CN106082840A - A kind of inorganic powder decoration diatom ooze - Google Patents
A kind of inorganic powder decoration diatom ooze Download PDFInfo
- Publication number
- CN106082840A CN106082840A CN201610396139.1A CN201610396139A CN106082840A CN 106082840 A CN106082840 A CN 106082840A CN 201610396139 A CN201610396139 A CN 201610396139A CN 106082840 A CN106082840 A CN 106082840A
- Authority
- CN
- China
- Prior art keywords
- grams
- gram
- inorganic powder
- diatom ooze
- construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe present invention is about a kind of inorganic powder decoration diatom ooze，Including kieselguhr 800 mesh: 200 250 grams，Pulvis Talci 325 mesh: 50 60 grams，Inorganic adhesive powder: 40 50 grams，White cement 325#:200 250 grams，Cellulose 45 grams，Anion powder: 8 10 grams，Nano titanium oxide: 58 grams，Lignocellulose: 56 grams，Triple superphosphate 200 mesh: 180 200 grams，Dry powder defoamer: 12 grams，Dry powder retarder: 34 grams，Titanium dioxide: 8 10 grams，Mica powder: 8 10 grams，Inorganic bentonite: 8 10 grams，Bamboo charcoal powder: 10 20 grams，2 imidazolidinones: 10 20 grams，Antifungus agent: 35 grams，Snow Flower White 120 180 mesh: 200 250 grams，Nano zinc dioxide impact-resistant: 58 grams，Multifunction polypowder: 20 30 grams，Above-mentioned material is sufficiently mixed final vacuum and packs into bag.The present invention not only can accomplish 0 formaldehyde, can also purifying formaldehyde and absorption bring because of finishing pollution formaldehyde, benzene, radon, ammonia, the harmful gas such as TVOC, its plasticity is the strongest, the thick texture texture such as various pattern, sandstone, mortar can be made by hand, make the metope after construction without bubbling, without coming off, not skull patch, be difficult to the phenomenons such as armpit color, good decorating effect, functional by force, reach more than 20 years service life.
Description
Technical field
The present invention relates to a kind of inorganic powder decoration diatom ooze.
Background technology
All the time, wall surfacing is all the emphasis of house fitting, and this is not only because metope occupies indoor the most most
Number space, directly affects the style of finishing, especially because the quality of metope directly affects the environment in room, traditional household
Finishing is many based on intention, and existing simple paint can not meet the demand of a lot of owner, fits up the most attractive in appearance not all right, also
Wanting health, and puzzlement maximum in fitting up at present is exactly the pollution of formaldehyde, in the most a lot of finishing materials, the index of formaldehyde is very big,
Sometimes in order to disperse formaldehyde, for a long time can move in just renovated new house has but been wanted, it the soonest will be after 3-4 month
Just can move in.
Diatom ooze is one the most booming inorganic environment-friendly wall material, owing to having the outstanding feature of environmental protection and dress concurrently simultaneously
Decorations property, receives the welcome of numerous family.Therefore, on this basis, all exist above-mentioned for finishing material in the market
The deficiency of problem, applicant researches and develops a kind of structure utilizing this microporous molecular sieve of diatom ooze and has the strongest absorbability, its
Not only can accomplish 0 formaldehyde, moreover it is possible to accomplish purifying formaldehyde, the adsorbable formaldehyde that brings because of finishing pollution, benzene, radon, ammonia, TVOC etc. have
Evil gas, to reach the purpose purifying the air of a room and eliminating the unusual smell；It can absorb and discharge again hydrone and reach conditioning chamber endogenous dampness
The function of degree；Meanwhile, " air vitamin " anion that release is the most useful to human body, of great advantage to the health of human body, and
Diatom ooze adds water and will present the state of mud after stirring, and its plasticity is very strong, can make various texture, pattern by hand,
Not only can make the smooth sense of emulsion paint, the technique that can make again wallpaper flower is come, it is also possible to make the thick matter of sandstone, mortar
Sense texture, use the metope after present invention construction without bubbling, without coming off, not skull patch, be difficult to the phenomenons such as armpit color, it has tension
Stretch, Resisting fractre, noise resistance, acid and alkali-resistance, resistance to water, temperature-change resistance, abrasion resistance, stain resistance, efflorescence ageing-resistant, anti-and preapre for an unfavorable turn of events
The function of color, good decorating effect, functional service life is long by force, and its service life reaches the inorganic powder decoration of more than 20 years
Diatom ooze really belongs to necessary.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of structure utilizing this microporous molecular sieve of diatom ooze to be had very
Strong absorbability, it not only can accomplish 0 formaldehyde, moreover it is possible to accomplishes purifying formaldehyde, adsorbable bring because of finishing pollution formaldehyde,
The harmful gass such as benzene, radon, ammonia, TVOC, to reach the purpose purifying the air of a room and eliminating the unusual smell；It can absorb again and discharge moisture
Son reaches the function of conditioning chamber humidity；Meanwhile, " air vitamin " anion that release is the most useful to human body, to human body
Health is of great advantage, and diatom ooze adds water and will present the state of mud after stirring, and its plasticity is very strong, can make by hand
Various textures, pattern, not only can make the smooth sense of emulsion paint, and the technique that can make again wallpaper flower is come, it is also possible to make
Sandstone, the thick texture texture of mortar, use the metope after present invention construction without bubbling, without coming off, not skull patch, to be difficult to armpit color etc. existing
As, its have stretch-proof, Resisting fractre, noise resistance, acid and alkali-resistance, resistance to water, temperature-change resistance, abrasion resistance, stain resistance, resistance to always
Change, anti-efflorescence and the function of Anti-tarnishing, good decorating effect, functional service life is long by force, and its service life reaches more than 20 years
Inorganic powder decoration diatom ooze.The present invention is achieved through the following technical solutions:
A kind of inorganic powder decoration diatom ooze, including kieselguhr 800 mesh: 200-250 gram, Pulvis Talci 325 mesh: 50-60 gram, inorganic
Rubber powder: 40-50 gram, white cement 325#:200-250 gram, cellulose 4-5 gram, anion powder: 8-10 gram, nano titanium oxide: 5-
8 grams, lignocellulose: 5-6 gram, triple superphosphate 200 mesh: 180-200 gram, dry powder defoamer: 1-2 gram, dry powder retarder: 3-4 gram, titanium
White lead: 8-10 gram, mica powder: 8-10 gram, inorganic bentonite: 8-10 gram, bamboo charcoal powder: 10-20 gram, 2 imidazolidinones: 10-20 gram,
Antifungus agent: 3-5 gram, Snow Flower White 120-180 mesh: 200-250 gram, Nano zinc dioxide impact-resistant: 5-8 gram, multifunction polypowder: 20-30
Gram, above-mentioned material is sufficiently mixed final vacuum and packs into bag.
Further, this inorganic powder decoration diatom ooze temperature when construction requires to be more than 5 DEG C, relative humidity requirement
For less than 85%.
Further, this inorganic powder decoration diatom ooze construction method: step one, first ensure basal plane smooth, closely knit,
Cleaning, moisture content is less than 10%, and pH value is less than 10, and negative and positive angle and the horizontal flat heavily fortified point of lines are straight.
Step 2, according to construction volume prepare clear water, stirring container in add construction water amount 90% clear water, then fall
The raw material entering above-mentioned formula soaks 5-10 minute, stirs 10-20 minute by electric blender after immersion, and stirring is simultaneously introduced another
The clear water of outer 10%, allows mixture be sufficiently stirred for, fully dissolves, reacts and can start construction after completely uniformly.
The position that step 3, careful covering do not spray, checks that basal plane condition reaches can construct after regulation requires, notes protecting
Card adjusts speed of application in time, it is ensured that exterior wall wet-film thickness is 3, and exterior wall build is 2；Interior wall wet-film thickness is more than
1.2, interior wall build is 0.9.
Step 4, stirred after mixture divide twice and smeared, the thickness that first pass is smeared is 1-2 millimeter, is coated with
Stop 45-55 minute after having smeared, depending on dwell time is according to on-the-spot climatic condition, be advisable so that surface is tack-free；Then right then,
Body of wall carries out smearing second time, and the thickness smeared is 1.5-2 millimeter, receives light with spatula after smearing, and uses tool making figure the most again
Case, pattern Production Time is longer, and partial pattern needs again to receive light in the completed.
Step 5, all over spreading rate should 0.8 1.0/.
Further, raw material is 1:0.8 with the mass ratio of clear water.
Further, the viscosity of cellulose is 100,000.
Further, this inorganic powder decoration diatom ooze is after construction, require negative and positive angle horizontal and vertical error when checking and accepting
Less than 3mm.
Further, this inorganic powder decoration diatom ooze after construction, check and accept time require degree of plainness for wall surface error be less than
2mm。
Further, when air humidity is too high after construction for this inorganic powder decoration diatom ooze, metope table please don't be crumpled
Face；Clean with pellet when using this inorganic powder decoration diatom ooze construction metope rear surface to have floating dust；When this inorganic dry
Powder decoration diatom ooze is time there is spot on surface after construction, it is to avoid uses the wet cloth of band water to clean, rubber should be selected to dip in water and wipe gently
Wipe.
A kind of inorganic powder decoration diatom ooze of the present invention, including kieselguhr 800 mesh: 200-250 gram, Pulvis Talci 325 mesh:
50-60 gram, inorganic adhesive powder: 40-50 gram, white cement 325#:200-250 gram, cellulose 4-5 gram, anion powder: 8-10 gram, receive
Rice titanium dioxide: 5-8 gram, lignocellulose: 5-6 gram, triple superphosphate 200 mesh: 180-200 gram, dry powder defoamer: 1-2 gram, dry powder delays
Solidifying agent: 3-4 gram, titanium dioxide: 8-10 gram, mica powder: 8-10 gram, inorganic bentonite: 8-10 gram, bamboo charcoal powder: 10-20 gram, 2 imidazoles
Alkanone: 10-20 gram, antifungus agent: 3-5 gram, Snow Flower White 120-180 mesh: 200-250 gram, Nano zinc dioxide impact-resistant: 5-8 gram, multi-functional
Polymer powder: 20-30 gram, above-mentioned material is sufficiently mixed final vacuum and packs into bag.The present invention utilizes this microporous molecular sieve of diatom ooze
Structure there is the strongest absorbability, utilize nano titanium oxide and Nano zinc dioxide impact-resistant photocatalyst simultaneously, make this
Bright not only can accomplish 0 formaldehyde, its can also purifying formaldehyde, and adsorbable bring because of finishing pollution formaldehyde, benzene, radon, ammonia, TVOC etc.
Harmful gas, to reach the purpose purifying the air of a room and eliminating the unusual smell；It can absorb and discharge hydrone again and reach in conditioning chamber
The function of humidity；Meanwhile, " air vitamin " anion that release is the most useful to human body, of great advantage to the health of human body,
And diatom ooze adds water and will present the state of mud after stirring, its plasticity is very strong, can make various texture, flower by hand
Color, not only can make the smooth sense of emulsion paint, and the technique that can make again wallpaper flower is come, it is also possible to make sandstone, mortar
Thick texture texture, use the metope after present invention construction without bubbling, without coming off, not skull patch, be difficult to the phenomenons such as armpit color, it has anti-
Stretching, Resisting fractre, noise resistance, acid and alkali-resistance, resistance to water, temperature-change resistance, abrasion resistance, stain resistance, efflorescence ageing-resistant, anti-and anti-
The function of variable color, good decorating effect, functional service life is long by force, and its service life reaches more than 20 years.
Detailed description of the invention
Following example are used for illustrating the present invention, but are not limited to the scope of the present invention.
Experiment one, a kind of inorganic powder decoration diatom ooze, including kieselguhr 800 mesh: 210 grams, Pulvis Talci 325 mesh: 52 grams,
Inorganic adhesive powder: 43 grams, white cement 325#:220 gram, cellulose 4.4 grams, anion powder: 9 grams, nano titanium oxide: 6 grams, wooden
Cellulose: 5.2 grams, triple superphosphate 200 mesh: 190 grams, dry powder defoamer: 1.5 grams, dry powder retarder: 3.5 grams, titanium dioxide: 9 grams, cloud
Female powder: 9 grams, inorganic bentonite: 9 grams, bamboo charcoal powder: 12 grams, 2 imidazolidinones: 13 grams, antifungus agent: 4 grams, Snow Flower White 120-180
Mesh: 210 grams, Nano zinc dioxide impact-resistant: 6 grams, multifunction polypowder: 23 grams, above-mentioned material is sufficiently mixed final vacuum and packs into bag.
Wherein in an embodiment, this inorganic powder decoration diatom ooze temperature when construction is 20 DEG C, and relative humidity is
75%。
Wherein in an embodiment, the construction method of this inorganic powder decoration diatom ooze: step one, first guarantee basal plane are put down
Whole, closely knit, cleaning, moisture content is 9%, and pH value is 8, and negative and positive angle and the horizontal flat heavily fortified point of lines are straight.
Step 2, according to construction volume prepare clear water, stirring container in add construction water amount 90% clear water, then fall
The raw material entering above-mentioned formula soaks 8 minutes, stirs 18 minutes by electric blender after immersion, and stirring is simultaneously introduced other 10%
Clear water, allow mixture be sufficiently stirred for, fully dissolve, react construction after completely uniformly, can be started.
The position that step 3, careful covering do not spray, checks that basal plane condition reaches can construct after regulation requires, notes protecting
Card adjusts speed of application in time, it is ensured that exterior wall wet-film thickness is 3, and exterior wall build is 2；Interior wall wet-film thickness is more than
1.2, interior wall build is 0.9.
Step 4, stirred after mixture divide twice and smeared, the thickness that first pass is smeared is 1.4 millimeters, is coated with
Stop 48 minutes after having smeared, depending on dwell time is according to on-the-spot climatic condition, be advisable so that surface is tack-free；Then, then to wall
Body carries out smearing second time, and the thickness smeared is 1.6 millimeters, receives light with spatula after smearing, and uses instrument pattern-making the most again, figure
Case Production Time is longer, and partial pattern needs again to receive light in the completed.
Step 5, all over spreading rate should 0.85/.
Wherein in an embodiment, raw material is 1:0.8 with the mass ratio of clear water.
Wherein in an embodiment, the viscosity of cellulose is 100,000.
Wherein in an embodiment, this inorganic powder decoration diatom ooze after construction, negative and positive angle horizontal and vertical when checking and accepting
Error is 1.5mm.
Wherein in an embodiment, this inorganic powder decoration diatom ooze after construction, check and accept time degree of plainness for wall surface error
0.5mm。
Wherein in an embodiment, when air humidity is too high after construction for this inorganic powder decoration diatom ooze, please don't rub with the hands
Rub metope surface；Clean with pellet when using this inorganic powder decoration diatom ooze construction metope rear surface to have floating dust；When
This inorganic powder decoration diatom ooze is time there is spot on surface after construction, it is to avoid use the wet cloth of band water to clean, rubber should be selected to dip in
Water wiping gently.
Embodiment two, a kind of inorganic powder decoration diatom ooze, including kieselguhr 800 mesh: 240 grams, Pulvis Talci 325 mesh: 54
Gram, inorganic adhesive powder: 46 grams, white cement 325#:210 gram, cellulose 4.6 grams, anion powder: 8.5 grams, nano titanium oxide: 7
Gram, lignocellulose: 5.4 grams, triple superphosphate 200 mesh: 185 grams, dry powder defoamer: 1.2 grams, dry powder retarder: 3.2 grams, titanium dioxide:
9.5 grams, mica powder: 8.5 grams, inorganic bentonite: 9.5 grams, bamboo charcoal powder: 15 grams, 2 imidazolidinones: 16 grams, antifungus agent: 4.5 grams,
Snow Flower White 120-180 mesh: 235 grams, Nano zinc dioxide impact-resistant: 7 grams, multifunction polypowder: 25 grams, above-mentioned material is true after being sufficiently mixed
Sky is packed into bag.
Wherein in an embodiment, this inorganic powder decoration diatom ooze temperature when construction is 15 DEG C, and relative humidity is
65%。
Wherein in an embodiment, the construction method of this inorganic powder decoration diatom ooze: step one, first guarantee basal plane are put down
Whole, closely knit, cleaning, moisture content is 8%, and pH value is 7, and negative and positive angle and the horizontal flat heavily fortified point of lines are straight.
Step 2, according to construction volume prepare clear water, stirring container in add construction water amount 90% clear water, then fall
The raw material entering above-mentioned formula soaks 6 minutes, stirs 15 minutes by electric blender after immersion, and stirring is simultaneously introduced other 10%
Clear water, allow mixture be sufficiently stirred for, fully dissolve, react construction after completely uniformly, can be started.
The position that step 3, careful covering do not spray, checks that basal plane condition reaches can construct after regulation requires, notes protecting
Card adjusts speed of application in time, it is ensured that exterior wall wet-film thickness is 3, and exterior wall build is 2；Interior wall wet-film thickness is more than
1.2, interior wall build is 0.9.
Step 4, stirred after mixture divide twice and smeared, the thickness that first pass is smeared is 1.5 millimeters, is coated with
Stop 52 minutes after having smeared, depending on dwell time is according to on-the-spot climatic condition, be advisable so that surface is tack-free；Then, then to wall
Body carries out smearing second time, and the thickness smeared is 1.5 millimeters, receives light with spatula after smearing, and uses instrument pattern-making the most again, figure
Case Production Time is longer, and partial pattern needs again to receive light in the completed.
Step 5, all over spreading rate 0.9/.
Wherein in an embodiment, raw material is 1:0.8 with the mass ratio of clear water.
Wherein in an embodiment, the viscosity of cellulose is 100,000.
Wherein in an embodiment, this inorganic powder decoration diatom ooze after construction, negative and positive angle horizontal and vertical when checking and accepting
Error is 1mm.
Wherein in an embodiment, this inorganic powder decoration diatom ooze after construction, check and accept time degree of plainness for wall surface error be
1mm。
Wherein in an embodiment, when air humidity is too high after construction for this inorganic powder decoration diatom ooze, please don't rub with the hands
Rub metope surface；Clean with pellet when using this inorganic powder decoration diatom ooze construction metope rear surface to have floating dust；When
This inorganic powder decoration diatom ooze is time there is spot on surface after construction, it is to avoid use the wet cloth of band water to clean, rubber should be selected to dip in
Water wiping gently.
Embodiment three, a kind of inorganic powder decoration diatom ooze, including kieselguhr 800 mesh: 230 grams, Pulvis Talci 325 mesh: 58
Gram, inorganic adhesive powder: 49 grams, white cement 325#:245 gram, cellulose 4.9 grams, anion powder: 9.5 grams, nano titanium oxide: 7.5
Gram, lignocellulose: 5.8 grams, triple superphosphate 200 mesh: 195 grams, dry powder defoamer: 1.8 grams, dry powder retarder: 3.8 grams, titanium dioxide:
8.5 grams, mica powder: 9.5 grams, inorganic bentonite: 8.5 grams, bamboo charcoal powder: 18 grams, 2 imidazolidinones: 19 grams, antifungus agent: 3.5 grams,
Snow Flower White 120-180 mesh: 245 grams, Nano zinc dioxide impact-resistant: 7.5 grams, multifunction polypowder: 28 grams, after above-mentioned material is sufficiently mixed
Vacuum is packed into bag.
Wherein in an embodiment, this inorganic powder decoration diatom ooze temperature when construction is 23 DEG C, and relative humidity is
55%。
Wherein in an embodiment, the construction method of this inorganic powder decoration diatom ooze: step one, first guarantee basal plane are put down
Whole, closely knit, cleaning, moisture content is 7%, and pH value is 5.5, and negative and positive angle and the horizontal flat heavily fortified point of lines are straight.
Step 2, according to construction volume prepare clear water, stirring container in add construction water amount 90% clear water, then fall
The raw material entering above-mentioned formula soaks 7 minutes, stirs 12 minutes by electric blender after immersion, and stirring is simultaneously introduced other 10%
Clear water, allow mixture be sufficiently stirred for, fully dissolve, react construction after completely uniformly, can be started.
The position that step 3, careful covering do not spray, checks that basal plane condition reaches can construct after regulation requires, notes protecting
Card adjusts speed of application in time, it is ensured that exterior wall wet-film thickness is 3, and exterior wall build is 2；Interior wall wet-film thickness is more than
1.2, interior wall build is 0.9.
Step 4, stirred after mixture divide twice and smeared, the thickness that first pass is smeared is 1.7 millimeters, is coated with
Stop 50 minutes after having smeared, depending on dwell time is according to on-the-spot climatic condition, be advisable so that surface is tack-free；Then, then to wall
Body carries out smearing second time, and the thickness smeared is 1.3 millimeters, receives light with spatula after smearing, and uses instrument pattern-making the most again, figure
Case Production Time is longer, and partial pattern needs again to receive light in the completed.
Step 5, all over spreading rate 0.95/.
Wherein in an embodiment, raw material is 1:0.8 with the mass ratio of clear water.
Wherein in an embodiment, the viscosity of cellulose is 100,000.
Wherein in an embodiment, this inorganic powder decoration diatom ooze after construction, negative and positive angle horizontal and vertical when checking and accepting
Error is 0.5mm.
Wherein in an embodiment, this inorganic powder decoration diatom ooze after construction, check and accept time degree of plainness for wall surface error be
0.5mm。
Wherein in an embodiment, when air humidity is too high after construction for this inorganic powder decoration diatom ooze, please don't rub with the hands
Rub metope surface；Clean with pellet when using this inorganic powder decoration diatom ooze construction metope rear surface to have floating dust；When
This inorganic powder decoration diatom ooze is time there is spot on surface after construction, it is to avoid use the wet cloth of band water to clean, rubber should be selected to dip in
Water wiping gently.
The inorganic powder decoration diatom ooze using experiment one, experiment two, experiment three to make is carried out censorship, experiment
One, experiment two and experiment three detection project and testing result as follows: detection project one: condition in container: powdery, without knot
Block.Detection project two: application property: easily mix homogeneously, constructs accessible.Detection project three: initial dry cracking resistance (6h): without splitting
Stricture of vagina.Surface drying time (h): less than 30min.Detection project four: alkali resistance (48h) and temperature-resistant wet performance: without foaming, flawless, nothing
Substantially variable color.Detection project five: free formaldehyde: do not detect.Detection project six: purifying formaldehyde performance (%): more than 85%.Detection
Project six: mould proof endurance quality: one-level.Above-mentioned detection foundation is JC/T 2177-2013 " diatom ooze decorative wall material ".
A kind of inorganic powder decoration diatom ooze of the present invention, including kieselguhr 800 mesh: 200-250 gram, Pulvis Talci 325 mesh:
50-60 gram, inorganic adhesive powder: 40-50 gram, white cement 325#:200-250 gram, cellulose 4-5 gram, anion powder: 8-10 gram, receive
Rice titanium dioxide: 5-8 gram, lignocellulose: 5-6 gram, triple superphosphate 200 mesh: 180-200 gram, dry powder defoamer: 1-2 gram, dry powder delays
Solidifying agent: 3-4 gram, titanium dioxide: 8-10 gram, mica powder: 8-10 gram, inorganic bentonite: 8-10 gram, bamboo charcoal powder: 10-20 gram, 2 imidazoles
Alkanone: 10-20 gram, antifungus agent: 3-5 gram, Snow Flower White 120-180 mesh: 200-250 gram, Nano zinc dioxide impact-resistant: 5-8 gram, multi-functional
Polymer powder: 20-30 gram, above-mentioned material is sufficiently mixed final vacuum and packs into bag.The present invention utilizes this microporous molecular sieve of diatom ooze
Structure there is the strongest absorbability, utilize nano titanium oxide and Nano zinc dioxide impact-resistant photocatalyst simultaneously, make this
Bright not only can accomplish 0 formaldehyde, its can also purifying formaldehyde, and adsorbable bring because of finishing pollution formaldehyde, benzene, radon, ammonia, TVOC etc.
Harmful gas, to reach the purpose purifying the air of a room and eliminating the unusual smell；It can absorb and discharge hydrone again and reach in conditioning chamber
The function of humidity；Meanwhile, " air vitamin " anion that release is the most useful to human body, of great advantage to the health of human body,
And diatom ooze adds water and will present the state of mud after stirring, its plasticity is very strong, can make various texture, flower by hand
Color, not only can make the smooth sense of emulsion paint, and the technique that can make again wallpaper flower is come, it is also possible to make sandstone, mortar
Thick texture texture, use the metope after present invention construction without bubbling, without coming off, not skull patch, be difficult to the phenomenons such as armpit color, it has anti-
Stretching, Resisting fractre, noise resistance, acid and alkali-resistance, resistance to water, temperature-change resistance, abrasion resistance, stain resistance, efflorescence ageing-resistant, anti-and anti-
The function of variable color, good decorating effect, functional service life is long by force, and its service life reaches more than 20 years.
The present invention is not limited to above-mentioned preferred forms, anyone draw under the enlightenment of the present invention other any with
Product as the present invention is same or like, within all falling within protection scope of the present invention.
Claims (8)
1. inorganic powder decoration diatom ooze, it is characterised in that: include kieselguhr 800 mesh: 200-250 gram, Pulvis Talci 325
Mesh: 50-60 gram, inorganic adhesive powder: 40-50 gram, white cement 325#:200-250 gram, cellulose 4-5 gram, anion powder: 8-10 gram,
Nano titanium oxide: 5-8 gram, lignocellulose: 5-6 gram, triple superphosphate 200 mesh: 180-200 gram, dry powder defoamer: 1-2 gram, dry powder
Retarder: 3-4 gram, titanium dioxide: 8-10 gram, mica powder: 8-10 gram, inorganic bentonite: 8-10 gram, bamboo charcoal powder: 10-20 gram, 2 miaows
Oxazolidone: 10-20 gram, antifungus agent: 3-5 gram, Snow Flower White 120-180 mesh: 200-250 gram, Nano zinc dioxide impact-resistant: 5-8 gram, many merits
Energy polymer powder: 20-30 gram, above-mentioned material is sufficiently mixed final vacuum and packs into bag.
A kind of inorganic powder decoration diatom ooze the most according to claim 1, it is characterised in that: this inorganic powder decoration diatom
The mud temperature when construction requires that relative humidity requires as less than 85% for more than 5 DEG C.
A kind of inorganic powder decoration diatom ooze the most according to claim 1, it is characterised in that: this inorganic powder decoration diatom
The construction method of mud: step one, first guarantee basal plane are smooth, closely knit, cleaning, and moisture content is less than 10%, and pH value is less than 10, negative and positive
Angle and the horizontal flat heavily fortified point of lines are straight；
Step 2, according to construction volume prepare clear water, stirring container in add construction water amount 90% clear water, be subsequently poured into
The raw material stating formula soaks 5-10 minute, stirs 10-20 minute by electric blender after immersion, and stirring is simultaneously introduced additionally
The clear water of 10%, allows mixture be sufficiently stirred for, fully dissolves, reacts and can start construction after completely uniformly；
The position that step 3, careful covering do not spray, check basal plane condition reach regulation require after can construct, notes guarantee and
Time adjust speed of application, it is ensured that exterior wall wet-film thickness is 3, and exterior wall build is 2；Interior wall wet-film thickness is more than 1.2,
Interior wall build is 0.9；
Step 4, stirred after mixture divide twice and smeared, the thickness that first pass is smeared is 1-2 millimeter, has smeared
Stop 45-55 minute after one-tenth, depending on dwell time is according to on-the-spot climatic condition, be advisable so that surface is tack-free；Then, then to body of wall
Carrying out smearing second time, the thickness smeared is 1.5-2 millimeter, receives light with spatula after smearing, and uses instrument pattern-making the most again, figure
Case Production Time is longer, and partial pattern needs again to receive light in the completed；
Step 5, all over spreading rate should 0.8 1.0/.
A kind of inorganic powder decoration diatom ooze the most according to claim 3, it is characterised in that: raw material and the quality of clear water
Ratio is 1:0.8.
A kind of inorganic powder decoration diatom ooze the most according to claim 1, it is characterised in that: the viscosity of cellulose is 10
Ten thousand.
A kind of inorganic powder decoration diatom ooze the most according to claim 1, it is characterised in that: this inorganic powder decoration diatom
Mud is after construction, require that negative and positive angle horizontal and vertical error is less than 3mm when checking and accepting.
A kind of inorganic powder decoration diatom ooze the most according to claim 1, it is characterised in that: this inorganic powder decoration diatom
Mud is after construction, require that degree of plainness for wall surface error is less than 2mm when checking and accepting.
A kind of inorganic powder decoration diatom ooze the most according to claim 1, it is characterised in that: when this inorganic powder decorates silicon
Algae mud time air humidity is too high after construction, please don't crumple metope surface；When using this inorganic powder decoration diatom ooze construction wall
Rear surface, face cleans with pellet when having floating dust；When there is spot on surface to this inorganic powder decoration diatom ooze after construction, keep away
The wet cloth exempting to use band water is cleaned, and rubber should be selected to dip in water wiping gently.