CN106084270A - 一种橡胶胶片隔离剂 - Google Patents

一种橡胶胶片隔离剂 Download PDF

Info

Publication number
CN106084270A
CN106084270A CN201610474466.4A CN201610474466A CN106084270A CN 106084270 A CN106084270 A CN 106084270A CN 201610474466 A CN201610474466 A CN 201610474466A CN 106084270 A CN106084270 A CN 106084270A
Authority
CN
China
Prior art keywords
rubber film
isolating agent
film isolating
parts
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610474466.4A
Other languages
English (en)
Inventor
周松涛
顾建荣
刘天成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG XINBANG CHEMICAL CO Ltd
Original Assignee
NANTONG XINBANG CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG XINBANG CHEMICAL CO Ltd filed Critical NANTONG XINBANG CHEMICAL CO Ltd
Priority to CN201610474466.4A priority Critical patent/CN106084270A/zh
Publication of CN106084270A publication Critical patent/CN106084270A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种橡胶胶片隔离剂，它是由按重量份计的以下原料构成：硬脂酸钙 10‑40份，无机填充物20‑50份，表面活性剂5‑20份，无机凝胶 1‑10份，羟甲基纤维素 1‑10份，消泡剂 1‑10份，外观为白色或类白色细微粉末，PH值（2%水分散液）8‑10，含固量（用减量法在低型称量瓶内取2g样品(精确至0.01g)，将称量瓶敞口放入105℃烘箱内烘2h,取出至于干燥器中冷却30min后称量。剩余物的百分比）大于80%，分散性 在水中以2‑6%浓度，在10‑90℃的冷水或热水中分散性良好，且不沉降在水中溶解或稀释后不会出现沉淀现象的、可避免在橡胶胶片表面留下结块而藉以保障后道的复合顺利进行的、能在胶片表面表现出均匀覆盖而既有助于确保不粘连，又有利于提高胶片的冷却、干燥速度的橡胶胶片隔离剂。

Description

一种橡胶胶片隔离剂
技术领域
本发明涉及一种橡胶胶片隔离剂，用于在炼胶过程中对橡胶胶片与胶片之间起隔离、冷却作用。
背景技术
目前，市售的橡胶胶片隔离剂主要存在以下欠缺：一是当隔离剂在溶解稀释后容易产生沉淀，起不到应有的隔离效果；二是在橡胶胶片表面产生结斑或称结块，对后道工艺的复合造成影响，因为结块部位的复合效果甚差；三是在橡胶胶片表面无法表现出覆盖均匀的效果，导致隔离不稳定、效果低下，乃至影响冷却、干燥速度，干燥时间通常在40min以上。
发明内容
本发明的任务是要提供一种在水中溶解或稀释后不会出现沉淀现象的、可避免在橡胶胶片表面留下结块而藉以保障后道的复合顺利进行的、能在胶片表面表现出均匀覆盖而既有助于确保不粘连，又有利于提高胶片的冷却、干燥速度的橡胶胶片隔离剂。
本发明的任务是这样来完成的，一种橡胶胶片隔离剂，它是由按重量份计的以下原料构成：
硬脂酸钙 10-40份
无机填充物 20-50份
表面活性剂 5-20份
无机凝胶 1-10份
羟甲基纤维素 1-10份
消泡剂 1-10份。
优选的，所述硬脂酸钙为白色细微粉末状工业硬脂酸钙。
优选的，所述无机填充物为滑石粉、陶土、高岭土、绢英粉、稀土尾矿粉、轻质碳酸钙中的任意一种或两种或两种以上相混合的混合物。
优选的，所述无机凝胶为膨润土类人工合成或天然非金属矿物质主要成分硅酸镁锂和硅酸镁钠。
优选的，所述羟甲基纤维素为高粘度羟甲基纤维素粘度为1200-3000cps。
优选的，所述表面活性剂为脂肪醇聚氧乙烯醚类非离子表面活性剂。
优选的，所述的表面活性剂消泡剂为窗体顶端。
优选的，所述消泡剂为有机硅类消泡剂如聚二甲基硅氧烷。
具体实施
一种橡胶胶片隔离剂，它是由按重量份计的以下原料构成：硬脂酸钙 10-40份，无机填充物20-50份，表面活性剂5-20份，无机凝胶 1-10份，羟甲基纤维素 1-10份，消泡剂 1-10份，硬脂酸钙为白色细微粉末状工业硬脂酸钙，无机填充物为滑石粉、陶土、高岭土、绢英粉、稀土尾矿粉、轻质碳酸钙中的任意一种或两种或两种以上相混合的混合物，所述无机凝胶为膨润土类人工合成或天然非金属矿物质主要成分硅酸镁锂和硅酸镁钠，羟甲基纤维素为高粘度羟甲基纤维素粘度为1200-3000cps，所述的表面活性剂为脂肪醇聚氧乙烯醚类非离子表面活性剂，所述的消泡剂为有机硅类消泡剂如聚二甲基硅氧烷,第一步，在带搅拌反应釜中加入水10份，AEO-3 10份，二甲基硅油5份，羟甲基纤维素5份搅拌均匀备用,第二步，在捏合机中搅拌下加入膨润土5份，硬脂酸钙35份，轻质碳酸钙30份，再将上述备用液倒入，搅拌均匀。放料包装。此胶片隔离剂在水推荐用量为4-5%的重量百分比浓度。

Claims (9)

1.一种橡胶胶片隔离剂，其特征在于它是由按重量份计的以下原料构成：
硬脂酸钙 10-40份
无机填充物 20-50份
表面活性剂 5-20份
无机凝胶 1-10份
羟甲基纤维素 1-10份
消泡剂 1-10份。
2.根据权利要求1所述的一种橡胶胶片隔离剂，其特征在于:所述的硬脂酸钙为白色细微粉末状工业硬脂酸钙。
3.根据权利要求2所述的一种橡胶胶片隔离剂，其特征在于:所述的无机填充物为滑石粉、陶土、高岭土、绢英粉、稀土尾矿粉、轻质碳酸钙中的任意一种或两种或两种以上相混合的混合物。
4.根据权利要求1所述的一种橡胶胶片隔离剂，其特征在于:所述的无机凝胶为膨润土类人工合成或天然非金属矿物质主要成分硅酸镁锂和硅酸镁钠。
5.根据权利要求1所述的一种橡胶胶片隔离剂，其特征在于:所述的羟甲基纤维素为高粘度羟甲基纤维素粘度为1200-3000cps。
6.根据权利要求1所述的一种橡胶胶片隔离剂，其特征在于:所述的表面活性剂为脂肪醇聚氧乙烯醚类非离子表面活性剂。
7.根据权利要求1所述的一种橡胶胶片隔离剂，其特征在于：所述的表面活性剂泡剂为窗体顶端。
8.根据权利要求1所述的一种橡胶胶片隔离剂，其特征在于:所述的消泡剂为有机硅类消泡剂如聚二甲基硅氧烷。
9.根据权利要求3所述的橡胶胶片隔离剂，其特征在于所述的相混合的混合比为任意比例混合。
CN201610474466.4A 2016-06-27 2016-06-27 一种橡胶胶片隔离剂 Pending CN106084270A (zh)