CN106739427A - 一种用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的工艺 - Google Patents

一种用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的工艺 Download PDF

Info

Publication number
CN106739427A
CN106739427A CN201611096498.1A CN201611096498A CN106739427A CN 106739427 A CN106739427 A CN 106739427A CN 201611096498 A CN201611096498 A CN 201611096498A CN 106739427 A CN106739427 A CN 106739427A
Authority
CN
China
Prior art keywords
silver
etchant solution
colored version
version
colored
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611096498.1A
Other languages
English (en)
Inventor
曹娅
李子木
唐娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU BANKNOTE PRINTING Co Ltd
Original Assignee
CHENGDU BANKNOTE PRINTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU BANKNOTE PRINTING Co Ltd filed Critical CHENGDU BANKNOTE PRINTING Co Ltd
Priority to CN201611096498.1A priority Critical patent/CN106739427A/zh
Publication of CN106739427A publication Critical patent/CN106739427A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的工艺，所述腐蚀溶液为水溶液，其主要成分及含量为：1mol/L～2mol/L的Fe(NO3)2；0.1mol/L～0.5mol/L的HNO3；所述腐蚀溶液的婆美度为28～32be，温度为30～40℃，所述的腐蚀溶液蚀刻银版的工艺是：a）银版版基的表面处理；b）在银版表面上涂布感光胶；c）采用紫外光将软片图纹晒制到银版上；d）显影；e）烘烤；f）配制所述腐蚀溶液；g）采用无粉腐蚀机对银版进行腐蚀；h）脱胶。本发明通过配制的腐蚀溶液对银版或银制品进行蚀刻，其蚀刻的图文精细、蚀刻速度快、图文的边缘效果好，防伪性能佳等特点，适宜制作各类尺寸规格的银版画或具有精细图文的银制品，有效克服了激光雕刻、机械冲压存在的弊端，能满足银版画的收藏、银制品的多元需求。

Description

一种用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的 工艺
技术领域
本发明涉及一种用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的工艺。
背景技术
现有银版的制作主要有激光雕刻、机械冲压及腐蚀等方式，其中，采用激光雕刻或机械冲压的制作方式存在成型的图文不够精细，图文的边缘效果不好，而且制作速度慢、无法适用于制作各类尺寸规格的银版画或图文的银制品等弊端，而采用腐蚀的制作方式，其蚀刻银版的腐蚀溶液在对银版进行腐蚀后，易在银版表面形成氧化膜，造成银版表面钝化。
发明内容
本发明的目的在于：针对上述存在的问题，提供一种能够使银版蚀刻的图文精细、蚀刻速度快、图文边缘效果好的用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的工艺。
本发明的技术方案是这样实现的：一种用于银制品的腐蚀溶液，其特征在于：所述腐蚀溶液为水溶液，其主要成分及含量为：1mol/L～2mol/L的Fe(NO3)2；0.1mol/L～0.5mol/L的HNO3；所述腐蚀溶液的婆美度为28～32be，温度为30～40℃。
本发明采用的腐蚀溶液区别于常用腐蚀溶液FeCl3，因为FeCl3与Ag发生反应生成AgCl沉淀附着在图纹侧壁，造成腐蚀停滞，因此FeCl3的腐蚀溶液无法腐蚀具有精细图纹的银版或银制品。而采用Fe(NO3) 2的腐蚀溶液腐蚀银版或银制品时，反应生成的AgNO3为可溶物，不会阻止腐蚀反应进一步进行，因此采用所配制的Fe(NO3) 2腐蚀溶液具有腐蚀速度快、腐蚀还原性好等特点。
一种采用上述腐蚀溶液蚀刻银版的工艺，其特征在于： 包括以下步骤：
a）银版版基的表面处理：采用一定比例的碳酸钙去掉版面油污，再用洗洁净，并用晶相砂纸边清洗边打磨；
b）在银版表面上涂布感光胶：在涂布机内将感光胶均匀地涂布于银版版基上，采用转速100～150转/分、温度40～45℃、时间15～20min，使得感光胶均匀稳固地附着于银版上；
c）采用紫外光将软片图纹晒制到银版上：将软片与银版基平稳地放置于晒版机内，抽气并采用紫外光曝光，曝光5～8min，使得软片的图纹完全复制还原到银版上；
d）显影：采用60～70℃温水进行显影，确保所有未感光的胶全部脱掉；
e）烘烤：在190～210℃的烤版机内烘烤10～15min；
f）配制所述腐蚀溶液：按照上述银制品的腐蚀溶液进行配制，将配置好的腐蚀溶液搅拌30～60min；
g）采用无粉腐蚀机对银版进行腐蚀：将银版固定于无粉腐蚀机内，采用400～450转/分的转速腐蚀5～10min；
h）脱胶：腐蚀完成后，将银版表面的感光胶去掉。
本发明采用上述腐蚀溶液蚀刻银版的工艺，能将软片图纹准确地反应在银版上，并能调整腐蚀时间、腐蚀速度等获得不同需求的图纹深度，图纹腐蚀还原效果好。
本发明利用Fe(NO3)2与Ag置换反应以及HNO3与Ag反应的特点，通过配制的腐蚀溶液对银版或银制品进行蚀刻，其蚀刻的图文精细、蚀刻速度快、图文的边缘效果好，适宜制作各类尺寸规格的银版画或具有精细图文的银制品，有效克服了激光雕刻、机械冲压存在的弊端。
具体实施方式
下面对本发明作详细的说明。
为了使本发明的目的、技术方案及优点更加清楚明白，以下对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例1：一种用于银制品的腐蚀溶液，所述腐蚀溶液为水溶液，其主要成分及含量为：1mol/L～2mol/L的Fe(NO3)2；0.1mol/L～0.5mol/L的HNO3；所述腐蚀溶液的婆美度为28～32be，温度为30～40℃。
一种采用上述腐蚀溶液蚀刻银版的工艺， 包括以下步骤：
a）银版版基的表面处理：采用一定比例的碳酸钙去掉版面油污，再用洗洁净，并用晶相砂纸边清洗边打磨；
b）在银版表面上涂布感光胶：在涂布机内将感光胶均匀地涂布于银版版基上，采用转速100～150转/分、温度40～45℃、时间15～20min，使得感光胶均匀稳固地附着于银版上；
c）采用紫外光将软片图纹晒制到银版上：将软片与银版基平稳地放置于晒版机内，抽气并采用紫外光曝光，曝光5～8min，使得软片的图纹完全复制还原到银版上；
d）显影：采用60～70℃温水进行显影，确保所有未感光的胶全部脱掉；
e）烘烤：在190～210℃的烤版机内烘烤10～15min；
f）配制所述腐蚀溶液：按照上述银制品的腐蚀溶液进行配制，将配置好的腐蚀溶液搅拌30～60min；
g）采用无粉腐蚀机对银版进行腐蚀：将银版固定于无粉腐蚀机内，采用400～450转/分的转速腐蚀5～10min；
h）脱胶：腐蚀完成后，将银版表面的感光胶去掉。
本发明利用Fe(NO3)2与Ag置换反应以及HNO3与Ag反应的特点：
Fe(NO3)2+2Ag=2AgNO3+Fe
2HNO3+2Ag=2AgNO3+H2↑。
通过配制的腐蚀溶液对银版进行蚀刻，其蚀刻的图文精细、蚀刻速度快、图文的边缘效果好，防伪性能佳等特点，适宜制作各类尺寸规格的银版画或具有精细图文的银制品，有效克服了激光雕刻、机械冲压存在的弊端，能满足银版画的收藏、银制品的多元需求。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在发明的保护范围之内。

Claims (2)

1.一种用于银制品的腐蚀溶液，其特征在于：所述腐蚀溶液为水溶液，其主要成分及含量为：1mol/L～2mol/L的Fe(NO3)2；0.1mol/L～0.5mol/L的HNO3；所述腐蚀溶液的婆美度为28～32be，温度为30～40℃。
2.一种采用上述腐蚀溶液蚀刻银版的工艺，其特征在于： 包括以下步骤：
a）银版版基的表面处理：采用一定比例的碳酸钙去掉版面油污，再用洗洁净，并用晶相砂纸边清洗边打磨；
b）在银版表面上涂布感光胶：在涂布机内将感光胶均匀地涂布于银版版基上，采用转速100～150转/分、温度40～45℃、时间15～20min，使得感光胶均匀稳固地附着于银版上；
c）采用紫外光将软片图纹晒制到银版上：将软片与银版基平稳地放置于晒版机内，抽气并采用紫外光曝光，曝光5～8min，使得软片的图纹完全复制还原到银版上；
d）显影：采用60～70℃温水进行显影，确保所有未感光的胶全部脱掉；
e）烘烤：在190～210℃的烤版机内烘烤10～15min；
f）配制所述腐蚀溶液：按照上述银制品的腐蚀溶液进行配制，将配置好的腐蚀溶液搅拌30～60min；
g）采用无粉腐蚀机对银版进行腐蚀：将银版固定于无粉腐蚀机内，采用400～450转/分的转速腐蚀5～10min；
h）脱胶：腐蚀完成后，将银版表面的感光胶去掉。
CN201611096498.1A 2016-12-02 2016-12-02 一种用于银制品的腐蚀溶液及采用该腐蚀溶液蚀刻银版的工艺 Pending CN106739427A (zh)