CN104877470A - Transparent sound insulation coating - Google Patents
Transparent sound insulation coating Download PDFInfo
- Publication number
- CN104877470A CN104877470A CN201510273466.3A CN201510273466A CN104877470A CN 104877470 A CN104877470 A CN 104877470A CN 201510273466 A CN201510273466 A CN 201510273466A CN 104877470 A CN104877470 A CN 104877470A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- sound insulation
- transparent
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a transparent sound insulation coating, and relates to the technical field of building materials. The transparent sound insulation coating is prepared from the following raw materials in parts by weight: 20-50 parts of rubber powder, 30-45 parts of mica powder, 15-32 parts of gypsum powder, 10-23 parts of clay, 5-13 parts of cotton fiber, 12-18 parts of isocyanate, 5-10 parts an emulsifier, 1-3 parts of an dispersant, 4-9 parts of a binder, 2-10 parts a decolorizing agent and a proper amount of deionized water. Compared with the prior art, the coating provided by the invention has the transparent sound insulation effect; when glass is coated with the coating, the double sound insulation effect can be realized; when a wall is coated with the coating, not only is the sound insulation effect realized, but also original pattern and color of the wall cannot be affected.
Description
Technical field
The present invention relates to building material technical field, especially a kind of transparent deadener.
Background technology
We live in the world of a sound, but sound is excessive, become noise, will bring infringement to people.According to international standard, in bustling urban district, outdoor noise, daytime can not more than 55 decibels, and night can not more than 45 decibels; General residential district, daytime can not more than 45 decibels, and night can not more than 35 decibels.If people's Long contact time noise, untoward reaction can be produced and may bring out " noise is sick ".Except the infringement sense of hearing, noise also can affect the other system of health, and band serves physiological signs, such as insomnia, neurasthenia, autonomic nervous dysfunction, unstable blood pressure etc.Usually the people of noise effect is suffered can to produce dysphoria, easily tired, difficult concentrating, the syndrome such as slow in reacting.Although have wall and glass port in housing types, play certain soundproof effect, general DeGrain, existing deadener does not mostly have transparent effect, can not be coated onto on glass port, is coated onto on wall and affects the original layout of wall and color.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of transparent deadener, and it has the effect of sound insulation, can solve the problem that deadener is transparent.
In order to solve the problem, the technical solution adopted in the present invention is: this transparent deadener, is made up of the raw material of following weight part: rubber powder 20 ~ 50 parts, mica powder 30 ~ 45 parts, terra alba 15 ~ 32 parts, clay 5 ~ 15 parts, 5 ~ 13 parts, cotton fibre, isocyanic ester 12 ~ 18 parts, emulsifying agent 5 ~ 10 parts, dispersion agent 1 ~ 3 part, 4 ~ 9 parts, tackiness agent, whipping agent 1 ~ 3 part, discoloring agent 2 ~ 10 parts, deionized water 12 ~ 20 parts.
In technique scheme, technical scheme can also be more specifically: be made up of the raw material of following weight part: rubber powder 35 parts, mica powder 38 parts, terra alba 28 parts, clay 10 parts, 10 parts, cotton fibre, isocyanic ester 15 parts, emulsifying agent 8 parts, dispersion agent 2 parts, 7 parts, tackiness agent, whipping agent 2 parts, discoloring agent 6 parts, deionized water 16 parts.
Owing to have employed technique scheme, the present invention compared with prior art has following beneficial effect:
1, rubber powder, mica powder, terra alba, cotton fibre and isocyanic ester have flexible and soundproof effect preferably, mix clay in the present invention, can strengthen the intensity of coating; Mix discoloring agent in the present invention, coating can be decoloured, make water white deadener.
2, during finishing, wall or glass window are smeared sound-proof material of the present invention and both noise decibel can be reduced, play the effect of dual sound insulation, do not affect again the outward appearance of wall, do not affect the perspective of glass window.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described:
Embodiment 1:
This transparent deadener, is made up of the raw material of following weight part: rubber powder 20 parts, mica powder 30 parts, terra alba 15 parts, clay 5 parts, 5 parts, cotton fibre, isocyanic ester 12 parts, emulsifying agent 5 parts, dispersion agent 1 part, 4 parts, tackiness agent, whipping agent 1 part, discoloring agent 2 parts, deionized water 12 parts.
Method for making: by rubber powder, mica powder, terra alba, clay, cotton fibre and isocyanic ester mix, and add deionized water and stirring evenly, add dispersion agent, tackiness agent, whipping agent mixing, stir and obtain mixture, add emulsifying agent again, through emulsifying process, finally add discoloring agent, slag in filtering mixt, makes that mixture is transparent can obtain transparent sound-proof material.
Embodiment 2:
This transparent deadener, is made up of the raw material of following weight part: rubber powder 50 parts, mica powder 45 parts, terra alba 32 parts, clay 15 parts, 13 parts, cotton fibre, isocyanic ester 18 parts, emulsifying agent 10 parts, dispersion agent 3 parts, 9 parts, tackiness agent, whipping agent 3 parts, discoloring agent 10 parts, deionized water 20 parts.
Method for making: by rubber powder, mica powder, terra alba, clay, cotton fibre and isocyanic ester mix, and add deionized water and stirring evenly, add dispersion agent, tackiness agent, whipping agent mixing, stir and obtain mixture, add emulsifying agent again, through emulsifying process, finally add discoloring agent, slag in filtering mixt, makes that mixture is transparent can obtain transparent sound-proof material.
Embodiment 3:
This transparent deadener, is made up of the raw material of following weight part: rubber powder 35 parts, mica powder 38 parts, terra alba 28 parts, clay 10 parts, 10 parts, cotton fibre, isocyanic ester 15 parts, emulsifying agent 8 parts, dispersion agent 2 parts, 7 parts, tackiness agent, whipping agent 2 parts, discoloring agent 6 parts, deionized water 16 parts.
Method for making: by rubber powder, mica powder, terra alba, clay, cotton fibre and isocyanic ester mix, and add deionized water and stirring evenly, add dispersion agent, tackiness agent, whipping agent mixing, stir and obtain mixture, add emulsifying agent again, through emulsifying process, finally add discoloring agent, slag in filtering mixt, makes that mixture is transparent can obtain transparent sound-proof material.
Claims (2)
1. a transparent deadener, is characterized in that being made up of the raw material of following weight part: rubber powder 20 ~ 50 parts, mica powder 30 ~ 45 parts, terra alba 15 ~ 32 parts, clay 5 ~ 15 parts, 5 ~ 13 parts, cotton fibre, isocyanic ester 12 ~ 18 parts, emulsifying agent 5 ~ 10 parts, dispersion agent 1 ~ 3 part, 4 ~ 9 parts, tackiness agent, whipping agent 1 ~ 3 part, discoloring agent 2 ~ 10 parts, deionized water 12 ~ 20 parts.
2. transparent deadener according to claim 1, is characterized in that: rubber powder 35 parts, mica powder 38 parts, terra alba 28 parts, clay 10 parts, 10 parts, cotton fibre, isocyanic ester 15 parts, emulsifying agent 8 parts, dispersion agent 2 parts, 7 parts, tackiness agent, whipping agent 2 parts, discoloring agent 6 parts, deionized water 16 parts.