CN106882920A - 一种裂缝釉陶瓷釉料 - Google Patents
一种裂缝釉陶瓷釉料 Download PDFInfo
- Publication number
- CN106882920A CN106882920A CN201510928707.3A CN201510928707A CN106882920A CN 106882920 A CN106882920 A CN 106882920A CN 201510928707 A CN201510928707 A CN 201510928707A CN 106882920 A CN106882920 A CN 106882920A
- Authority
- CN
- China
- Prior art keywords
- glaze
- crack
- ceramic
- ceramics
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种裂缝釉陶瓷釉料,其由以下物质按重量百分比配制而成:钾长石35-45 %,高岭土30-50 %,碳酸镁1-5 %,皂土2%,消光剂5-10%,发色剂5-10 %。本发明解决了现有裂纹釉陶瓷在釉面上所形成的裂纹形状比较小的缺点,它可让陶瓷上的釉面具有较大的裂纹,使得陶瓷上的上釉面看起来更加自然,满足了更多人的观赏需求,提高了陶瓷的观赏性。
Description
技术领域
本发明涉及一种裂缝釉陶瓷釉料。
背景技术
裂纹釉因为釉面纹路均匀、清晰,布满器面,给人一种特别的美感,深受人们的喜爱与赞赏。而现有裂纹釉陶瓷的表面所形成的裂纹釉的裂纹都比较细小不够自然美观,满足不了人们的观赏需求。
发明内容
本发明为克服现有技术的不足,提供了一种裂缝陶瓷釉料,它可在陶瓷表面形成具有较大裂纹的釉面,使釉面上的裂缝看起来更加美观自然,提高了观赏性。本发明的裂缝釉陶瓷釉料,其由以下物质按重量百分比配制而成:
钾长石 35-45 %
高岭土 30-50%
碳酸镁 1-5%
皂土 2%
消光剂 5-10 %
发色剂 5-10%
作为本发明的优选方案,其中
钾长石 40 %
高岭土 40%
碳酸镁 1%
皂土 2%
消光剂 7%
发色剂 10%
本发明的裂缝釉陶瓷釉料,解决了现有裂纹釉陶瓷的表面所形成的裂纹釉的裂纹都比较细小不够自然美观的缺点,它可在陶瓷表面形成具有较大裂纹的釉面,使釉面上的裂缝看起来更加美观自然,提高了观赏性。
具体实施方式:
实施例一
本实施例的裂缝釉陶瓷釉料由以下物质按重量百分比配制而成:
钾长石 40 %
高岭土 40%
碳酸镁 1%
皂土 2%
消光剂 7%
发色剂 10%
制作时,将上述物质按比例混合,向混合物内加水40%-45%搅拌均匀,将釉料研磨24个小时,将釉料均匀施在陶瓷胚体表面,再至窑炉烧成,烧成11小时,前3小时温度从0℃加温烧至1270℃,再进行3.5小时的还原烧成,温度到1290℃,再进行4.5小时的氧化烧成,温度到1330℃,烧成兼保温再2小时后,开窑逐渐降温至常温,该技术需要将釉料加热至形成裂纹釉面然后经过收缩形成裂缝釉面。
实施例二
本实施例的裂缝釉陶瓷釉料由以下物质按重量百分比配制而成:
钾长石 45%
高岭土 30%
碳酸镁 5%
皂土 2%
消光剂 10%
发色剂 8%
制作方法与使用方法同实施例一。
实施例三
本实施例的裂缝釉陶瓷釉料由以下物质按重量百分比配制而成:
钾长石 35%
高岭土 50%
碳酸镁 2%
皂土 2%
消光剂 5%
发色剂 6%
制作方法与使用方法同实施例一。
实施例四
本实施例的裂缝釉陶瓷釉料由以下物质按重量百分比配制而成:
钾长石 42 %
高岭土 38%
碳酸镁 4%
皂土 2%
消光剂 9%
发色剂 5%
制作方法与使用方法同实施例一。
以上所述,仅为本发明较佳实施例,故不能以此限定本发明实施的范围,即依本发明申请专利范围及说明书内容所作的等效变化与修饰,皆应仍属本发明专利涵盖的范围。
Claims (2)
1.一种裂缝釉陶瓷釉料,其特征在于由以下物质按重量百分比配制而成:
钾长石 35-45 %
高岭土 30-50%
碳酸镁 1-5%
皂土 2%
消光剂 5-10 %
发色剂 5-10%。
2.如权利要求1所述的一种裂缝釉陶瓷釉料,其特征在于由以下物质按重量百分比配制而成:
钾长石 40 %
高岭土 40%
碳酸镁 1%
皂土 2%
消光剂 7%
发色剂 10%。