CN104672896B - 一种耐高温型断路器外壳 - Google Patents
一种耐高温型断路器外壳 Download PDFInfo
- Publication number
- CN104672896B CN104672896B CN201510066950.9A CN201510066950A CN104672896B CN 104672896 B CN104672896 B CN 104672896B CN 201510066950 A CN201510066950 A CN 201510066950A CN 104672896 B CN104672896 B CN 104672896B
- Authority
- CN
- China
- Prior art keywords
- parts
- circuit breaker
- high temperature
- temperature resistant
- resistant type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种耐高温型断路器外壳，该外壳材料包括以下重量份组分：聚酰胺PA66：195～205份，热稳定剂：6～7份，玻璃纤维：30～35份，金红石型钛白粉：1.3～1.8份，增白剂：0.3～0.5份，硅微粉：0.5～1份，硼酸：1～3份，聚乙烯蜡：0.3～0.5份，群青：0.005～0.01，与传统的断路器外壳相比具备更好的耐高温性及阻燃绝缘效果。
Description
技术领域
本发明涉及一种耐高温型断路器外壳。
技术背景
外壳式断路器一般作配电用，亦可为保护电动机之用。在正常情况下，断路器可分别作为线路的不频繁转换及电动机的不频繁起动之用，配电用断路器，在配电网络中用来分配电能且作为线路及电源设备的过载、短路和欠电压保护，所以断路器作为最后一道防线，在高温等恶劣环境条件下，其稳定性尤为重要。
发明内容
本发明解决的技术问题提供了一种耐高温型断路器外壳，与传统的断路器外壳相比具备更好的耐高温性及阻燃绝缘效果。
为解决上述技术问题，本发明采用如下技术方案：一种耐高温型断路器外壳，该外壳材料包括以下重量组分：聚酰胺PA66：195～205份，热稳定剂：6～7份，玻璃纤维：30～35份，金红石型钛白粉：1.3～1.8份，增白剂：0.3～0.5份，硅微粉：0.5～1份，硼酸：1～3份，聚乙烯蜡：0.3～0.5份，群青：0.005～0.01份。
优选的，该外壳壳体中的材料重量组分如下：聚酰胺PA66：200份，热稳定剂：6份，玻璃纤维：30份，金红石型钛白粉：1.5份，增白剂：0.3份，硅微粉：0.8份，硼酸：1份，聚乙烯蜡：0.4份，群青：0.008份。
优选的，所述的硅微粉为纯度99.7％的电工级硅微粉。
优选的，所述的热稳定剂为钙锌复合稳定剂。
优选的，所述的外壳材料中还包括抗氧剂，抗氧剂的重量组分为0.5～1份。
优选的，所述的抗氧剂由主抗氧化剂乳液和辅助抗氧剂乳液组成，主抗氧化剂乳液和辅助抗氧剂乳液在抗氧剂中的重量比例为65％和35％。
优选的，所述的外壳材料中还包括增塑剂，增塑剂的重量组分为1份。
优选的，所述的外壳材料中还包括润滑剂，润滑剂的重量组分为3份。
优选的，所述的润滑剂为矿物润滑剂、动物润滑剂、植物润滑剂中的其中一种。
本发明中的有益效果为：与传统的断路器外壳相比，添加了金红石型钛白粉的金属粉末具备很好的耐高温性，另外本方案中增加了玻璃纤维使得外壳更具备良好的耐腐蚀性，长期工作不易老化，另外断路器外壳作为电路工作器件，其阻燃绝缘效果也不容忽视，所以本方案中特意增加了硅微粉以增加外壳的阻燃绝缘效果，因为金红石型钛白粉为金属粉末，硅微粉可以有效减弱金红石型钛白粉在本方案中的导电性能，另外的增白剂、聚乙烯蜡等添加剂都能使外壳表面更加光滑，表面光泽度更好。
具体实施方式
一种耐高温型断路器外壳，该外壳材料包括以下重量组分：聚酰胺PA66：195～205份，热稳定剂：6～7份，玻璃纤维：30～35份，金红石型钛白粉：1.3～1.8份，增白剂：0.3～0.5份，硅微粉：0.5～1份，硼酸：1～3份，聚乙烯蜡：0.3～0.5份，群青：0.005～0.01份。
本发明的其中一种实施例：该外壳壳体中的材料重量组分如下：聚酰胺PA66：200份，热稳定剂：6份，玻璃纤维：30份，金红石型钛白粉：1.5份，增白剂：0.3份，硅微粉：0.8份，硼酸：1份，聚乙烯蜡：0.4份，群青：0.008份。
其中，金红石型钛白粉为金属粉末，可以增加外壳的耐高温性，玻璃纤维则具有耐腐蚀性能好、介电性能好、热性能良好的优点，可以有效提高断路器外壳的使用寿命，硅微粉是由纯净经先进的超细研磨工艺加工而成，是用途极为广泛的无机非金属材料，具有介电性能优异、热膨胀系数低、导热系数高、悬浮性能好等优点，是一种很好的阻燃材料，作为优选，所述的硅微粉为纯度99.7％的电工级硅微粉，电工级硅微粉是很好的绝缘浇注材料，而且因为本方案中添加了一定的金属粉末，利用硅微粉可以很好阻隔这一部分金属粉末的导电性能；而硼酸在本方案中的作用主要是作为一种添加剂使用，首先可以起到各个粉末之间的粘结作用，主要是聚酰胺、金红石型钛白、硅微粉之间的粘结，使得各组分之间混合地更均匀、稳定，其次硼酸本身也具备一定的阻燃效果，配合硅微粉可以将外壳的阻燃效果进一步提升；而另外的增白剂、聚乙烯蜡等添加剂都能使外壳表面更加光滑，表面光泽度更好，尤其是聚乙烯蜡，其本身也是白色颗粒粉末，与增白剂一起能起到类似色母的作用，而且聚乙烯蜡还具备润滑效果，不仅能使各组分之间混合更好，也能使外壳表面更加光滑。
作为优选，所述的热稳定剂为钙锌复合稳定剂，使得外壳化学性能更为稳定。
优选的，所述的外壳材料中还包括抗氧剂，抗氧剂的重量组分为0.5～1份，抗氧剂的作用是防止外壳在空气中老化，可以起到提高使用寿命的效果，因为本方案相对于传统的塑料混合了一定量的金属粉末，抗氧化性也尤为必要，本方案中所述的抗氧剂由主抗氧化剂乳液和辅助抗氧剂乳液组成，主抗氧化剂乳液和辅助抗氧剂乳液在抗氧剂中的的重量比例为65％和35％。
优选的，所述的外壳材料中还包括增塑剂，增塑剂的重量组分为1份，增塑剂可以增加塑料材质的韧性，在本方案中同样为了增加外壳的使用寿命，防止其老化、脆化。
优选的，所述的外壳材料中还包括润滑剂，润滑剂的重量组分为3份。润滑剂在注塑料材料中作用也比较明显，尤其是对于减少塑料与金属之间的摩擦特别有效果，因为本方案中一般都会与一些金属闸刀等配合使用，所以外壳本身的润滑性也非常重要，优选的，所述的润滑剂为矿物润滑剂、动物润滑剂、植物润滑剂中的其中一种。
本发明通过注塑方式制备断路器外壳，具体方法为：将本发明的各组分按配比混合均匀后，倒入注塑机进料口，控制注塑机加热温度蠕变变化率为0.06％/次，逐渐加温至240℃以上，各组份熔化，使注塑机出料至注塑模后，常温冷却成型，本方案制作的外壳的性能，其热变形温度(1.8MPa)在230℃以上，简支梁缺口冲击1.85KJ/m2以上，断裂应力承受最大载荷：65/43Mpa。
Claims (9)
1.一种耐高温型断路器外壳，其特征在于：该外壳材料包括以下重量组分：
聚酰胺PA66：195～205份，热稳定剂：6～7份，玻璃纤维：30～35份，金红石型钛白粉：1.3～1.8份，增白剂：0.3～0.5份，硅微粉：0.5～1份，硼酸：1～3份，聚乙烯蜡：0.3～0.5份，群青：0.005～0.01份。
2.根据权利要求1所述的一种耐高温型断路器外壳，其特征在于：该外壳壳体中的材料重量组分如下：
聚酰胺PA66：200份，热稳定剂：6份，玻璃纤维：30份，金红石型钛白粉：1.5份，增白剂：0.3份，硅微粉：0.8份，硼酸：1份，聚乙烯蜡：0.4份，群青：0.008份。
3.根据权利要求1所述的一种耐高温型断路器外壳，其特征在于：所述的硅微粉为纯度99.7％的电工级硅微粉。
4.根据权利要求1所述的一种耐高温型断路器外壳，其特征在于：所述的热稳定剂为钙锌复合稳定剂。
5.根据权利要求1所述的一种耐高温型断路器外壳，其特征在于：所述的外壳材料中还包括抗氧剂，抗氧剂的重量组分为0.5～1份。
6.根据权利要求5所述的一种耐高温型断路器外壳，其特征在于：所述的抗氧剂由主抗氧化剂乳液和辅助抗氧剂乳液组成，主抗氧化剂乳液和辅助抗氧剂乳液在抗氧剂中的重量比例为65％和35％。
7.根据权利要求1所述的一种耐高温型断路器外壳，其特征在于：所述的外壳材料中还包括增塑剂，增塑剂的重量组分为1份。
8.根据权利要求1所述的一种耐高温型断路器外壳，其特征在于：所述的外壳材料中还包括润滑剂，润滑剂的重量组分为3份。
9.根据权利要求8所述的一种耐高温型断路器外壳，其特征在于：所述的润滑剂为矿物润滑剂、动物润滑剂、植物润滑剂中的其中一种。