CN108749225A - A kind of unidirectional moisture conducting function fabric - Google Patents
A kind of unidirectional moisture conducting function fabric Download PDFInfo
- Publication number
- CN108749225A CN108749225A CN201810385579.6A CN201810385579A CN108749225A CN 108749225 A CN108749225 A CN 108749225A CN 201810385579 A CN201810385579 A CN 201810385579A CN 108749225 A CN108749225 A CN 108749225A
- Authority
- CN
- China
- Prior art keywords
- fabric
- conducting function
- unidirectional moisture
- moisture conducting
- outer shell
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The purpose of the present invention is to provide a kind of unidirectional moisture conducting function fabrics, it is made through bonding of fabric and outer shell fabric, fabric is the fabric with dry and comfortable characteristic, and outer shell fabric is the fabric with Moisture absorbing & quick drying property, and the fabric of ectonexine is to be bonded as composite material by adhesive.The beneficial effects of the invention are as follows the outer layers for during exercise, enabling the sweat that human body generates quickly be transmitted to by fabric fabric from the internal layer of fabric, and keep internal layer dry and comfortable.
Description
Technical field
The invention belongs to textile engineering technical field, it is related to a kind of unidirectional moisture conducting function fabric and its production method, the face
Expect the movement for wearing next to the skin and sportswear.
Background technology
The physiological metabolism of human normal contains the wet metabolism of heat, wherein wet metabolism is shown in the form of sweat gas or sweat
Come.Human body is in hot environment or carry out movement or when labor operation, will produce sweat, and take away heat, and human body is maintained with this
Physiological equilibrium.Human sweat needs to absorb and distribute by garment material, uses the fabric system for well leading wet and scattered wet performance
At clothes the sweat of human body can be made to be discharged in time, to realize the comfortable of human body.Using leading, wet and scattered wet performance is bad
Fabric made of clothes often cause the accumulation of human heat and sweat, to cause uncomfortable feeling even can cause phase
Related disorders jeopardize health.
Traditional garment material worn next to the skin pays close attention to soft, moisture absorption and breathes freely mostly, and for dissipating wet and holding human body
Dry and comfortable performance then pay close attention to not enough.In recent years, the reinforcing with movement in people's lives, to adapt to movement to clothes
The demand of fabric, the fabric with hydroscopic fast-drying function are praised highly by people, current hydroscopic fast-drying fabric for sports & casual wear
It is mainly manifested in the simply hydroscopic fast-drying to fabric to arrange, so that it is had good wet transmitting performance, this fabric is to a certain degree
On can make people experience this fabric hot wet migration essence exist, but for largely show sweat dressing person for, this
Human body very effectively can not be shown sweat discharge by kind fabric, cannot be formed the wet difference of fabric inside and outside layer, can not be made human skin
Keep dry and comfortable.Can human sweat be effectively transmitted to fabric from the inner layer of fabric with the garment material for unidirectionally leading sweat function
Outer layer so that the overwhelming majority for the sweat that human body generates is absorbed by the outer layer of fabric, and the inner layer of fabric hardly picks up sweat,
Human body is set to remain dry and comfortable.
There are mainly two types of modes, i.e. coating and yarn to be modified method for the mode that one-way wet-guide fabric is realized at present.Coating
Mode is mainly using water repellent finishing agent to having good hygroscopic fabric inner layer to carry out coating, such as american cotton company
What Wicking windows technologies were taken is exactly this mode.Yarn modification method is exactly the yarn for using water repellent to be modified and general
Logical yarn is interleaved, then realizes unidirectional moisture conducting function by specific knitted structure, such as patent CN200420076289, U.S.
The Transdry technologies etc. of cotton company of state are exactly this mode.Coating makes one-way wet-guide fabric, simple for process, controllability
It is good, but the dry and comfortable effect of fabric inner layer is poor.Yarn is modified legal system and makees one-way wet-guide fabric, and the dry and comfortable effect of fabric inner layer is good, but work
Skill is complicated, and technique controlling difficulty is larger, and production cost is high, and there is the discharge of the Organic fluoride for the environment that is difficult to degrade, pollute.
Invention content
The purpose of the present invention is to provide a kind of unidirectional moisture conducting function fabric, the beneficial effects of the invention are as follows during exercise,
So that the sweat that human body generates quickly is transmitted to the outer layer of fabric from the internal layer of fabric by fabric, and keeps internal layer dry and comfortable.
The technical solution adopted in the present invention is made of fabric and outer shell fabric through bonding, fabric be with
The fabric of dry and comfortable characteristic, outer shell fabric are the fabric with Moisture absorbing & quick drying property, the fabric of ectonexine be by adhesive by its
It is bonded as composite material.
Further, outer shell fabric is the knitting by hydrophilic finish with good wet transmitting performance or shuttle-woven fabric,
Raw material be pure cotton, it is pure wash, polyester-cotton blend is blended, polyester-cotton blend interweave, grammes per square metre > 190g/m2, the hair suction height > 15cm/30min of fabric.
Further, fabric is knitting fabric, and used yarn is polyester DTY or FDY, and fabric grammes per square metre <
100g/m2。
Further, outer shell fabric needs to carry out hydrophilic finiss, and the method for arrangement is:Fabric → washing oil → high-temperature pressure dyeing
→ washing → dehydration → 8%NaOH solution, TF-620 finishing agents → bakes sizing, and the fabric after arrangement has hydrophilic well
Property, measure wicking height integrated value is 20-40cm/30min.
Further, fabric needs to carry out dry and comfortable arrangement, and the method for arrangement is:Fabric → washing oil → high-temperature pressure dyeing
→ washing → is dehydrated, and → rolling water and oil repellant auxiliary agent C6 → bakes sizing, and the fabric after arrangement does not get wet, non-hygroscopic, has centainly
Waterproofing function, surface contact angle are 95 ° -120 °.
Further, fabric and outer shell fabric are bonded used in two kinds of fabrics to together by adhesive bonding
Adhesive is by three kinds of polyester compound adhesive, isocyanates, bridging agent ingredients with 100:45:15 ratios mix, coating weight
For 15-20g/m2, and shape at a temperature of 140-170 DEG C.
Further, one-way wet-guide ability R > 200%.
Description of the drawings
Fig. 1 is fabric structure schematic diagram of the present invention;
Fig. 2 is fabric structure layer schematic diagram of the present invention.
Specific implementation mode
The present invention is described in detail With reference to embodiment.
As shown in Figure 1, the present invention using a kind of fabric two kinds of different performances through bonding and made of two-layer compound face
Material, the fabric internal layer 2 (skin-proximal layer) of the composite material are the fabric with dry and comfortable characteristic, fabric outer layer 1 be with
The fabric of Moisture absorbing & quick drying property, the fabric of ectonexine are to be bonded as composite material by adhesive.
Specific embodiment 1:
A kind of outer shell fabric of the fabric of unidirectional moisture conducting function is pure cotton knitted fabric, and after hydrophilic finish, grammes per square metre is
200g/m2, it is 15.8cm/30min that the hair of fabric, which inhales height,.The fabric of unidirectional moisture conducting function fabric is polyester DTY, through dry
After refreshing arrangement, grammes per square metre 90g/m2。
To the outer layer pure cotton knitted fabric of unidirectional moisture conducting function fabric, hydrophilic finish is carried out, the method for arrangement is:Fabric →
Washing oil → high-temperature pressure dyeing → washing → dehydration → 8%NaOH solution, TF-620 finishing agents 6g/L (two leachings two are rolled) → bakes
Sizing.It is 35.37cm/30min that fabric after arrangement, which has good hydrophily, measure wicking height integrated value,.
To the polyester knitting object object of unidirectional moisture conducting function fabric, dry and comfortable arrangement is carried out, the method for arrangement is:Fabric → washing oil
→ high-temperature pressure dyeing → washing → is dehydrated, and → rolling water and oil repellant auxiliary agent (a concentration of 1g/L of C6 water repellents) → bakes sizing.Water repellent
Agent concentration formula is adhesive:20%, sodium sulfocyanate:0.1g/L, sodium alginate:2.5%, epoxychloropropane:3%.After arrangement
Fabric do not get wet, it is non-hygroscopic, have certain waterproofing function, surface contact angle be 115 °.
The fabric and outer shell fabric of unidirectional moisture conducting function fabric are to bond two kinds to together by adhesive bonding
Adhesive used in fabric is by three kinds of polyester compound adhesive, isocyanates, bridging agent ingredients with 100:45:15 ratios mix and
At coating weight 18g/m2, and shape at a temperature of 160 DEG C.
Specific embodiment 2:
A kind of outer shell fabric of the fabric of unidirectional moisture conducting function is polyester-cotton blend blended fabric, after hydrophilic finish, gram
Weight is 195g/m2, it is 16.3cm/30min that the hair of fabric, which inhales height,.The fabric of unidirectional moisture conducting function fabric is polyester DTY,
After dry and comfortable arrangement, grammes per square metre 90g/m2。
To the outer layer pure cotton knitted fabric of unidirectional moisture conducting function fabric, hydrophilic finish is carried out, the method for arrangement is:Fabric →
Washing oil → high-temperature pressure dyeing → washing → dehydration → 8%NaOH solution, TF-620 finishing agents 6g/L (two leachings two are rolled) → bakes
Sizing.It is 37.85cm/30min that fabric after arrangement, which has good hydrophily, measure wicking height integrated value,.
To the polyester knitting object object of unidirectional moisture conducting function fabric, dry and comfortable arrangement is carried out, the method for arrangement is:Fabric → washing oil
→ high-temperature pressure dyeing → washing → is dehydrated, and → rolling water and oil repellant auxiliary agent (a concentration of 1g/L of C6 water repellents) → bakes sizing.Water repellent
Agent concentration formula is adhesive:20%, sodium sulfocyanate:0.1g/L, sodium alginate:2.5%, epoxychloropropane:3%.After arrangement
Fabric do not get wet, it is non-hygroscopic, have certain waterproofing function, surface contact angle be 115 °.
Specific embodiment 3:
A kind of outer shell fabric of the fabric of unidirectional moisture conducting function is pure cotton woven fabric, and after hydrophilic finish, grammes per square metre is
230g/m2, it is 15.2cm/30min that the hair of fabric, which inhales height,.The fabric of unidirectional moisture conducting function fabric is polyester DTY, through dry
After refreshing arrangement, grammes per square metre 90g/m2。
To the outer layer pure cotton knitted fabric of unidirectional moisture conducting function fabric, hydrophilic finish is carried out, the method for arrangement is:Fabric →
Washing oil → high-temperature pressure dyeing → washing → dehydration → 8%NaOH solution, TF-620 finishing agents 6g/L (two leachings two are rolled) → bakes
Sizing.It is 30.31cm/30min that fabric after arrangement, which has good hydrophily, measure wicking height integrated value,.
To the polyester knitting object object of unidirectional moisture conducting function fabric, dry and comfortable arrangement is carried out, the method for arrangement is:Fabric → washing oil
→ high-temperature pressure dyeing → washing → is dehydrated, and → rolling water and oil repellant auxiliary agent (a concentration of 1g/L of C6 water repellents) → bakes sizing.Water repellent
Agent concentration formula is adhesive:20%, sodium sulfocyanate:0.1g/L, sodium alginate:2.5%, epoxychloropropane:3%.After arrangement
Fabric do not get wet, it is non-hygroscopic, have certain waterproofing function, surface contact angle be 115 °.
The fabric and outer shell fabric of unidirectional moisture conducting function fabric are to bond two kinds to together by adhesive bonding
Adhesive used in fabric is by three kinds of polyester compound adhesive, isocyanates, bridging agent ingredients with 100:45:15 ratios mix and
At coating weight 18g/m2, and shape at a temperature of 160 DEG C.
The one-way wet-guide ability R > 200% (AATCC195-2012) of unidirectional moisture conducting function fabric.
Unidirectional moisture conducting function fabric of the present invention makes simply, without Organic fluoride pollutant emission in production, is produced into
This is low, and the unidirectional moisture conducting function of fabric is strong, is the ideal fabric of movement and sportswear.
The above is only the better embodiment to the present invention, not makees limit in any form to the present invention
System, every any simple modification that embodiment of above is made according to the technical essence of the invention, equivalent variations and modification,
Belong in the range of technical solution of the present invention.
Claims (7)
1. a kind of unidirectional moisture conducting function fabric, it is characterised in that:It is made through bonding of fabric and outer shell fabric, fabric
For the fabric with dry and comfortable characteristic, outer shell fabric is the fabric with Moisture absorbing & quick drying property, and the fabric of ectonexine is to pass through bonding
Agent is bonded as composite material.
2. according to a kind of unidirectional moisture conducting function fabric described in claim 1, it is characterised in that:The outer shell fabric is by hydrophilic
Property the knitting with good wet transmitting performance that arranges or shuttle-woven fabric, raw material be pure cotton, it is pure wash, polyester-cotton blend is blended, polyester-cotton blend intertexture,
Its grammes per square metre > 190g/m2, the hair suction height > 15cm/30min of fabric.
3. according to a kind of unidirectional moisture conducting function fabric described in claim 1, it is characterised in that:The fabric is knitted side
Material, used yarn are polyester DTY or FDY, and fabric grammes per square metre < 100g/m2。
4. according to a kind of unidirectional moisture conducting function fabric described in claim 1, it is characterised in that:The outer shell fabric needs to carry out parent
Water arranges, and the method for arrangement is:Fabric → washing oil → high-temperature pressure dyeing → washing → dehydration → 8%NaOH solution, TF-620
Finishing agent → bake sizing, it is 20-40cm/30min that the fabric after arrangement, which has good hydrophily, measure wicking height integrated value,.
5. according to a kind of unidirectional moisture conducting function fabric described in claim 1, it is characterised in that:The fabric is done
Refreshing to arrange, the method for arrangement is:Fabric → washing oil → high-temperature pressure dyeing → washing → be dehydrated → roll water and oil repellant auxiliary agent C6 →
Sizing is baked, the fabric after arrangement does not get wet, non-hygroscopic, and it is 95 ° -120 ° to have certain waterproofing function, surface contact angle.
6. according to a kind of unidirectional moisture conducting function fabric described in claim 1, it is characterised in that:The fabric and outer shell fabric
It is by adhesive bonding to together, it is by polyester compound adhesive, isocyanates, bridge formation to bond the adhesive used in two kinds of fabrics
Three kinds of ingredients of agent are with 100:45:15 ratios mix, coating weight 15-20g/m2, and it is fixed at a temperature of 140-170 DEG C
Type.
7. according to a kind of unidirectional moisture conducting function fabric described in claim 1, it is characterised in that:The one-way wet-guide ability R >
200%.