CN108165072A - A kind of antibacterial environment protection interior wall coating and preparation method thereof - Google Patents
A kind of antibacterial environment protection interior wall coating and preparation method thereof Download PDFInfo
- Publication number
- CN108165072A CN108165072A CN201810117362.7A CN201810117362A CN108165072A CN 108165072 A CN108165072 A CN 108165072A CN 201810117362 A CN201810117362 A CN 201810117362A CN 108165072 A CN108165072 A CN 108165072A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior wall
- environment protection
- wall coating
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of antibacterial environment protection interior wall coatings and preparation method thereof, are related to coating for wall surface technical field, include the raw material of following parts by weight meter:1.2 2.5 parts of 30 45 parts of biuret polyisocyanates, 12 20 parts of butyl acrylate, 50 65 parts of deionized water, 15 25 parts of diatom ooze, 20 25 parts of dicalcium powder, 10 14 parts of bamboo charcoal powder, 12 16 parts of calcium silicates, 12 16 parts of clay, 59 parts of fiber, 25 parts of negative ion powder, 14 parts of nano aluminium oxide, 13 parts of bacteriostatic agent, 2.8 5.4 parts of anti-settling agent and coalescents;The noxious materials such as formaldehydes in interior wall coating raw material of the present invention, there is the substance of adsorption function added with bamboo charcoal powder, diatom ooze, negative ion powder etc., it can be with pure and fresh room air, it is environmentally protective, and coatings chemistry property of the present invention is stablized, and good mechanical property is not easily to fall off, preparation process is simple, has good market prospects.
Description
Technical field
The present invention relates to coating for wall surface technical fields, and in particular to a kind of antibacterial environment protection interior wall coating and preparation method thereof.
Background technology
Its major function of interior wall coating is decoration and protection indoor wall, makes its beautiful and clean, and the mankind is allowed to be in preferable
In living environment.But pollution of indoor environment is also brought with the development of coatings industry, since indoor coating contains volatility
Elements in Organic Solvents can mainly generate volatile organic compounds, free formaldehyde, solubility during construction and use
The harmful substances such as the heavy metals such as lead, cadmium, chromium and mercury and benzene,toluene,xylene, can result in indoor air quality decline with
And it is possible that influence health.
It is to spend indoors that the life of people, which is about 70% to 90% time, and if indoor harmful substance is exceeded,
The a variety of diseases of human body may be caused, mass data proves, the disease of many people, as eye obscures, fatigue, tuberculosis, allergy and
Obesities etc. are even more serious, and such as leukaemia, cancer and birth defect, children's intelligence declines, all related with living condition.And
Interior, which is put between pernicious gas and interior wall coating, direct relation.
The organic matter that coating is volatilized through respiratory tract sucking can make one the symptoms such as dizziness, headache and nausea occur, to eye,
Nose has certain stimulation, and asthma, obnubilation, vomiting and bronchitis etc. can be caused when serious.Formaldehyde is to skin, eyes
And respiratory tract has very strong irritation, makes human body that sensitivity response occur, International Cancer Research Center has been classified as the mankind can
Doubt carcinogen.Lead, cadmium, chromium, mercury are to common are malicious pollutant, and soluble matter has human body apparent harm.
Invention content
For problems of the prior art, the present invention provides a kind of antibacterial environment protection interior wall coating and its preparation sides
Method, the noxious materials such as formaldehydes in interior wall coating raw material of the present invention have added with bamboo charcoal powder, diatom ooze, negative ion powder etc. and inhale
The substance of attached function, can be environmentally protective with pure and fresh room air, and coatings chemistry property of the present invention is stablized, good mechanical property,
Not easily to fall off, preparation process is simple, has good market prospects.
In order to achieve the above object, the present invention is achieved through the following technical solutions:
A kind of antibacterial environment protection interior wall coating includes the raw material of following parts by weight meter:
30-45 parts of biuret polyisocyanates, 12-20 parts of butyl acrylate, 50-65 parts of deionized water, diatom ooze 15-25
Part, 20-25 parts of dicalcium powder, 10-14 parts of bamboo charcoal powder, 12-16 parts of calcium silicates, 12-16 parts of clay, 5-9 parts of fiber, negative ion powder 2-
1.2-2.5 parts of 5 parts, 1-4 parts of nano aluminium oxide, 1-3 parts of bacteriostatic agent, 2.8-5.4 parts of anti-settling agent and coalescents.
Preferably, include the raw material of following parts by weight meter:38 parts of biuret polyisocyanates, are gone 15 parts of butyl acrylate
55 parts of ionized water, 20 parts of diatom ooze, 23 parts of dicalcium powder, 12 parts of bamboo charcoal powder, 14 parts of calcium silicates, 13 parts of clay, 8 parts of fiber, bear from
2.1 parts of sub- 4 parts of powder, 3 parts of nano aluminium oxide, 2 parts of bacteriostatic agent, 1.2 parts of anti-settling agent and coalescents.
Preferably, the fiber is plant fiber and synthetic fibers according to 1:2 mixing compositions;
The plant fiber is one or more of bamboo fibre, stalk fibre, cocoanut fiber, flaxen fiber and cotton fiber knot
It closes;
The chemical fibre is ceramic fibre, carbon fiber, boron fibre and aramid fiber according to mass ratio 2:1:1:2
Mixing composition.
Preferably, the negative ion powder is iron dravite powder and lanthanide oxide according to mass ratio 2:1 mixing composition.
Preferably, the bacteriostatic agent is any one of isothiazolinone, organic amine and piperazine triazines.
Preferably, the anti-settling agent is organobentonite.
Preferably, the coalescents are propylene-glycol ethyl ether, butyl glycol ether, propandiol butyl ether, butyl glycol ether acetic acid
The combination of one or more of ester and Lauryl Alcohol ester.
Preferably, the antibacterial environment protection interior wall coating further include 3-8 parts nano-titanium dioxide and 0.3-1 parts of pigment.
Preferably, the pigment is the combination of one or more of titanium white, chrome oxide green, barba hispanica, iron oxide red.
A kind of preparation method of above-mentioned antibacterial environment protection interior wall coating is also disclosed in the present invention, specifically, including following step
Suddenly:
(1) each raw material is weighed according to the raw material weight number of antibacterial environment protection interior wall coating;
(2) biuret polyisocyanates, butyl acrylate and deionized water are mixed, are stirred with 500-800 revs/min
15-25 minutes are mixed to get mixture a, it is spare;
(3) diatom ooze, dicalcium powder, bamboo charcoal powder, calcium silicates, clay, cellulose, negative ion powder, nano aluminium oxide are mixed
Uniformly, abrasive grains grain size is then fed into grinder to 300-500 mesh to get mixture b, it is spare;
(4) by mixture a and mixture b after mixing, bacteriostatic agent, anti-settling agent and film forming is added in thereto successively to help
Agent stirs 30-45 minutes to get the antibacterial environment protection interior wall coating with 1000-1500 revs/min.
The present invention has following advantageous effect:
(1) noxious materials such as formaldehydes in interior wall coating raw material of the present invention, added with bamboo charcoal powder, diatom ooze, negative ion powder
, can be environmentally protective with pure and fresh room air Deng the substance with adsorption function, and coatings chemistry property of the present invention is stablized, machine
Tool performance is good, not easily to fall off, and preparation process is simple, has good market prospects;
(2) biuret polyisocyanates are added in raw material of the present invention as main base, biuret polyisocyanates are made
The easy quick-drying of product, good mechanical property, chemically-resistant and against weather are good, have not yellowing characteristic, and with very strong cementability, system
It is standby not easily to fall off into coating;
(3) there are countless small holes added with diatom ooze, diatom ooze particle surface in raw material of the present invention, porosity reaches
More than 90% molecular sieve structure has very strong absorption property, can adjust indoor air humidity, and can with adsorption moisture
With slow sustained release negative oxygen ion, harmful carcinogen such as energy effectively decomposing formaldehyde, benzene, radon gas;
(4) there is cellular microcellular structure added with bamboo charcoal powder, bamboo charcoal powder in raw material of the present invention, this microcellular structure makes bamboo
Charcoal has special adsorption capacity, there is the moisture absorption, filtering, purification, disinfection, accumulation of heat, moisturizing.And with superpower absorption
Function and generation anion, radiation infrared, increase alkalinity and other effects, can purify air and water quality, moisture absorption damping is mould proof
It is antibacterial, radiation is blocked, can be promoted blood circulation with human contact and metabolic;
(5) it can not only effectively be improved added with fiber, synthetic fibers and plant fiber mixing composition in raw material of the present invention
The strength and stiffness of coating, and the toughness and corrosion resistance of coating can be increased, the comprehensive physicochemical property for improving coating.
(6) added with anti-settling agent in coating of the present invention, anti-settling agent can prevent the storage time increase with coating, effectively
Particle is deposited on bottom, causes paint ingredient uneven, influences the performance of coating;
(7) smoothness of coating and anti-machine can be improved added with nano aluminium oxide, nano aluminium oxide in raw material of the present invention
Tool impact property.
Specific embodiment
The specific embodiment of the present invention is further described with reference to embodiment, following embodiment is only used for more
Technical scheme of the present invention is clearly demonstrated, and is not intended to limit the protection scope of the present invention and limits the scope of the invention.
Embodiment 1
A kind of antibacterial environment protection interior wall coating includes the raw material of following parts by weight meter:
30 parts of biuret polyisocyanates, 12 parts of butyl acrylate, 50 parts of deionized water, 15 parts of diatom ooze, dicalcium powder 20
Part, 10 parts of bamboo charcoal powder, 12 parts of calcium silicates, 12 parts of clay, 5 parts of fiber, 2 parts of negative ion powder, 1 part of nano aluminium oxide, bacteriostatic agent 1
1.2 parts of part, 2.8 parts of anti-settling agent and coalescents.
Fiber is plant fiber and synthetic fibers according to 1:2 mixing compositions;
Plant fiber is bamboo fibre and stalk fibre mixing composition;
Chemical fibre is ceramic fibre, carbon fiber, boron fibre and aramid fiber according to mass ratio 2:1:1:2 mixing
Composition.
Negative ion powder is iron dravite powder and lanthanide oxide according to mass ratio 2:1 mixing composition.
Bacteriostatic agent is isothiazolinone.
Anti-settling agent is organobentonite.
Coalescents are propylene-glycol ethyl ether, butyl glycol ether and propandiol butyl ether according to mass ratio 1:1:1 mixing composition.
Antibacterial environment protection interior wall coating further include 3 parts nano-titanium dioxide and 0.3 part of pigment.
Pigment is titanium white and chrome oxide green according to mass ratio 2:1 mixing composition.
A kind of preparation method of above-mentioned antibacterial environment protection interior wall coating is also disclosed in the present embodiment, specifically, including following
Step:
(1) each raw material is weighed according to the raw material weight number of antibacterial environment protection interior wall coating;
(2) biuret polyisocyanates, butyl acrylate and deionized water are mixed, with 500 revs/min of stirrings 15
Minute is spare to get mixture a;
(3) diatom ooze, dicalcium powder, bamboo charcoal powder, calcium silicates, clay, cellulose, negative ion powder, nano aluminium oxide are mixed
Uniformly, abrasive grains grain size is then fed into grinder to 300 mesh to get mixture b, it is spare;
(4) by mixture a and mixture b after mixing, bacteriostatic agent, anti-settling agent and film forming is added in thereto successively to help
Agent stirs 30 minutes to get the antibacterial environment protection interior wall coating with 1000 revs/min.
Embodiment 2
A kind of antibacterial environment protection interior wall coating includes the raw material of following parts by weight meter:
45 parts of biuret polyisocyanates, 20 parts of butyl acrylate, 65 parts of deionized water, 25 parts of diatom ooze, dicalcium powder 25
Part, 14 parts of bamboo charcoal powder, 16 parts of calcium silicates, 16 parts of clay, 9 parts of fiber, 5 parts of negative ion powder, 4 parts of nano aluminium oxide, bacteriostatic agent 3
2.5 parts of part, 5.4 parts of anti-settling agent and coalescents.
Fiber is plant fiber and synthetic fibers according to 1:2 mixing compositions;
Plant fiber is flaxen fiber and cotton fiber according to mass ratio 1:1 mixing composition;
Chemical fibre is ceramic fibre, carbon fiber, boron fibre and aramid fiber according to mass ratio 2:1:1:2 mixing
Composition.
Negative ion powder is iron dravite powder and lanthanide oxide according to mass ratio 2:1 mixing composition.
Bacteriostatic agent is organic amine.
Anti-settling agent is organobentonite.
Coalescents are butyl glycol ether acetic acid esters and Lauryl Alcohol ester according to mass ratio 1:1 mixing composition.
Antibacterial environment protection interior wall coating further include 8 parts nano-titanium dioxide and 1 part of pigment.
Pigment is titanium white and barba hispanica according to mass ratio 2:1 mixing composition.
A kind of preparation method of above-mentioned antibacterial environment protection interior wall coating is also disclosed in the present embodiment, specifically, including following
Step:
(1) each raw material is weighed according to the raw material weight number of antibacterial environment protection interior wall coating;
(2) biuret polyisocyanates, butyl acrylate and deionized water are mixed, with 800 revs/min of stirrings
15-25 minutes to get mixture a, it is spare;
(3) diatom ooze, dicalcium powder, bamboo charcoal powder, calcium silicates, clay, cellulose, negative ion powder, nano aluminium oxide are mixed
Uniformly, abrasive grains grain size is then fed into grinder to 500 mesh to get mixture b, it is spare;
(4) by mixture a and mixture b after mixing, bacteriostatic agent, anti-settling agent and film forming is added in thereto successively to help
Agent stirs 45 minutes to get the antibacterial environment protection interior wall coating with 1500 revs/min.
Embodiment 3
A kind of antibacterial environment protection interior wall coating includes the raw material of following parts by weight meter:
38 parts of biuret polyisocyanates, 15 parts of butyl acrylate, 55 parts of deionized water, 20 parts of diatom ooze, dicalcium powder 23
Part, 12 parts of bamboo charcoal powder, 14 parts of calcium silicates, 13 parts of clay, 8 parts of fiber, 4 parts of negative ion powder, 3 parts of nano aluminium oxide, bacteriostatic agent 2
2.1 parts of part, 5 parts of anti-settling agent and coalescents.
Fiber is plant fiber and synthetic fibers according to 1:2 mixing compositions;
Plant fiber is bamboo fibre and cocoanut fiber according to mass ratio 1:1 mixing composition;
Chemical fibre is ceramic fibre, carbon fiber, boron fibre and aramid fiber according to mass ratio 2:1:1:2 mixing
Composition.
Negative ion powder is iron dravite powder and lanthanide oxide according to mass ratio 2:1 mixing composition.
Bacteriostatic agent is piperazine triazines.
Anti-settling agent is organobentonite.
Coalescents are propandiol butyl ether and butyl glycol ether acetic acid esters according to mass ratio 1:1 mixing composition.
Antibacterial environment protection interior wall coating further include 6 parts nano-titanium dioxide and 0.6 part of pigment.
Pigment is titanium white and iron oxide red according to mass ratio 3:1 mixing composition.
A kind of preparation method of above-mentioned antibacterial environment protection interior wall coating is also disclosed in the present embodiment, specifically, including following
Step:
(1) each raw material is weighed according to the raw material weight number of antibacterial environment protection interior wall coating;
(2) biuret polyisocyanates, butyl acrylate and deionized water are mixed, with 700 revs/min of stirrings 20
Minute is spare to get mixture a;
(3) diatom ooze, dicalcium powder, bamboo charcoal powder, calcium silicates, clay, cellulose, negative ion powder, nano aluminium oxide are mixed
Uniformly, abrasive grains grain size is then fed into grinder to 400 mesh to get mixture b, it is spare;
(4) by mixture a and mixture b after mixing, bacteriostatic agent, anti-settling agent and film forming is added in thereto successively to help
Agent stirs 38 minutes to get the antibacterial environment protection interior wall coating with 1200 revs/min.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Example is applied the present invention is described in detail, it for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example modifies or carries out equivalent replacement to which part technical characteristic.All essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (10)
1. a kind of antibacterial environment protection interior wall coating, which is characterized in that including following raw material by weight:Biuret polyisocyanic acid
30-45 parts of fat, 12-20 parts of butyl acrylate, 50-65 parts of deionized water, 15-25 parts of diatom ooze, 20-25 parts of dicalcium powder, bamboo charcoal
10-14 parts of powder, 12-16 parts of calcium silicates, 12-16 parts of clay, 5-9 parts of fiber, 2-5 parts of negative ion powder, 1-4 parts of nano aluminium oxide,
1.2-2.5 parts of 1-3 parts of bacteriostatic agent, 2.8-5.4 parts of anti-settling agent and coalescents.
2. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that include the raw material of following parts by weight meter:
38 parts of biuret polyisocyanates, 15 parts of butyl acrylate, 55 parts of deionized water, 20 parts of diatom ooze, 23 parts of dicalcium powder, bamboo charcoal powder
12 parts, 14 parts of calcium silicates, 13 parts of clay, 8 parts of fiber, 4 parts of negative ion powder, 3 parts of nano aluminium oxide, 2 parts of bacteriostatic agent, anti-settling agent
1.2 parts and 2.1 parts of coalescents.
3. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that the fiber is plant fiber and synthesis
Fiber is according to 1:2 mixing compositions;
The plant fiber is the combination of one or more of bamboo fibre, stalk fibre, cocoanut fiber, flaxen fiber and cotton fiber;
The chemical fibre is ceramic fibre, carbon fiber, boron fibre and aramid fiber according to mass ratio 2:1:1:2 mixing
Composition.
4. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that the negative ion powder is iron dravite
Powder and lanthanide oxide are according to mass ratio 2:1 mixing composition.
5. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that the bacteriostatic agent is isothiazolinone
Any one of class, organic amine and piperazine triazines.
6. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that the anti-settling agent is organobentonite.
7. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that the coalescents are propylene glycol second
The combination of one or more of ether, butyl glycol ether, propandiol butyl ether, butyl glycol ether acetic acid esters and Lauryl Alcohol ester.
8. antibacterial environment protection interior wall coating according to claim 1, which is characterized in that the antibacterial environment protection interior wall coating also wraps
Include 3-8 parts nano-titanium dioxide and 0.3-1 parts of pigment.
9. antibacterial environment protection interior wall coating according to claim 8, which is characterized in that the pigment for titanium white, chrome oxide green,
The combination of one or more of barba hispanica, iron oxide red.
10. the preparation method of a kind of antibacterial environment protection interior wall coating as described in claim 1-9, which is characterized in that including following
Step:
(1) each raw material is weighed according to the raw material weight number of antibacterial environment protection interior wall coating;
(2) biuret polyisocyanates, butyl acrylate and deionized water are mixed, with 500-800 revs/min of stirring
15-25 minutes to get mixture a, it is spare;
(3) diatom ooze, dicalcium powder, bamboo charcoal powder, calcium silicates, clay, cellulose, negative ion powder, nano aluminium oxide are uniformly mixed,
Abrasive grains grain size is then fed into grinder to 300-500 mesh to get mixture b, it is spare;
(4) by mixture a and mixture b after mixing, bacteriostatic agent, anti-settling agent and coalescents are added in thereto successively, with
1000-1500 revs/min is stirred 30-45 minutes to get the antibacterial environment protection interior wall coating.