CN108395775A - A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent - Google Patents
A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent Download PDFInfo
- Publication number
- CN108395775A CN108395775A CN201810353936.0A CN201810353936A CN108395775A CN 108395775 A CN108395775 A CN 108395775A CN 201810353936 A CN201810353936 A CN 201810353936A CN 108395775 A CN108395775 A CN 108395775A
- Authority
- CN
- China
- Prior art keywords
- parts
- negative ion
- formaldehyde catching
- agent
- phenylpropyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent, and raw material includes following components by weight:10 20 parts of styrene-acrylic emulsion, 10 20 parts of diatomite, 10 16 parts of nano titania slurry, 46 parts of antimicrobial nano titanium dioxide, 50 60 parts of flyash, 10 20 parts of titanium dioxide, 10 20 parts of powdered whiting, 13 parts of negative ion powder, 13 parts of hydroxyethyl cellulose solution, 35 parts of formaldehyde catching agent, 0.5 1.0 parts of dispersant, 0.2 0.5 parts of antifoaming agent, 1.0 2.5 parts of coalescents, 0.5 0.9 parts of thickener, 13 parts of antifreezing agent, 40 60 parts of deionized water.
Description
Technical field
The present invention relates to a kind of coating, and in particular to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent and its preparation
Method.
Background technology
With economic rapid development, people increasingly pay attention to the health of itself, gather around there are one health environment be to maintain from
The primary premise of body health.Currently, most of coating is solvent based coating, in solvent based coating containing about 50% it is organic molten neat
IJ, can discharge a large amount of VOC gas after the spraying of these coating, not only seriously endanger the health to user, can also be to big
Gas pollutes, and damages ecological environment.According to statistics, the VOC that the life and production activity of the mankind is discharged into air accounts for global big
The 15% of gas contaminant capacity, and the VOC amounts that coating processing and production release account for the 20 °/Γ 30% of its total emission volumn, are only second to vapour
The discharge of tail gas and occupy contaminant capacity second.Therefore, the discharge of control coating VOC is increasingly valued by people.Water
Property ideal substitute of the coating as solvent based coating, it is safe and nontoxic with its, pollution-free the advantages that, receive all circles research and development scholar
Concern.Many public places just will produce great security risk when losing light source, as underpass, stair are walked
Corridor etc..At this time, just there is an urgent need for being coated with fluorescent paint in these places, to reduce security risk.Elsewhere, as various safety are answered
The danger signals such as anxious active flag, high-voltage electricity, it is also desirable to this coating.Anion is known as air vitamin, has environmentally friendly, strong
Health, sterilizing three zones, can not only purify air, moreover it is possible to which the resistance for enhancing people boosts metabolism, existing medical research
It is 1000-2000/cm3 to show to maintain the anion number of health of people, and the anion number of the present residential district, office only has
40-50/cm3, far less than the standard requirement for maintaining health, coating type is various, is all widely answered in many fields
With.
Most of interior/exterior decoration material on the market is organic material or organic/inorganic composite material, they contain greatly
Measure VOC, such as formaldehyde, benzene noxious material, be easy after making moist colour fading, yellowing, it is mouldy, fall off, and there is a problem of sum easy to aging
Inflammable security risk.Therefore research safety, nontoxic, good weatherability, can eliminate formaldehyde and can discharge the novel of anion
Coating becomes research hotspot, greatly develops the needs of demand and reality that such new coating is the epoch.
Invention content
The purpose of the present invention provides a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent aiming at existing issue,
A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent is using styrene-acrylic emulsion as film forming matter, the diatomite of addition, nanometer two
Titania slurry, antimicrobial nano titanium dioxide, flyash, titanium dioxide, powdered whiting, negative ion powder, hydroxyethyl cellulose are molten
The face of a variety of multifunctionalities such as liquid, formaldehyde catching agent, filler, and part of auxiliary is added, the one kind being prepared is caught containing formaldehyde
Catch the phenylpropyl alcohol negative ion paint of agent.A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent not only has good fragrance
Property, water resistance, alkali resistance, abrasion resistance, polluting proofing property and ageing resistance, but also with static sustained release anion, dispel
The advantages that except the pernicious gases such as formaldehyde, ammonia, benzene, antibacterial bacteriostatic, pollution-free, environmentally protective, high-decoration energy.
The technical solution adopted in the present invention is as follows to achieve the above object:A kind of phenylpropyl alcohol containing formaldehyde catching agent bear from
Sub- coating, raw material include following components by weight:10-20 parts of styrene-acrylic emulsion, 10-20 parts of diatomite, nano-titanium dioxide
10-16 parts of slurry, 4-6 parts of antimicrobial nano titanium dioxide, 50-60 parts of flyash, 10-20 parts of titanium dioxide, powdered whiting 10-20
Part, 1-3 parts of negative ion powder, 1-3 parts of hydroxyethyl cellulose solution, 3-5 parts of formaldehyde catching agent, 0.5-1.0 parts of dispersant, defoaming
0.2-0.5 parts of agent, 1.0-2.5 parts of coalescents, 0.5-0.9 parts of thickener, 1-3 parts of antifreezing agent, 40-60 parts of deionized water.
Further, the titanium dioxide rutile type titanium white, grain size are 100~150 μm.
Further, the negative ion powder is the tourmaline powder that granularity is 80-150nm.
Further, the formaldehyde catching agent is adipic dihydrazide.
Further, the pentasodium triphosphate of dispersing agent.
Further, the antifoaming agent is AMP-19.
Further, the coalescents are Texanol.
Further, the thickener is polyacrylic acid.
Further, the antifreezing agent is ethylene glycol.
Further, preparation method includes the following steps:
S10, required various raw material materials are weighed;
S11, deionized water, dispersant, antifreezing agent, half antifoaming agent, ethoxy fibre are added in the case where disperseing sand mill high speed dispersion
After the plain solution of dimension, formaldehyde catching agent, flyash, high speed dispersion 10-20min, 120-240min is being sanded, is obtaining loaded modified powder
Coal ash slurry;
S12, will obtain loaded modified flyash slurry and nano material nano titania slurry, antimicrobial nano titanium dioxide and
Titanium dioxide, powdered whiting, negative ion powder, coalescents, thickener, remaining antifoaming agent are after high speed dispersion is uniform, into sand
Grinding machine after being ground to suitable fineness, into dispersion machine, is added styrene-acrylic emulsion low speed dispersion mixing and uniformly contains up to required one kind
There is the phenylpropyl alcohol negative ion paint of formaldehyde catching agent.
It is compared with the prior art, the invention has the advantages that:
1, at it after a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent in the present invention is wet-process modified to flyash progress
Area load formaldehyde catching agent, can obtain modified flyash powder, prepare interior wall coating using it as filler, pass through inventor
Its powder of detection and the interior wall coating have eradicating efficacy to formaldehyde in indoor air.The result shows that:Formaldehyde catching agent can be very well
The fly ash grain surface of ground load after modification;Loading fine coal coal ash and its coating there is elimination well to imitate indoor formaldehyde
Fruit, especially when the pigment volume concentration (PVC) of fine coal(PVC)With critical pigment volume concentration(CPVC)When close, coating has optimal
Formaldehyde catching eradicating efficacy;Traditional performance can also meet corresponding coating technology requirement simultaneously, can be applied to interior wall coating
In;
2, nano-titanium dioxide shielding ultraviolet rays are added in a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent of the present invention
Effect is strong, prevents the infringement of ultraviolet light, improves the service life of coating.Meanwhile higher hardness, density, dielectric constant
And refractive index, help to improve the covering power of coating, covering power growth rate is about 27.61%, improve coating workability and
Environmental protection and energy saving performance has corresponding high-decoration, breathing humidity;
3, the aqueous architectural of addition composite Nano TiO2 applies in a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent of the present invention
Material has sterilizing function, and the coating containing nano TiO 2 is after ultraviolet light irradiates 30min, to staphylococcus aureus, Escherichia coli
Bactericidal effect is preferable, and bacteriostasis rate is respectively 78.70%, 80.19%, but in the case where no ultraviolet light irradiates, without apparent bactericidal effect;
4, it is diatomite the primary functional components of diatom ooze decorative wall material to be added in the present invention, since diatomite has porous knot
Structure, when indoor humidity is high, diatomite can be by Vapor adsorption, when indoor humidity is low, and steam, which can be desorbed, for diatomite discharges, and makes interior
The relative humidity in space is automatically adjusted in 40%~70%, this is exactly the comfortable humidity section of body-sensing.Diatom ooze decorative wall material can
The relative humidity of the interior space is set to be maintained at 70% hereinafter, can prevent from condensing.Since diatomite has porous structure, in gap
Dry air has preferable heat-proof quality.90% or more relative humidity easily mildews bacterium, and relative humidity is 70% hereinafter, can prevent
Mould growth.The bait mould that not will produce acarid, can be anti-mite.Due to tourmaline powder load nano-titanium dioxide generate bear from
Son has sterilizing function, can play preferable bactericidal effect.Pernicious gas is adsorbed by diatom ooze, then by anion and pernicious gas
Reaction, pernicious gas is decomposed, and deodorization and can prevent finishing pollution syndrome.The anion of generation passes through respiratory tract, skin quilt
In suction body, harmful active oxygen is neutralized, finishing pollution syndrome can be treated.Give feeling that is soft, pleasant, loosening, can receive
To good conditioning and treating effect, environmentally protective performance is strong;
5, a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent of the invention not only have good armaticity, water resistance,
Alkali resistance, abrasion resistance, polluting proofing property and ageing resistance, but also with static sustained release anion, dispel formaldehyde, ammonia,
The advantages that pernicious gases such as benzene, antibacterial bacteriostatic, pollution-free, environmentally protective, high-decoration energy.
Specific implementation mode
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.The specific embodiments described herein are merely illustrative of the present invention, is not used to limit
The present invention.
Embodiment 1
A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent, raw material include following components by weight:Styrene-acrylic emulsion 10
Part, 10 parts of diatomite, 10 parts of nano titania slurry, 4 parts of antimicrobial nano titanium dioxide, 50 parts of flyash, 10 parts of titanium dioxide,
10 parts of powdered whiting, 1 part of negative ion powder, 1 part of hydroxyethyl cellulose solution, 3 parts of formaldehyde catching agent, 0.5 part of dispersant, defoaming
0.2 part of agent, 1.0 parts of coalescents, 0.5 part of thickener, 1 part of antifreezing agent, 40 parts of deionized water.
The titanium dioxide rutile type titanium white, grain size are 100 μm.
The negative ion powder is the tourmaline powder that granularity is 80nm.
The formaldehyde catching agent is adipic dihydrazide.
The pentasodium triphosphate of dispersing agent.
The antifoaming agent is AMP-19.
The coalescents are Texanol.
The thickener is polyacrylic acid.
The antifreezing agent is ethylene glycol.
Preparation method includes the following steps:
S10, required various raw material materials are weighed;
S11, deionized water, dispersant, antifreezing agent, half antifoaming agent, ethoxy fibre are added in the case where disperseing sand mill high speed dispersion
After the plain solution of dimension, formaldehyde catching agent, flyash, high speed dispersion 10min, 120min is being sanded, is obtaining loaded modified coal ash pulp
Material;
S12, will obtain loaded modified flyash slurry and nano material nano titania slurry, antimicrobial nano titanium dioxide and
Titanium dioxide, powdered whiting, negative ion powder, coalescents, thickener, remaining antifoaming agent are after high speed dispersion is uniform, into sand
Grinding machine after being ground to suitable fineness, into dispersion machine, is added styrene-acrylic emulsion low speed dispersion mixing and uniformly contains up to required one kind
There is the phenylpropyl alcohol negative ion paint of formaldehyde catching agent.
Embodiment 2
A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent, raw material include following components by weight:Styrene-acrylic emulsion 20
Part, 20 parts of diatomite, 16 parts of nano titania slurry, 6 parts of antimicrobial nano titanium dioxide, 60 parts of flyash, 20 parts of titanium dioxide,
20 parts of powdered whiting, 3 parts of negative ion powder, 3 parts of hydroxyethyl cellulose solution, 5 parts of formaldehyde catching agent, 1.0 parts of dispersion, defoaming
0.5 part of agent, 2.5 parts of coalescents, 0.9 part of thickener, 3 parts of antifreezing agent, 60 parts of deionized water.
The titanium dioxide rutile type titanium white, grain size are 150 μm.
The negative ion powder is the tourmaline powder that granularity is 150nm.
The formaldehyde catching agent is adipic dihydrazide.
The pentasodium triphosphate of dispersing agent.
The antifoaming agent is AMP-19.
The coalescents are Texanol.
The thickener is polyacrylic acid.
The antifreezing agent is ethylene glycol.
Preparation method includes the following steps:
S10, required various raw material materials are weighed;
S11, deionized water, dispersant, antifreezing agent, half antifoaming agent, ethoxy fibre are added in the case where disperseing sand mill high speed dispersion
After the plain solution of dimension, formaldehyde catching agent, flyash, high speed dispersion 20min, 240min is being sanded, is obtaining loaded modified coal ash pulp
Material;
S12, will obtain loaded modified flyash slurry and nano material nano titania slurry, antimicrobial nano titanium dioxide and
Titanium dioxide, powdered whiting, negative ion powder, coalescents, thickener, remaining antifoaming agent are after high speed dispersion is uniform, into sand
Grinding machine after being ground to suitable fineness, into dispersion machine, is added styrene-acrylic emulsion low speed dispersion mixing and uniformly contains up to required one kind
There is the phenylpropyl alcohol negative ion paint of formaldehyde catching agent.
Embodiment 3
A kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent, raw material include following components by weight:Styrene-acrylic emulsion 15
Part, 15 parts of diatomite, 12 parts of nano titania slurry, 5 parts of antimicrobial nano titanium dioxide, 55 parts of flyash, 15 parts of titanium dioxide,
15 parts of powdered whiting, 2 parts of negative ion powder, 2 parts of hydroxyethyl cellulose solution, 4 parts of formaldehyde catching agent, 0.6 part of dispersant, defoaming
0.4 part of agent, 1.5 parts of coalescents, 0.8 part of thickener, 2 parts of antifreezing agent, 45 parts of deionized water.
The titanium dioxide rutile type titanium white, grain size are 120 μm.
The negative ion powder is the tourmaline powder that granularity is 120nm.
The formaldehyde catching agent is adipic dihydrazide.
The pentasodium triphosphate of dispersing agent.
The antifoaming agent is AMP-19.
The coalescents are Texanol.
The thickener is polyacrylic acid.
The antifreezing agent is ethylene glycol.
Preparation method includes the following steps:
S10, required various raw material materials are weighed;
S11, deionized water, dispersant, antifreezing agent, half antifoaming agent, ethoxy fibre are added in the case where disperseing sand mill high speed dispersion
After the plain solution of dimension, formaldehyde catching agent, flyash, high speed dispersion 15min, 180min is being sanded, is obtaining loaded modified coal ash pulp
Material;
S12, will obtain loaded modified flyash slurry and nano material nano titania slurry, antimicrobial nano titanium dioxide and
Titanium dioxide, powdered whiting, negative ion powder, coalescents, thickener, remaining antifoaming agent are after high speed dispersion is uniform, into sand
Grinding machine after being ground to suitable fineness, into dispersion machine, is added styrene-acrylic emulsion low speed dispersion mixing and uniformly contains up to required one kind
There is the phenylpropyl alcohol negative ion paint of formaldehyde catching agent.
Table 1 is a kind of phenylpropyl alcohol negative ion paint antibacterial bacteriostatic performance detection table containing formaldehyde catching agent in the present invention
Table 2 is a kind of phenylpropyl alcohol negative ion paint elimination formaldehyde performance detection table containing formaldehyde catching agent in the present invention
Table 3 is a kind of phenylpropyl alcohol negative ion paint anion-generating capacity detection table containing formaldehyde catching agent in the present invention
From the data in the table, coating anion average increase of the invention is 126/scm2.
Above-described embodiment is only intended to clearly illustrate the application example, and does not limit the embodiments.
For those of ordinary skill in the art, other various forms of variations can also be made on the basis of the above description
Or it changes.There is no necessity and possibility to exhaust all the enbodiments.And the obvious variation thus amplified out
Or among changing still in the protection domain of the application type.
Claims (10)
1. a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent, which is characterized in that its raw material includes with the following group by weight
Point:10-20 parts of styrene-acrylic emulsion, 10-20 parts of diatomite, 10-16 parts of nano titania slurry, antimicrobial nano titanium dioxide 4-6
Part, 50-60 parts of flyash, 10-20 parts of titanium dioxide, 10-20 parts of powdered whiting, 1-3 parts of negative ion powder, hydroxyethyl cellulose are molten
1-3 parts of liquid, 3-5 parts of formaldehyde catching agent, 0.5-1.0 parts of dispersant, 0.2-0.5 parts of antifoaming agent, 1.0-2.5 parts of coalescents,
0.5-0.9 parts of thickener, 1-3 parts of antifreezing agent, 40-60 parts of deionized water.
2. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Titanium dioxide rutile type titanium white, grain size be 100~150 μm.
3. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Negative ion powder be tourmaline powder that granularity is 80-150nm.
4. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Formaldehyde catching agent be adipic dihydrazide.
5. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Pentasodium triphosphate of dispersing agent.
6. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Antifoaming agent be AMP-19.
7. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Coalescents be Texanol.
8. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Thickener be polyacrylic acid.
9. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is described
Antifreezing agent be ethylene glycol.
10. according to a kind of phenylpropyl alcohol negative ion paint containing formaldehyde catching agent described in claim 1, it is characterised in that:It is made
Preparation Method includes the following steps:
S10, required various raw material materials are weighed;
S11, deionized water, dispersant, antifreezing agent, half antifoaming agent, ethoxy fibre are added in the case where disperseing sand mill high speed dispersion
After the plain solution of dimension, formaldehyde catching agent, flyash, high speed dispersion 10-20min, 120-240min is being sanded, is obtaining loaded modified powder
Coal ash slurry;
S12, will obtain loaded modified flyash slurry and nano material nano titania slurry, antimicrobial nano titanium dioxide and
Titanium dioxide, powdered whiting, negative ion powder, coalescents, thickener, remaining antifoaming agent are after high speed dispersion is uniform, into sand
Grinding machine after being ground to suitable fineness, into dispersion machine, is added styrene-acrylic emulsion low speed dispersion mixing and uniformly contains up to required one kind
There is the phenylpropyl alcohol negative ion paint of formaldehyde catching agent.