CN106190491A - 一种混凝土浇筑用建筑模板脱模剂 - Google Patents

一种混凝土浇筑用建筑模板脱模剂 Download PDF

Info

Publication number
CN106190491A
CN106190491A CN201610559547.4A CN201610559547A CN106190491A CN 106190491 A CN106190491 A CN 106190491A CN 201610559547 A CN201610559547 A CN 201610559547A CN 106190491 A CN106190491 A CN 106190491A
Authority
CN
China
Prior art keywords
parts
sufficiently mixed
template
butyl
heated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610559547.4A
Other languages
English (en)
Inventor
陈建宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongzhi Oasis Environmental Protection Chemical Co Ltd
Original Assignee
Dongzhi Oasis Environmental Protection Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongzhi Oasis Environmental Protection Chemical Co Ltd filed Critical Dongzhi Oasis Environmental Protection Chemical Co Ltd
Priority to CN201610559547.4A priority Critical patent/CN106190491A/zh
Publication of CN106190491A publication Critical patent/CN106190491A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种混凝土浇筑用建筑模板脱模剂，涉及脱模剂生产技术领域，由如下重量份数的原料制成：改性硅油40‑45份、聚氧化丙烯二醇200015‑20份、C9石油树脂8‑12份、火山灰6‑10份、海泡石粉5‑8份、乙烯‑四氟乙烯共聚物5‑8份、甲苯二异氰酸酯4‑6份、菜籽饼3‑5份、油酸聚氧乙烯酯2‑3份、纳米氧化铝2‑3份、玻璃纤维粉2‑3份、三正丁基甲氧基锡1‑2份、硫酸化蓖麻油1‑2份、醋酸丁酯10‑15份、正丁醇10‑15份。本发明脱模剂能显著提高混凝土的脱模效果，防止脱模时混凝土粘附在模板上，以保护模板和混凝土表面结构；同时不会对模板产生任何腐蚀作用，从而充分延长模板的使用寿命。

Description

一种混凝土浇筑用建筑模板脱模剂
技术领域：
本发明涉及脱模剂生产技术领域，具体涉及一种混凝土浇筑用建筑模板脱模剂。
背景技术：
混凝土成型需借助建筑模板来固定，待混凝土形成一定强度后需要拆除模板。为了防止模板拆除过程中混凝土粘连在模板上，给模板的再使用增加处理难度，通常会在模板内壁喷涂脱模剂。脱模剂在模板与混凝土表面之间起隔离与润滑作用，用以克服模板与混凝土表面的粘结力，使拆模时模板能顺利脱离混凝土，既保持混凝土形状完好无损，又保护模板表面不受损坏。
传统建筑模板脱模剂以废机油、地沟油和大豆油为主，虽然成本低，但脱模效果一般。目前，随着人们对脱模剂的深入研究，有机硅高分子树脂乳液分散体系类产品应运而生，但其使用成本高，并且在合成过程中产生的废弃物存在一定环保问题。另外，部分脱模剂虽然脱模效果好，但存在易产生气孔、粉化和腐蚀模板的缺陷。
发明内容：
本发明所要解决的技术问题在于提供一种使用方便、脱模效果好且不会产生腐蚀现象的混凝土浇筑用建筑模板脱模剂。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种混凝土浇筑用建筑模板脱模剂，由如下重量份数的原料制成：
改性硅油40-45份、聚氧化丙烯二醇200015-20份、C9石油树脂8-12份、火山灰6-10份、海泡石粉5-8份、乙烯-四氟乙烯共聚物5-8份、甲苯二异氰酸酯4-6份、菜籽饼3-5份、油酸聚氧乙烯酯2-3份、纳米氧化铝2-3份、玻璃纤维粉2-3份、三正丁基甲氧基锡1-2份、硫酸化蓖麻油1-2份、醋酸丁酯10-15份、正丁醇10-15份；
所述改性硅油的制备方法为：向40-50份二甲基硅油中加入6-9份氢化松香和3-5份巴西棕榈蜡，加热至完全熔化后保温混合10min，并于微波频率2450MHz、功率700W下微波处理10min，再转入室温下静置1h，然后继续微波处理5min，处理结束后趁热加入2-3份鲸蜡醇和1-2份纳米钛白粉，充分混合后于超声频率40kHz、功率100W下超声处理30min，待混合物自然冷却至30-35℃后转入0-5℃环境中，静置12h，即得改性硅油。
其制备方法包括如下步骤：
(1)将聚氧化丙烯二醇2000于100-105℃下干燥3h，干燥结束后自然冷却至60-65℃加入甲苯二异氰酸酯和三正丁基甲氧基锡，保温搅拌30min后继续加热至70-75℃，并于70-75℃保温搅拌15min，然后再继续加热至80-85℃保温搅拌2h，即得物料I；
(2)向C9石油树脂中加入乙烯-四氟乙烯共聚物、纳米氧化铝和硫酸化蓖麻油，充分混合后加热至100-105℃保温混合10min，再自然冷却至65-70℃，然后继续加热至135-140℃保温混合10min，即得物料II；
(3)向改性硅油中加入火山灰和海泡石粉，充分混合后于0-5℃静置2h，再加入菜籽饼和玻璃纤维粉，然后加热至95-100℃保温混合10min，即得物料III；
(4)向物料I中加入物料II和物料III，充分混合后于微波频率2450MHz、功率700W下微波处理10min，然后自然冷却至70-75℃，再加入油酸聚氧乙烯酯、醋酸丁酯和正丁醇，充分混合均匀。
所述火山灰使用前经过预处理，其处理方法为：将30-40份火山灰加入等量水中，充分混合后送入砂磨机中，砂磨至细度小于10um，再加入10-15份凹凸棒土和2-4份纳米氧化锌，充分混合后继续球磨5-8h，然后将混合物送入喷雾干燥机，所得颗粒最后经粉碎机制成粉末。
二甲基硅油通过改性处理，不仅能增强其成膜性，还能提高耐腐蚀性、耐水性和耐候性，从而提高脱模剂的使用性能。
火山灰经过预处理，显著增强其填充性，添加于脱模剂后能增加脱模剂成膜后的韧性和耐高温性，从而进一步提高脱模剂的使用性能。
本发明的有益效果是：本发明以改性硅油为主要原料，辅以多种助剂制得混凝土浇筑用建筑模板脱模剂，该脱模剂使用方便，喷涂于建筑模板后能够形成一层隔离膜，提高混凝土的脱模效果，防止脱模时混凝土粘附在模板上，以保护模板和混凝土表面结构；同时不会对模板产生任何腐蚀作用，从而充分延长模板的使用寿命。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
(1)将15份聚氧化丙烯二醇2000于100-105℃下干燥3h，干燥结束后自然冷却至60-65℃加入4份甲苯二异氰酸酯和1份三正丁基甲氧基锡，保温搅拌30min后继续加热至70-75℃，并于70-75℃保温搅拌15min，然后再继续加热至80-85℃保温搅拌2h，即得物料I；
(2)向8份C9石油树脂中加入5份乙烯-四氟乙烯共聚物、2份纳米氧化铝和1份硫酸化蓖麻油，充分混合后加热至100-105℃保温混合10min，再自然冷却至65-70℃，然后继续加热至135-140℃保温混合10min，即得物料II；
(3)向40份改性硅油中加入6份火山灰和8份海泡石粉，充分混合后于0-5℃静置2h，再加入3份菜籽饼和2份玻璃纤维粉，然后加热至95-100℃保温混合10min，即得物料III；
(4)向物料I中加入物料II和物料III，充分混合后于微波频率2450MHz、功率700W下微波处理10min，然后自然冷却至70-75℃，再加入2份油酸聚氧乙烯酯、15份醋酸丁酯和10份正丁醇，充分混合均匀。
改性硅油的制备：向45份二甲基硅油中加入6份氢化松香和3份巴西棕榈蜡，加热至完全熔化后保温混合10min，并于微波频率2450MHz、功率700W下微波处理10min，再转入室温下静置1h，然后继续微波处理5min，处理结束后趁热加入2份鲸蜡醇和1份纳米钛白粉，充分混合后于超声频率40kHz、功率100W下超声处理30min，待混合物自然冷却至30-35℃后转入0-5℃环境中，静置12h，即得改性硅油。
火山灰的预处理：将40份火山灰加入等量水中，充分混合后送入砂磨机中，砂磨至细度小于10um，再加入15份凹凸棒土和3份纳米氧化锌，充分混合后继续球磨8h，然后将混合物送入喷雾干燥机，所得颗粒最后经粉碎机制成粉末。
实施例2
(1)将20份聚氧化丙烯二醇2000于100-105℃下干燥3h，干燥结束后自然冷却至60-65℃加入5份甲苯二异氰酸酯和1份三正丁基甲氧基锡，保温搅拌30min后继续加热至70-75℃，并于70-75℃保温搅拌15min，然后再继续加热至80-85℃保温搅拌2h，即得物料I；
(2)向10份C9石油树脂中加入5份乙烯-四氟乙烯共聚物、2份纳米氧化铝和1份硫酸化蓖麻油，充分混合后加热至100-105℃保温混合10min，再自然冷却至65-70℃，然后继续加热至135-140℃保温混合10min，即得物料II；
(3)向40份改性硅油中加入8份火山灰和5份海泡石粉，充分混合后于0-5℃静置2h，再加入4份菜籽饼和2份玻璃纤维粉，然后加热至95-100℃保温混合10min，即得物料III；
(4)向物料I中加入物料II和物料III，充分混合后于微波频率2450MHz、功率700W下微波处理10min，然后自然冷却至70-75℃，再加入3份油酸聚氧乙烯酯、10份醋酸丁酯和15份正丁醇，充分混合均匀。
改性硅油的制备：向45份二甲基硅油中加入8份氢化松香和3份巴西棕榈蜡，加热至完全熔化后保温混合10min，并于微波频率2450MHz、功率700W下微波处理10min，再转入室温下静置1h，然后继续微波处理5min，处理结束后趁热加入2份鲸蜡醇和1份纳米钛白粉，充分混合后于超声频率40kHz、功率100W下超声处理30min，待混合物自然冷却至30-35℃后转入0-5℃环境中，静置12h，即得改性硅油。
火山灰的预处理：将40份火山灰加入等量水中，充分混合后送入砂磨机中，砂磨至细度小于10um，再加入10份凹凸棒土和3份纳米氧化锌，充分混合后继续球磨8h，然后将混合物送入喷雾干燥机，所得颗粒最后经粉碎机制成粉末。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (3)

1.一种混凝土浇筑用建筑模板脱模剂，其特征在于，由如下重量份数的原料制成：
改性硅油40-45份、聚氧化丙烯二醇2000 15-20份、C9石油树脂8-12份、火山灰6-10份、海泡石粉5-8份、乙烯-四氟乙烯共聚物5-8份、甲苯二异氰酸酯4-6份、菜籽饼3-5份、油酸聚氧乙烯酯2-3份、纳米氧化铝2-3份、玻璃纤维粉2-3份、三正丁基甲氧基锡1-2份、硫酸化蓖麻油1-2份、醋酸丁酯10-15份、正丁醇10-15份；
所述改性硅油的制备方法为：向40-50份二甲基硅油中加入6-9份氢化松香和3-5份巴西棕榈蜡，加热至完全熔化后保温混合10min，并于微波频率2450MHz、功率700W下微波处理10min，再转入室温下静置1h，然后继续微波处理5min，处理结束后趁热加入2-3份鲸蜡醇和1-2份纳米钛白粉，充分混合后于超声频率40kHz、功率100W下超声处理30min，待混合物自然冷却至30-35℃后转入0-5℃环境中，静置12h，即得改性硅油。
2.根据权利要求1所述的混凝土浇筑用建筑模板脱模剂，其特征在于，其制备方法包括如下步骤：
(1)将聚氧化丙烯二醇2000于100-105℃下干燥3h，干燥结束后自然冷却至60-65℃加入甲苯二异氰酸酯和三正丁基甲氧基锡，保温搅拌30min后继续加热至70-75℃，并于70-75℃保温搅拌15min，然后再继续加热至80-85℃保温搅拌2h，即得物料I；
(2)向C9石油树脂中加入乙烯-四氟乙烯共聚物、纳米氧化铝和硫酸化蓖麻油，充分混合后加热至100-105℃保温混合10min，再自然冷却至65-70℃，然后继续加热至135-140℃保温混合10min，即得物料II；
(3)向改性硅油中加入火山灰和海泡石粉，充分混合后于0-5℃静置2h，再加入菜籽饼和玻璃纤维粉，然后加热至95-100℃保温混合10min，即得物料III；
(4)向物料I中加入物料II和物料III，充分混合后于微波频率2450MHz、功率700W下微波处理10min，然后自然冷却至70-75℃，再加入油酸聚氧乙烯酯、醋酸丁酯和正丁醇，充分混合均匀。
3.根据权利要求1或2所述的混凝土浇筑用建筑模板脱模剂，其特征在于，所述火山灰使用前经过预处理，其处理方法为：将30-40份火山灰加入等量水中，充分混合后送入砂磨机中，砂磨至细度小于10um，再加入10-15份凹凸棒土和2-4份纳米氧化锌，充分混合后继续球磨5-8h，然后将混合物送入喷雾干燥机，所得颗粒最后经粉碎机制成粉末。
CN201610559547.4A 2016-07-15 2016-07-15 一种混凝土浇筑用建筑模板脱模剂 Withdrawn CN106190491A (zh)