CN106267327A - 一种用于缝合伤口的胶水及其制备方法 - Google Patents

一种用于缝合伤口的胶水及其制备方法 Download PDF

Info

Publication number
CN106267327A
CN106267327A CN201610760918.5A CN201610760918A CN106267327A CN 106267327 A CN106267327 A CN 106267327A CN 201610760918 A CN201610760918 A CN 201610760918A CN 106267327 A CN106267327 A CN 106267327A
Authority
CN
China
Prior art keywords
parts
glue
wound
sewing
portions
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610760918.5A
Other languages
English (en)
Inventor
裴寿益
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610760918.5A priority Critical patent/CN106267327A/zh
Publication of CN106267327A publication Critical patent/CN106267327A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种用于缝合伤口的胶水及其制备方法，以重量份计，所述胶水包括10份‑20份α‑氰基丙烯酸甲酯、2份‑3份纤维蛋白、10份‑20份对苯二酚、30份‑50份芦荟纳米微粉、1份‑3份海藻酸钠、1份‑2份果胶、3份‑4份聚乙烯醇、3份‑7份乙烯醇、1份‑2份胶原蛋白、1份‑3份抗菌剂。本发明的医用胶水粘结强度高，抗冲击能力好，降解速度快，抗菌性好。

Description

一种用于缝合伤口的胶水及其制备方法
技术领域
本发明涉及新材料技术领域，具体涉及一种用于缝合伤口的胶水及其制备方法。
背景技术
医用胶水是代替缝针用的新兴医用产品，在创面血液和组织液中阴离子的作用下，能快速聚合固化成膜并与创面镶嵌紧密。医用胶粘法和传统的缝合法相比，能够快速止血、粘合过程没有痛苦，不需要麻醉，伤口呈线性愈合，不需要承受拆线的痛苦。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种用于缝合伤口的胶水及其制备方法。
本发明解决上述技术问题的技术方案如下：一种用于缝合伤口的胶水，以重量份计，包括10份-20份α-氰基丙烯酸甲酯、2份-3份纤维蛋白、10份-20份对苯二酚、30份-50份芦荟纳米微粉、1份-3份海藻酸钠、1份-2份果胶、3份-4份聚乙烯醇、3份-7份乙烯醇、1份-2份胶原蛋白、1份-3份抗菌剂。
本发明的有益效果是：本发明的医用胶水粘结强度高，抗冲击能力好，降解速度快，抗菌性好。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，以重量份计，包括10份α-氰基丙烯酸甲酯、2份纤维蛋白、10份对苯二酚、30份芦荟纳米微粉、1份海藻酸钠、1份果胶、3份聚乙烯醇、3份乙烯醇、1份胶原蛋白、1份抗菌剂。
进一步，以重量份计，包括20份α-氰基丙烯酸甲酯、3份纤维蛋白、20份对苯二酚、50份芦荟纳米微粉、3份海藻酸钠、2份果胶、4份聚乙烯醇、7份乙烯醇、2份胶原蛋白、3份抗菌剂。
进一步，以重量份计，包括15份α-氰基丙烯酸甲酯、2.5份纤维蛋白、15份对苯二酚、40份芦荟纳米微粉、2份海藻酸钠、1.5份果胶、3.5份聚乙烯醇、5份乙烯醇、1.5份胶原蛋白、2份抗菌剂。
进一步，所述抗菌剂为氧化锌、氧化铜、磷酸二氢铵和碳酸锂的至少一种。
一种如上所述的用于缝合伤口的胶水的制备方法，按照配比称取各个原料，将α-氰基丙烯酸甲酯、纤维蛋白、对苯二酚、芦荟纳米微粉、海藻酸钠、胶原蛋白、聚乙烯醇混合均匀后，升温至50℃-55℃，再加入抗菌剂、果胶和乙烯醇，搅拌均匀，保温1h-2h后再冷却至20℃-25℃即得到所述胶水。
本发明的有益效果是：本发明的方法简单，适宜工业化生产。
具体实施方式
以下对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1
本实施例的一种用于缝合伤口的胶水，以重量份计，包括10份α-氰基丙烯酸甲酯、2份纤维蛋白、10份对苯二酚、30份芦荟纳米微粉、1份海藻酸钠、1份果胶、3份聚乙烯醇、3份乙烯醇、1份胶原蛋白、1份抗菌剂。
本实施例的医用胶水粘结强度高，抗冲击能力好，降解速度快，抗菌性好。
本实施例的所述抗菌剂为氧化锌、氧化铜、磷酸二氢铵和碳酸锂的至少一种。
本实施例的一种如上所述的用于缝合伤口的胶水的制备方法，按照配比称取各个原料，将α-氰基丙烯酸甲酯、纤维蛋白、对苯二酚、芦荟纳米微粉、海藻酸钠、胶原蛋白、聚乙烯醇混合均匀后，升温至50℃，再加入抗菌剂、果胶和乙烯醇，搅拌均匀，保温1h后再冷却至20℃即得到所述胶水。
本实施例的方法简单，适宜工业化生产。
实施例2
本实施例的一种用于缝合伤口的胶水，以重量份计，包括20份α-氰基丙烯酸甲酯、3份纤维蛋白、20份对苯二酚、50份芦荟纳米微粉、3份海藻酸钠、2份果胶、4份聚乙烯醇、7份乙烯醇、2份胶原蛋白、3份抗菌剂。
本实施例的所述抗菌剂为氧化锌、氧化铜、磷酸二氢铵和碳酸锂的至少一种。
本实施例的一种如上所述的用于缝合伤口的胶水的制备方法，按照配比称取各个原料，将α-氰基丙烯酸甲酯、纤维蛋白、对苯二酚、芦荟纳米微粉、海藻酸钠、胶原蛋白、聚乙烯醇混合均匀后，升温至52℃，再加入抗菌剂、果胶和乙烯醇，搅拌均匀，保温1.5h后再冷却至22℃即得到所述胶水。
本实施例的方法简单，适宜工业化生产。
实施例3
本实施例的一种用于缝合伤口的胶水，以重量份计，包括15份α-氰基丙烯酸甲酯、2.5份纤维蛋白、15份对苯二酚、40份芦荟纳米微粉、2份海藻酸钠、1.5份果胶、3.5份聚乙烯醇、5份乙烯醇、1.5份胶原蛋白、2份抗菌剂。
本实施例的所述抗菌剂为氧化锌、氧化铜、磷酸二氢铵和碳酸锂的至少一种。
本实施例的一种如上所述的用于缝合伤口的胶水的制备方法，按照配比称取各个原料，将α-氰基丙烯酸甲酯、纤维蛋白、对苯二酚、芦荟纳米微粉、海藻酸钠、胶原蛋白、聚乙烯醇混合均匀后，升温至55℃，再加入抗菌剂、果胶和乙烯醇，搅拌均匀，保温2h后再冷却至25℃即得到所述胶水。
本实施例的方法简单，适宜工业化生产。
对实施例1、实施例2和实施例3中的医用胶水进行临床试验。对50名需要缝合伤口的患者进行伤口缝合，其中有45名患者在伤口缝合一周后，伤口愈合，且疤痕颜色与皮肤颜色接近；有5名患者在伤口缝合10天后，伤口愈合，且疤痕颜色呈粉红色。临床试验中的50名患者均没有出现伤口感染的现象。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种用于缝合伤口的胶水，其特征在于，以重量份计，包括10份-20份α-氰基丙烯酸甲酯、2份-3份纤维蛋白、10份-20份对苯二酚、30份-50份芦荟纳米微粉、1份-3份海藻酸钠、1份-2份果胶、3份-4份聚乙烯醇、3份-7份乙烯醇、1份-2份胶原蛋白、1份-3份抗菌剂。
2.根据权利要求1所述一种用于缝合伤口的胶水，其特征在于，以重量份计，包括10份α-氰基丙烯酸甲酯、2份纤维蛋白、10份对苯二酚、30份芦荟纳米微粉、1份海藻酸钠、1份果胶、3份聚乙烯醇、3份乙烯醇、1份胶原蛋白、1份抗菌剂。
3.根据权利要求1所述一种用于缝合伤口的胶水，其特征在于，以重量份计，包括20份α-氰基丙烯酸甲酯、3份纤维蛋白、20份对苯二酚、50份芦荟纳米微粉、3份海藻酸钠、2份果胶、4份聚乙烯醇、7份乙烯醇、2份胶原蛋白、3份抗菌剂。
4.根据权利要求1所述一种用于缝合伤口的胶水，其特征在于，以重量份计，包括15份α-氰基丙烯酸甲酯、2.5份纤维蛋白、15份对苯二酚、40份芦荟纳米微粉、2份海藻酸钠、1.5份果胶、3.5份聚乙烯醇、5份乙烯醇、1.5份胶原蛋白、2份抗菌剂。
5.根据权利要求1至4任一项所述一种用于缝合伤口的胶水，其特征在于，所述抗菌剂为氧化锌、氧化铜、磷酸二氢铵和碳酸锂的至少一种。
6.一种如权利要求1至5任一项所述的用于缝合伤口的胶水的制备方法，其特征在于，按照配比称取各个原料，将α-氰基丙烯酸甲酯、纤维蛋白、对苯二酚、芦荟纳米微粉、海藻酸钠、胶原蛋白、聚乙烯醇混合均匀后，升温至50℃-55℃，再加入抗菌剂、果胶和乙烯醇，搅拌均匀，保温1h-2h后再冷却至20℃-25℃即得到所述胶水。
CN201610760918.5A 2016-08-30 2016-08-30 一种用于缝合伤口的胶水及其制备方法 Pending CN106267327A (zh)