CN106318045A - Antibacterial paint for table lamp and preparation method of paint - Google Patents
Antibacterial paint for table lamp and preparation method of paint Download PDFInfo
- Publication number
- CN106318045A CN106318045A CN201610662528.4A CN201610662528A CN106318045A CN 106318045 A CN106318045 A CN 106318045A CN 201610662528 A CN201610662528 A CN 201610662528A CN 106318045 A CN106318045 A CN 106318045A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- antibacterial
- prepared
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses antibacterial paint for a table lamp. The paint is prepared from polypropylene resin, vinyl acetate-acrylic emulsion, polymethyl methacrylate, polyurethane resin, terephthalic acid, bamboo charcoal powder, diethylene glycol, propylene glycol monomethyl ether, an appropriate amount of water, a catalyst, an antibacterial agent, nanometer titania, dimethyl carbonate and rosin-modified resin; a preparation method of the paint sequentially comprises the following steps that 1, primarily mixed liquid is prepared; 2, intermediate liquid is prepared; 3, mixed liquid is prepared; 4, the mixed liquid obtained in the third step is put into a ball mill to be milled, sieving is conducted, and the finished product is obtained. The preparation method is scientific and reasonable, by adopting organic polymer materials with a good comprehensive property and conducting optimal combination, the antibacterial property of the composition is improved, an the paint is low in cost, short in production cycle and suitable for industrial batched production.
Description
Technical field
The invention belongs to coating industry technical field, particularly relate to a kind of desk lamp antibiotic paint and preparation method thereof.
Background technology
Coating, at the entitled paint of Chinese tradition, refer to coat body surface can form thin film under certain conditions and
Play protection, a class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Because of early stage
Coating is mostly with vegetable oil as primary raw material, therefore also referred to as paint.Synthetic resin instead of vegetable oil now, therefore is referred to as being coated with
Material.Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.Current according to the modern times
The classification of chemical products, coating belongs to fine chemical product.Modern coating the most progressively becomes a polyfunctional engineering of class
Material, is an important industry in chemical industry.At present, the coating industry of China is the most ripe, and market is close to saturated, in addition
Green economy globalization overall situation under, people become more concerned with economy the most flourishing after, environment is by great destruction.Along with
The environmental protection such as newly " environmental law " promulgates, country " environmental protection, beautiful China " advocate the most no longer to stay on slogan, but real
Execute execution, implement to promote energetically the development of green science and technology industry.
At present, the covering with paint of household electrical appliance has had bigger change, and traditional thermohardening lacquer is by the water of environmental protection
Property coating etc. substitute, but different electrical equipment has different requirements due to the difference of the aspects such as function to coating, more environmentally friendly, more individual
Property has become as the pursuit direction of household electrical appliances coating.Before the market demand huge in the face of household electrical appliances coating and ever-increasing application
Scape, strengthens research and development capabilities, and updates and improving product performance, accelerates product quality upgrading, develops technically, cost
Above, the household electrical appliances coating more showing powerful competitive advantage in performance has the meaning of reality and the wide market space.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of desk lamp antibiotic paint and system thereof
Preparation Method, this coating products excellent performance, there are good anti-microbial property, and energy-conserving and environment-protective, possess preferable economic benefit and
Social benefit.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of desk lamp antibiotic paint, is prepared by the raw materials in: acrylic resin 35~45 parts, acrylate and vinyl acetate emulsion 10
~15 parts, polymethyl methacrylate 2~5 parts, polyurethane resin 5~12 parts, p-phthalic acid 8~15 parts, bamboo charcoal powder 2~6
Part, diethylene glycol 1~3 parts, propylene glycol monomethyl ether 6~12 parts, water is appropriate, catalyst 1.5~3 parts, antibacterial 1.5~2.5 parts, receive
Rice titanium dioxide 1~5 parts, dimethyl carbonate 5~10 parts, modified rosin resin 5~12 parts;
Its preparation method in turn includes the following steps:
(1) p-phthalic acid, bamboo charcoal powder, diethylene glycol, propylene glycol monomethyl ether, nano titanium oxide and suitable quantity of water are joined
In reaction vessel, it is heated to 50~65 DEG C, stirs 20~30 minutes under 900~1200 revs/min, obtain the most mixed after mix homogeneously
Liquid;
(2) acrylic resin, acrylate and vinyl acetate emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate are mixed
Join in the first mixed liquid that step (1) obtains, be heated to 65~80 DEG C, continue stirring 30~40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and Abietyl modified
Resin, mix and blend 50~80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Preferably, described catalyst is sulfonic acid zinc.
Preferably, described antibacterial is lithium carbonate.
The beneficial effects of the present invention is:
Preparation method of the present invention is scientific and reasonable, by using combination property preferably high-molecular organic material and being optimized
Combination, improves the anti-microbial property of compositions, and the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good,
The indexs such as hot strength are superior to common coating, and can meet coated-body the most comprehensively uses requirement;Cost of the present invention is relatively low,
Achieving making full use of of resource and the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production,
Possess preferable economic benefit and social benefit.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of desk lamp antibiotic paint, is prepared by the raw materials in: acrylic resin 35 parts, acrylate and vinyl acetate emulsion 10 parts,
Polymethyl methacrylate 2 parts, polyurethane resin 5 parts, p-phthalic acid 8 parts, bamboo charcoal powder 2 parts, diethylene glycol 1 part, propylene glycol
Methyl ether 6 parts, water are appropriate, catalyst 1.5 parts, antibacterial 1.5 parts, nano titanium oxide 1 part, dimethyl carbonate 5 parts, Abietyl modified
Resin 5 parts;
Its preparation method in turn includes the following steps:
(1) p-phthalic acid, bamboo charcoal powder, diethylene glycol, propylene glycol monomethyl ether, nano titanium oxide and suitable quantity of water are joined
In reaction vessel, it is heated to 50~65 DEG C, stirs 20 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) acrylic resin, acrylate and vinyl acetate emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate are mixed
Join in the first mixed liquid that step (1) obtains, be heated to 65~80 DEG C, continue stirring 30 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and Abietyl modified
Resin, mix and blend 50 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Embodiment 2:
A kind of desk lamp antibiotic paint, is prepared by the raw materials in: acrylic resin 45 parts, acrylate and vinyl acetate emulsion 15 parts,
Polymethyl methacrylate 5 parts, polyurethane resin 12 parts, p-phthalic acid 15 parts, bamboo charcoal powder 6 parts, diethylene glycol 3 parts, the third two
Alcohol methyl ether 12 parts, water are appropriate, catalyst 3 parts, antibacterial 2.5 parts, nano titanium oxide 5 parts, dimethyl carbonate 10 parts, Colophonium change
Property resin 12 parts;
Its preparation method in turn includes the following steps:
(1) p-phthalic acid, bamboo charcoal powder, diethylene glycol, propylene glycol monomethyl ether, nano titanium oxide and suitable quantity of water are joined
In reaction vessel, it is heated to 50~65 DEG C, stirs 30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) acrylic resin, acrylate and vinyl acetate emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate are mixed
Join in the first mixed liquid that step (1) obtains, be heated to 65~80 DEG C, continue stirring 40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and Abietyl modified
Resin, mix and blend 80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
In the above embodiment of the present invention:
Described catalyst is sulfonic acid zinc;
Described antibacterial is lithium carbonate.
During the present invention implements, by using combination property preferably high-molecular organic material and carrying out optimum organization, improve
The anti-microbial property of compositions, the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good, hot strength etc.
Index is superior to common coating, and can meet coated-body the most comprehensively uses requirement;Cost of the present invention is relatively low, it is achieved that resource
With making full use of of the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although reference
The present invention has been described in detail by above-described embodiment, it will be appreciated by those skilled in the art that and still can carry out the present invention
Amendment or equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should be contained
In scope of the presently claimed invention.
Claims (3)
1. a desk lamp antibiotic paint, it is characterised in that be prepared by the raw materials in: acrylic resin 35~45 parts,
Acrylate and vinyl acetate emulsion 10~15 parts, polymethyl methacrylate 2~5 parts, polyurethane resin 5~12 parts, p-phthalic acid 8~15 parts,
Bamboo charcoal powder 2~6 parts, diethylene glycol 1~3 parts, propylene glycol monomethyl ether 6~12 parts, water are appropriate, catalyst 1.5~3 parts, antibacterial 1.5
~2.5 parts, nano titanium oxide 1~5 parts, dimethyl carbonate 5~10 parts, modified rosin resin 5~12 parts;
Its preparation method in turn includes the following steps:
(1) p-phthalic acid, bamboo charcoal powder, diethylene glycol, propylene glycol monomethyl ether, nano titanium oxide and suitable quantity of water are joined reaction
In container, it is heated to 50~65 DEG C, stirs 20~30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) mixing of acrylic resin, acrylate and vinyl acetate emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate is added
In the first mixed liquid that step (1) obtains, it is heated to 65~80 DEG C, continues stirring 30~40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and modified rosin resin,
Mix and blend 50~80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
A kind of desk lamp antibiotic paint the most according to claim 1, it is characterised in that described catalyst is sulfonic acid zinc.
A kind of desk lamp antibiotic paint the most according to claim 1, it is characterised in that described antibacterial is lithium carbonate.