CN103242062A - 一种釉下五彩油彩装饰和修补的工艺方法 - Google Patents

一种釉下五彩油彩装饰和修补的工艺方法 Download PDF

Info

Publication number
CN103242062A
CN103242062A CN2013101471619A CN201310147161A CN103242062A CN 103242062 A CN103242062 A CN 103242062A CN 2013101471619 A CN2013101471619 A CN 2013101471619A CN 201310147161 A CN201310147161 A CN 201310147161A CN 103242062 A CN103242062 A CN 103242062A
Authority
CN
China
Prior art keywords
porcelain
glaze
temperature
firing
picture
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101471619A
Other languages
English (en)
Inventor
陈金华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN LILING ERASOUL CERAMICS CO Ltd
Original Assignee
HUNAN LILING ERASOUL CERAMICS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN LILING ERASOUL CERAMICS CO Ltd filed Critical HUNAN LILING ERASOUL CERAMICS CO Ltd
Priority to CN2013101471619A priority Critical patent/CN103242062A/zh
Publication of CN103242062A publication Critical patent/CN103242062A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种釉下五彩油彩装饰和修补的工艺方法，包括颜料的制备、装饰绘制和装饰画面修补、施釉烧制而成，香油颜料的制备采用无机颜料与乳香油按其重量配比4:1混合调配，撵磨2小时，再将调制好的香油颜料按需要用樟脑油稀释，然后进行装饰绘制和画面修补；将绘制修补好的瓷器送入200℃的抽屉窑内烘干，烘干后，取出瓷器施透明高温釉，再入抽屉窑烧制，用氧化焰烧至1000℃后，再用还原焰烧制，还原焰烧制温度为1380℃，整个烧制过程为6小时，经自然降温后即成。本发明是釉下五彩传统工艺的突破和工艺补充；弥补了釉下五彩传统工艺的局限性，提升工艺表现手法，降低次品率使其出现全新艺术效果的釉下五彩工艺陶瓷。

Description

一种釉下五彩油彩装饰和修补的工艺方法
技术领域
本发明涉及一种釉下五彩油彩装饰和修补的工艺方法，它是运用油彩的装饰表现手法来装饰绘制高温釉下五彩瓷和修补釉下五彩瓷在用色和艺术效果不理想的一种工艺方法。
背景技术
目前，陶瓷行业釉下五彩工艺基本上都是沿用传统的双勾汾水工艺和釉下素坯绘制工艺，都是在陶瓷坯体上绘制好图案再施釉烧制，现有釉下五彩传统工艺存在着局限性，即表象手法单一，在艺术效果上无法突破和创新；还存在着瓷器烧制完成后缺陷不能修补，只能作为次品处理或者低价销售。
发明内容
本发明的目的在于克服上述不足和缺陷，提供一种弥补釉下五彩传统工艺的局限性全新装饰绘制工艺方法，对出现用色或者艺术效果不理想、降低次品率的釉下五彩油彩修补的工艺方法。
本发明的技术方案：一种釉下五彩油彩装饰和修补的工艺方法，其特征在于所述的该工艺方法是采用高温釉下无机颜料和乳香油在高温瓷器上装饰绘制和在已烧制好有装饰缺陷的次品高温瓷器上进行装饰画面修补，即该工艺方法包括颜料的制备、装饰绘制和装饰画面修补、施釉烧制而成，具体步骤如下：
A、香油颜料的制备
香油颜料是采用市售釉下彩的高温无机颜料与乳香油按其重量配比4:1混合调配，在玻璃盘上用调色刀反复撵磨2小时，调制到香油颜料混合均匀至香油颜料颗粒细腻即可；
市售高温釉下无机颜料为釉下五彩专用陶瓷高温无机颜料，其烧成温度为1380℃以上；
B、装饰绘制和装饰画面修补
在经1380℃以上高温烧制的瓷器上和有装饰画面陷的成品瓷器上进行装饰绘制和画面修补，即将调制好的香油颜料用陶瓷绘画毛笔按绘画创作的需要蘸适量的樟脑油稀释，然后进行装饰绘制和画面修补；
C、施釉烧制
将绘制和画面修补完成的瓷器送入温度为200℃的抽屉窑内烘干，烘干后，取出瓷器施透明高温釉，施釉厚度为0.5mm，再入抽屉窑，加温烧制，先用氧化焰烧至1000℃后，再调到还原焰继续烧制，还原焰烧制温度为1380℃，整个烧制过程为6小时，经自然降温后即成。
本发明是釉下五彩传统工艺的突破和工艺补充；主要是弥补釉下五彩传统工艺的局限性，提升工艺表现手法，降低次品率。应用于高温釉下五彩瓷器，将釉下五彩无机颜料用油彩的乳香油调配，在高温瓷上运用樟脑油调配稀释已调配好的釉下五彩无机颜料进行绘制。绘制完后经过烘干，施透明白釉。入窑1380度烧制。它是高温釉下五彩瓷行业的全新工艺方法，适用于装饰绘制釉下五彩瓷器和修补各种釉下五彩用色或艺术效果不理想缺陷和工艺弥补；降低次品率，使其出现全新艺术效果的釉下五彩工艺陶瓷。
具体实施方式
一种釉下五彩油彩装饰和修补的工艺方法，其特征在于所述的该工艺方法是采用高温釉下无机颜料和乳香油在高温瓷器上装饰绘制和在已烧制好有装饰缺陷的次品高温瓷器上进行装饰画面修补，即该工艺方法包括颜料的制备、装饰绘制和装饰画面修补、施釉烧制而成，具体步骤如下：
A、香油颜料的制备
香油颜料是采用市售釉下彩的高温无机颜料与乳香油按其重量配比4:1混合调配，在玻璃盘上用调色刀反复撵磨2小时，调制到香油颜料混合均匀至香油颜料颗粒细腻即可；
市售高温釉下无机颜料为醴陵釉下五彩专用陶瓷高温无机颜料，其烧成温度为1380℃以上；
B、装饰绘制和装饰画面修补
在经1380℃以上高温烧制的瓷器上和有装饰画面陷的成品瓷器上进行装饰绘制和画面修补，即将调制好的香油颜料用陶瓷绘画毛笔按绘画创作的需要蘸适量的樟脑油稀释，然后进行装饰绘制和画面修补；
C、施釉烧制
将绘制和画面修补完成的瓷器送入温度为200℃的抽屉窑内烘干，烘干后，取出瓷器施透明高温釉，施釉厚度为0.5mm，再入抽屉窑，加温烧制，先用氧化焰烧至1000℃后，再调到还原焰继续烧制，还原焰烧制温度为1380℃，整个烧制过程为6小时，经自然降温后即成。
本发明是釉下五彩传统工艺的突破和工艺补充；主要是弥补釉下五彩传统工艺的局限性，提升工艺表现手法，降低次品率。应用于高温釉下五彩瓷器，将釉下五彩无机颜料用油彩的乳香油调配，在高温瓷上运用樟脑油调配稀释已调配好的釉下五彩无机颜料进行绘制。绘制完后经过烘干，施透明白釉。入窑1380度烧制。它是高温釉下五彩瓷行业的全新工艺方法，适用于装饰绘制釉下五彩瓷器和修补各种釉下五彩用色或艺术效果不理想缺陷和工艺弥补；降低次品率，使其出现全新艺术效果的釉下五彩工艺陶瓷。

Claims (1)

1. 一种釉下五彩油彩装饰和修补的工艺方法，其特征在于所述的该工艺方法是采用高温釉下无机颜料和乳香油在高温瓷器上装饰绘制和在已烧制好有装饰缺陷的次品高温瓷器上进行装饰画面修补，即该工艺方法包括颜料的制备、装饰绘制和装饰画面修补、施釉烧制而成，具体步骤如下：
A、香油颜料的制备
香油颜料是采用市售釉下彩的高温无机颜料与乳香油按其重量配比4:1混合调配，在玻璃盘上用调色刀反复撵磨2小时，调制到香油颜料混合均匀至香油颜料颗粒细腻即可；
市售高温釉下无机颜料为釉下五彩专用陶瓷高温无机颜料，其烧成温度为1380℃以上；
B、装饰绘制和装饰画面修补
在经1380℃以上高温烧制的瓷器上和有装饰画面陷的成品瓷器上进行装饰绘制和画面修补，即将调制好的香油颜料用陶瓷绘画毛笔按绘画创作的需要蘸适量的樟脑油稀释，然后进行装饰绘制和画面修补；
C、施釉烧制
将绘制和画面修补完成的瓷器送入温度为200℃的抽屉窑内烘干，烘干后，取出瓷器施透明高温釉，施釉厚度为0.5mm，再入抽屉窑，加温烧制，先用氧化焰烧至1000℃后，再调到还原焰继续烧制，还原焰烧制温度为1380℃，整个烧制过程为6小时，经自然降温后即成。
CN2013101471619A 2013-04-25 2013-04-25 一种釉下五彩油彩装饰和修补的工艺方法 Pending CN103242062A (zh)