CN106914154A - PEG‑TiO2/PES/PVA亲水超滤膜的制备方法与应用 - Google Patents
PEG‑TiO2/PES/PVA亲水超滤膜的制备方法与应用 Download PDFInfo
- Publication number
- CN106914154A CN106914154A CN201710106547.3A CN201710106547A CN106914154A CN 106914154 A CN106914154 A CN 106914154A CN 201710106547 A CN201710106547 A CN 201710106547A CN 106914154 A CN106914154 A CN 106914154A
- Authority
- CN
- China
- Prior art keywords
- peg
- tio
- pes
- pva
- hydrophilic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及超滤膜改性技术领域,尤其涉及一种PEG‑TiO2/PES/PVA亲水超滤膜的制备方法与应用,PEG‑TiO2/PES/PVA亲水超滤膜,是以PEG‑TiO2为添加剂对PES/PVA复合超滤膜进行亲水改性制得,所述PEG‑TiO2是以聚乙二醇为表面活性剂对纳米二氧化钛进行修饰后所得,所述PEG‑TiO2/PES/PVA亲水超滤膜中PEG‑TiO2的含量为2~3wt.%,该PEG‑TiO2/PES/PVA亲水超滤膜在焦化污水处理的应用。该PEG‑TiO2/PES/PVA亲水超滤膜具有较好的亲水性以及较高的COD截留率。
Description
技术领域
本发明涉及超滤膜改性技术领域,尤其涉及一种PEG-TiO2/PES/PVA亲水超滤膜的制备方法与应用。
背景技术
膜技术是21世纪兴起的一种新型分离、净化、浓缩技术,以其过程清洁、简单,能耗低,出水水质优良等特点在污水处理领域引起特别关注。膜技术已成功在海水、苦咸水淡化,纯水、超纯水制备以及工业废水处理等方面得到规模化应用,近年来,国内外许多学者也做了关于污水膜处理的研究。目前常用的膜过滤技术是微滤和超滤,分离膜根据其表面性质不同可分为:疏水性膜和亲水性膜。疏水性膜机械强度高,膜的比表面积和能耗较亲水性膜小,受表面活性剂影响小,当孔径足够小时可产生较好的破乳效果,但是膜的抗污染性差,导致其重复利用率低。亲水性膜的水通量高,抗污染能力强,若增强膜表面的亲水性,则可进一步提高膜的抗污染能力,使其利用率相对提高。
聚醚砜(PES)是目前应用最广泛的分离膜材料之一,常作为微滤和超滤的膜原料。据大量研究可知,PES膜在应用中虽表现出良好的机械性能,但伴随的膜污染却是膜应用的瓶颈,而疏水性是造成膜污染的主要原因。针对PES膜的膜污染问题,许多学者研究将PES与PVA(聚乙烯醇)进行共混得到PES/PVA复合超滤膜,但是,PES/PVA复合超滤膜的亲水仍然不佳,应用于污水处理中时,其COD截留率仅为50~60%。因此,亟需一种对PES膜更有效的改性方法,来提高PES膜的亲水性。
发明内容
为解决以上问题,本发明的目的是提供一种PEG-TiO2/PES/PVA亲水超滤膜的制备方法与应用,该PEG-TiO2/PES/PVA亲水超滤膜具有较好的亲水性以及较高的COD截留率。
为实现上述目的,本发明所设计的技术方案是:
PEG-TiO2/PES/PVA亲水超滤膜,是以PEG-TiO2为添加剂对PES/PVA复合超滤膜进行亲水改性制得,所述PEG-TiO2是以聚乙二醇为表面活性剂对纳米二氧化钛进行修饰后所得,所述PEG-TiO2/PES/PVA亲水超滤膜中PEG-TiO2的含量为2~3wt.%。
PEG-TiO2/PES/PVA亲水超滤膜的制备方法,包括以下步骤:
1)制备PEG-TiO2添加剂:将纳米二氧化钛分散于蒸馏水中后与聚乙二醇溶液混合,搅拌均匀后静置,倒去上层清液,将下层悬浊液洗涤干净后离心、干燥、粉碎得到PEG-TiO2添加剂粉末;
2)配制铸膜液:将聚醚砜树脂、聚乙烯醇树脂、致孔剂以及PEG-TiO2添加剂粉末共混于溶剂中,加热搅拌至混合液澄清透亮后静置脱泡得到铸膜液;
3)浸没沉淀相转化法成膜:将铸膜液倾倒于玻璃板上刮膜,使铸膜液在玻璃板上呈均匀薄层,待薄层由透明变为白色后浸入凝固浴中,薄层从玻璃板表面脱落后用蒸馏水洗涤浸泡晾干即得PEG-TiO2/PES/PVA亲水超滤膜。
作为优选,所述步骤2)按质量百分比计,聚醚砜树脂14~17%,聚乙烯醇树脂1~4%,致孔剂为1~5%,PEG-TiO2添加剂粉末为2~3%。按照这个比例制得的PEG-TiO2/PES/PVA亲水超滤膜的稳定性均一性较好。
作为优选,所述致孔剂为聚吡络烷酮与氯化锂的混合物,聚吡络烷酮与氯化锂的质量比为1~2:1;所述溶剂为二甲基亚砜。
作为优选,所述步骤1)中聚乙二醇与纳米二氧化钛的质量比为0.2~0.3:99.7~99.8。
作为优选,所述步骤2)中,先将PEG-TiO2添加剂粉末超声分散于溶剂中,待PEG-TiO2添加剂粉末均匀分散于溶剂中后再加入聚醚砜树脂、聚乙烯醇树脂以及致孔剂,搅拌均匀。由于PEG-TiO2添加剂粉末较难充分均匀分散在溶剂中,若直接将聚醚砜树脂、聚乙烯醇树脂、致孔剂与PEG-TiO2添加剂粉末同时投入溶剂中,PEG-TiO2添加剂粉末易结块,更加不容易分散均匀。
作为优选,所述步骤3)中玻璃板的边缘贴有与玻璃板平面垂直的胶带;所述凝固浴为去离子水,凝固浴温度为30℃。
PEG-TiO2/PES/PVA亲水超滤膜在焦化污水处理中的应用,应用于焦化污水中,PEG-TiO2/PES/PVA亲水超滤膜的COD截留率为87.62~91.81%。
本发明的原理为:PES是疏水性膜,PVA是一种亲水性高聚物,若仅将PES与PVA共混得到的PES/PVA复合超滤膜的亲水性仍然不佳,本发明通过向其中添加无机分子-纳米TiO2,制得有机-无机共混复合膜,但是纳米TiO2颗粒表面张力大,分散不均匀,易发生吸附而团聚,很大程度上影响了其实际应用效果,本发明利用聚乙二醇为表面活性剂对纳米TiO2进行修饰后,有效地解决了纳米TiO2分散不均匀的问题。
本发明中的所使用的原料:PES平均分子量为3.7×104g.mol-1,密度为1.37g.cm-3;PVA平均分子量(1750±50)g.mol-1,密度为1.31g.cm-3;聚吡络烷酮(PVP-K30,平均分子量4×104g.mol-1)。
本发明的优点在于:
1,通过以PEG作为表面活性剂对纳米TiO2改性,使纳米TiO2的团聚性改善,在铸膜液中的分散性提高,对膜的纳米亲水改性效果也显著提高,并且PEG所含亲水基团与PES相同,所以PEG-TiO2添加剂与PES相容性好,膜性能稳定。
2,通过将PES与PVA共混,由于PVA是一种亲水性高聚物,因此能一定程度上改善PES的亲水性,然后再以PEG-TiO2为添加剂对PES/PVA复合超滤膜进行亲水改性,其亲水性能显著提升。
3,得到的PEG-TiO2/PES/PVA亲水超滤膜的COD截留率高,具有较好的污水处理性能。而且与传统的水处理膜相比,其水通量得到较大的提升,进一步改善了其抗污染性能。
附图说明
图1A为对比例得到的PES/PVA复合超滤膜的表面电镜扫描图;
图1B为对比例得到的PES/PVA复合超滤膜的断面电镜扫描图;
图2A为实施例1得到的PEG-TiO2/PES/PVA亲水超滤膜的表面电镜扫描图;
图2B为实施例1得到的PEG-TiO2/PES/PVA亲水超滤膜的断面电镜扫描图;
具体实施方式
为更好地理解本发明,以下将结合附图和具体实例对发明进行详细的说明。
PEG-TiO2/PES/PVA亲水超滤膜的制备方法,包括以下步骤:
1)制备PEG-TiO2添加剂:将纳米二氧化钛分散于蒸馏水中后与聚乙二醇溶液混合,聚乙二醇与纳米二氧化钛的质量比为0.2~0.3:99.7~99.8,搅拌均匀后静置,倒去上层清液,将下层悬浊液用蒸馏水反复漂洗2~3次后离心、放入干燥箱内干燥72h,燥箱温度设定为80℃,干燥完成后粉碎得到PEG-TiO2添加剂粉末;
2)配制铸膜液:将聚醚砜树脂、聚乙烯醇树脂、致孔剂以及PEG-TiO2添加剂粉末共混于溶剂中,搅拌混合均匀得到铸膜液;
先将PEG-TiO2添加剂粉末超声分散于二甲基亚砜溶剂中,待PEG-TiO2添加剂粉末均匀分散于二甲基亚砜溶剂中后再加入聚醚砜树脂、聚乙烯醇树脂以及致孔剂,85℃条件下加热搅拌均匀,待混合液呈澄清透亮后停止搅拌,60℃下真空静置脱泡6h后得到铸膜液;按质量百分比计,聚醚砜树脂14~17%,聚乙烯醇树脂1~4%,致孔剂为1~5%,PEG-TiO2添加剂粉末为2~3%。其中,致孔剂为聚吡络烷酮与氯化锂的混合物,聚吡络烷酮与氯化锂的质量比为1~2:1;所述聚醚砜树脂与聚乙烯醇树脂的质量比为17~3.5:1;
3)浸没沉淀相转化法成膜:将铸膜液倾倒于玻璃板上刮膜,其玻璃板的边缘贴有与玻璃板平面垂直的胶带,使铸膜液在玻璃板上呈均匀薄层,薄层膜厚度为12~14μm,待薄层由透明变为白色后浸入30℃去离子水凝固浴中,薄层从玻璃板表面脱落后用蒸馏水洗涤浸泡晾干即得PEG-TiO2/PES/PVA亲水超滤膜。
实施例1~3按照上述的操作过程,其具体的组分比例分别如表1~3所示,其中实施例1得到的PEG-TiO2/PES/PVA亲水超滤膜的表面及断面电镜扫描图如图2A与2B所示;
实施例1各组分参数见下表1:
表1
实施例2各组分参数见下表2:
表2
实施例3各组分参数见下表3:
表3
对比例1与实施例1的区别在于未添加PEG-TiO2添加剂组分,其他操作过程相同,对比例各组分参数见下表4:
表4
对比例得到的PES/PVA复合超滤膜的表面及断面电镜扫描图如图1A与图1B所示。
膜上表面接触角通过JC200OC1接触角测量仪测定。膜孔隙率采用干湿膜称重法测得。膜上表面与断面结构形态通过超高分辨场发射扫描电子显微镜Nova 400拍摄观察。水通量采用通量测试仪测量所得。并在室温0.1MPa下预压15min至压力稳定后测定膜的渗透水量,并测定膜对CODcr值为378.693mg/L的焦化污水的COD截留率。对比例与实施例1~3所制备得到的膜的接触角、孔隙率、水通量、COD截留率见表5:
表5
以上所述实施例仅表达了本发明的几种实施方式,其描述较为具体和详细,但并不能因此而理解为对本发明专利范围的限制。应当指出的是,对于本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进,这些都属于本发明的保护范围。因此,本发明专利的保护范围应以所附权利要求为准。
Claims (8)
1.一种PEG-TiO2/PES/PVA亲水超滤膜,其特征在于:它是以PEG-TiO2为添加剂对PES/PVA复合超滤膜进行亲水改性制得,所述PEG-TiO2是以聚乙二醇为表面活性剂对纳米二氧化钛进行修饰后所得,所述PEG-TiO2/PES/PVA亲水超滤膜中PEG-TiO2的含量为2~3wt.%。
2.一种PEG-TiO2/PES/PVA亲水超滤膜的制备方法,其特征在于:包括以下步骤:
1)制备PEG-TiO2添加剂:将纳米二氧化钛超声分散于蒸馏水中后与聚乙二醇溶液混合,搅拌均匀后静置,倒去上层清液,将下层悬浊液洗涤干净后离心、干燥、粉碎得到PEG-TiO2添加剂粉末;
2)配制铸膜液:将聚醚砜树脂、聚乙烯醇树脂、致孔剂以及PEG-TiO2添加剂粉末共混于溶剂中,加热搅拌混合至澄清透亮后静置脱泡得到铸膜液;
3)浸没沉淀相转化法成膜:将铸膜液倾倒于玻璃板上刮膜,使铸膜液在玻璃板上呈均匀薄层,待薄层由透明变为白色后浸入凝固浴中,薄层从玻璃板表面脱落后用蒸馏水洗涤晾干即得PEG-TiO2/PES/PVA亲水超滤膜。
3.根据权利要求2所述的PEG-TiO2/PES/PVA亲水超滤膜的制备方法,其特征在于:所述步骤2)按质量百分比计,聚醚砜树脂14~17%,聚乙烯醇树脂1~4%,致孔剂为1~5%,PEG-TiO2添加剂粉末为2~3%。
4.根据权利要求2或3所述的PEG-TiO2/PES/PVA亲水超滤膜的制备方法,其特征在于:所述致孔剂为聚吡络烷酮与氯化锂的混合物,聚吡络烷酮与氯化锂的质量比为1~2:1;所述溶剂为二甲基亚砜。
5.根据权利要求2所述的PEG-TiO2/PES/PVA亲水超滤膜的制备方法,其特征在于:所述步骤1)中聚乙二醇与纳米二氧化钛的质量比为0.2~0.3:99.7~99.8。
6.根据权利要求2所述的PEG-TiO2/PES/PVA亲水超滤膜的制备方法,其特征在于:所述步骤2)中,先将PEG-TiO2添加剂粉末超声分散于溶剂中,待PEG-TiO2添加剂粉末均匀分散于溶剂中后再加入聚醚砜树脂、聚乙烯醇树脂以及致孔剂,搅拌均匀。
7.根据权利要求2所述的PEG-TiO2/PES/PVA亲水超滤膜的制备方法,其特征在于:所述步骤3)中玻璃板的边缘贴有与玻璃板平面垂直的胶带;所述凝固浴为去离子水,凝固浴温度为30℃。
8.一种权利要求1所述的PEG-TiO2/PES/PVA亲水超滤膜在焦化污水处理的应用,其特征在于:应用于焦化污水中,PEG-TiO2/PES/PVA亲水超滤膜的COD截留率为87.62~91.81%。