CN106835463A - One kind is reversely led wet ice and is relaxed dry and comfortable sportswear fabric and preparation method thereof - Google Patents
One kind is reversely led wet ice and is relaxed dry and comfortable sportswear fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106835463A CN106835463A CN201710178074.8A CN201710178074A CN106835463A CN 106835463 A CN106835463 A CN 106835463A CN 201710178074 A CN201710178074 A CN 201710178074A CN 106835463 A CN106835463 A CN 106835463A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yarn
- hydrophilic
- dry
- reversely
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Wet ice is reversely led the invention discloses one kind to relax dry and comfortable sportswear fabric, the sportswear fabric is the institutional framework for including internal layer and outer bilayer fabric, internal layer is the alternate form of hydrophilic region and water repellent region being made up of hydrophilic yarn and water repellency yarn, outer layer is hydrophilic yarn, and hydrophilic yarn is the high hydrophilic bio-based ice silk polyester fiber in shaped grooves section.The invention also discloses the preparation method of the sportswear fabric, including fabric weaving → fabric pre-treatment → dyeing → reduction cleaning → setting.It is of the invention reversely lead wet ice relax dry and comfortable sportswear fabric have it is good lead wet, ice relax, rapid-curing cutback, dry and comfortable, permeability;And its method for preparing fabric is simple, it is not required to change dyeing or rear whole technique because of the change of fabric face performance, so as to reduce the difficulty of the techniques such as follow-up dyeing, solves the problems, such as that water-proof aagent arranges pollution environment, greatly reduces processing cost.
Description
Technical field
The invention belongs to weaving face fabric production technical field, and in particular to one kind reversely lead wet ice relax dry and comfortable sportswear fabric and
Its preparation method.
Background technology
CRUX clothes are a rings important during people wear, and with the lifting of living standard, people not only only focus on
The style of clothes, increasingly focuses on the functions such as the snugness of fit of garment material, one-way wet-guide, absorbing fast-drying.Fabric
One-way wet-guide, absorbing fast-drying are weaved by selecting the raw material of different hygroscopicity and wet guilding, or after weaving by right
It (can also be that two surfaces carry out hydrophilic treated and refuse respectively that one surface of fabric carries out hydrophilic, hydrophobic modified or arrangement
Water process), using the yarn of wet guilding difference as inner surface, and the strong yarn of wet ability as superficies will be led, surfaces externally and internally
Capillary is differential to make inner surface yarn rapidly lead outer layer by the yarn of outer surface after sweat is absorbed, and evaporates quick-drying, greatly
Residence time of the sweat on human body skin is reduced, fabric is reached comfortable dry and comfortable effect.
Wet-guide quick-drying fabric is by increasing disengagement area, sweat is quickly spread on fabric, reach the purpose of quick-drying.
One-way wet-guide quick-drying fabric is hydrophilic by the hydrophily and hydrophobic difference, i.e. outer fabric layer of ectonexine fabric fibre and knits
Thing internal layer major part is hydrophobic, and sweat is transferred to the hydrophily outer layer of fabric from the hydrophilic position of internal layer fraction, and fast in outer layer
Speed is evaporated.Most of hydrophobic internal layer makes to wear non-sticky body during perspiring, adds outer fabric layer moisture rapid evaporation band
Substantial amounts of heat energy is walked, and then makes human body sensory nice and cool, comfortable.One-way wet-guide quick-drying fabric is a kind of with environmental change (such as human body
Produce sweat) and the fabric that responds automatically (sweat is drained into outer fabric layer automatically), therefore, it belongs to a kind of intelligence weaving
Fabric.
Such as:Patent CN101962885A discloses a kind of method for preparing the product with unidirectional moisture conducting function, the method
Including 1) carrying out hydrophiling pretreatment to fabric;2) one side of working solution of the use containing water repellent finishing agent to the fabric after treatment
Spray processing is carried out, to cause that it is 0.1-2mm's that a diameter of 0.1-2mm and spacing each other are formed on the face of fabric
Drop, so as to obtain the product with unidirectional moisture conducting function.Patent CN101775701A discloses a kind of cotton of one-way wet-guide
Spunlace non-woven cloth, product and its manufacture method, cotton spunlace non-woven cloth include cotton spunlace non-woven cloth matrix, the cotton spun lacing
Non-woven fabrics matrix includes hydrophobic surface and hydrophilic surface, and the hydrophobic surface contains for moisture to be conducted to the parent from the hydrophobic surface
The hydrophobic substance of the water surface.Cotton material is selected in the invention, and the frivolous softness of quality, one-way wet-guide effect is good, can effectively absorb and
Infiltration moisture, it is to avoid moisture countercurrently, makes to keep dry and comfortable with the hydrophobic surface of human body skin directly contact.Patent CN101956327A is public
A kind of wool fabric with unidirectional moisture conducting function is opened, it is characterised in that there is irregular point in any surface of the wool fabric
The water repellent region of cloth, the area in the water repellent region is 0.01-4mm2 and spacing each other is 0.1-2mm.The wool fabric
Fabric two sides on construct hydrophilic, hydrophobic property different " two sided structure " and the water repellent in the one side with hydrophobic property
The region in region is smaller and structure is more simple.Patent CN102505301A discloses a kind of new with unidirectional moisture conducting function
Knitting fabric, it is characterised in that:It is two-layer fabric structure, and the two-layer fabric structure includes internal layer water repellent fiber and outer layer parent
Water cellulose, the internal layer hydrophobic fiber is polypropylene fiber.Present invention also offers a kind of knitted side with unidirectional moisture conducting function
The processing technology of material, it is comprised the following steps that:Fabric weaving → fabric pre-treatment → dyeing → reduction cleaning → setting.Again
As patent CN103696110A discloses a kind of cotton of one-way wet-guide absorbing fast-drying/brocade compound knitted fabric, the fabric is using double
The institutional framework of face plain weave, leads more by force the poor cotton yarn of wet ability and weaves into fabric internal layer by large circle machine by wettability power, and
The excellent super fine denier chinlon filament of moisture absorption, wet guilding ability weaves into fabric outer layer.
From above-mentioned prior art, one-way wet-guide, absorbing fast-drying mainly use the difference of surfaces externally and internally Moisture absorption & moisture conductivity
It is different, the sweat of human body surface is rapidly discharged and quick-drying is evaporated, typically there are following two methods:One kind is by hydrophilic finiss
Or the method such as hydrophobic finishing or modified, stamp causes inner surface hydrophobic or surface and hydrophilic outer, increases the capillary between surfaces externally and internally
Gap edge, so as to reach the effect of one-way wet-guide and absorbing fast-drying, but the fabric of this class is deficient in moisture-penetrable ventilated property
Lack, and the stability of chemical finishing agent is not high, influences the durability (above-mentioned part of the patent application is exactly this class) of fabric;Separately
A kind of weaved by the raw material (not having treated yarn) from different hygroscopicity and wet guilding, with water repellent fiber
It is inner surface, hydrophilic fibers are outer surface, realizes the effect of one-way wet-guide, absorbing fast-drying, but because the water repellent of inner surface is fine
Dimension is usually chemical fibre, and snugness of fit is not good (above-mentioned to have part of the patent application to fall within this class).
The content of the invention
The present invention for the knitting fabric of existing wet guiding function be generally modified working process product, unidirectional moisture conducting function it is resistance to
The problem of long property difference and the problem that fabric processing technology complexity, processing efficiency are low, water-proof aagent pollutes environment, there is provided
One kind is reversely led wet ice and is relaxed dry and comfortable sportswear fabric and preparation method thereof.
To achieve the above object, the present invention uses following technical scheme:
The first aspect of the invention be to provide it is a kind of reversely lead wet ice and relax dry and comfortable sportswear fabric, the sportswear fabric is bag
The institutional framework of internal layer and outer bilayer fabric is included, the internal layer is the hydrophilic area being made up of hydrophilic yarn and water repellency yarn
The alternate form in domain and water repellent region, the outer layer is hydrophilic yarn, and the hydrophilic yarn is the height in shaped grooves section
Hydrophilic bio-based ice silk polyester fiber.
Further, the materials ratio of hydrophilic yarn and water repellency yarn is 1 in the internal layer:3-5.
Further, hydrophilic region and water repellent region are interval striped in the internal layer;Or the hydrophilic region is any
Geometric figure is arranged with a matrix type, and the hydrophilic region is 1 with the area ratio in the water repellent region:2-4.
Further, the water repellency yarn is fasciated yarn structure, and its yarn core is hygroscopic acetate fiber, and outsourcing yarn is
The polypropylene fiber of wet guilding, the acetate fiber is 1 with polypropylene fiber amount ratio:2-3.
The second aspect of the invention be to provide it is a kind of reversely lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, including with
Lower step:Fabric weaving → fabric pre-treatment → dyeing → reduction cleaning → setting.
Further, the fabric pre-treating technology is:Fabric is imported in L-type HTHP overflow dyeing machine, normal temperature
Add 2g/L-6g/L soda ash and 2g/L-7g/L to deoil yarn agent, 95-120 DEG C of insulation is warming up to 2-5 DEG C per minute of speed
10min, draining, overflow washing.
Further, the dyeing is:By the fabric water inlet after pre-treatment, 35-40 DEG C of addition 0.3g/L- is warming up to
0.4g/L glacial acetic acid, adds HTHP levelling agent 0.2g/L-0.4g/L, emulsifying agent 0.2g/L-0.4g/L, hydroscopic fast-drying auxiliary agent
0.5g/L-5g/L, high temperature modification disperse dyes are added after operation 10-20min, are then warming up to 80 with 2-3 DEG C per minute of speed
DEG C, after insulation 10-15min, 130-135 DEG C is warming up to again with 1-2 DEG C per minute, it is incubated 40-60min.
Further, the reduction cleaning technique is:70-75 DEG C is cooled to 1-2 DEG C per minute of speed, 10- is incubated
After 15 minutes, the NaOH and 1g/LNa of 2g/L are added2S2O3, 20min is incubated after being warming up to 85-90 DEG C, it is cooled to 70 DEG C, discharge opeing
Intake after washing, in overflow dyeing machine and add 0.6g/L glacial acetic acid to run 15min, wash out cylinder.
Further, the setting process is:Fabric after reduction cleaning is first in fabric table before cabinet setting is entered
Spray the steam dewing of 3-5Kg pressure in face;Subsequently into forming machine, it is 10-25m/ that setting temperature is 160 DEG C -185 DEG C, machine is fast
min。
Further, the hydroscopic fast-drying auxiliary agent is usedMoisture control agent SW;The high temperature modification dispersion
The high temperature modification disperse dyes of the ForonRD-E models that dyestuff is produced using Clariant companies.
The present invention uses above-mentioned technical proposal, compared with prior art, have the following technical effect that:
Of the invention reversely to lead wet ice and relax in dry and comfortable sportswear fabric, internal layer uses the alternate shape of hydrophilic region and water repellent region
State, outer layer is, using the total hydrophilic region of hydrophilic fibers, on the basis of its snugness of fit is ensured, to effectively increase it and lead
Wet, ice relaxes, rapid-curing cutback performance, and with the multiple function such as good durability, dry-ness, gas permeability;The present invention prepares fabric
Method is simple, is not required to change dyeing or rear whole technique because of the change of fabric face performance, so as to reduce the techniques such as follow-up dyeing
Difficulty, solve the problems, such as water-proof aagent arrange pollution environment, greatly reduce processing cost.
Brief description of the drawings
Fig. 1 is that the present invention is a kind of reversely to be led wet ice and relaxes the structural representation of dry and comfortable sportswear fabric;
Fig. 2 is a kind of distribution schematic diagram in hydrophilic region and water repellent region in sportswear fabric internal layer of the present invention;
Fig. 3 is another distribution schematic diagram in hydrophilic region and water repellent region in sportswear fabric internal layer of the present invention.
Specific embodiment
The present invention is described in more detail below by specific embodiment, for a better understanding of the present invention,
But following embodiments are not intended to limit the scope of the invention.
As illustrated in fig. 1 and 2, the embodiment of the invention provides and a kind of reversely lead wet ice and relax dry and comfortable sportswear fabric, the moving surface
Material is formed using woven the making of knitted jacquard, its two-layer fabric institutional framework for including internal layer 1 and outer layer 2, and internal layer 1 is by hydrophily
The alternate form of hydrophilic region 4 and water repellent region 3 that yarn and water repellency yarn are constituted, outer layer is hydrophilic yarn, hydrophily
Yarn is the high hydrophilic bio-based ice silk polyester fiber in shaped grooves section.
In order on the basis of the dry-ness and comfortableness for ensureing fabric dress, there is provided its wet transmitting performance, sent out through research
Existing, the materials ratio of hydrophilic yarn and water repellency yarn is 1 in internal layer:3-5, preferably 1:3.5-4.5, more preferably 1:4.This
Outward, for the alternate form of hydrophilic region 4 on the fabric internal layer and water repellent region 3, hydrophilic region and water repellent region in internal layer
It is interval striped;Preferably, hydrophilic region is arranged for any geometric figure with a matrix type;It is highly preferred that hydrophilic region is
Diamond structure, as shown in figure 3, its lead it is wet better.
In the present embodiment fabric internal layer, hydrophilic region is 1 with the area ratio in water repellent region:2-4;Preferably 1:2.5-3.5;
More preferably 1:3.Used water repellency yarn is fasciated yarn structure, and its yarn core is acetate fiber, and outsourcing yarn is polypropylene fiber, vinegar
Ester fiber is 1 with polypropylene fiber amount ratio:2-3;Preferably 1:2.5.
The present embodiment additionally provide it is a kind of reversely lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, comprise the following steps:
Fabric weaving → fabric pre-treatment → dyeing → reduction cleaning → setting, wherein:
Fabric pre-treating technology is:Fabric is imported in L-type HTHP overflow dyeing machine, normal temperature adds 2g/L-6g/L
Soda ash and 2g/L-7g/L are deoiled yarn agent, and 95-120 DEG C of insulation 10min, draining, overflow are warming up to 2-5 DEG C per minute of speed
Washing.
Dyeing is:By the fabric water inlet after pre-treatment, 35-40 DEG C of addition 0.3g/L-0.4g/L glacial acetic acid is warming up to,
HTHP levelling agent 0.2g/L-0.4g/L, emulsifying agent 0.2g/L-0.4g/L, hydroscopic fast-drying auxiliary agent 0.5g/L-5g/L are added,
High temperature modification disperse dyes are added after operation 10-20min, then 80 DEG C is warming up to 2-3 DEG C per minute of speed, 10- is incubated
After 15min, 130-135 DEG C is warming up to again with 1-2 DEG C per minute, be incubated 40-60min.
Reduction cleaning technique is:70-75 DEG C is cooled to 1-2 DEG C per minute of speed, after being incubated 10-15 minutes, is added
The NaOH and 1g/LNa of 2g/L2S2O3, 20min is incubated after being warming up to 85-90 DEG C, it is cooled to 70 DEG C, after discharge opeing washing, overflow dyeing machine
Interior water inlet simultaneously adds 0.6g/L glacial acetic acid to run 15min, washes out cylinder.
Setting process is:Fabric after reduction cleaning is first sprayed into 3-5Kg pressure before cabinet setting is entered in web surface
Steam dewing;Subsequently into forming machine, it is 10-25m/min that setting temperature is 160 DEG C -185 DEG C, machine is fast.
Hydroscopic fast-drying auxiliary agent is usedMoisture control agent SW;High temperature modification disperse dyes are public using Clariant
Take charge of the high temperature modification disperse dyes of the ForonRD-E models of production.
Relative to independent hydrophilic layer in the prior art and water repellent layer bilayer moisture-guiding fabric fabric, sportswear fabric of the invention exists
On the basis of existing double-deck wet cloth, alternatively distributed hydrophilic area is formed using hydrophilic yarn and water repellency yarn in internal layer
Domain 4 and water repellent region 3, ensure fabric it is dry and comfortable it is comfortable on the basis of, effectively increase the hydrophobic efficiency of fabric internal layer outer layers.
Specific embodiment of the invention has been described in detail above, but it is intended only as example, and the present invention is not limited
It is formed on particular embodiments described above.To those skilled in the art, any equivalent modifications carried out to the present invention and
Replacement is also all among scope of the invention.Therefore, the impartial conversion made without departing from the spirit and scope of the invention and
Modification, all should be contained within the scope of the invention.
Claims (10)
1. one kind is reversely led wet ice and is relaxed dry and comfortable sportswear fabric, it is characterised in that the sportswear fabric is to include that internal layer and outer layer are double
The institutional framework of layer fabric, the internal layer is the hydrophilic region and the friendship of water repellent region being made up of hydrophilic yarn and water repellency yarn
The form replaced, the outer layer is hydrophilic yarn, and the hydrophilic yarn is the high hydrophilic bio-based ice silk in shaped grooves section
Polyester fiber.
2. it is according to claim 1 reversely to lead wet ice and relax dry and comfortable sportswear fabric, it is characterised in that hydrophily in the internal layer
The materials ratio of yarn and water repellency yarn is 1:3-5.
3. it is according to claim 1 reversely to lead wet ice and relax dry and comfortable raw material fabric, it is characterised in that hydrophilic area in the internal layer
Domain is interval striped with water repellent region;It is described hydrophilic or the hydrophilic region is arranged for any geometric figure with a matrix type
Region is 1 with the area ratio in the water repellent region:2-4.
4. it is according to claim 1 reversely to lead wet ice and relax dry and comfortable raw material fabric, it is characterised in that the water repellency yarn is
Fasciated yarn structure, its yarn core is hygroscopic acetate fiber, and outsourcing yarn is the polypropylene fiber of wet guilding, the acetate fiber and third
Synthetic fibre fiber consumption ratio is 1:2-3.
5. the wet ice of reversely leading as described in claim any one of 1-4 relaxes the preparation method of dry and comfortable sportswear fabric, it is characterised in that
Comprise the following steps:Fabric weaving → fabric pre-treatment → dyeing → reduction cleaning → setting.
6. it is according to claim 5 reversely to lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, it is characterised in that the base
Cloth pre-treating technology is:Fabric is imported in L-type HTHP overflow dyeing machine, normal temperature adds 2g/L-6g/L soda ash and 2g/L-
7g/L is deoiled yarn agent, and 95-120 DEG C of insulation 10min, draining, overflow washing are warming up to 2-5 DEG C per minute of speed.
7. it is according to claim 6 reversely to lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, it is characterised in that the dye
Color technique is:By the fabric water inlet after pre-treatment, 35-40 DEG C of addition 0.3g/L-0.4g/L glacial acetic acid is warming up to, adds high temperature high
Pressure levelling agent 0.2g/L-0.4g/L, emulsifying agent 0.2g/L-0.4g/L, hydroscopic fast-drying auxiliary agent 0.5g/L-5g/L, run 10-
High temperature modification disperse dyes are added after 20min, then 80 DEG C, after insulation 10-50min is warming up to 2-3 DEG C per minute of speed, with
1-2 DEG C per minute is warming up to 130-135 DEG C again, is incubated 40-60min.
8. it is according to claim 7 reversely to lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, it is characterised in that it is described also
Former cleaning is:70-75 DEG C is cooled to 1-2 DEG C per minute of speed, after being incubated 10-15 minutes, the NaOH of 2g/L is added
And 1g/LNa2S2O3, 20min is incubated after being warming up to 85-90 DEG C, 70 DEG C are cooled to, after discharge opeing washing, intake in overflow dyeing machine and added
Enter 0.6g/L glacial acetic acid operation 15min, wash out cylinder.
9. it is according to claim 8 reversely to lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, it is characterised in that described fixed
Shape technique is:Fabric after reduction cleaning is first sprayed into the steam dewing of 3-5Kg pressure before cabinet setting is entered in web surface;
Subsequently into forming machine, it is 10-25m/min that setting temperature is 160-185 DEG C, machine is fast.
10. it is according to claim 9 reversely to lead wet ice and relax the preparation method of dry and comfortable sportswear fabric, it is characterised in that described
Hydroscopic fast-drying auxiliary agent is usedMoisture control agent SW;The high temperature modification disperse dyes are given birth to using Clariant companies
The high temperature modification disperse dyes of the ForonRD-E models of product.