CN106544084A - A kind of metal cutting technology lubricant compositions - Google Patents
A kind of metal cutting technology lubricant compositions Download PDFInfo
- Publication number
- CN106544084A CN106544084A CN201610962472.4A CN201610962472A CN106544084A CN 106544084 A CN106544084 A CN 106544084A CN 201610962472 A CN201610962472 A CN 201610962472A CN 106544084 A CN106544084 A CN 106544084A
- Authority
- CN
- China
- Prior art keywords
- lubricant compositions
- metal cutting
- cutting technology
- technology lubricant
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of metal cutting technology lubricant compositions, using oil based on HMI150, coordinate various compound additives.Including:Antioxidant, metal deactivator, oiliness improver, friction improver, antiwear additive, anti-foaming agent, anti emulsifier, antirust agent, urge cryogen, dispersant, oxidation and corrosion inhibitor etc..The composition of the present invention has good cooling, lubricity, diffusivity, cleaning, anti-corrosive properties, a low volatility, and thermal capacity is big, is conducive to cutter protection, and good high, anticorrosive to the intermiscibility that paints, surface smoothness, usage cycles are long.
Description
Technical field
A kind of metal cutting technology lubricant compositions of the present invention belong to metal working lubricant field.
Background technology
The resistance of deformation of metal is little, and ingot casting is not required to heating and can use the techniques such as rolling, extruding to make sheet material, band, pipe
Material, bar and wire rod, and it is not required to intermediate annealing process.The tensile strength of metal is 3~7kgf/mm2, than other gold of great majority
Category alloy is much lower.
Lead alloy surface produces oxide, sulfide or other compound salt overlay films in corrosion process, has prevention oxygen
The effects such as change, sulfuration, dissolving or volatilization.There is good corrosion resistance in air, sulfuric acid, fresh water and seawater.Metal such as contains
Have and be not solid-solution in lead or form the impurity such as the bismuth of the second phase, magnesium, zinc, then corrosion resistance can be reduced;Add tellurium, selenium eliminate impurity bismuth
To corrosion proof adverse effect.Antimony and tellurium are added in the metal of bismuth-containing, can crystal grain thinning tissue, increase intensity, suppress bismuth
Illeffects, improve corrosion resistance.
Metal fusing point low (below 327 DEG C), good fluidity, solidification shrinkage rate are little, and melting loss is few, composition transfer during remelting
It is little, complex-shaped, clear-cut device is may be cast as, is widely used in casting font and is made model etc..Pewter is used
Existing more than the 500 years history in printing industry.Due to the shearing of metal, creep strength it is low, in certain load and rolling
Under shear effect, metal is easily deformable and thinning becomes foil-like;And the self-lubricity of metal, running-in ability and damping property are good, make an uproar
Sound is little, thus is good bearing metal.It is suitable to make the heavy-duty machine bearing that top load, high rotating speed, temperature resistance rise.Metal has
There is the characteristic for being difficult to be penetrated by X and gamma-rays, the protective materials of radiation work can be made.
The processing method of metal is various, but machining is most common, most widely used one kind all the time.Metal cutting is
Important mechanical processing toolses, as used by which, cutting element type can be divided into two big class;One class is that the cutting carried out with cutter adds
Work;Another kind of is to carry out grinding with abrasive material.Metal cutting and grinding are a kind of using the cutting element (knife with cutting edge
Tool or emery wheel) excess metal of workpiece is cut on stock-removing machine, so as to be that workpiece obtains regular geometry, size is smart
The processing method of degree and surface quality.Metal cutting process is commonly divided into two stages, that is, the generation cut and in time removing.
The two stages have the friction between cutter and workpiece, cutter and chip, and the energy conversion that this friction is consumed is heat, it
Working (machining) efficiency and workpiece quality can be affected.As serious friction produces substantial amounts of heat, make cutter and workpiece overheated, reduce cutter
In the life-span, affect Product Precision.In order to cool down and lubricate cutter and workpiece, it is necessary to produced with taking away cutting in time using cutting lubricant
Raw heat, reduces the temperature of cutter and workpiece and plays lubrication;Workpiece surface finish is improved, and extends making for cutter
Use the life-span.
Cutting oil is different from plain oil applying working condition, plain oil be in the constant rubbing surface that moves repeatedly it
Between, despite pressure it is very big, but easily form lubricating oil film.And cut the fresh table that oil is then that constantly contact cutting is formed
Face, machined surface recur elastic deformation, thus the pressure born between cutter and machined surface is bigger than general lubricating status
Much.It is required that there is lubricant good cooling, lubricity, bearing capacity, antifriction vibration damping, cleaning and chip removal to act on, antirust,
It is antioxygen anticorrosion, defoaming, anti-corrupt, low smell, nonirritant.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of with good cooling, lubricity, diffusivity, cleaning
Property, anti-corrosive properties, low volatility, thermal capacity is big, is conducive to cutter protection, it is good it is high to the intermiscibility that paints, surface smoothness,
It is anticorrosive, the metal cutting technology lubricant compositions of usage cycles length.
The present invention solves above-mentioned technical problem by following technical solution:
A kind of metal cutting technology lubricant compositions, using oil based on HMI150, coordinate various being combined to add
Plus agent, its each mass percent into being grouped into:
Component | Mass percentage content |
Base oil | Surplus |
Antioxidant | 0.05%~0.2% |
Metal deactivator | 0.03%~0.2% |
Oiliness improver | 3%~8% |
Friction improver | 1%~2% |
Antiwear additive | 3%~5% |
Anti-foaming agent | 10ppm~30ppm |
Anti emulsifier | 0.3%~1% |
Antirust agent | 0.08%~0.3% |
Urge cryogen | 1%~2% |
Dispersant | 1%~4% |
Oxidation and corrosion inhibitor | 1%~2% |
The mass percent summation of above each component is 100%.
Antioxidant is that the N- PAs of the phenolic ester type antioxidant T508 and 50% of mass ratio 50% are combined.
Metal deactivator is benzotriazole derivative T551.Oiliness improver is rice bran oil.
Friction improver is benzotriazole aliphatic acid amine salt T406.Antiwear additive is chlorinated paraffin T301.
Anti-foaming agent is ethyl silicon oil.Anti emulsifier is polyether high molecular compound DL32.
Antirust agent is that the lanolin magnesium soap of the alkenyl succinic acid T746 and 50% of mass ratio 50% is combined.
Cryogen is urged to be petroleum sodium sulfonate T702.Dispersant is diene base succimide T152.
Oxidation and corrosion inhibitor is dialkyl dithio amino formate.
The remarkable advantage of the present invention:The present composition has good cooling, lubricity, diffusivity, cleaning, anti-
Corruption, low volatility, thermal capacity are big, are conducive to cutter protection, good, anti-corruption high to the intermiscibility that paints, surface smoothness
Erosion, usage cycles are long.
Specific embodiment
Embodiment 1:
Following each component is pressed the mediation of row mass percent to form:
Component | Mass percentage content |
HMI150 | Surplus |
The phenolic ester type antioxidant (T508) of mass ratio 50% is combined with 50% N- PAs | 0.05% |
Benzotriazole derivative (T551) | 0.03% |
Rice bran oil | 3% |
Benzotriazole aliphatic acid amine salt (T406) | 1% |
Chlorinated paraffin (T301) | 3% |
Ethyl silicon oil | 10ppm |
Polyether high molecular compound (DL32) | 0.3% |
The alkenyl succinic acid (T746) of mass ratio 50% is combined with 50% lanolin magnesium soap | 0.08% |
Petroleum sodium sulfonate (T702) | 1% |
Diene base succimide (T152) | 1% |
Dialkyl dithio amino formate | 1% |
Above each component mass percentage content summation is 100%.
Embodiment 2:
Following each component is pressed the mediation of row mass percent to form:
Component | Mass percentage content |
HMI150 | Surplus |
The phenolic ester type antioxidant (T508) of mass ratio 50% is combined with 50% N- PAs | 0.1% |
Benzotriazole derivative (T551) | 0.1% |
Rice bran oil | 6% |
Benzotriazole aliphatic acid amine salt (T406) | 1.5% |
Chlorinated paraffin (T301) | 4% |
Ethyl silicon oil | 20ppm |
Polyether high molecular compound (DL32) | 0.6% |
The alkenyl succinic acid (T746) of mass ratio 50% is combined with 50% lanolin magnesium soap | 0.2% |
Petroleum sodium sulfonate (T702) | 1.5% |
Diene base succimide (T152) | 2% |
Dialkyl dithio amino formate | 1.5% |
Above each component mass percentage content summation is 100%.
Embodiment 3:
Following each component is pressed the mediation of row mass percent to form:
Component | Mass percentage content |
HMI150 | Surplus |
The phenolic ester type antioxidant (T508) of mass ratio 50% is combined with 50% N- PAs | 0.2% |
Benzotriazole derivative (T551) | 0.2% |
Rice bran oil | 8% |
Benzotriazole aliphatic acid amine salt (T406) | 2% |
Chlorinated paraffin (T301) | 5% |
Ethyl silicon oil | 30ppm |
Polyether high molecular compound (DL32) | 1% |
The alkenyl succinic acid (T746) of mass ratio 50% is combined with 50% lanolin magnesium soap | 0.3% |
Petroleum sodium sulfonate (T702) | 2% |
Diene base succimide (T152) | 4% |
Dialkyl dithio amino formate | 2% |
Above each component mass percentage content summation is 100%.
The typical physiochemical techniques index of 1 product of embodiment:
The typical physiochemical techniques index of 2 product of embodiment:
The typical physiochemical techniques index of 3 product of embodiment:
Claims (10)
1. a kind of metal cutting technology lubricant compositions, it is characterised in that:Using oil based on HMI150, coordinate many
Kind of compound additive, its each mass percent into being grouped into:
The mass percent summation of above each component is 100%.
2. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that antioxidant is
The N- PAs of the phenolic ester type antioxidant T508 and 50% of mass ratio 50% are combined.
3. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that metal deactivating
Agent is benzotriazole derivative T551.
4. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that oiliness improver is
Rice bran oil;Friction improver is benzotriazole aliphatic acid amine salt T406.
5. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that antiwear additive is
Chlorinated paraffin T301.
6. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that anti-foaming agent is
Ethyl silicon oil;Anti emulsifier is polyether high molecular compound DL32.
7. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that antirust agent is
The lanolin magnesium soap of the alkenyl succinic acid T746 and 50% of mass ratio 50% is combined.
8. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that urge the cryogen to be
Petroleum sodium sulfonate T702.
9. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that dispersant is
Diene base succimide T152.
10. a kind of metal cutting technology lubricant compositions as claimed in claim 1, it is characterised in that the anti-corruption of antioxygen
Agent is dialkyl dithio amino formate.