CN106745036B - 具有微孔-介孔的多级孔ssz-13分子筛及其合成方法和应用 - Google Patents
具有微孔-介孔的多级孔ssz-13分子筛及其合成方法和应用 Download PDFInfo
- Publication number
- CN106745036B CN106745036B CN201710163804.7A CN201710163804A CN106745036B CN 106745036 B CN106745036 B CN 106745036B CN 201710163804 A CN201710163804 A CN 201710163804A CN 106745036 B CN106745036 B CN 106745036B
- Authority
- CN
- China
- Prior art keywords
- ssz
- crystallization
- molecular sieve
- silicon source
- synthetic method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种具有微孔‑介孔的多级孔结构SSZ‑13分子筛及其合成方法和应用，合成方法为选用聚季铵盐作为晶化合成反应助剂，调配碱源、硅源、铝源、模板剂、聚季铵盐和水的摩尔配比，并采用分段进行动态/静态晶化的方式。具体合成步骤包括成胶与陈化、晶化、洗涤、脱模板剂并活化、离子交换和活化等步骤，可以得到微孔‑介孔有序分布的高结晶度多级孔SSZ‑13分子筛。得到的分子筛具有两种尺寸包括2～5nm和5～15nm范围的介孔孔径分布，微孔体积>0.20cm3/g，介孔体积>0.35cm3/g，比表面积>400m2/g，晶化产品的产率可达到85％以上。这种SSZ‑13分子筛除具有微孔沸石优点外，还具备介孔中大分子扩散等优点，该材料在石油化工、MTO反应、尾气净化及精细化工等领域具有广泛的应用前景。
Description
技术领域
本发明提供一种具有微孔-介孔的多级孔SSZ-13分子筛及其合成方法，具体涉及合成硅铝溶胶混合物中引入聚季铵盐离子作为晶化助剂，晶化反应中逐渐形成微孔-介孔的多级孔道结构的SSZ-13分子筛。
背景技术
传统的制备方法获得的分子筛粒径比较大，对于分子筛催化寿命有着严重的限制。多级孔道分子筛概念的引入缩短了分子扩散距离，使得反应产物比较容易从活性位扩散到外表面，抑制了结焦的形成，增加了催化剂的寿命。多级孔道分子筛合成已经得到了业界的广泛关注。
文献(Advanced Functional Materials,2009,19(1):164-172)中通过焙烧条件的改变，脱除Beta分子筛中的部分模板剂，然后在碱性碱性条件下脱硅，最终得到具有等级孔结构的Beta分子筛。脱铝、脱硅法虽然能在微孔分子筛中有效的引入中孔结构，但是硅或铝的脱除，容易导致结晶度的降低以及骨架结构的破坏。
文献(Chemistry-A European Journal,2011,17(51):14618-14627)将充满纳米晶体的溶液与十六烷基三甲基溴化铵(CTAB)模板剂混合，在乙醇/水溶液中水热合成介孔ZSM-5分子筛。然而该方法最终并没有合成结晶的分子筛，仅仅是沸石纳米晶体根据模板剂胶束进行的组装。
文献(ACS Catalysis.2013,3(2):192-195)使用季铵盐表面活性剂作为结构导向剂，在不同配比的条件下合成出纳米颗粒结构BEA、MTW和MRE分子筛，该分子筛同时具有微孔与介孔结构。
专利CN201410386943以不同碳链长度的八头Bola型季铵盐表面活性剂为模板剂，在碱性条件以水热法制备同时具有介孔和微孔结构的Beta多级孔沸石分子筛。八头季铵盐表面活性剂作为Beta分子筛的结构导向剂产生了微孔结构，模板剂的疏水长链尾基聚集产生胶束则使分子筛形成介孔结构，制备的多级孔分子筛具有介孔和晶态微孔结构。
专利CN201210287411以六铵基阳离子型季铵盐表面活性剂作为模板剂，在碱性条件下通过水热合成法制备含有介孔和Beta沸石微孔的多级孔沸石分子筛。六铵基阳离子型季铵盐表面活性剂作为Beta沸石结构导向剂产生了微孔，其憎水的长链烷基之间的聚集则形成了介孔，制备的多级孔沸石分子筛同时具有介孔和晶态的微孔。
上述这些专利描述了多级孔结构的Beta分子筛和ZSM-5分子筛合成方法，合成过程控制条件比较苛刻，并不能适用于8元环CHA型的小孔SSZ-13分子筛多孔级结构合成。
SSZ-13分子筛是美国化学家Zones于20世纪80年代通过水热法合成的，属于微孔中的小孔沸石。它具有良好的热稳定性，同时由于骨架中AlO4和SiO4四面体的存在，使其骨架具有阳离子交换性和酸性可调性，从而使SSZ-13具有了很好的催化性能，包括烃类化合物的催化裂化，加氢裂化，以及烯烃和芳烃构造反应。与常规SSZ-13微孔为稠环芳烃堵塞、外表面为积炭覆盖形成强烈对比，多级孔SSZ-13孔道得到充分利用，拥有更快的反应速率，反应产物比较容易从活性位扩散到外表面，抑制了结焦的形成，增加了催化剂的寿命。
发明内容
本发明的目的是提供一种微孔-介孔的多级孔结构SSZ-13分子筛，作为一种催化剂提高催化反应活性，大大提高了传质速率，显著抑制了催化剂的积炭失活，延长了催化剂的寿命。
本发明的目的是提供一种利用聚季铵盐作为晶化助剂的合成多级孔道SSZ-13分子筛的方法，这种孔分布结构的分子筛有利于MTO等反应。
本发明解决其技术问题所采用的技术方案是用碱源、硅源、有机结构导向剂、聚季铵盐和水为原料加热搅拌成溶胶，然后按照配比逐次搅拌中加入铝源，混合形成硅铝胶，室温陈化后，置于晶化釜中进行晶化反应，将产物过滤、脱模板剂、离子交换和活化得到多级孔SSZ-13分子筛催化剂。
本发明所述多级孔道SSZ-13分子筛的合成方法，其特征在于具体步骤如下：
1)按照反应原料配比称取一定量的聚季铵盐溶解在去离子水中形成溶液并搅拌分散，然后加入硅源、碱源和有机模板剂，在30～50℃条件下搅拌5～10小时，得到硅源混合溶液；
2)在30～80℃下，按照反应原料配比将铝源溶液滴加到1)中形成的硅源溶液中，剧烈搅拌30～120min后，室温静置陈化2～12小时得到硅铝溶胶。
3)将2)中得到的硅铝溶胶混合物置于水热合成釜中120～190℃分2段晶化，第二段温度比第一段高20℃，待48～168小时晶化完全后，离心分离出固体产物，再将固体产物用去离子水反复洗涤至中性，然后在100～130℃条件下干燥12～48小时，并在400～600℃焙烧2～10小时脱除有机模板剂，得到多级孔SSZ-13分子筛原粉；
4)将SSZ-13分子筛原粉与NH4 +离子溶液进行离子交换、洗涤、干燥后400～600℃焙烧2～10小时得到H型的多级孔SSZ-13分子筛催化剂。
本发明合成方法中所述的投料晶化的硅铝胶混合物中硅源以SiO2计，铝源以Al2O3计，有机模板剂以SDA计，聚季铵盐以PQA计，晶化反应原料摩尔配比为：Na2O：SiO2：Al2O3：SDA：PQA：H2O＝0.35～0.65：1：0.0025～0.01：0.05～0.5：0.01～0.05：10～50。
本发明所述聚季铵盐PQA，为聚合度10～100000的聚合物，所述聚合度指平均聚合度，即聚合物大分子链上所含重复单元数目的平均值。
其中，所述聚季铵盐-2为聚[双(2-氯乙基)醚-alt-1,3-双[3-(二甲氨基)丙基]脲]季铵化溶液，分子式为(C11H26N4O)n.(C4H8Cl2O)n，n为正整数；结构式为：
其中，所述聚季铵盐-6为二甲基二烯丙基氯化铵的共聚物，分子式为(C8H16ClN)n，n为正整数；结构式为：
其中，所述聚季铵盐-7为二甲基二丙烯基氯化铵-丙烯酰胺共聚物溶液，分子式为(C8H16ClN)n.(C3H5NO)m，n和m为正整数，结构式为：
其中，所述聚季铵盐-10为氯化-2-羟基-3-(三甲氨基)丙基聚环氧乙烷纤维素醚，结构式为：
其中，所述聚季铵盐-11为聚[(2-甲基丙烯酸二甲氨基乙基硫酸二乙酯-co(1-乙烯基-2-吡咯烷酮)]，结构式为：
其中，所述聚季铵盐-22为二甲基二烯丙基氯化铵-丙烯酸共聚物(C8H16ClN)n.(C3H5NO)m，n和m为正整数，结构式为：
其中，所述聚季铵盐-32为2-甲基丙烯酰氧乙基三甲基氯化铵-丙烯酰胺共聚物(C9H18ClNO2)n.(C3H5NO)m，n和m为正整数，结构式为：
其中，所述聚季铵盐-33为N,N,N-三甲基-2-(1-氧代-2-丙烯基氧基)乙基氯化铵-丙烯酰胺共聚物，(C8H16ClNO2)n.(C3H5NO)m，n和m为正整数，结构式为：
其中，所述聚季铵盐-44为N-乙烯吡咯烷酮和季铵化乙烯咪唑共聚物，(C6H9N2)x.(C6H9NO)x.(CH3O4S)x，x为正整数，结构式为：
本发明合成方法中所涉及到的硅源为白炭黑、活性二氧化硅、硅酸钠、硅酸乙酯或硅酸甲酯的一种；铝源为异丙醇铝、偏铝酸钠、硝酸铝、硫酸铝、氯化铝、氢氧化铝或拟薄水铝石的一种。
本发明合成方法中所涉及到的有机模板剂是N,N,N-三甲基-1-金刚烷氢氧化铵(TMADa+)、苄基三甲基氢氧化铵(BTMA+)中任意一种或两种。
本发明合成方法中所述晶化方式是动态晶化或静态晶化，优选动态晶化方式。
本发明中涉及到SSZ-13分子筛进行离子交换的铵离子的盐溶液为硝酸铵、硫酸铵、氯化铵或碳酸氢铵的水溶液，铵离子的浓度为0.5～1.5mol/L。
本发明得到的多级孔道的SSZ-13分子筛，特征在于其孔道在<2nm、2～5nm和5～15nm范围均有孔径分布，微孔体积>0.20cm3/g，介孔体积>0.35cm3/g，比表面积>400m2/g。
本发明提供上述SSZ-13分子筛在甲醇制烯烃或尾气催化还原反应中的应用。
与现有技术相比，本发明具有以下优点和有益效果：
本发明利用聚季铵盐为晶化合成的助剂，原料廉价易得，而降低昂贵的N,N,N-三甲基-1-金刚烷氢氧化铵用量，大大降低了SSZ-13分子筛的生产成本，为大规模工业应用奠定了基础。
本发明制备的SSZ-13分子筛同时具有微孔和介孔，避免了单一孔道的缺陷，在大分子吸附和催化方面有着广阔的应用前景。
本发明得到的多级孔SSZ-13分子筛除具有微孔沸石优点外，还具备介孔材料孔径大有利于大分子扩散等优点。利用聚季铵盐作为合成的助剂得到多级孔道SSZ-13分子筛，相对于其它软模板合成多级孔道沸石具有廉价、易得的特点，该材料在石油化工、煤化工及精细化工等领域具有广泛的应用前景，特别是在甲醇制烯烃(MTO)和尾气催化还原反应(SCR)等领域有良好的应用，不仅提高催化反应活性而且延长的催化剂的使用寿命。
附图说明
下面结合附图及实施例对本发明作进一步描述：
图1是本发明实施例1中样品1的多级孔SSZ-13分子筛SEM图；
图2是本发明的实施例1中样品2的多级孔SSZ-13分子筛SEM图；
图3是本发明的实施例1中样品1的多级孔SSZ-13分子筛XRD图。
具体实施方式
通过实施例和对比例子进一步说明本发明实施方式和所产生的效果，但本发明的保护范围并不限于实施例所列的内容。
实施例1
按照表1中所列，反应原料配比称取定量的聚季铵盐溶解在去离子水中形成溶液并搅拌分散，然后加入硅源、碱源，在40℃条件下搅拌6小时，得到硅源混合溶液；在60℃下，按照反应原料配比将铝源溶液滴加到硅源混合溶液中，剧烈搅拌90min后，静置陈化12小时得到混合物凝胶。将混合物凝胶置于水热合成釜中120～190℃分2段晶化，第二段温度比第一段高20℃，待晶化完全后，离心分离出固体产物，再将固体产物用去离子水反复洗涤至中性，然后在120℃条件下干燥24小时，并在550℃焙烧4小时脱除有机模板剂，得到多级孔SSZ-13分子筛原粉；将SSZ-13分子筛原粉与1.0mol/L的NH4 +离子溶液按照固液比＝1:10的比例在90℃进行离子交换2小时、洗涤、120℃干燥24小时后550℃焙烧2小时得到H型的多级孔SSZ-13分子筛催化剂。所合成SSZ-13分子筛原粉样品1～20#的初始凝胶中的原料类型及配比、晶化温度、晶化时间、铵离子盐种类以及所得产物的产率和硅铝比分别如表1和表2所示。该SSZ-13分子筛产品具有微孔-介孔的多级孔结构形貌，介孔孔道尺寸范围2～15nm。
表1
表2
实施例2
对实施例1中所合成的SSZ-13分子筛样品1～20采用Micromeritics ASAP 2020型氮气物理吸附仪进行表征分析。分析之前样品的预处理方法如下：在常温下将分子筛样品抽真空处理，当达到真空条件后，在130℃处理2h；之后在350℃处理2h。氮气物理吸附结果表明，样品1～20微孔孔径为0.3～0.5nm，均含有介孔结构，介孔孔径分布、介孔平均孔径、介孔体积和比表面积如表3所示。
表3
实施例3
对实施例1中所制备的样品1～20进行XRD表征以确认为SSZ-13分子筛。所采用仪器为PANalytical X’Pert型X射线衍射仪，铜靶，Kα辐射源仪器工作电压为40kv，工作电流为40mA。所得到的样品1～20的XRD谱图与标准SSZ-13分子筛的特征谱图一致。典型的XRD图谱(如图3)以样品1为代表，2θ在5°～50°主要衍射峰位置和峰强度如表4所示。其他样品数据结果与样品1相比，衍射峰位置和形状相同，依合成条件的变化相对峰强度在±5％范围内波动，表明合成产物具有SSZ-13分子筛结构的特征。
表4
| 特征峰序号 | 2Theta(°) | 相对强度％ |
| 1<sup>#</sup> | 9.4 | 100.0％ |
| 2<sup>#</sup> | 12.78 | 16.6％ |
| 3<sup>#</sup> | 15.88 | 9.0％ |
| 4<sup>#</sup> | 17.52 | 13.9％ |
| 5<sup>#</sup> | 20.44 | 62.6％ |
| 6<sup>#</sup> | 22.22 | 5.3％ |
| 7<sup>#</sup> | 22.84 | 27.1％ |
| 8<sup>#</sup> | 24.6 | 23.2％ |
| 9<sup>#</sup> | 25.72 | 5.7％ |
| 10<sup>#</sup> | 27.44 | 4.1％ |
| 11<sup>#</sup> | 27.8 | 8.1％ |
| 12<sup>#</sup> | 30.38 | 43.1％ |
| 13<sup>#</sup> | 30.7 | 36.9％ |
| 14<sup>#</sup> | 35.58 | 14.7％ |
| 15<sup>#</sup> | 43.06 | 6.0％ |
| 16<sup>#</sup> | 43.66 | 3.4％ |
实施例4
催化剂的评价：将实施例1中所得到的1～8催化剂原粉进行压片，破碎至20～40目。称取0.3g样品装入固定床反应器，进行MTO评价。在500℃下通氮气活化1.5小时，然后降温至450℃。甲醇由氮气携带，氮气流速为15ml/min，甲醇重量空速4.0h-1。所得到的产物由在线气相色谱(Agilent7890)进行分析，结果见表5。从其中可以看出，8个样品均具有极高催化寿命，同时乙烯和丙烯的总收率超过了83.0％。
表5
t50：转化率从100％降低到50％所经历的时间；t98：转化率从100％降低到98％所经历的时间。
由表5可以看出，本发明提供的方法制备的多级孔SSZ-13分子筛催化剂在MTO反应中，具有更高的低碳烯烃(C2 ＝+C3 ＝)选择性可达84.6％以上，且转化率下降到50％前的转化寿命在13小时以上，说明该多级孔SSZ-13分子筛催化剂具有MTO反应良好的寿命。
所述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (5)
1.一种具有微孔-介孔多级孔道结构的SSZ-13分子筛的合成方法，其特征在于包括如下步骤：
1)按照反应原料配比称取一定量的聚季铵盐溶解在水中形成溶液并搅拌分散，然后加入硅源、碱源和有机模板剂，在30～50℃条件下搅拌5～10小时，得到硅源混合溶液；
2)在30～80℃下，按照反应原料配比将铝源溶液滴加到1)中形成的硅源溶液中，剧烈搅拌30～120min后，室温静置陈化2～12小时得到硅铝溶胶；
3)将2)中得到的硅铝溶胶置于水热合成釜中120～190℃分2段晶化，第二段温度比第一段高20℃，待48～168小时晶化完全后，离心分离出固体产物，再将固体产物用去离子水反复洗涤至中性，然后在100～130℃条件下干燥12～48小时，并在400～600℃焙烧2～10小时脱除有机模板剂，得到多级孔SSZ-13分子筛原粉；
4)将SSZ-13分子筛原粉与NH4 +离子溶液进行离子交换、洗涤、干燥后400～600℃焙烧2～10小时得到H型的多级孔SSZ-13分子筛催化剂；
其中，投料晶化的硅铝溶胶中硅源以SiO2计，铝源以Al2O3计，有机模板剂以SDA计，聚季铵盐以PQA计，晶化反应原料摩尔配比为：Na2O：SiO2：Al2O3：SDA：PQA：H2O＝0.35～0.65：1：0.0025～0.01：0.05～0.5：0.01～0.05：10～50；
所述聚季铵盐包括聚季铵[双(2-氯乙基)醚-1,3-双[3-(二甲氨基)丙基]脲]聚合物、聚二烯丙基二甲基氯化铵、二甲基二烯丙基氯化铵-丙烯酰胺共聚物、氯化-2-羟基-3-(三甲氨基)丙基聚环氧乙烷纤维素醚、二甲基二烯丙基氯化铵-丙烯酸共聚物、2-甲基丙烯酰氧乙基三甲基氯化铵-丙烯酰胺共聚物、N,N,N-三甲基-2-[(2-甲基-1-氧-2-丙烯基)氧基]乙胺盐酸盐的均聚物、二甲基二烯丙基氯化铵-丙烯酰胺-丙烯酸共聚物、N-乙烯吡咯烷酮和季铵化乙烯咪唑共聚物中一种或多种；
步骤1)中有机模板剂是N,N,N-三甲基-1-金刚烷氢氧化铵、苄基三甲基氢氧化铵中任意一种或两种。
2.根据权利要求1所述的合成方法，其特征在于：硅源为白炭黑、活性二氧化硅、硅酸钠、硅酸乙酯或硅酸甲酯的一种。
3.根据权利要求1所述的合成方法，其特征在于：铝源为异丙醇铝、偏铝酸钠、硝酸铝、硫酸铝、氯化铝、氢氧化铝或拟薄水铝石的一种。
4.根据权利要求1所述的合成方法，其特征在于：步骤1)中晶化方式是动态晶化或静态晶化。
5.根据权利要求1所述的合成方法，其特征在于：步骤4)中所述NH4 +离子溶液为铵离子的盐溶液，选自硝酸铵、硫酸铵、氯化铵或碳酸氢铵的水溶液，铵离子的浓度为0.5～1.5mol/L。