CN106280880A - A kind of anti-scratch coating of electric iron and preparation method thereof - Google Patents
A kind of anti-scratch coating of electric iron and preparation method thereof Download PDFInfo
- Publication number
- CN106280880A CN106280880A CN201610663405.2A CN201610663405A CN106280880A CN 106280880 A CN106280880 A CN 106280880A CN 201610663405 A CN201610663405 A CN 201610663405A CN 106280880 A CN106280880 A CN 106280880A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- electric iron
- acrylate
- firming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-scratch coating of electric iron, be made up of following raw materials according: epoxy resin, acrylate and vinyl acetate emulsion, hydroxymethyl cellulose, polyacrylonitrile fibre, aliphatic dicarboxylic acid, montmorillonite powder, isopropanol, glycol ether, water are appropriate, catalyst, firming agent, calcium carbonate superfine powder, urethane acrylate, organic silica gel；Its preparation method in turn includes the following steps: the most mixed liquid of (1) preparation；(2) intermediate liquid is prepared；(3) mixed liquor is prepared；(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.Preparation method of the present invention is scientific and reasonable, by using combination property preferably high-molecular organic material and carrying out optimum organization, improves the anti-scratch performance of compositions, and its cost is relatively low, with short production cycle, is suitable to industrialized mass production.
Description
Technical field
The invention belongs to coating industry technical field, particularly relate to a kind of anti-scratch coating of electric iron and preparation method thereof.
Background technology
Coating, at the entitled paint of Chinese tradition, refer to coat body surface can form thin film under certain conditions and
Play protection, a class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Because of early stage
Coating is mostly with vegetable oil as primary raw material, therefore also referred to as paint.Synthetic resin instead of vegetable oil now, therefore is referred to as being coated with
Material.Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.Current according to the modern times
The classification of chemical products, coating belongs to fine chemical product.Modern coating the most progressively becomes a polyfunctional engineering of class
Material, is an important industry in chemical industry.At present, the coating industry of China is the most ripe, and market is close to saturated, in addition
Green economy globalization overall situation under, people become more concerned with economy the most flourishing after, environment is by great destruction.Along with
The environmental protection such as newly " environmental law " promulgates, country " environmental protection, beautiful China " advocate the most no longer to stay on slogan, but real
Execute execution, implement to promote energetically the development of green science and technology industry.
At present, the covering with paint of household electrical appliance has had bigger change, and traditional thermohardening lacquer is by the water of environmental protection
Property coating etc. substitute, but different electrical equipment has different requirements due to the difference of the aspects such as function to coating, more environmentally friendly, more individual
Property has become as the pursuit direction of household electrical appliances coating.Before the market demand huge in the face of household electrical appliances coating and ever-increasing application
Scape, strengthens research and development capabilities, and updates and improving product performance, accelerates product quality upgrading, develops technically, cost
Above, the household electrical appliances coating more showing powerful competitive advantage in performance has the meaning of reality and the wide market space.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of anti-scratch coating of electric iron and
Its preparation method, this coating products excellent performance, there are good anti-scratch performance, and energy-conserving and environment-protective, possess preferable economy
Benefit and social benefit.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of anti-scratch coating of electric iron, is prepared by the raw materials in: epoxy resin 35～45 parts, acrylate and vinyl acetate emulsion
10～15 parts, hydroxymethyl cellulose 2～5 parts, polyacrylonitrile fibre 5～12 parts, aliphatic dicarboxylic acid 8～15 parts, montmorillonite powder 2
～6 parts, isopropanol 1～3 parts, glycol ether 6～12 parts, water are appropriate, catalyst 1.5～3 parts, firming agent 1.5～2.5 parts, super
Thin calcium carbonate 1～5 parts, urethane acrylate 5～10 parts, organic silica gel 5～12 parts；
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, montmorillonite powder, isopropanol, glycol ether, calcium carbonate superfine powder and suitable quantity of water are joined instead
Answer in container, be heated to 50～65 DEG C, stir 20～30 minutes under 900～1200 revs/min, obtain the most mixed after mix homogeneously
Liquid；
(2) epoxy resin, acrylate and vinyl acetate emulsion, hydroxymethyl cellulose, polyacrylonitrile fibre and urethane acrylate are mixed
Join in the first mixed liquid that step (1) obtains, be heated to 65～80 DEG C, continue stirring 30～40 minutes, obtain intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 40～50 DEG C, adds catalyst, firming agent and organic silica gel,
Mix and blend 50～80 minutes, obtain mixed liquor；
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Preferably, described catalyst is sulfonic acid zinc.
Preferably, described firming agent is pyridine.
The beneficial effects of the present invention is:
Preparation method of the present invention is scientific and reasonable, by using combination property preferably high-molecular organic material and being optimized
Combination, improves the anti-scratch performance of compositions, and the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, gloss retention
Good, the index such as hot strength is superior to common coating, and can meet coated-body the most comprehensively uses requirement；Cost of the present invention is relatively
Low, it is achieved that making full use of of resource and the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrial mass raw
Produce, possess preferable economic benefit and social benefit.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of anti-scratch coating of electric iron, is prepared by the raw materials in: epoxy resin 35 parts, acrylate and vinyl acetate emulsion 10
Part, hydroxymethyl cellulose 2 parts, polyacrylonitrile fibre 5 parts, aliphatic dicarboxylic acid 8 parts, montmorillonite powder 2 parts, isopropanol 1 part, binary
Alcohol ether 6 parts, water are appropriate, catalyst 1.5 parts, 1.5 parts of firming agent, calcium carbonate superfine powder 1 part, urethane acrylate 5 parts, organosilicon
5 parts of glue；
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, montmorillonite powder, isopropanol, glycol ether, calcium carbonate superfine powder and suitable quantity of water are joined instead
Answer in container, be heated to 50～65 DEG C, stir 20 minutes under 900～1200 revs/min, after mix homogeneously, obtain the most mixed liquid；
(2) epoxy resin, acrylate and vinyl acetate emulsion, hydroxymethyl cellulose, polyacrylonitrile fibre and urethane acrylate are mixed
Join in the first mixed liquid that step (1) obtains, be heated to 65～80 DEG C, continue stirring 30 minutes, obtain intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 40～50 DEG C, adds catalyst, firming agent and organic silica gel,
Mix and blend 50 minutes, obtains mixed liquor；
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Embodiment 2:
A kind of anti-scratch coating of electric iron, is prepared by the raw materials in: epoxy resin 45 parts, acrylate and vinyl acetate emulsion 15
Part, hydroxymethyl cellulose 5 parts, polyacrylonitrile fibre 12 parts, aliphatic dicarboxylic acid 15 parts, montmorillonite powder 6 parts, isopropanol 3 parts, two
Unit's alcohol ether 12 parts, water are appropriate, catalyst 3 parts, 2.5 parts of firming agent, calcium carbonate superfine powder 5 parts, urethane acrylate 10 parts, organic
12 parts of silica gel；
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, montmorillonite powder, isopropanol, glycol ether, calcium carbonate superfine powder and suitable quantity of water are joined instead
Answer in container, be heated to 50～65 DEG C, stir 30 minutes under 900～1200 revs/min, after mix homogeneously, obtain the most mixed liquid；
(2) epoxy resin, acrylate and vinyl acetate emulsion, hydroxymethyl cellulose, polyacrylonitrile fibre and urethane acrylate are mixed
Join in the first mixed liquid that step (1) obtains, be heated to 65～80 DEG C, continue stirring 40 minutes, obtain intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 40～50 DEG C, adds catalyst, firming agent and organic silica gel,
Mix and blend 80 minutes, obtains mixed liquor；
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
In the above embodiment of the present invention:
Described catalyst is sulfonic acid zinc；
Described firming agent is pyridine.
During the present invention implements, by using combination property preferably high-molecular organic material and carrying out optimum organization, improve
The anti-scratch performance of compositions, the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good, hot strength
Being superior to common coating etc. index, can meet coated-body the most comprehensively uses requirement；Cost of the present invention is relatively low, it is achieved that money
Making full use of of source and the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although reference
The present invention has been described in detail by above-described embodiment, it will be appreciated by those skilled in the art that and still can carry out the present invention
Amendment or equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should be contained
In scope of the presently claimed invention.
Claims (3)
1. the anti-scratch coating of electric iron, it is characterised in that be prepared by the raw materials in: epoxy resin 35～45
Part, acrylate and vinyl acetate emulsion 10～15 parts, hydroxymethyl cellulose 2～5 parts, polyacrylonitrile fibre 5～12 parts, aliphatic dicarboxylic acid 8～15
Part, montmorillonite powder 2～6 parts, isopropanol 1～3 parts, glycol ether 6～12 parts, water is appropriate, catalyst 1.5～3 parts, firming agent
1.5～2.5 parts, calcium carbonate superfine powder 1～5 parts, urethane acrylate 5～10 parts, organic silica gel 5～12 parts；
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, montmorillonite powder, isopropanol, glycol ether, calcium carbonate superfine powder and suitable quantity of water join reaction to hold
In device, it is heated to 50～65 DEG C, stirs 20～30 minutes under 900～1200 revs/min, after mix homogeneously, obtain the most mixed liquid；
(2) mixing of epoxy resin, acrylate and vinyl acetate emulsion, hydroxymethyl cellulose, polyacrylonitrile fibre and urethane acrylate is added
In the first mixed liquid that step (1) obtains, it is heated to 65～80 DEG C, continues stirring 30～40 minutes, obtain intermediate liquid；
(3) intermediate liquid that step (2) obtains is cooled to 40～50 DEG C, adds catalyst, firming agent and organic silica gel, mixing
Stir 50～80 minutes, obtain mixed liquor；
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
A kind of anti-scratch coating of electric iron the most according to claim 1, it is characterised in that described catalyst is sulfonic acid zinc.
A kind of anti-scratch coating of electric iron the most according to claim 1, it is characterised in that described firming agent is pyridine.