CN109467997A - Type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray - Google Patents
Type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray Download PDFInfo
- Publication number
- CN109467997A CN109467997A CN201811375189.7A CN201811375189A CN109467997A CN 109467997 A CN109467997 A CN 109467997A CN 201811375189 A CN201811375189 A CN 201811375189A CN 109467997 A CN109467997 A CN 109467997A
- Authority
- CN
- China
- Prior art keywords
- antique
- modelled
- parts
- blue bricks
- light steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of light steel house sprays to build type blue bricks wall covering modelled after an antique, raw material including following parts by weight: 20~30 parts of conch meal, 20~30 parts of film-forming resin, 5~15 parts of diatom ooze, 5~15 parts of clay, 5~10 parts of glass fibre, 5~10 parts of gypsum, 1~5 part of pigment, 5~10 parts of adhesive, 1~3 part of additive.Present invention blue bricks wall covering modelled after an antique, good decorating effect, appearance, texture and match volume with blue bricks, fidelity is high, give plain, sedate, simple and unsophisticated, natural, quiet aesthetic feeling, also have the function of cultivating the moral character and nourishing the nature, and passes on the traditional culture in China in another way；Its function admirable has very strong moisture-proof, waterproof, fire prevention, heat-proof quality, good air permeability, and low-temperature stabilization, and fugitive color, not environmentally protective, economizes on resources；Using professional spray gun, one-pass molding can be shortened the construction period, and improve work efficiency, i.e., brush is lived, and can greatly save cost.
Description
Technical field
The present invention relates to building material technical field, type blue bricks wall covering modelled after an antique is built in specifically a kind of light steel house spray.
Background technique
Light steel house is the novel house building technology of current international popular, this new building technology of light steel house is
Full system structural model has been overturned in the project that country widelys popularize, its invention, is improved living environment, is favored by people.It is light-duty
The building technology of steel construction low-rise dwelling is evolved on the basis of the style timber structure building technology of North America, by a century
Above development, formd excellent physical properties, space and body flexibly, be easy to build, various informative mature build body
System.It is known as the best North American continent of living environment in the world, there is 95% or more low layer civil buildings, including house, quotient
Field, school, office building etc. are built using timber structure or lightweight steel construction.Lightweight steel construction occupies absolutely excellent in whole building market
Gesture.Currently, climbing up and up with timber price, the market development of North America lightweight steel construction system just be more than 30% growth rate
Rapid growth is gradually accepted extensively by market, while also largely being used in Japan, South Korea and Australia.
Light steel house is mainly made of light steel skeleton, light steel cap, light steel bottom beam, light steel truss structure support and connector, is built
Can reduce when making as playing with building blocks, in work progress noise, save water power more than half, using space have more 4% -8% a left side
It is right；All accessories in house are all in the factorial production, and mechanization, commercialized degree are high.The steel of lightweight steel construction can recycle
It uses, building waste will not be become, cause huge pressure to environment.Light steel building construction is formed with strength screw connection, is resisted
Shock stability is very good, will not occur that wall collapses or floor falls down and jeopardizes personal safety because of rocking for earthquake.In addition, light steel
House also has good fire prevention, heat preservation, heat-insulated, sound insulation property.Light steel house properties are far more than the mixed brick structure of tradition,
Almost meet and required, is environmentally protective energy-saving residence, it is the outstanding representative of green building, becomes governments at all levels and room
The novel industry of promotion that business men, investor pay close attention to.The yield of China's steel industry has occupy world forefront, but steel are in construction industry
Use ratio be far below level of developed countries, lightweight steel construction low layer residential construction technology meet country to construction industry
Direction of industry.According to prediction industrial research institute market intelligence report, steel construction is expected to agitate many trillion Green Building Market, prospect hair
It is boundless to open up space.
With the development of national economy and science and technology, higher want is proposed to the performance of decorative material for wall surface of building
It asks.Traditional solvent type building coating seriously affects environmental and human health impacts because having a large amount of VOC and free monomer release.Working as
Under " with light packs to repair, reset decorations " mainstream prevailing decorate consciousness, traditional ornament materials and form drawback highlight --- visual perception
Dullness, poor intention, the pernicious gases such as formaldehyde, vinyl chloride monomer content is high, and the smell is awful, and the feature of environmental protection is poor, house fitting-up pollution
It causes serious injury safely to human health；Metope is handled, spray painting is smoothed out, partition is installed, process is especially complex, dust from flying,
It is time-consuming and laborious etc..Therefore, environmental protection, functionalization, superior interior wall coating how are developed and produce to human lives and ring
The sound development in border is of great significance.
Wall covering, which refers to, plays decoration and protection for building wall, keeps building wall beautiful and clean, while can also rise
To protection building wall, the effect prolonged its service life.Wall covering includes interior wall coating and exterior wall by building wall classification
Coating two large divisions.Interior wall coating focuses on decoration and environmental protection；Exterior coating focus on protection and it is durable.Wall covering in addition to itself
Outside decoration and protective effect, also to rich and varied, fashion, health environment-friendly trend development.It is desirable to decorative effect streamers to overflow
Coloured silk, magnificent mansion, elegant, romance, warmth；Also prefer to that material itself is pollution-free, health environment-friendly, individual character and rich in vertical
Body-sensing.There are no the light dedicated wall coverings in steel house in currently available technology, development and stream with light steel house in China
Row, light steel house and its various construction materials will become the demand of people.
Blue bricks is to belong to fired brick, and the primary raw material of ancient blue bricks is clay, and after clay tempers, extrusion forming is reentered
Brickkiln is baked to (1000 degree or so) and is water-cooled, and allows iron incomplete oxidation in clay, generates ferroso-ferric oxide, then Cheng Qing
Color, blue bricks have the characteristics such as better weather resistance, water-fast with respect to common brick.Blue bricks modelled after an antique give it is plain, sedate, simple and unsophisticated, natural,
Quiet aesthetic feeling, have the characteristics that gas permeability, water imbibition, it is anti-oxidant, purification air, be house wall, road surface decoration it is a
Desired decoration material becomes one of the product that designer recommends to the utmost in recent years.But cooling means in the production process of blue bricks
It is that water is cooling, is that a kind of anoxic is cooling in fact, operates more troublesome；In glazing mode, the existing spray of wet process glazing
Glaze has leaching glaze or the two to combine again, and dry glazing then needs friction glazing, removes dried glaze powder, applies dry granular, is aided with work of water sprinkling for better material moisture and glue spraying
The craft methods such as solidification, production process is complicated, and the production time, cost was larger generally at 25-30 days or so, so production at present
It is fewer.Blue bricks modelled after an antique is applying above with having wall integrated trend, upper more flexible and changeable in paving decoration, therefore,
The sensibilities coating for studying a kind of blue bricks modelled after an antique that can spray the type of building has good market prospects.
Summary of the invention
The object of the present invention is to provide a kind of light steel house sprays to build type blue bricks wall covering modelled after an antique, wall covering decoration effect
Fruit is good, and appearance, texture and match volume with blue bricks, fidelity is high, gives plain, sedate, simple and unsophisticated, natural, quiet
Aesthetic feeling also has the function of cultivating the moral character and nourishing the nature；The wall covering function admirable has very strong moisture-proof, waterproof, fire prevention, thermal insulation
Can, good air permeability, and low-temperature stabilization, fugitive color, not environmentally protective, economizes on resources；Using professional spray gun, one-pass molding,
It can shorten the construction period, improve work efficiency, i.e., brush is lived, and can greatly save cost.
The invention is realized by the following technical scheme:
Type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray, the raw material including following parts by weight: 20~30 parts of conch meal,
20~30 parts of film-forming resin, 5~15 parts of diatom ooze, 5~15 parts of clay, 5~10 parts of glass fibre, 5~10 parts of gypsum, pigment 1
~5 parts, 5~10 parts of adhesive, 1~3 part of additive.
The conch meal the preparation method comprises the following steps: by shell 0.5~1h of acid soak, then wash with distilled water 2~3
Secondary, dry 5~6h under conditions of being placed in 75~85 DEG C is ground into the shell coarse powder that partial size is 0.5~1.0mm, is subsequently placed in 800
DEG C~1200 DEG C under the conditions of calcining 1~2h of catalysis, crushed after cooling with nano grinder, it is 500nm that average grain diameter, which is made,
Conch meal.
The film-forming resin is formed by one of acrylic resin, epoxy resin, styrene resin or multiple combinations.
The partial size of the clay is no more than 2 μm.
The pigment is phthalocyanine green, the combination of two or more in iron oxide green, iron oxide brown, carbon black forms.
The adhesive is that one of white glue with vinyl, cloud stone glue, epoxy acrylic ester gum or multiple combinations form.
The additive is trimellitic anhydride, methyl tetrahydro phthalic anhydride, dioctyl phthalate, hydroxypropyl methyl fiber
Element is composed.
The blue bricks wall covering modelled after an antique has redesigned blue bricks in use, first clean out the impurity on metope, dust
Size frame bar, directly sprayed and built on the metope in light steel house, being prepared into the outer of blue bricks modelled after an antique using dedicated spray building machine device
It sees.
The preparation method of the blue bricks wall covering modelled after an antique the following steps are included: conch meal and glass fibre are mixed,
It stirs evenly, 600~1000r/min of mixing speed, diatom ooze, gypsum, acrylic acid floor paint, clay is then added while stirring
And adhesive, 20~30min is stirred, 1200~1500r/min of mixing speed is eventually adding pigment and additive, continues to stir
It is uniform to color.
The conch meal that the present invention uses is to be made using natural shell as raw material by grinding and high-temperature calcination, has and inhales
Function that is attached, decomposing these pernicious gases.Conch meal is shell by high-temperature calcination powder pulverized powder, 95% main component
It is calcium carbonate and chitin, there are also a small amount of amino acid and polysaccharide materials.With universal, the application field of conch meal technology
It is increasingly wider, finishing field is gradually expanded to from initial beauty industry and food additives.The exclusive Double-helical molecule of shell
Structure, porosity are 5000~6000 times of bamboo charcoal, nocuousness that can utmostly in the air such as formaldehyde adsorption, TVOC heavy metal
Floating material, the main composition-calcium carbonate of its own belong to alkalinity, and formaldehyde encounters the oxygen in air and becomes formic acid, is coated onto the shell of metope
Powder can directly be decomposed by formaldehyde absorbing and using the principle of acid-base integration.Therefore, shell powder paint has fire prevention well
Fire-retardant, adjusting air humidity, absorbing sound and lowering noise, antistatic and antibacterial, it is antibacterial the effects of, and its specific gravity is small, and workability is good, more
The soft and smooth visual effect of texture.Conch meal belongs to inorganic material, and color is soft, the wall color low-key decorated with shell powder paint
It is soft, visual fatigue can be effectively relieved, protect eyesight.Conch meal metope does not inhale dust simultaneously, not fugitive color, and metope is for a long time such as
Newly, repetition finishing number can be reduced, decoration cost is saved.
Conch meal is renewable resource, can make full use of China's shell resource abundant, turn waste into wealth.Ocean area accounts for
The 71% of earth surface product, shellfish fertility is again strong, so the shell of ocean ecosystem production has been just a huge number
According to almost annual it can be seen that sea shells, which are arbitrarily piled up, influences the report of coastal people's life.There are also many cultivation are big
Family, their shell yield is surprising, because cannot handle, just abandons shell heap onto beach, annual National Environmental Protection Agency will
Substantial contribution is spent to handle the shell that these oneself cannot disappear.The processing approach of conch meal usually prepared feed in the past, but
It is that processing quantity is extremely limited, so the birth of conch meal ecologic coating is a revolutionary invention, had both handled in ocean
And the shellfish or spiral shell waste of artificial breeding, rationally recycling for natural resources is realized, and finishing environment can be allowed to become more
Add environmental protection.
Diatom ooze is a kind of using diatomite as the green inner wall decoration wall material of main raw material(s), and diatom ooze, which is taken, lives in number
Aquatic class of swimming before 1000000 years is biological --- and natural materials made of diatom deposition, main component is opal, rich in a variety of
Beneficial mineral matter, quality are light and soft.Not any pollution of diatom ooze itself, it is pure natural, and also there are many functions, in construction diatom
Insipidness during mud, it is pure natural, convenient for repairing.Diatom ooze health environment-friendly not only has fine dicoration, also has fire prevention
The functions such as fire-retardant, absorbing sound and lowering noise, insulation, adjusting air humidity are the interior decorations of new generation for substituting wallpaper and emulsion paint
Material.
Clay, also known as clay, generally by being formed after silicate mineral at the earth's surface weathering, ingredient is mainly silica
With aluminium oxide, Se Bai and fire resisting, for the primary raw material for preparing china clay.Clay has good plasticity and associativity, Ke Yihe
Aplastic raw material combines well.The advantages of clay is non-toxic and tasteless with its, safety and environmental protection is welcomed by the people.
Glass fibre is a kind of inorganic non-metallic material haveing excellent performance, and has that good insulating, heat resistance be strong, corrosion resistance
Well, the advantages that high mechanical strength.Glass fibre is seven kinds of pyrophillite, quartz sand, lime stone, dolomite, bechilite, boromagnesite mines
Stone is raw material through caused by the techniques systems such as high temperature melting, wire drawing, doff, woven fabric, the diameter of monofilament is several microns to 20
Several meters microns are equivalent to the 1/20-1/5 of a hairline, and every bundle fiber precursor is all by hundreds of even thousands of monofilament
Composition.Glass fibre is typically used as the reinforcing material in composite material, electrically insulating material and heat-insulating material, circuit substrate etc.
National economy every field.The purpose of glass fibre is added in the present invention: the rigidity and hardness of rear metope are built in enhancing spray, are increased and are inhaled
It is moist, improve that metope is heat-resisting and fire protecting performance.
Gypsum is monoclinic system mineral, be main chemical compositions be calcium sulfate hydrate, gypsum have microcellular structure and
Thermal dehydration makes it have excellent sound insulation, heat-insulated and fire protecting performance.World's country variant to the consumption structure of gypsum not
Together, the consumption of developed country's gypsum deep processed product accounts for larger specific gravity, gypsum consumption structure are as follows: produces product and accounts for 45%, cement is raw
Production accounts for 45%, and other each fields account for 10%.Developing country biases toward the primary application of ore more, depends on cement industry, gypsum
The specific gravity of product has the tendency that incrementally increasing with economic development.The consumption structure of China is substantially are as follows: 84% is used as the slow of manufacture of cement
Solidifying agent, 6.5% is used for ceramic mold, and 4.0% is used for plastering, materials for wall, and 5.5% is used for chemical industry and other industries；In
The continuous increase of state's cement output, the demand to gypsum increase accordingly, while with the rapid growth of China's economic, gypsum industry
Especially a great development space will be present in plastering, and various gypsum, which produce product and gypsum wall, can obtain high speed
Development, green, environmental protection, the gypsum building material of health and production product will widely be applied in people's lives.
Iron oxide pigment has a following good characteristic: highly concentrated miniature, without resin, environmental protection, and color content is high, tinting strength, tinting power
By force, chromatography is complete, for a long time storage not loose colour, regardless of water, do not sink to the bottom, good fluidity, and have very strong weatherability, anti-mildew
The application performances such as property, dispersibility and scrubbing resistance；Also there is good acidproof, alkaline-resisting, fast light, heat resistance, it is water-fast, oil resistant, resistance to
Infiltration of solvent etc..Phthalocyanine green appearance is yellow light green powder, bright in color light, strong coloring force, not soluble in water, ethyl alcohol and organic molten
Agent.Density is 2.69~2.72g/cm3, and oil absorption is 35% ± 5%, and light resistance is 7~8 grades, heat resistance≤200 DEG C.Phthalocyanine green
Fast light, good weatherability, strong coloring force, bright in colour, color difference is small, and color developing and good fluidity are widely used in medium-to-high grade ring
Protect exterior coating.
Beneficial effects of the present invention:
1, type blue bricks wall covering modelled after an antique is built in light steel house spray of the present invention, and scrubbing resistance, mould proof, alkali resistant, antipollution have very
Strong moisture-proof, waterproof, fire prevention, heat-proof quality, good air permeability, and low-temperature stabilization, fugitive color, not environmentally protective, through detecting
Without any poisonous and harmful substance, there is no any influence to human health, i.e. brush is lived, and quality assurance also, can save China
Clay resource saves preparation cost.
2, type blue bricks wall covering modelled after an antique is built in light steel house spray of the present invention, and using professional spray gun, one-pass molding can
Cost is greatlyd save, the investment of manpower and material resources is reduced, reduces the process of processing, can be shortened the construction period, work efficiency is improved；Spray can before building
With designed, designed pattern, it is prepared into the texture of various blue bricks modelled after an antique.
3, type blue bricks wall covering modelled after an antique is built in light steel house spray of the present invention, and good decorating effect is outer with blue bricks
It sees, texture and match volume, fidelity height give plain, sedate, simple and unsophisticated, natural, quiet aesthetic feeling, it is warm can to carry life
It is fragrant simple and unadorned, also have the function of cultivating the moral character and nourishing the nature, and pass on the traditional culture in China in another way.
4, raw material sources of the present invention are extensive, and low manufacture cost, preparation method is simple to operation, not high to equipment requirement, right
Environmental nonpollution, to no damage to human body, environmental-protecting performance reaches EU criteria, and combines the excellent of traditional decoration product environmental protection
Point avoids the disadvantage of traditional product decorative effect difference；Also have the function of mould proof alkali resistant, antipollution, moistureproof and waterproof.
5, type blue bricks wall covering modelled after an antique is built in light steel house spray of the present invention, and energy conservation and environmental protection has centainly flexible
Property and excellent crack resistance, can effectively cover the fine cracks on metope, keep coating securely and smooth, it is persistently resistance to
With.
6, blue bricks wall covering modelled after an antique of the present invention, conch meal is added and makes it have following advantages: (1) purification is empty
Gas: the oyster shell whiting subparticle by calcination processing is porous fibrous double helix construction construction, can be effectively removed in air
Harmful substances such as free formaldehyde, benzene, ammonia and because of peculiar smell caused by pet, smoking, rubbish, purify the air of a room.(2) it eliminates different
Taste: the compound of calcium is chiefly used in eliminating smell agent in life, thus conch meal can to indoor smoke, infant, patient, pet,
The smell and indoor miscellaneous taste that mould is distributed, which all have, effectively dispels effect, the oxidation especially distributed indoors to cigarette
Carbon and dust Capacity have suction-operated.(3) antibacterial bacteriostatic: have by the special oyster shell whiting film for firing processing to Escherichia coli
In addition extremely strong antibacterial and bactericidal effect also have significant effect to salmonella, yellow glucose fungus, not only with high performance anti-
Bacterium property also has the function of anti-corrosion, anti-tick.(4) antistatic: oyster shell whiting biology coating is by the natural mostly micro- of specially treated
Fine texture duct shell is raw material, and ingredient 100% is calcium, has good antistatic performance.(5) adjusting air humidity: warp
The conch meal itself for crossing calcination processing is high intensity, porous structure, so having good aquatic respiration function, in low pressure, high humility
Metope does not condense under state, and in dry conditions, the moisture stored within the walls can slowly be discharged.Therefore its work of breathing
It can be the regulator of indoor humidity, prevent the generation of moisture condensation and microorganism.(6) fire protection flame retarding: conch meal is by inorganic material group
At, therefore do not burn, even if fire occurs, only there is molten condition in conch meal, will not generate any gas being harmful to the human body
Body smog.
Specific embodiment
In order to keep technical solution of the present invention and advantage clearer, below with reference to the embodiment of the present invention, to the present invention
Technical solution be clearly and completely described.
Embodiment 1
Type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray, the raw material including following parts by weight: 25 parts of conch meal, film forming
26 parts of resin, 12 parts of diatom ooze, 8 parts of clay, 8 parts of glass fibre, 6 parts of gypsum, 4 parts of pigment, 6 parts of adhesive, 1 part of additive.
The conch meal the preparation method comprises the following steps: by shell 1 h of acid soak, then wash with distilled water 2 times, be placed in
Dry 5h under conditions of 80 DEG C, is ground into the shell coarse powder that partial size is 1.0mm, forges under the conditions of being subsequently placed in 1100 DEG C~1200 DEG C
Catalysis 1.5h is burnt, is crushed after cooling with nano grinder, the conch meal that average grain diameter is 500nm is made.
The film-forming resin is formed by acrylic resin and Styrenic Resin Composition.
The partial size of the clay is no more than 2 μm.
The pigment is that phthalocyanine green, iron oxide green and iron oxide brown are composed.
The adhesive is that white glue with vinyl and epoxy acrylic ester gum are composed.
The additive is trimellitic anhydride, methyl tetrahydro phthalic anhydride, dioctyl phthalate, hydroxypropyl methyl fiber
Element is composed.
The blue bricks wall covering modelled after an antique has redesigned blue bricks in use, first clean out the impurity on metope, dust
Size frame bar, directly sprayed and built on the metope in light steel house, being prepared into the outer of blue bricks modelled after an antique using dedicated spray building machine device
It sees.
The preparation method of the blue bricks wall covering modelled after an antique the following steps are included: conch meal and glass fibre are mixed,
It stirs evenly, mixing speed 800r/min, diatom ooze, gypsum, acrylic acid floor paint, clay and gluing is then added while stirring
25min is stirred in agent, and mixing speed 1300r/min is eventually adding pigment and additive, and it is uniform to color to continue stirring.
Embodiment 2
Type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray, the raw material including following parts by weight: 22 parts of conch meal, film forming
28 parts of resin, 14 parts of diatom ooze, 8 parts of clay, 7 parts of glass fibre, 6 parts of gypsum, 4 parts of pigment, 6 parts of adhesive, additive 1.5
Part.
The conch meal the preparation method comprises the following steps: by shell 1 h of acid soak, then wash with distilled water 2 times, be placed in
Dry 5h under conditions of 80 DEG C, is ground into the shell coarse powder that partial size is 1.0mm, forges under the conditions of being subsequently placed in 1100 DEG C~1200 DEG C
Catalysis 1.5h is burnt, is crushed after cooling with nano grinder, the conch meal that average grain diameter is 500nm is made.
The film-forming resin is formed by acrylic resin, epoxy resin and Styrenic Resin Composition.
The partial size of the clay is no more than 2 μm.
The pigment is that phthalocyanine green, iron oxide green and carbon black are composed.
The adhesive is that cloud stone glue and epoxy acrylic ester gum are composed.
The additive is trimellitic anhydride, methyl tetrahydro phthalic anhydride, dioctyl phthalate, hydroxypropyl methyl fiber
Element is composed.
The blue bricks wall covering modelled after an antique has redesigned blue bricks in use, first clean out the impurity on metope, dust
Size frame bar, directly sprayed and built on the metope in light steel house, being prepared into the outer of blue bricks modelled after an antique using dedicated spray building machine device
It sees.
The preparation method of the blue bricks wall covering modelled after an antique the following steps are included: conch meal and glass fibre are mixed,
It stirs evenly, mixing speed 800r/min, diatom ooze, gypsum, acrylic acid floor paint, clay and gluing is then added while stirring
25min is stirred in agent, and mixing speed 1300r/min is eventually adding pigment and additive, and it is uniform to color to continue stirring.
Embodiment 3
Type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray, the raw material including following parts by weight: 26 parts of conch meal, film forming
30 parts of resin, 14 parts of diatom ooze, 10 parts of clay, 8 parts of glass fibre, 7 parts of gypsum, 3 parts of pigment, 6 parts of adhesive, 2 parts of additive.
The conch meal the preparation method comprises the following steps: by shell 1 h of acid soak, then wash with distilled water 2 times, be placed in
Dry 5h under conditions of 80 DEG C, is ground into the shell coarse powder that partial size is 1.0mm, forges under the conditions of being subsequently placed in 1100 DEG C~1200 DEG C
Catalysis 1.5h is burnt, is crushed after cooling with nano grinder, the conch meal that average grain diameter is 500nm is made.
The film-forming resin is acrylic resin.
The partial size of the clay is no more than 2 μm.
The pigment is that phthalocyanine green, iron oxide green, iron oxide brown and carbon black are composed.
The adhesive is that white glue with vinyl and epoxy acrylic ester gum are composed.
The additive is trimellitic anhydride, methyl tetrahydro phthalic anhydride, dioctyl phthalate, hydroxypropyl methyl fiber
Element is composed.
The blue bricks wall covering modelled after an antique has redesigned blue bricks in use, first clean out the impurity on metope, dust
Size frame bar, directly sprayed and built on the metope in light steel house, being prepared into the outer of blue bricks modelled after an antique using dedicated spray building machine device
It sees.
The preparation method of the blue bricks wall covering modelled after an antique the following steps are included: conch meal and glass fibre are mixed,
It stirs evenly, mixing speed 800r/min, diatom ooze, gypsum, acrylic acid floor paint, clay and gluing is then added while stirring
25min is stirred in agent, and mixing speed 1300r/min is eventually adding pigment and additive, and it is uniform to color to continue stirring.
Claims (9)
1. type blue bricks wall covering modelled after an antique is built in a kind of light steel house spray, which is characterized in that the raw material including following parts by weight: shellfish
20~30 parts of shell powder, 20~30 parts of film-forming resin, 5~15 parts of diatom ooze, 5~15 parts of clay, 5~10 parts of glass fibre, gypsum 5
~10 parts, 1~5 part of pigment, 5~10 parts of adhesive, 1~3 part of additive.
2. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the conch meal
The preparation method comprises the following steps: by shell 0.5~1h of acid soak, then wash with distilled water 2~3 times, it is placed in 75~85 DEG C of condition
5~6h of lower drying is ground into the shell coarse powder that partial size is 0.5~1.0mm, calcines under the conditions of being subsequently placed in 800 DEG C~1200 DEG C
It is catalyzed 1~2h, is crushed after cooling with nano grinder, the conch meal that average grain diameter is 500nm is made.
3. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the film forming tree
Rouge is formed by one of acrylic resin, epoxy resin, styrene resin or multiple combinations.
4. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the grain of the clay
Diameter is no more than 2 μm.
5. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the pigment is
Phthalocyanine green, iron oxide green, iron oxide brown, the combination of two or more in carbon black form.
6. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the adhesive
It is formed for one of white glue with vinyl, cloud stone glue, epoxy acrylic ester gum or multiple combinations.
7. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the additive
It is composed for trimellitic anhydride, methyl tetrahydro phthalic anhydride, dioctyl phthalate, hydroxypropyl methyl cellulose.
8. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the blueness modelled after an antique
Brick wall coating materials have redesigned the size frame bar of blue bricks, using special in use, first clean out the impurity on metope, dust
Spray building machine device, which directly sprays, to be built on the metope in light steel house, and the appearance of blue bricks modelled after an antique is prepared into.
9. type blue bricks wall covering modelled after an antique is built in light steel house spray according to claim 1, which is characterized in that the blueness modelled after an antique
The preparation method of brick wall coating materials stirs evenly, mixing speed 600 the following steps are included: by conch meal and glass fibre mixing
~1000r/min, is then added diatom ooze, gypsum, acrylic acid floor paint, clay and adhesive while stirring, and stirring 20~
30min, 1200~1500r/min of mixing speed, is eventually adding pigment and additive, and it is uniform to color to continue stirring.