CN103304271A - 一种用于大红釉中瓷面的水墨方法 - Google Patents
一种用于大红釉中瓷面的水墨方法 Download PDFInfo
- Publication number
- CN103304271A CN103304271A CN2013102196695A CN201310219669A CN103304271A CN 103304271 A CN103304271 A CN 103304271A CN 2013102196695 A CN2013102196695 A CN 2013102196695A CN 201310219669 A CN201310219669 A CN 201310219669A CN 103304271 A CN103304271 A CN 103304271A
- Authority
- CN
- China
- Prior art keywords
- ink
- minutes
- glaze
- degrees centigrade
- red glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种用于大红釉中瓷面的水墨方法,其包括:1)选取骨瓷坯体,清洗,烘干;2)采用大红釉料将骨瓷坯体经1050度-1150度高温烧制成包裹大红色釉的半成品;3)将牛胶、色墨与水按2:1:3的质量比调配,且水温为60摄氏度浸泡色墨、牛胶60分钟后研磨30分钟,存放24小时制成基础色墨;4)将乳香油与樟脑油按1:1的体积比搅拌30分钟制成油料;5)用基础色墨在半成品上勾勒山水,浓淡度通过油料的加入量来实现;6)图案完成后,将绘制好图案的半成品于40摄氏度烘干10分钟,再提升到80摄氏度-100摄氏度烘干40分钟,接着放入1050摄氏度-1250摄氏度的电窑烧制3小时,保温50分钟,自然降温至室温,即成。
Description
技术领域
本发明属于大红陶瓷釉面彩绘方法,具体涉及一种用于大红釉中瓷面的水墨方法。
背景技术
红色向征着喜庆与吉祥,是中华民族最喜爱的一种颜色。千百年来,人们一直对红色瓷器有着不解的情结。从古代的缸豆红,祭红,郎红等,一路发展至今天的中国红,由于红色难与其他颜色融合,进窑烧制之后易发生色变,通常采用小面积其它色彩与之融合。特别是釉中工艺下,大面积使用同一颜色的色料,色料渗入釉层冷却后易出现起泡等问题。近年来,科研人员一直致力于此项目的精心研究。
红瓷釉中彩工艺是近年来红瓷工艺的一项重大突破。这种方法主要是使色料的熔剂成分不含铅或少含铅,按釉上彩方法施于器物釉面,通过1050摄氏度-1150摄氏度的高温烧结后,釉面软化熔融,使颜料渗入釉层内,冷却后釉面封闭。此技法生产的产品无铅镉或少铅镉,细腻晶莹、滋润炫目,但此技法由于对画面、对颜料使用的厚度有着严格的要求(图案部分的厚度均不超过0.3mm),因而采用的仍是传统的技法制作。
水墨是中国画的一种表现形式,其颜色画面由墨色的焦、浓、重、淡、清产生丰富的变化,用于表现物象有独到的艺术效果,被视为中国传统绘画,也是国画的代表。原本的水墨画,仅有水与墨,黑色与白色,其主要是以墨为主要原料加以不同份量的清水而引为浓墨、淡墨、干墨、湿墨、焦墨等,画出不同浓淡(黑、白、灰)层次,别有一番韵味,因而称之为“墨韵”,并由此而形成水墨为主的一种绘画形式。
如果能够将红色瓷器与中国水墨技法有效地结合起来,便是对中华民族文化最好的诠释。但,目前还没有关于在大红色釉中使用水墨工艺技法的报道。
大红釉中工艺采用水墨技法的制作难点有以下方面:
一是大红色釉料中含有高温下活泼的硫、硒,而墨粉中主要含碳,化学反应不活泼,但经过1000摄氏度的高温后,墨色进入釉层中与红釉层发生反应,被红釉层遮盖,成为釉下色,达不到理想的效果。
二是物理方面,沉入大红釉中的墨色由于施墨不均,厚的地方突显,画面整体凹凸不平。
因此要烧制出水墨工艺下的釉中大红瓷必须解决以下几个问题:
1、防止硫、硒、色墨在高温釉面溶入时的化学反应。
2、对色墨进行筛选,调制各种深浅适宜的色墨与红色釉在釉中的反应。
解决烧制的温度,时间与溶入的关系。
发明内容
本发明目的在于提供一种用于大红釉中瓷面的水墨方法。采用该方法制作的红色瓷器,表面平整光滑,耐磨环保,使中华两大传统技术和现在先进工艺完美融合,彰显了文化科技的独特魅力。
本发明一种用于大红釉中瓷面的水墨方法,包括下列步骤:
1)选取骨瓷坯体,用清水除去表面的污渍与灰尘,烘干后待用;
2)采用大红釉料将骨瓷坯体经1050度-1150度高温烧制成包裹大红色釉的半成品;
3)将牛胶、色墨与水按2:1:3的质量比例调配,且保持水的温度为55-65摄氏度浸泡色墨、牛胶55-65分钟后再研磨28-32分钟,存放24小时制成基础色墨;
4)将乳香油与樟脑油按1:1的体积比例均匀搅拌28-32分钟,制成油料;
5)用基础色墨在包裹大红色釉的半成品上勾勒山水,根据画面景物远近,来确定基础色墨的浓淡,浓淡度通过加入油料的量来实现;
6)图案一次性绘制完成后,将绘制好图案的半成品于40摄氏度烘干10分钟,再提升到80摄氏度-100摄氏度烘干40分钟,接着放入炉温为1050摄氏度-1150摄氏度电窑烧制3小时,并保温50分钟后切断电源,自然降温至室温,制成成品。
本发明方法的优势为:
1、由于色墨主要由碳元素构成,在烧制温度的控制下,其能快速被釉料包化使其不与红釉中的镉、硒等发生反应,从而解决了色墨在高温区与红釉的相互反应,使釉中画案色彩厚度达到均一的要求。
2、色墨与油料的完全融合,画面沉入釉中被釉面包化,表面平整光滑,晶润。本方法的推出,完善了釉中彩装饰的单一格局,解决釉中彩烧制色料大面积成块画制的问题,更将古典与现代完美融合,表面光滑,耐磨,无气泡,针孔,网纹问题。
具体实施方式
实施例1:
1)选取一个尺寸为25*31的骨瓷幸福瓶坯体,用清水除去表面的污渍与灰尘,100摄氏度烘干后待用。
2)该骨瓷幸福瓶坯体的瓷面采用大红釉料经1050度-1150度高温烧制,观察初步成色情况,制成包裹大红色釉的半成品;
3)色墨来源:日本井泽颜料
型号:66704
基础色墨配制:牛胶、色墨与水,按2:1:3的质量比例调配,水的温度为60摄氏度浸泡色墨、牛胶55-65分钟后再研磨28-32分钟,存放24小时即成。
4)油料调配
乳香油来源:江西景德镇市新都陶瓷民营园108-5号
樟脑油来源:江西景德镇
将乳香油与樟脑油按1:1的体积比例均匀搅拌30分钟,制成油料。
5)图案绘制山水:
用基础色墨在包裹大红色釉的半成品上勾勒山水,根据画面景物远近,来确定基础色墨的浓淡,浓淡度通过加入油料的量来实现。
6)所有图案一次性绘制完成后,用40摄氏度烘干10分钟,再提升到80摄氏度-100摄氏度烘干40分钟,接着取出放入炉温为1050摄氏度-1150摄氏度的电窑烧制3小时,保温50分钟切断电源,自然降温至室温,制成成品。
Claims (1)
1.一种用于大红釉中瓷面的水墨方法,其特征在于包括下列步骤:
1)选取骨瓷坯体,用清水除去表面的污渍与灰尘,烘干后待用;
2)采用大红釉料将骨瓷坯体经1050度-1150度高温烧制成包裹大红色釉的半成品;
3)将牛胶、色墨与水按2:1:3的质量比例调配,且保持水的温度为55-65摄氏度浸泡色墨、牛胶55-65分钟后再研磨28-32分钟,存放24小时制成基础色墨;
4)将乳香油与樟脑油按1:1的体积比例均匀搅拌28-32分钟,制成油料;
5)用基础色墨在包裹大红色釉的半成品上勾勒山水,根据画面景物远近,来确定基础色墨的浓淡,浓淡度通过加入油料的量来实现;
6)图案一次性绘制完成后,将绘制好图案的半成品于40摄氏度烘干10分钟,再提升到80摄氏度-100摄氏度烘干40分钟,接着放入炉温为1050摄氏度-1250摄氏度电窑烧制3小时,并保温50分钟后切断电源,自然降温至室温,制成成品。