CN106047109A - Antibacterial coating for electric massager and preparation method thereof - Google Patents
Antibacterial coating for electric massager and preparation method thereof Download PDFInfo
- Publication number
- CN106047109A CN106047109A CN201610665238.5A CN201610665238A CN106047109A CN 106047109 A CN106047109 A CN 106047109A CN 201610665238 A CN201610665238 A CN 201610665238A CN 106047109 A CN106047109 A CN 106047109A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- preparation
- electric massager
- mixed liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial coating for an electric massager. The antibacterial coating is prepared from the following raw materials: alkyd resin, silicone-acrylic emulsion, polymethyl methacrylate, polyurethane resin, aliphatic dicarboxylic acid, jade powder, polyester diol, propylene glycol methyl ether, a proper amount of water, a catalyst, an antibacterial agent, nanometer zinc oxide, dimethyl carbonate and epoxy glue. The preparation method comprises the following successive steps: (1) preparing preliminarily mixed liquid; (2) preparing intermediate liquid; (3) preparing mixed liquid; and (4) adding the mixed liquid obtained in the step (3) into a ball mill for grinding and carrying out sieving so as to obtain the finished antibacterial coating. The preparation method is scientific and reasonable, improves the antibacterial resistance of the composition by using organic polymer materials with good performance and carrying out optimized combination, and is low in cost, short in production period and suitable for industrial mass production.
Description
Technical field
The invention belongs to coating industry technical field, particularly relate to a kind of electric massager antibiotic paint and preparation side thereof
Method.
Background technology
Coating, at the entitled paint of Chinese tradition, refer to coat body surface can form thin film under certain conditions and
Play protection, a class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Because of early stage
Coating is mostly with vegetable oil as primary raw material, therefore also referred to as paint.Synthetic resin instead of vegetable oil now, therefore is referred to as being coated with
Material.Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.Current according to the modern times
The classification of chemical products, coating belongs to fine chemical product.Modern coating the most progressively becomes a polyfunctional engineering of class
Material, is an important industry in chemical industry.At present, the coating industry of China is the most ripe, and market is close to saturated, in addition
Green economy globalization overall situation under, people become more concerned with economy the most flourishing after, environment is by great destruction.Along with
The environmental protection such as newly " environmental law " promulgates, country " environmental protection, beautiful China " advocate the most no longer to stay on slogan, but real
Execute execution, implement to promote energetically the development of green science and technology industry.
At present, the covering with paint of household electrical appliance has had bigger change, and traditional thermohardening lacquer is by the water of environmental protection
Property coating etc. substitute, but different electrical equipment has different requirements due to the difference of the aspects such as function to coating, more environmentally friendly, more individual
Property has become as the pursuit direction of household electrical appliances coating.Before the market demand huge in the face of household electrical appliances coating and ever-increasing application
Scape, strengthens research and development capabilities, and updates and improving product performance, accelerates product quality upgrading, develops technically, cost
Above, the household electrical appliances coating more showing powerful competitive advantage in performance has the meaning of reality and the wide market space.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of electric massager antibiotic paint
And preparation method thereof, this coating products excellent performance, there are good anti-microbial property, and energy-conserving and environment-protective, possess preferable economy
Benefit and social benefit.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of electric massager antibiotic paint, is prepared by the raw materials in: alkyd resin 35~45 parts, silicon the third breast
Liquid 10~15 parts, polymethyl methacrylate 2~5 parts, polyurethane resin 5~12 parts, aliphatic dicarboxylic acid 8~15 parts, jade
Powder 2~6 parts, polyester-diol 1~3 parts, propylene glycol monomethyl ether 6~12 parts, water are appropriate, catalyst 1.5~3 parts, antibacterial 1.5~
2.5 parts, nano zine oxide 1~5 parts, dimethyl carbonate 5~10 parts, epoxy glue 5~12 parts;
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, jade powder, polyester-diol, propylene glycol monomethyl ether, nano zine oxide and suitable quantity of water are joined
In reaction vessel, it is heated to 50~65 DEG C, stirs 20~30 minutes under 900~1200 revs/min, obtain the most mixed after mix homogeneously
Liquid;
(2) mixing of alkyd resin, silicone acrylic emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate is added
Enter to step (1) in the first mixed liquid obtained, be heated to 65~80 DEG C, continue stirring 30~40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and epoxy glue, mixed
Close stirring 50~80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Preferably, described catalyst is sodium sulfonate.
Preferably, described antibacterial is ammonium dihydrogen phosphate.
The beneficial effects of the present invention is:
Preparation method of the present invention is scientific and reasonable, by using combination property preferably high-molecular organic material and being optimized
Combination, improves the anti-microbial property of compositions, and the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good,
The indexs such as hot strength are superior to common coating, and can meet coated-body the most comprehensively uses requirement;Cost of the present invention is relatively low,
Achieving making full use of of resource and the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production,
Possess preferable economic benefit and social benefit.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of electric massager antibiotic paint, is prepared by the raw materials in: alkyd resin 35 parts, silicone acrylic emulsion 10
Part, polymethyl methacrylate 2 parts, polyurethane resin 5 parts, aliphatic dicarboxylic acid 8 parts, jade powder 2 parts, polyester-diol 1 part, third
Glycol methyl ether 6 parts, water are appropriate, catalyst 1.5 parts, antibacterial 1.5 parts, nano zine oxide 1 part, dimethyl carbonate 5 parts, epoxy glue
5 parts;
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, jade powder, polyester-diol, propylene glycol monomethyl ether, nano zine oxide and suitable quantity of water are joined
In reaction vessel, it is heated to 50~65 DEG C, stirs 20 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) mixing of alkyd resin, silicone acrylic emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate is added
Enter to step (1) in the first mixed liquid obtained, be heated to 65~80 DEG C, continue stirring 30 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and epoxy glue, mixed
Close stirring 50 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Embodiment 2:
A kind of electric massager antibiotic paint, is prepared by the raw materials in: alkyd resin 45 parts, silicone acrylic emulsion 15
Part, polymethyl methacrylate 5 parts, polyurethane resin 12 parts, aliphatic dicarboxylic acid 15 parts, jade powder 6 parts, polyester-diol 3 parts,
Propylene glycol monomethyl ether 12 parts, water are appropriate, catalyst 3 parts, antibacterial 2.5 parts, nano zine oxide 5 parts, dimethyl carbonate 10 parts, epoxy
12 parts of glue;
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, jade powder, polyester-diol, propylene glycol monomethyl ether, nano zine oxide and suitable quantity of water are joined
In reaction vessel, it is heated to 50~65 DEG C, stirs 30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) mixing of alkyd resin, silicone acrylic emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate is added
Enter to step (1) in the first mixed liquid obtained, be heated to 65~80 DEG C, continue stirring 40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, antibacterial and epoxy glue, mixed
Close stirring 80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
In the above embodiment of the present invention:
Described catalyst is sodium sulfonate;
Described antibacterial is ammonium dihydrogen phosphate.
During the present invention implements, by using combination property preferably high-molecular organic material and carrying out optimum organization, improve
The anti-microbial property of compositions, the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good, hot strength etc.
Index is superior to common coating, and can meet coated-body the most comprehensively uses requirement;Cost of the present invention is relatively low, it is achieved that resource
With making full use of of the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although reference
The present invention has been described in detail by above-described embodiment, it will be appreciated by those skilled in the art that and still can carry out the present invention
Amendment or equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should be contained
In scope of the presently claimed invention.
Claims (3)
1. an electric massager antibiotic paint, it is characterised in that be prepared by the raw materials in: alkyd resin 35~45
Part, silicone acrylic emulsion 10~15 parts, polymethyl methacrylate 2~5 parts, polyurethane resin 5~12 parts, aliphatic dicarboxylic acid 8~
15 parts, jade powder 2~6 parts, polyester-diol 1~3 parts, propylene glycol monomethyl ether 6~12 parts, water are appropriate, catalyst 1.5~3 parts, antibacterial
Agent 1.5~2.5 parts, nano zine oxide 1~5 parts, dimethyl carbonate 5~10 parts, epoxy glue 5~12 parts;
Its preparation method in turn includes the following steps:
(1) aliphatic dicarboxylic acid, jade powder, polyester-diol, propylene glycol monomethyl ether, nano zine oxide and suitable quantity of water are joined reaction
In container, it is heated to 50~65 DEG C, stirs 20~30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) alkyd resin, silicone acrylic emulsion, polymethyl methacrylate, polyurethane resin and dimethyl carbonate are mixed to join
In the first mixed liquid that step (1) obtains, it is heated to 65~80 DEG C, continues stirring 30~40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains being cooled to 40~50 DEG C, add catalyst, antibacterial and epoxy glue, mixing is stirred
Mix 50~80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
A kind of electric massager antibiotic paint the most according to claim 1, it is characterised in that described catalyst is sulfonic acid
Sodium.
A kind of electric massager antibiotic paint the most according to claim 1, it is characterised in that described antibacterial is di(2-ethylhexyl)phosphate
Hydrogen ammonium.