CN105948634A - Conch-powder ecological interior wall coating material - Google Patents
Conch-powder ecological interior wall coating material Download PDFInfo
- Publication number
- CN105948634A CN105948634A CN201610277432.6A CN201610277432A CN105948634A CN 105948634 A CN105948634 A CN 105948634A CN 201610277432 A CN201610277432 A CN 201610277432A CN 105948634 A CN105948634 A CN 105948634A
- Authority
- CN
- China
- Prior art keywords
- parts
- conch
- mesh
- coating material
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a conch-powder ecological interior wall coating material which is a green, environment-friendly and circular-economy reuse product. The conch-powder ecological interior wall coating material is prepared from the following raw materials in parts by weight: 675 parts of conch powder, 20 parts of quartz sand, 190 parts of ash calcium, 15 parts of hydroxypropyl methylcellulose, 6 parts of propylene glycol ether, 6 parts of wood fibers, 20 parts of hydrated magnesium silicate, 39 parts of white cement, 20 parts of polyvinyl alcohol, 5 parts of nano alumina, 1 part of lyase and 3 parts of antifoamer. The conch-powder ecological interior wall coating material has the advantages that the coating material is non-toxic, harmless and pollution-free; the effect of the product is better; functional characteristic effects of the conch-powder coating material are more remarkable; and the problem, i.e., later-stage shrinkage crack of the coating material is solved, and many characteristics such as water resistance, wet resistance, heat resistance, strength, stability, compactness, water retention property and scratch resistance of the conch-powder coating material are improved.
Description
Technical field
The present invention relates to a kind of environmental protection, recycling economy recycling product, be a kind of conch meal ecological interior wall coating.
Background technology
Along with people require to fit up improving constantly of quality, composite more and more uses in house decoration, its
The noxious substance produced is flooded with each family, endangers the healthy of people.Show according to investigations, the disease of the mankind 68% with
Indoor decoration pollution is relevant.Conch meal ecologic coating should need and give birth to, and meets people to modern wall material health, environmental protection, attractive in appearance etc.
All consumption demands, enter the conch meal epoch from this metope wall material.
" code for indoor environmental pollution control of civil building engineering " of country's issuing and implementation lists five kinds of pollutant: formaldehyde,
Benzene, ammonia, radioactive radon, total volatile organic compound (TOVC), APEO.The component of coating is different, and the effect of performance is different.
In existing formulation for coating material, Kaolin: (1) can be with isochrome grey, yellow, brown when there is impurity.(2) a lot of metal is comprised
Mineral.(3) as additive, autogenous shrinkage in early days can be increased, increase the danger of early crack.Triple superphosphate: (1) triple superphosphate
Owing to granule is excessive, any surface finish, specific surface area is little, and therefore oil factor is relatively low.(2) intensity adjustable extent is little, tensile strength
Low.(3) the uncertain effect not reached.(4) constriction coefficient is big, easily produces contraction fissure.(5) meet water easily to soften.(6) construction
Phase is short, and the engineering time is nervous.(7) water stability and frost property are poor.Titanium dioxide: in (1) conventional Chinese white, relative density is minimum,
The largest surface area of the Chinese white of equal quality, volume is the highest.(2) pollution that the production of titanium dioxide causes is the biggest.Acetic acid second
Alkene ester: (1) flammable liquid, explosion limit (2.65%-38%).It is (2) poisonous that (eyes and the skin of people are had stimulation to make by its steam
With) nervus centralis there is is injury effect, stimulating mucosal causing is shed tears simultaneously.(3) there is thermoplasticity, poor heat resistance.(4) water-fast
Property and moisture-proof are poor.Repellence and difference to warm water.Polydimethylsiloxane: anemia of pregnant woman is harmful to.Water reducer: (1) naphthalene system diminishing
Agent: aqueous alkali effect is general, has crystallization, impact construction winter.(2) aliphatic high-efficiency water reducing agent: color is the reddest.(3) polycarboxylic acids subtracts
Water preparation: the shelf-life is short, is difficult to make powder.Adaptability ratio is relatively limited, and cost of material is high.Affect product quality.
Summary of the invention
It is an object of the invention to produce shell powder paint for above-mentioned deficiency and current enterprise and there is asking in physical property
A kind of conch meal ecological interior wall coating inscribed and provide.Solve tradition interior trim wall material to use that the time is short, variable color, crack, do not hinder
Combustion, shedding, whiteness, the problem of bulge, solve indoor humidity, air freshness problem, solve " formaldehyde, benzene, ammonia, radon
Organic compound (TOVC), APEO " pollution problem.Improve coating quality.
The technical solution of the present invention is: a kind of conch meal ecological interior wall coating, by the raw material system of following parts by weight
Become: conch meal 615-740 part, quartz sand 18-22 part, ash calcium 170-210 part, hydroxypropyl methyl cellulose 13-17 part, third
Pure ether, 5-7 part, wood fibre 5-7 part, hydrated magnesium silicate 18-22 part, white cement 35-45 part, polyvinyl alcohol 18-22
Part, nano aluminium oxide 4-6 part, catabolic enzyme 1-1.5 part, defoamer 2.5-3.5 part.
Preferably conch meal ecological interior wall coating, is made up of the raw material of following parts by weight: conch meal: 675 parts, granularity 600
Mesh, 800 mesh, 900 mesh or 1000 mesh；Quartz sand: 20 parts, granularity 400 mesh；Ash calcium: 190 parts, granularity 600 mesh；Hydroxypropyl methyl
Cellulose: 15 parts；Third pure ether: 6 parts；Wood fibre: 6 parts；Hydrated magnesium silicate: 20 parts, granularity 800 mesh；White cement: 39 parts；Poly-
Vinyl alcohol: 20 parts, granularity 150 mesh；Nano aluminium oxide: 5 parts；Catabolic enzyme: 1 part；Defoamer: 3 parts.
The method of conch meal ecological interior wall coating, is characterized in that the tap water of scallop shell 30-35 DEG C is soaked 3h, through clear
The each 0.3h of secondary washed by force by lotion, sends into drying machine and is dried dehydration at a temperature of 350-400 DEG C, removing dust device dust removal process,
It is re-fed into calcining dehydrator calcining, calcines catalytic temperature 850-1000 DEG C, shell entrance cooling system cooling after calcining, broken,
Extra-fine grinding, dedusting, prepare conch meal.
Purposes: be directly used in interior wall coating.
Calciner uses 1200mm*1200mm roller dryer, and this owner will be by revolving body, lifting blade, and transmission fills
Put, support means and seals and other component composition. having rational in infrastructure, yield is high, consumes energy low, and operating is convenient.Technique uses certainly
Dynamic control temperature 850 DEG C-1000 DEG C, intake air temperature 700 DEG C.
Micronizer technique uses micropowder process equipment, is suitable for the brittle material that the non-flammable of Mohs' hardness≤6 grade is explosive.
Characteristic: efficiently, under finish fineness and motor power (output) same case, double than airflow milling, Ball-stirring mill, the yield of ball mill
Above；Attrition component is long for service life, and grinding roller, bull ring use special material forging to form, and make producing level be greatly improved, at thing
Under material and finish fineness same case, the consumable accessory of specific impulse impact crusher and turbine grinder is long 2-3 times for service life, processing
Calcium carbonate service life is up to 2-5；Product fineness is high, and product fineness disposably can reach d97 5um；Environmental protection: pulse dust removal
The use of device and acoustic filter can alleviate dust pollution, reduces noise, reaches the environmental protection standard of country, to surrounding without dirt
Dye.
Micronizer by flour mill, powder concentrator, powder collector, cleaner unit, fans silencer, soundproof room, disintegrating machine, elevator,
Feed bin, batcher form.
Bulk materials, after crusher in crushing becomes little granule, is sent into feed bin by elevator, then by batcher and inclination
Fuel shuffling tube, delivers to uniformly by material on the bulk cargo dish on rotating disk top.During flour mill work, tens grinding rollers are in circuit inward turning
Turning, roll, material dissipates under the action of the centrifugal to periphery and falls into mill chamber, is gone out by grinding roller, rolls rolling, grinds in circuit.
Along with the air within high pressure positive blower continuous pumping equipment machine, the material after multilamellar is pulverized, it is brought into and selects powder
Machine, it is screened by the impeller of high speed rotating, and underproof material falls after rise to be refaced, and qualified material then enters whirlwind with air-flow
Powder collector, major part grit falls, the discharge valve of bottom discharge and be finished product, and the thinner dust of small part then enters with air-flow
Cleaner unit, and stick to filter bag surface, pulse valve control high pressure draught is ejected into inside filter bag in moment and causes the violent ripple of filter bag
Dynamic, adhere to dust thereon and fall because of the shake suddenly of filter bag, the conveyer of bottom then the material collected at two send into
Row finished product packing, is filtered the air of dust and the few micronic dust of content then through filter bag, finally at acoustic filter air outlet
Discharge.
Prepare material content to illustrate:
1, conch meal: Main Ingredients and Appearance is calcium carbonate, conch meal calcium carbonate is porous fibre cave-shaped double helix structure after calcining,
Can effectively remove the free formaldehyde in air, ammonia and by smoking, the abnormal flavour that house pet, toilet, kitchen produce, in clean room
Air.It addition, the loose structure of conch meal calcium carbonate is conducive to making the ecological wall material with photocatalyst characteristic.Conch meal carbonic acid
Calcium has antibacterial, sterilizing ability, can be electric by supported active nano titanic oxide and nanometer in conch meal calcium carbonate micropore
Stone powder realizes.After nano level titanium dioxide and nano level tourmaline powder load among the micropore of conch meal calcium carbonate, with
Conch meal calcium carbonate is that one closely and firmly combines, and will not come off because of scouring, can be permanent discharge negative oxygen ion
Room air is purified and sterilization processing.
2, quartz sand: unique Wuli-Shili-Renli system approach that quartz sand is had so that it is at Aeronautics and Astronautics, electronics, machine
Tool and the IT industry that develops rapidly now occupy very important status, particularly in molecular chain structure, crystal shape in it
Shape and lattice variations rule so that it is have high temperature resistant, thermal coefficient of expansion is little, high-insulation, corrosion-resistant, piezoelectric effect, resonance
Effect and the optical characteristics of its uniqueness, play more and more important in many high-tech products.Purposes: manufacture fire proofed wood
Material, grinding-material, quartz products utilizes it to have the strongest acid-resisting medium etch ability under construction, is used for producing acidproof coagulation
Soil and acid resisting mortar.Quartz sand as silicon raw material core material silicon raw material production with supply in play irreplaceable heavy
It is the filler (can improve the weatherability of coating) in coating to want basic role, solidifying soil and the additive of blast furnace fireproof material, with
Increase its wearability, heat-resisting quantity, scour resistance, electrostatic screen, radioprotective.
3, ash calcium: ash calcium another name calcium hydroxide.It is a kind of air hardening cementitious materials, is applied in building coating to improve
The resistance to water of coating, abrasion resistance, good leveling property.The main component of sierozem power is Ca (OH)2, CaO and a small amount of CaCO3Mixing
Thing, is the intensely processed products of Calx.Sierozem power is by with CaCO3For the natural fat lime stone of main component, through high-temperature calcination
After become quick lime (CaO) after, then through selected, partial digested, pulverized by high speed selecting crude drugs with winnower beater grinder the most again,
Its apparent pure white exquisiteness.In recent years, due to the progress of Powder Processing Technology in China, market has fineness more than 600 mesh
Or the sierozem power commodity of higher fineness.
Sierozem power adds in coating, and along with the coating film forming of coating, (calcium oxide also becomes hydroxide after meeting water to calcium hydroxide
Calcium) can be with the CO in air2Reaction generates calcium carbonate crystal and produces intensity, and then can provide for coating composition in film
Certain caking property, and give coating significant resistance to water.The various building coatings produced for chief active filler with sierozem power
There is the features such as low cost, water-tolerant.
4, hydroxypropyl methyl cellulose:
(1). building industry: water-retaining agent, retarder as cement mortar make mortar have pumping.At slurry of plastering, gypsum material, greasy
Sub-powder or other building materials, as adhesive, improve smear and extend operable time.As sticking brick, marble,
Decorative plastic, pastes reinforcing agent, it is also possible to reduce cement consumption.The water retention property of HPMC makes the slurry will not be because of dry after smearing
Obtain too fast and chap, strengthen intensity after hardening.
(2). coatings industry: in coatings industry as thickening agent, dispersant and stabilizer, all have good in water or organic solvent
Good intermiscibility.As paint stripper.
5, the third pure ether:
Third pure ether is that one self can produce a kind of inorganic colloid out in the case of HPMC meets aqueous alkali.And this colloid
Can effectively play hydrophobic, solve dry linting, increase hardness, the effect of the most water funk flushing.
Third pure ether is a kind of odorless, colourless, water solublity and hygroscopic liquid, and viscosity is medium.It is powder of lacquer putty for use on additive, permissible
Increase powder of lacquer putty for use on workability.
(1) outward appearance is white or slightly yellow fine crystals, soluble in water, and micro-have ammonia taste, does not fires, nontoxic, can extensively add
Additive etc. is gone out in inner and external wall putty powder, dry-mixed mortar, coagulation.Adhesive property and intensity can be increased, also may be used in powder of lacquer putty for use on
To increase the effects such as workability.Can directly be dry mixed with other powders.
The characteristic that (2) third pure ethers are exclusive, is possible not only to reduce cost, more can improve the quality of product.
(3) through repeatedly testing proof: the third pure ether is that one self can can produce one in the case of HPMC meets aqueous alkali
Plant inorganic colloid out.And this colloid can effectively play hydrophobic, solve dry linting, increase hardness, the work of the most water funk flushing
With, more preferable than using water reducer to improve hardness, intensity and water-reducing effect.
(4) third pure ethers do not burn can be fire-retardant, with calcium carbonate compatibility, more preferably embodies flame retardant effect.
6, wood fibre: be widely used in concrete mortar, plastering, take in the fresh timber matter fiber pulp sponge, drip again
The fields such as blue or green road, to preventing, coating cracking, raising water-retaining property, the stability improving production and the conformance of construction, increase are strong
Degree, enhancing have good effect to the adhesive force etc. on surface.Its technical role is mainly: thixotroping, protect, absorb, carrier and filling out
Fill agent.
Due to the capillarity of fibre structure, the moisture of internal system is promptly transferred to pulp surface and interface,
The distribution of the uniform moisture within slurry is made to significantly reduce skinning.And adhesion strength and surface strength are significantly improved,
This mechanism also due in dry run the minimizing of tension force and substantially play the effect of cracking resistance.Wood fibre dimensional stability and heat
Stability serves good thermal-insulating and anti-cracking effect in insulation material.
Wood fibre characteristic: nontoxic, tasteless, pollution-free, "dead".Lignocellulose acid and alkaline water insoluble, weak
Solution；PH value is neutral, can improve system corrosion resistance.Lignocellulose proportion is little, specific surface area is big, have excellent insulation,
Heat insulation, insulate against sound, insulate and permeability, thermal expansion is not the most flaked and is not ftractureed；Higher wet film intensity and coverage effect.Wooden
Cellulose has excellent pliability and dispersibility, forms tridimensional network, enhance the support force of system and resistance to after mixing
Power, can improve the stability of system, intensity, degree of compaction and the uniformity for a long time.The structural viscosity of wood fibre, make to process is prefabricated
The uniformity of slurry (dry and wet material) maintains the original state and stablizes and reduce contraction and the expansion of system, and the precision making construction or prefabricated component is big
Big raising.Wood fibre has the strongest antifreeze and solar heat protection ability, when temperature reaches 150 DEG C of energy heat insulation a couple of days；When up to 200 DEG C
Heat insulation tens of hours of energy；When also can heat insulation a few hours more than 220 DEG C.
Wood fibre main uses: water-proof putty powder.Exterior-wall heat insulation is starched.Mineral mortar.Ceramic tile bond.Wall surface mortar.
PVC filters.Water-proof putty powder.External insulating mortar.Mineral mortar.Ceramic tile bond.Textured coating.Coating for internal and external wall.External thermal insulation
Mortar.Water-proof putty powder.Mineral mortar.Ceramic tile bond.Textured coating.
(1) wood fibre be natural reproducible timber through chemical treatment, Mechanical Method processing obtain organic wadding fibrous
Material.
(2) it is widely used in building trade, to preventing coating cracking, improving water-retaining property, the stability of raising production and execute
The conformance of work, increase intensity, enhancing have good effect to the adhesive force etc. on surface.Its effect is mainly: thixotroping, protection,
Absorption, carrier and filler.
(3) due to the capillarity of fibre structure, the moisture of internal system is promptly transferred to pulp surface and boundary
Face so that the uniform moisture distribution within slurry significantly reduces skinning.And adhesion strength and surface strength are substantially carried
Height, this skin texture also due in dry run tension force reduce and substantially play the effect of cracking resistance.Wood fibre size prepattern and
Heat stability serves good thermal-insulating and anti-cracking effect in insulation material.
(4) nontoxic, tasteless, pollution-free, non-emissive, water insoluble, weak acid and alkaline solution.PH value is neutral, can improve
System corrosion resistance.
(5) wood fibre proportion is little, specific surface area is big, have excellent insulation, heat insulation, insulate against sound, insulate and permeability,
Thermal expansion is not the most flaked and is not ftractureed；Higher wet film intensity and coverage effect.
(6) wood fibre has excellent pliability and dispersibility, forms tridimensional network, enhance system after mixing
Support force and endurance, the stability series of system, intensity, degree of compaction and the uniformity can be improved.Than using vinyl acetate effect
More preferably.
(7) structural viscosity of wood fibre, makes the uniformity of the prefabricated slurry (dry and wet material) processed maintain the original state stable
And reduce contraction and the expansion of system.
(8) wood fibre has the strongest antifreeze and emission capacity, when mixed degree reaches 150 DEG C of energy heat insulation a couple of days；When up to
Heat insulation tens of hours of 200 DEG C of energy, when also can heat insulation a few hours more than 220 DEG C.
7, hydrated magnesium silicate (Pulvis Talci): Talcum main component is the magnesium silicate that Talcum is aqueous, molecular formula is Mg3?
Si4O10(OH)2.Hydrated magnesium silicate: chemical grade Pulvis Talci, is used for strengthening modification filler.Feature: increase the steady of product line shape
Fixed, increase tensile strength, shear strength, flexing intensity, the intensity of pressure, reduce and deform, extension rate, thermal coefficient of expansion, whiteness height,
The features such as epigranular dispersibility is strong.
Talcum has lubricity, anti-glutinous, fluidizer, fire resistance, acid-resisting, insulating properties, fusing point height, chemical torpescence, screening
The excellent Wuli-Shili-Renli system approach such as lid power is good, softness, good luster, absorption affinity are strong.
8, white cement: (1) white cement is the abbreviation of white portland cement, burns to part molten with the raw material of proper composition
Melting, be able to calcium silicates is main component, and the poor grog of irony adds appropriate Gypsum Fibrosum, and the white water of levigate processing procedure is rigid
Binder Materials.
(2) white cement mostly is ornamental use, and its manufacturing process is more a lot of than ordinary cement.
(3) white cement has higher whiteness, bright color, is typically used as various building and ornament materials, typically has powder
Brush, sculpture, ground, terrazzo product, white cement can be also used for making white and color concrete head and shoulder, is production scale
Maximum decoration cement kind.
(4) whiteness is minimum is not less than 87.
9, polyvinyl alcohol: be called for short PVA.Outward appearance is white powder, is that a kind of purposes water soluble polymer the most widely gathers
Compound, performance, between plastics and rubber, has the strong adherence of uniqueness, epithelium pliability, flatness, oil resistivity, resistance to
Solvent borne, protecting colloid, gas barrier performance, wearability and the specially treated resistance to water having, be widely used as bonding
Agent.
10, nano aluminium oxide: Hardening is effective, scattered, there is the functions such as Hardening scratch resistance.
The performance of nano aluminium oxide:
(1) goods rigidity and hardness are strengthened.
(2) deformation that goods are shrinkage and cause is reduced because of contraction.
(3) good dispersion, has preferable surface gloss.
(4) transparent, white, ash color masterbatch, flexibly configurable produces the product of shades of colour.
(5) there is antioxidation and aging resistance effect, extend goods service life.
(6) production cost is reduced.
Feature:
(1) anti-wear performance that nano aluminium oxide is excellent, is widely used in paint of coating field.Add the nanometer of 10-20%
The coating that aluminium oxide prepares can be greatly improved coating abrasion performance, anti-scratch performance, improves 2-5 times than traditional coating wearability.
(2) scratch resistance scratch-resistant: after having added nano aluminium oxide inside coating, can form one layer the thinnest at coating surface
Close, uniform and adamantine network structure, protects following polymer enamelled coating without damage, the anti-ruled area of nano-paint
3 times can be improve than original paint.
(3) wear-resistant: the anti-wear performance that nano aluminium oxide is excellent, it is widely used in paint field.Add 5-10%
The coating for preparing of nano aluminium oxide can be greatly improved coating abrasion performance, improve 2-4 times than traditional coating wearability.
(4) improving hardness: add nano-aluminium oxide, can significantly improve the hardness of coating, adding about 20% can reach
To 6-7H.
(5) transparency: do not affect the transparency of coating.
11, catabolic enzyme: the harmful substances such as the formaldehyde that decomposition absorption chamber interior decoration synergistic effect produces.
12, defoamer: easily disperse, antifoaming speed is fast, suds is lasting, does not results in the secondary pollution of water.Defoamer suds
Property strong, do not affect the various technical parameters of system.Consumption is few, and efficiency is high.
The invention have the advantage that
1. purify air, remove formaldehyde: free formaldehyde that the floor after new house finishing, marble, furniture etc. distribute, benzene, ammonia,
Ten hundreds of aperture that the toxic heavy metal harmful substance such as radon, TVOC is opened by conch meal absorbs, decomposes, eliminates.Conch meal
Throwing the net to treat the harmful substance that indoor every day constantly distributes, release is how many, it is how many to decompose.
2. breathe damping: breathing damping is the basic function of conch meal, when indoor moisture is more than 70%, conch meal micro-
Moisture inspiration in air is removed deposit by hole, when air humidity is less than 40%, is discharged by moisture, so people's handle
Conch meal referred to as " wall that can breathe ", without humidifier, need not artificially be handled, and keeps indoor to reach the humidity of human body the most comfortable,
It addition, conch meal also ensures that quilt, medicated clothing will not be moist.Body of wall does not contains Signs of Mould yet and occurs.
3. weaken noise: countless micropores can absorb, intercept noise.His effect is equivalent to the cement mortar of condition of equivalent thickness
With more than 2 times of slabstone, the most also absorb 50% lingering sound.
4. eliminate abnormal flavour: the various abnormal flavour that domestic pollution produces can be removed.Such as: the fishlike smell breeded fish, the body odor of house pet
Taste.The abnormal flavour that kitchen, toilet, smoking bring, adsorbable and discharged by cross-ventilation, the moment keeps indoor air clear
Newly.
5. fire protection flame retarding: conch meal wall material is high temperature resistant 1200 degrees Celsius, only fusing point does not has a burning-point, meets naked light and does not burns,
Do not produce any toxic smog.
The most antibacterial, antibacterial, sterilizing: do not grow any mushroom, never go mouldy, it is possible to that effectively kills in air is various
Influenza and infectious disease pathogenic bacteria.
7. service life is long: the conch meal as finishing material is up to more than 20 years service life, never fades, does not sticks up
Limit, does not falls off, resistance to oxidation, all the time as new.
The most easily repairing: local damage, easily repair, the metope after repairing is consistent with substance, and local pollution rubber both may be used
Wipe.
9. antistatic: conch meal is natural mineral, main component is calcium, self does not contains heavy metal, does not produce electrostatic,
So not dust suction, forever guarantor's indoor wall cleaning.
10. preventing light pollution: light absorptive is strong, reflection light is soft the most dazzling, and eye is the most tired, reduces child myopia probability.
11. colors are soft: because conch meal is made up, rich in each seed coat of the calcining of sea shells powder, grind into powder
The aminoacid of skin regeneration needs and trace element, calcium, phosphorus, manganese, zinc, copper, ferrum, potassium, magnesium etc., have holding to moisten, bring back to life regeneration
Effect, thus it is possible to vary dull-looking skin, can predict skin aging, is suitable for various skin quality.
12. heat-insulating and energy-savings: the pyroconductivity that morphosis determines conch meal is the lowest, thermal and insulating performance is the best, than
Cement and mortar are high more than 6 times, are greatly saved power consumption and heating cost.
13. releasing negative oxygen ions and far infrared: conch meal every square centimeter more than 1800 negative oxygen ion of release, negative oxygen from
Son swims the most everywhere, and people is as lived in the Nature, and far infrared is conducive to regulating microcirculation in human body, improves people
Sleep quality.
In a word, to have (1) nontoxic, harmless, pollution-free for the present invention.(2) product effect is more preferable.(3) shell powder paint is made
The effect of functional characteristic is more notable.(4) problem solving coating later stage contraction fissure, improves many spies of shell powder paint
Property: resistance to water, moisture-proof, thermostability, intensity, stability, degree of compaction, water-retaining property, anti-zoned ability etc..
Detailed description of the invention
Embodiment 1
Conch meal ecological interior wall coating, it is characterised in that be made up of the raw material of following parts by weight:
Conch meal 675 parts, granularity 600 mesh, 800 mesh, 900 mesh or 1000 mesh；Quartz sand 20 parts, granularity 400 mesh；Ash calcium 190 parts,
Granularity 600 mesh；Hydroxypropyl methyl cellulose 15 parts；Third 6 parts of pure ether；Wood fibre 6 parts；Hydrated magnesium silicate 20 parts, granularity 800
Mesh；White cement 39 parts；Polyvinyl alcohol 20 parts, granularity 150 mesh；Nano aluminium oxide 5 parts；Catabolic enzyme 1 part；Defoamer 3 parts.
Embodiment 2
Conch meal preparation method: be that scallop shell is soaked 3h with the tap water of 30 DEG C-35 DEG C so that it is by abundant desalination and softening dirt
Dirt, washes by force each 0.3h of secondary through shell cleaning machine, sends into dryer system and carries out dehydrate at a temperature of 350 DEG C-400 DEG C,
After removing dust device dust removal process, sending into drum-type rotary kiln and calcine, calcining catalytic temperature is set in 850 DEG C-1000 DEG C, forges
After burning catalysis, shell is sent into cooling system cooling, crushes after cooling, send into grinder extra-fine grinding, after grinder with elevator
Putting cleaner and carry out dedusting, prepare conch meal raw material, agitated machine adds auxiliary material stirring, enters and adjusts face tank to mix colours
After, metering packing.
Claims (3)
1. a conch meal ecological interior wall coating, it is characterised in that be made up of the raw material of following parts by weight: conch meal 615-
740 parts, quartz sand 18-22 part, ash calcium 170-210 part, hydroxypropyl methyl cellulose 13-17 part, the third pure ether, 5-7 part, wood
Matter fiber 5-7 part, hydrated magnesium silicate 18-22 part, white cement 35-45 part, polyvinyl alcohol 18-22 part, nano aluminium oxide 4-
6 parts, catabolic enzyme 1-1.5 part, defoamer 2.5-3.5 part.
2. according to the conch meal ecological interior wall coating described in claim 1, it is characterised in that by the raw material system of following parts by weight
Become: conch meal 675 parts, granularity 600 mesh, 800 mesh, 900 mesh or 1000 mesh；Quartz sand 20 parts, granularity 400 mesh；Ash calcium 190 parts,
Granularity 600 mesh；Hydroxypropyl methyl cellulose 15 parts；Third 6 parts of pure ether；Wood fibre 6 parts；Hydrated magnesium silicate 20 parts, granularity 800
Mesh；White cement 39 parts；Polyvinyl alcohol 20 parts, granularity 150 mesh；Nano aluminium oxide 5 parts；Catabolic enzyme 1 part；Defoamer 3 parts.
3. the method preparing conch meal ecological interior wall coating according to claim 1 and 2, is characterized in that scallop shell
Soak 3h with the tap water of 30-35 DEG C, wash by force each 0.3h of secondary for cleaned dose, send into drying machine and enter at a temperature of 350-400 DEG C
Row drying and dehydrating, removing dust device dust removal process, it is re-fed into calcining dehydrator calcining, calcines catalytic temperature 850-1000 DEG C, calcining
Rear shell enters cooling system cooling, broken, extra-fine grinding, dedusting, prepares conch meal.