CN106122305A - 一种耐腐蚀离合器面片总成及制造方法 - Google Patents
一种耐腐蚀离合器面片总成及制造方法 Download PDFInfo
- Publication number
- CN106122305A CN106122305A CN201610562624.1A CN201610562624A CN106122305A CN 106122305 A CN106122305 A CN 106122305A CN 201610562624 A CN201610562624 A CN 201610562624A CN 106122305 A CN106122305 A CN 106122305A
- Authority
- CN
- China
- Prior art keywords
- fibre
- dough sheet
- steel disc
- compound fabric
- wide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐腐蚀离合器面片总成及制造方法,包括钢片,钢片正反面硫化连接面片,采用FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成的高强度复合线,再将此线织成100Kg、1米宽的复合布,复合布涂布涂料,风干至不粘手为止,复合布剪切成10mm宽的长布料,长布料绕制的圆盘状结构的面片;将圆状面片料放入下模具内,放入钢片,钢片正反面涂刷FH11‑128胶浆;在钢片上再放入圆状面片料,压合上模具;电热加温开启压机,硫化成型得无铆接试汽车离合器面片。
Description
技术领域
本发明涉及离合器技术,具体说是一种耐腐蚀离合器面片总成及制造方法。
背景技术
传统的汽车离合器面片采用铆接式,面片铆接在钢片上,费事费工,铆钉铆接影响面片使用寿命和使用安全。现有的无铆接式结构,如专利号为201210157147.2公开的一种耐腐蚀离合器面片,采用多种材料无序混合后与钢片硫化连接,内部结构不稳定,影响使用性能。另外,面片长期处于摩擦、高温状态下,一旦使用环境恶劣,极易造成面片表面腐蚀,影响摩擦性能。
发明内容
针对现有技术中无铆接式结构的上述不足,本发明提供了一种工艺简单,适于汽车离合器面片制造使用,能有效确保内部结构稳定和表面抗腐蚀能力,提高使用性能的耐腐蚀离合器面片总成及制造方法。
本发明采用的技术方案是:一种耐腐蚀离合器面片总成,包括钢片,钢片正反面硫化连接面片,其特征在于:采用FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布,复合布涂布涂料,风干至不粘手为止,复合布剪切成10mm宽的长布料,长布料绕制的圆盘状结构的面片。
所述涂料按质量分数配比:耐高温472℃纳米液体树脂80-90份、异佛尔酮二异氰酸酯10-20份、异丙醇10-15份、马来酸酐接枝EVA5-8份 、白刚玉粉3-5份、氟硅酸钠2-3份、二硫化钼1-1.5份、氧化铝空心球2-3份、三氧化钒2-3份、硅酸锆1-2份,依次混合搅拌的涂料。
一种耐腐蚀离合器面片总成制造方法,包括以下步骤:
a.选取原料:FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布;
b.将上述1米宽复合布涂布上述权利要求2的涂料,风干至不粘手为止;
c.用剪切机将1米宽复合布剪切成10mm宽的每片面片用料,采用缠绕机绕成圆状面片料;
d.将圆状面片料放入下模具内,放入钢片,钢片正反面涂刷FH11-128胶浆;
e.在钢片上再放入圆状面片料,压合上模具;
f.电热加温至175-180℃,开启压机,压力至30-35MPa,保温、保压40-45分钟出模,硫化成型得无铆接试汽车离合器面片。
本发明的耐腐蚀离合器面片总成不损坏发动机飞轮面和压盘面,面片无需钻孔,无需铆接,使用寿命长,其制作工艺简单,有序制备复合线、复合布、绕制线条和圆状面片料,有效确保其内部结构稳定,有利于提高面片总成的使用安全性能和稳定性,延长其使用寿命。采用耐高温472℃纳米液体树脂、异佛尔酮二异氰酸酯、马来酸酐接枝EVA 、白刚玉粉、氟硅酸钠、二硫化钼、聚四氟乙烯蜡共混制备耐磨耐高温涂料,有利于提高面片结构的摩擦性能和高温下的抗腐蚀能力,延长使用寿命。
具体实施方式
以下对本发明作进一步说明。
实施例一
一种耐腐蚀离合器面片总成,包括钢片,钢片正反面硫化连接面片,采用FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布,复合布涂布涂料,风干至不粘手为止,复合布剪切成10mm宽的长布料,长布料绕制的圆盘状结构的面片。
所述涂料按质量分数配比:耐高温472℃纳米液体树脂80份、异佛尔酮二异氰酸酯10份、异丙醇10份、马来酸酐接枝EVA5份 、白刚玉粉3份、氟硅酸钠2份、二硫化钼1份、氧化铝空心球2份、三氧化钒2份、硅酸锆1份,依次混合搅拌的涂料。
一种耐腐蚀离合器面片总成制造方法,包括以下步骤:
a.选取原料:FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布;
b.将上述1米宽复合布涂布上述权利要求2的涂料,风干至不粘手为止;
c.用剪切机将1米宽复合布剪切成10mm宽的每片面片用料,采用缠绕机绕成圆状面片料;
d.将圆状面片料放入下模具内,放入钢片,钢片正反面涂刷FH11-128胶浆;
e.在钢片上再放入圆状面片料,压合上模具;
f.电热加温至175℃,开启压机,压力至30MPa,保温、保压40分钟出模,硫化成型得无铆接试汽车离合器面片。
实施例二
一种耐腐蚀离合器面片总成,包括钢片,钢片正反面硫化连接面片,采用FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布,复合布涂布涂料,风干至不粘手为止,复合布剪切成10mm宽的长布料,长布料绕制的圆盘状结构的面片。
所述涂料按质量分数配比:耐高温472℃纳米液体树脂90份、异佛尔酮二异氰酸酯20份、异丙醇15份、马来酸酐接枝EVA8份 、白刚玉粉5份、氟硅酸钠3份、二硫化钼1.5份、氧化铝空心球3份、三氧化钒3份、硅酸锆2份,依次混合搅拌的涂料。
一种耐腐蚀离合器面片总成制造方法,包括以下步骤:
g.选取原料:FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布;
a.将上述1米宽复合布涂布上述权利要求2的涂料,风干至不粘手为止;
b.用剪切机将1米宽复合布剪切成10mm宽的每片面片用料,采用缠绕机绕成圆状面片料;
c.将圆状面片料放入下模具内,放入钢片,钢片正反面涂刷FH11-128胶浆;
d.在钢片上再放入圆状面片料,压合上模具;
e.电热加温至180℃,开启压机,压力至35MPa,保温、保压45分钟出模,硫化成型得无铆接试汽车离合器面片。
实施例三
一种耐腐蚀离合器面片总成,包括钢片,钢片正反面硫化连接面片,采用FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布,复合布涂布涂料,风干至不粘手为止,复合布剪切成10mm宽的长布料,长布料绕制的圆盘状结构的面片。
所述涂料按质量分数配比:耐高温472℃纳米液体树脂85份、异佛尔酮二异氰酸酯15份、异丙醇12份、马来酸酐接枝EVA6份 、白刚玉粉4份、氟硅酸钠2.5份、二硫化钼1.2份、氧化铝空心球2.3份、三氧化钒2.5份、硅酸锆1.5份,依次混合搅拌的涂料。
一种耐腐蚀离合器面片总成制造方法,包括以下步骤:
a.选取原料:FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布;
b.将上述1米宽复合布涂布上述权利要求2的涂料,风干至不粘手为止;
c.用剪切机将1米宽复合布剪切成10mm宽的每片面片用料,采用缠绕机绕成圆状面片料;
d.将圆状面片料放入下模具内,放入钢片,钢片正反面涂刷FH11-128胶浆;
e.在钢片上再放入圆状面片料,压合上模具;
电热加温至178℃,开启压机,压力至32MPa,保温、保压44分钟出模,硫化成型得无铆接试汽车离合器面片。
Claims (3)
1.一种耐腐蚀离合器面片总成,包括钢片,钢片正反面硫化连接面片,其特征在于:采用FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布,复合布涂布涂料,风干至不粘手为止,复合布剪切成10mm宽的长布料,长布料绕制的圆盘状结构的面片。
2.根据权利要求1所述的一种耐腐蚀离合器面片总成,其特征在于:所述涂料按质量分数配比:耐高温472℃纳米液体树脂80-90份、异佛尔酮二异氰酸酯10-20份、异丙醇10-15份、马来酸酐接枝EVA5-8份 、白刚玉粉3-5份、氟硅酸钠2-3份、二硫化钼1-1.5份、氧化铝空心球2-3份、三氧化钒2-3份、硅酸锆1-2份,依次混合搅拌的涂料。
3.一种耐腐蚀离合器面片总成制造方法,包括以下步骤:
选取原料:FKF复合矿物纤维22Kg、陶瓷纤维8Kg、芳香族聚酰胺纤维15Kg、喷胶硅酸铝纤维15Kg、不锈钢纤维5Kg、海泡石纤维20Kg和玻璃纤维15Kg纺织成Ø4mm的高强度复合线,再将此线织成100Kg、1米宽的复合布;
将上述1米宽复合布涂布上述权利要求2的涂料,风干至不粘手为止;
用剪切机将1米宽复合布剪切成10mm宽的每片面片用料,采用缠绕机绕成圆状面片料;
将圆状面片料放入下模具内,放入钢片,钢片正反面涂刷FH11-128胶浆;
在钢片上再放入圆状面片料,压合上模具;
电热加温至175-180℃,开启压机,压力至30-35MPa,保温、保压40-45分钟出模,硫化成型得无铆接试汽车离合器面片。