agent, which is characterized in that including following component: propylene glycol, dispersing agent, defoaming agent, wetting agent, ammonia
Water, fungicide, titanium dioxide, coarse whiting, kaolin, coalescing agent, pure acrylate elastic emulsion, pure-acrylic emulsion, elastic defoaming agent, thickener
And deionized water, each component is according to mass percent are as follows: propylene glycol 1.5-2.0%, dispersing agent 0.2-0.5%, defoaming agent 0.1-
0.2%, wetting agent 0.05-0.1%, ammonium hydroxide 0.1-0.2%, fungicide 0.05-0.1%, titanium dioxide 12-15%, coarse whiting 10-
13%, kaolin 8-11%, coalescing agent 0.1-0.5%, pure acrylate elastic emulsion 25-30%, pure-acrylic emulsion 7-10%, elasticity disappear
Infusion 0.1-0.2%, thickener 1.0-1.5%, surplus are deionized water.
2. a kind of high tenacity joint trimming agent according to claim 1, which is characterized in that the coalescing agent is propylene glycol monomethyl ether
Acetate.
3. a kind of high tenacity joint trimming agent according to claim 1, which is characterized in that the mesh number of the titanium dioxide and coarse whiting is
400 mesh.
4. a kind of high tenacity joint trimming agent according to claim 1, which is characterized in that the preparation side of the high tenacity joint trimming agent
Method includes the following steps:
S1, first mixing, suitable deionized water is added into dispersator according to said ratio, then be added dispersing agent,
Defoaming agent and wetting agent, then booting carries out dispersion stirring, and control mixing speed is 30-50r/min, mixing time 2-
5min；
S2, pulvis is added, successively adds titanium dioxide, coarse whiting, kaolin in the solution after stirring according to said ratio into S1, mentions
High dispersive blender revolving speed to 800r/min-900r/min carry out high-speed stirred, mixing time 30-40min；
S3, sampling Detection take mixed liquor sampling Detection device fineness in S2, reach 100-110 μm for qualification, then mix qualified
It closes in liquid addition dispersion machine and carries out vulgar stirring, control mixing speed is 200-300r/min, is slowly added to while agitating
Propylene glycol and elastic defoaming agent are to stirring evenly；
S4, addition lotion, in the case where stirring at low speed, slowly by formula pure acrylate elastic emulsion, pure-acrylic emulsion, fungicide and at
Film auxiliary agent, which is added to, to carry out stirring at low speed dispersion in dispersion machine, adds ammonium hydroxide into mixed liquor after stirring to paste, adjusts whole
The pH value of a system is to 8.5-9；
S5, thickening add thickener according to said ratio into S4 neutral and alkali mixed liquor, and then low speed is dispersed to glue, dispersion
Later detect in mixed liquor and whether contain excessive bubble, if air bubble content excessively if stand mixed liquor to dissipation of air bubbles post package,
Complete the preparation of high tenacity joint trimming agent.