CN108976966A - A kind of super environmentally friendly aqueous joint trimming agent and preparation method thereof - Google Patents
A kind of super environmentally friendly aqueous joint trimming agent and preparation method thereof Download PDFInfo
- Publication number
- CN108976966A CN108976966A CN201810806133.6A CN201810806133A CN108976966A CN 108976966 A CN108976966 A CN 108976966A CN 201810806133 A CN201810806133 A CN 201810806133A CN 108976966 A CN108976966 A CN 108976966A
- Authority
- CN
- China
- Prior art keywords
- agent
- joint trimming
- aqueous
- parts
- aqueous joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of aqueous joint trimming agents and preparation method thereof, its weight includes: 26~50 parts of polymer emulsion, 1~10 part of pigment, 10~20 parts of cracking resistance auxiliary agent, 15~25 parts of fumed silica, 0.1~0.7 part of wetting dispersing agent, 0.1~0.5 part of defoaming agent, 0.6~1.5 part of antifreezing agent, 0.5~0.9 part of coalescing agent, 0.2~0.4 part of pH adjusting agent, 0.1~0.5 part of preservative, and the aqueous joint trimming agent is using plasma water emulsification dilution.Have the following beneficial effects: 1. solid contents height, glue consistency is moderate, and the glue film shrinking percentage of formation is small, has good filling effect；2. using special cracking resistance material, non-aging cracking is used for a long time；3. tensile strength is high, good toughness, it is effective against breaking strain caused by displacement；4. not mouldy, safety and environmental protection, bright-colored, glossiness is high.
Description
Technical field
The present invention relates to a kind of joint trimming agent, specifically a kind of water-based system, large arch dam, anti-aging cracking joint trimming agent,
The invention further relates to the preparation methods of above-mentioned aqueous joint trimming agent.
Summary of the invention
The purpose of the invention is to overcome techniques as described above defect, provide a kind of water-based system, it is large arch dam, anti-
The joint trimming agent of cracking, while also providing the preparation method of the joint trimming agent.
The invention is realized in this way a kind of aqueous joint trimming agent, includes: by weight ratio
26~50 parts of pigment of polymer emulsion, 1~10 part of cracking resistance auxiliary agent, 10~20 parts of 15~25 parts of fumed silicas,
0.1~0.7 part of wetting dispersing agent, 0.1~0.5 part of defoaming agent, 0.6~1.5 part of antifreezing agent, 0.5~0.9 part of coalescing agent, pH
It is worth 0.2~0.4 part of regulator, 0.1~0.5 part of preservative, the aqueous joint trimming agent is using plasma water emulsification dilution, existing skill
Joint trimming agent is diluted using benzyl alcohol in art, and the present invention is using plasma water emulsification dilution, after having the beneficial effect that AB glue mixing, not
Before solidification, formaldehyde on-site test is lower than 0.08MG/m3(even up to 0.04MG/m3)。
The polymer emulsion is at least one of acrylic emulsions, polyaminoester emulsion, epoxy resin, acrylic acid
Class lotion includes pure-acrylic emulsion, silicone acrylic emulsion, styrene-acrylic emulsion, acrylate and vinyl acetate emulsion.
The pigment is at least one of pearlescent pigment, fluorescent pigment, metallic pigments.
The cracking resistance auxiliary agent is the mixture of aqueous silane coupling agent, carboxymethyl cellulose, layer structure powder, by weight
Part proportion is measured, aqueous silane coupling agent: carboxymethyl cellulose: layer structure powder=0.4~1: 3~5: 0.1~0.5, wherein
Aqueous silane coupling agent is one of Silquest wetlink-78, KH-450, KH-460, and layer structure powder is Jiangxi
Paint-grade talc powder, one of the hexagonal boron nitride of province Shanggao County Chen Xin Chemical Co., Ltd. production.
The wetting dispersing agent is Tao Shi DOW TRITON CF-10, the modest FX365 of moral, Nuo Puke Hua Xue SN-5040, enlightening
At least one of high TEGO Dispers 750W.
The defoaming agent is Corning DISPELAIR@CF16,345 SN-DEFOAMER, in ADEKA NATE B-199
It is at least one.
The antifreezing agent is at least one of ethylene glycol, propylene glycol.
The film forming agent is to moisten at least one of safe chemistry C-12, Yi Shiman OE300, Yi Shiman Texanol.
The pH adjusting agent is DOW Chemical AMP-95, Wa KeAt least one of BS168.
The preservative is at least one of Tao Shi KATHON LXE, enlightening beauty KSG103.
A kind of preparation method of aqueous joint trimming agent of the invention, comprising the following steps:
By weight ratio successively by load weighted cracking resistance auxiliary agent, it is added to dispersion mixing in polymer emulsion, when mixing
Between be 10min~30min, be slow added into fumed silica, pigment, wetting dispersing agent, defoaming agent, antifreezing agent, pH value tune
Section agent is uniformly dispersed, and is eventually adding coalescing agent, preservative, discharges after mixing, and hydrophobic type is used in the preparation method
Silicon dioxide can make when colloid just gets uncured, higher in humidity just in colloidal shape at protective film
Environment in, protective film has completely cut off the moisture in air, is that colloid will not whiten, fade.
The present invention and market similar product compare, and have the following beneficial effects:
1. solid content is high, glue consistency is moderate, and the glue film shrinking percentage of formation is small, has good filling effect；
2. using special cracking resistance material, non-aging cracking is used for a long time under hygrothermal environment；
3. tensile strength is high, good toughness, it is effective against breaking strain caused by displacement；
4. not mouldy, safety and environmental protection, bright-colored, glossiness is high.
Specific embodiment
The present invention will be described for following embodiment, but the present invention is not limited to these examples system.To of the invention
Specific embodiment is modified or some technical features can be equivalently replaced, without departing from the spirit of the present invention program,
It should all cover within the scope of the technical scheme claimed by the invention.
Embodiment 1
By weight ratio successively by 2.1 parts of load weighted Silquest wetlink-78, carboxymethyl cellulose 15.3
Part, 2.6 parts of talcum powder, be added to 16 parts of pure-acrylic emulsion, dispersion mixing in 10 parts of polyaminoester emulsion, incorporation time 10min, then
It is slowly added to 40 parts of fumed silica, 1 part of pearlescent pigment, 0.1 part of Tao Shi DOWTRITON CF-10, SN-DEFOAMER
345 0.1 parts, ethylene glycol 0.6 part, watt gram 0.2 part of a SILRES@BS168 be uniformly dispersed, be eventually adding the safe chemistry C-12 0.5 of profit
Part, 0.2 part of enlightening beauty KSG103, discharge after mixing.
Embodiment 2
By weight ratio successively by 2.5 parts of load weighted KH-450,12.3 parts of carboxymethyl cellulose
0.2 part of hexagonal boron nitride, it is added to 15 parts of styrene-acrylic emulsion, dispersion mixing in 15 parts of polyaminoester emulsion, incorporation time
For 20min, it is slow added into 25 parts of fumed silica, 5 parts of fluorescent pigment, 0.5 part of the modest FX365 of moral, Corning DISPELAIR@
0.3 part of CF16,1 part of propylene glycol, AMP-950.3 parts of DOW Chemical be uniformly dispersed, be eventually adding 0.7 part of Yi Shiman OE300, pottery
0.1 part of family name KATHON LXE, discharges after mixing.
Embodiment 3
By weight ratio successively by 1.9 parts of load weighted KH-460,7.4 parts of carboxymethyl cellulose,
0.7 part of hexagonal boron nitride, it is added to dispersion mixing in 50 parts of silicone acrylic emulsion, incorporation time 30min, then slowly add
Enter 20 parts of fumed silica, 10 parts of metallic pigments, 0.7 part of Nuo Puke chemistry SN-5040, ADEKA NATE B-199 0.5
Part, 0.4 part of gram SILRES BS168 of propylene glycol 1.5 part, watt be uniformly dispersed, be eventually adding 0.9 part of Yi Shiman Texanol, pottery
0.5 part of family name KATHON LXE, discharges after mixing.
Comparative example 4
50 parts of silicone acrylic emulsion are added by weight ratio, is slowly added to 10 parts of fumed silica, carboxymethyl cellulose
12.3 parts, 10 parts of pearlescent pigment, 0.7 part of Nuo Puke chemistry SN-5040,0.5 part of ADEKA NATE B-199, propylene glycol 1.5
0.4 part of part, watt gram SILRES BS168 is uniformly dispersed, and is eventually adding 0.9 part of Yi Shiman Texanol, Tao Shi KATHON LXE
It 0.5 part, discharges after mixing.
Examples 1 to 3, a kind of correlated performance test method of aqueous joint trimming agent of comparative example 4 are as follows:
1. initial dry cracking resistance, dynamic cracking resistance: being surveyed according to JG/T157-2004 " putty for exterior use "
Examination；
2. dynamic cracking resistance (after hydrothermal aging): being opened according to dynamic in JG/T157-2004 " putty for exterior use " is anti-
Fragility test method prepares same test specimen, is placed in 90 DEG C of temperature, aging 7d in 80% constant temperature and moisture test machine of relative humidity, surveys
Try Dynamic cracking；
3. non-volatile content: being tested according to GB/T2793 " measurement of adhesive non-volatile content "；
4. tensile strength: according to the GB/T528-2009 " survey of vulcanized rubber or thermoplastic elastomer tensile stress-strain performance
It is fixed " it is tested；
5. glossiness: being tested according to GB/T 4893.6-2013 " test of furniture surface paint film physicochemical property ".
Examples 1 to 3, a kind of aqueous joint trimming agent the performance test results of comparative example 4 are as shown in table 1 below.
Table 1
As can be seen from the above table, a kind of aqueous joint trimming agent of the present invention is compared with the prior art (comparative example 4), dynamic cracking resistance
Property, the dynamic cracking resistance after hydrothermal aging it is excellent, non-volatile content is high, shrinks small, and tensile strength is high, is effective against position
Breaking strain caused by moving.
Further, the aqueous joint trimming agent of the present invention, which is emulsified compared with the prior art using plasma water, dilutes, beneficial
Effect are as follows: after AB glue mixing, before uncured, formaldehyde on-site test is lower than 0.08MG/m3(even up to 0.04MG/m3)。
Further, in the aqueous joint trimming agent process of reproduction of the present invention, hydrophobic type silicon dioxide is used, it can
So that when colloid just gets uncured, just in colloidal shape at protective film, in the higher environment of humidity, protective film isolation
Moisture in air, is colloid will not whiten, fade.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is by appended.
Claims (8)
1. a kind of aqueous joint trimming agent, feature place is, include: by weight ratio
26~50 parts of polymer emulsion, 1~10 part of pigment, 10~20 parts of cracking resistance auxiliary agent, 15~25 parts of fumed silica, wetting
0.1~0.7 part of dispersing agent, 0.1~0.5 part of defoaming agent, 0.6~1.5 part of antifreezing agent, 0.5~0.9 part of coalescing agent, pH value tune
0.2~0.4 part of agent, 0.1~0.5 part of preservative are saved, the aqueous joint trimming agent is using plasma water emulsification dilution.
2. a kind of aqueous joint trimming agent as described in claim 1, feature place is, polymer emulsion is acrylic compounds cream
At least one of liquid, polyaminoester emulsion, epoxy resin, acrylic emulsions include pure-acrylic emulsion, silicone acrylic emulsion, phenylpropyl alcohol cream
Liquid, acrylate and vinyl acetate emulsion.
3. a kind of aqueous joint trimming agent as described in claim 1, be in place of feature, pigment be pearlescent pigment, fluorescent pigment,
At least one of metallic pigments.
4. a kind of aqueous joint trimming agent as described in claim 1, feature place is, cracking resistance auxiliary agent is aqueous silane coupling
Agent, carboxymethyl cellulose, layer structure powder mixture, by weight ratio, aqueous silane coupling agent: carboxymethyl cellulose
: layer structure powder=0.4~1: 3~5: 0.1~0.5, wherein aqueous silane coupling agent be Silquest wetlink-78,
One of KH-450, KH-460, layer structure powder are the coating grade of Jiangxi Province Shanggao County Chen Xin Chemical Co., Ltd. production
One of talcum powder, hexagonal boron nitride.
5. a kind of aqueous joint trimming agent as described in claim 1, feature place is, wetting dispersing agent is Tao Shi DOW
At least one of the modest FX365 of TRITON CF-10, moral, Nuo Puke Hua Xue SN-5040, Digao TEGO Dispers 750W；Disappear
Infusion is at least one of Corning DISPELAIR@CF16,345 SN-DEFOAMER, ADEKA NATE B-199；Antifreezing agent
For at least one of ethylene glycol, propylene glycol；PH adjusting agent is DOW Chemical AMP-95, Wa KeBS168 is extremely
Few one kind.
6. a kind of aqueous joint trimming agent as described in claim 1, be in place of feature, film forming agent be moisten safe chemistry C-12, she
At least one of the graceful OE300 of scholar, Yi Shiman Texanol.
7. a kind of aqueous joint trimming agent as described in claim 1, be in place of feature, preservative be Tao Shi KATHON LXE,
At least one of enlightening beauty KSG103.
8. a kind of preparation method of aqueous joint trimming agent as described in claim 1, comprising the following steps:
Load weighted cracking resistance auxiliary agent is successively added to dispersion mixing in polymer emulsion by weight ratio, incorporation time is
10min~30min is slow added into fumed silica, pigment, wetting dispersing agent, defoaming agent, antifreezing agent, pH adjusting agent
It is uniformly dispersed, is eventually adding coalescing agent, preservative, discharges after mixing, hydrophobic type is used in the preparation method
silicon dioxide。