CN106280879A - A kind of electric massager heat radiation coating and preparation method thereof - Google Patents
A kind of electric massager heat radiation coating and preparation method thereof Download PDFInfo
- Publication number
- CN106280879A CN106280879A CN201610663214.6A CN201610663214A CN106280879A CN 106280879 A CN106280879 A CN 106280879A CN 201610663214 A CN201610663214 A CN 201610663214A CN 106280879 A CN106280879 A CN 106280879A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- heat radiation
- radiation coating
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of electric massager heat radiation coating, be made up of following raw materials according: epoxy resin, elastic emulsion, polyester resin, ferrotitanium powder, maleic acid, graphite powder, propylene glycol, dipropylene, water are appropriate, catalyst, dispersant, nano titanium oxide, 2-Butoxyethyl acetate, modified rosin resin;Its preparation method in turn includes the following steps: the most mixed liquid of (1) preparation;(2) intermediate liquid is prepared;(3) mixed liquor is prepared;(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.Preparation method of the present invention is scientific and reasonable, by using combination property preferably high-molecular organic material and carrying out optimum organization, improves the heat dispersion of compositions, and its cost is relatively low, with short production cycle, is suitable to industrialized mass production.
Description
Technical field
The invention belongs to coating industry technical field, particularly relate to a kind of electric massager heat radiation coating and preparation side thereof
Method.
Background technology
Coating, at the entitled paint of Chinese tradition, refer to coat body surface can form thin film under certain conditions and
Play protection, a class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Because of early stage
Coating is mostly with vegetable oil as primary raw material, therefore also referred to as paint.Synthetic resin instead of vegetable oil now, therefore is referred to as being coated with
Material.Coating belongs to organic chemical industry's macromolecular material, and the film formed belongs to macromolecular compound type.Current according to the modern times
The classification of chemical products, coating belongs to fine chemical product.Modern coating the most progressively becomes a polyfunctional engineering of class
Material, is an important industry in chemical industry.At present, the coating industry of China is the most ripe, and market is close to saturated, in addition
Green economy globalization overall situation under, people become more concerned with economy the most flourishing after, environment is by great destruction.Along with
The environmental protection such as newly " environmental law " promulgates, country " environmental protection, beautiful China " advocate the most no longer to stay on slogan, but real
Execute execution, implement to promote energetically the development of green science and technology industry.
At present, the covering with paint of household electrical appliance has had bigger change, and traditional thermohardening lacquer is by the water of environmental protection
Property coating etc. substitute, but different electrical equipment has different requirements due to the difference of the aspects such as function to coating, more environmentally friendly, more individual
Property has become as the pursuit direction of household electrical appliances coating.Before the market demand huge in the face of household electrical appliances coating and ever-increasing application
Scape, strengthens research and development capabilities, and updates and improving product performance, accelerates product quality upgrading, develops technically, cost
Above, the household electrical appliances coating more showing powerful competitive advantage in performance has the meaning of reality and the wide market space.
Summary of the invention
The invention aims to overcome the deficiencies in the prior art, it is provided that a kind of electric massager heat radiation coating
And preparation method thereof, this coating products excellent performance, there are good heat dispersion, and energy-conserving and environment-protective, possess preferable economy
Benefit and social benefit.
For solve above-mentioned technical problem, the present invention by the following technical solutions:
A kind of electric massager heat radiation coating, is prepared by the raw materials in: epoxy resin 35~45 parts, elastic breast
Liquid 10~15 parts, polyester resin 2~5 parts, ferrotitanium powder 5~12 parts, maleic acid 8~15 parts, graphite powder 2~6 parts, propylene glycol 1~3
Part, dipropylene 6~12 parts, water is appropriate, catalyst 1.5~3 parts, dispersant 1.5~2.5 parts, nano titanium oxide 1~
5 parts, 2-Butoxyethyl acetate 5~10 parts, modified rosin resin 5~12 parts;
Its preparation method in turn includes the following steps:
(1) maleic acid, graphite powder, propylene glycol, dipropylene, nano titanium oxide and suitable quantity of water are joined reaction
In container, it is heated to 50~65 DEG C, stirs 20~30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) epoxy resin, elastic emulsion, polyester resin, ferrotitanium powder and 2-Butoxyethyl acetate are mixed to join step
Suddenly in the first mixed liquid that (1) obtains, it is heated to 65~80 DEG C, continues stirring 30~40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, dispersant and Abietyl modified
Resin, mix and blend 50~80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Preferably, described catalyst is sodium sulfonate.
Preferably, described dispersant is sodium tripolyphosphate.
The beneficial effects of the present invention is:
Preparation method of the present invention is scientific and reasonable, by using combination property preferably high-molecular organic material and being optimized
Combination, improves the heat dispersion of compositions, and the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good,
The indexs such as hot strength are superior to common coating, and can meet coated-body the most comprehensively uses requirement;Cost of the present invention is relatively low,
Achieving making full use of of resource and the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production,
Possess preferable economic benefit and social benefit.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1:
A kind of electric massager heat radiation coating, is prepared by the raw materials in: epoxy resin 35 parts, elastic emulsion 10
Part, 2 parts of polyester resin, 5 parts of ferrotitanium powder, maleic acid 8 parts, graphite powder 2 parts, propylene glycol 1 part, dipropylene 6 parts, water are fitted
Amount, catalyst 1.5 parts, dispersant 1.5 parts, nano titanium oxide 1 part, 2-Butoxyethyl acetate 5 parts, modified rosin resin 5
Part;
Its preparation method in turn includes the following steps:
(1) maleic acid, graphite powder, propylene glycol, dipropylene, nano titanium oxide and suitable quantity of water are joined reaction
In container, it is heated to 50~65 DEG C, stirs 20 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) epoxy resin, elastic emulsion, polyester resin, ferrotitanium powder and 2-Butoxyethyl acetate are mixed to join step
Suddenly in the first mixed liquid that (1) obtains, it is heated to 65~80 DEG C, continues stirring 30 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, dispersant and Abietyl modified
Resin, mix and blend 50 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
Embodiment 2:
A kind of electric massager heat radiation coating, is prepared by the raw materials in: epoxy resin 45 parts, elastic emulsion 15
Part, 5 parts of polyester resin, 12 parts of ferrotitanium powder, maleic acid 15 parts, graphite powder 6 parts, propylene glycol 3 parts, dipropylene 12 parts, water
In right amount, catalyst 3 parts, dispersant 2.5 parts, nano titanium oxide 5 parts, 2-Butoxyethyl acetate 10 parts, modified rosin resin
12 parts;
Its preparation method in turn includes the following steps:
(1) maleic acid, graphite powder, propylene glycol, dipropylene, nano titanium oxide and suitable quantity of water are joined reaction
In container, it is heated to 50~65 DEG C, stirs 30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) epoxy resin, elastic emulsion, polyester resin, ferrotitanium powder and 2-Butoxyethyl acetate are mixed to join step
Suddenly in the first mixed liquid that (1) obtains, it is heated to 65~80 DEG C, continues stirring 40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, dispersant and Abietyl modified
Resin, mix and blend 80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
In the above embodiment of the present invention:
Described catalyst is sodium sulfonate;
Described dispersant is sodium tripolyphosphate.
During the present invention implements, by using combination property preferably high-molecular organic material and carrying out optimum organization, improve
The heat dispersion of compositions, the coating surface using the present invention to obtain is smooth, fine and smooth, smooth, and gloss retention is good, hot strength etc.
Index is superior to common coating, and can meet coated-body the most comprehensively uses requirement;Cost of the present invention is relatively low, it is achieved that resource
With making full use of of the energy, production process is environment friendly and pollution-free, with short production cycle, is suitable to industrialized mass production.
Finally it should be noted that above example only in order to illustrative not limiting technical scheme, although reference
The present invention has been described in detail by above-described embodiment, it will be appreciated by those skilled in the art that and still can carry out the present invention
Amendment or equivalent, any modification or partial replacement without departing from the spirit and scope of the present invention, it all should be contained
In scope of the presently claimed invention.
Claims (3)
1. an electric massager heat radiation coating, it is characterised in that be prepared by the raw materials in: epoxy resin 35~45
Part, elastic emulsion 10~15 parts, polyester resin 2~5 parts, ferrotitanium powder 5~12 parts, maleic acid 8~15 parts, graphite powder 2~6 parts,
Propylene glycol 1~3 parts, dipropylene 6~12 parts, water are appropriate, catalyst 1.5~3 parts, dispersant 1.5~2.5 parts, nanometer
Titanium dioxide 1~5 parts, 2-Butoxyethyl acetate 5~10 parts, modified rosin resin 5~12 parts;
Its preparation method in turn includes the following steps:
(1) maleic acid, graphite powder, propylene glycol, dipropylene, nano titanium oxide and suitable quantity of water are joined reaction vessel
In, it is heated to 50~65 DEG C, stirs 20~30 minutes under 900~1200 revs/min, after mix homogeneously, obtain the most mixed liquid;
(2) epoxy resin, elastic emulsion, polyester resin, ferrotitanium powder and 2-Butoxyethyl acetate are mixed to join step (1)
In the first mixed liquid obtained, it is heated to 65~80 DEG C, continues stirring 30~40 minutes, obtain intermediate liquid;
(3) intermediate liquid that step (2) obtains is cooled to 40~50 DEG C, adds catalyst, dispersant and modified rosin resin,
Mix and blend 50~80 minutes, obtain mixed liquor;
(4) mixed liquor step (3) obtained puts into grinding in ball grinder and processes, and sieves and gets product.
A kind of electric massager heat radiation coating the most according to claim 1, it is characterised in that described catalyst is sulfonic acid
Sodium.
A kind of electric massager heat radiation coating the most according to claim 1, it is characterised in that described dispersant is trimerization phosphorus
Acid sodium.