CN109486316A - A kind of wall material protective film and preparation method thereof - Google Patents
A kind of wall material protective film and preparation method thereof Download PDFInfo
- Publication number
- CN109486316A CN109486316A CN201811174375.4A CN201811174375A CN109486316A CN 109486316 A CN109486316 A CN 109486316A CN 201811174375 A CN201811174375 A CN 201811174375A CN 109486316 A CN109486316 A CN 109486316A
- Authority
- CN
- China
- Prior art keywords
- wall material
- protective film
- material protective
- catalytic
- lotion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The application belongs to Wall of building protection technique field, more particularly to a kind of wall material protective film and preparation method thereof.Contain peculiar smell, formaldehyde, benzene,toluene,xylene, VOC and some bacteriums in existing finishing wall material, is endangered to the health care belt of user.The application provides a kind of wall material protective film, and the wall material protective film is composed of the following raw materials in parts by weight: lotion 250~350, nano photo-catalytic 30~50, formaldehyde catching agent 15~250, active nano silver ion 70~120, deionized water are several.It with anti-shedding, light, good hand touch, scrubbing resistance, eliminates the unusual smell, sterilize, except formaldehyde, ammonia, benzene,toluene,xylene, VOC etc., purify the air of a room, beautify the environment.
Description
Technical field
The application belongs to Wall of building protection technique field, more particularly to a kind of wall material protective film and preparation method thereof.
Background technique
Wall material " refers to related wall plastering construction as its name suggests, the material handled common mortar face.It anticipates now
In justice, for " wall material " product that we are seen all titled with " environmental protection " wall material, perhaps this also just become a general character of wall material.City
The wall material product often having on face has, common wallpaper, wall cloth, liquid wallpaper, diatom ooze, volcanic mud, husky picture wall material, Sha Huani, sand
Draw paint etc..
Building decoration and fitment currently on the market, either family or public place use emulsion paint, conch meal mostly
Coating, diatom ooze coating or wallpaper etc., all have respective function concurrently, but fit up in wall material containing peculiar smell, formaldehyde, benzene,
Toluene, dimethylbenzene, VOC and some bacteriums, endanger to the health care belt of user.
Summary of the invention
1. technical problems to be solved
Based on building decoration and fitment currently on the market, either family or public place, emulsion paint, shellfish are used mostly
Shell powder coating, diatom ooze coating or wallpaper etc., all have respective function concurrently, but fit up in wall material containing peculiar smell, formaldehyde,
Benzene,toluene,xylene, VOC and some bacteriums, to user health care belt come the problem of harm, this application provides a kind of walls
Material protective film and preparation method thereof.
2. technical solution
To achieve the above object, this application provides a kind of wall material protective films, and the wall material protective film by weighing as follows
Measure the raw material composition of part: lotion 250~350, nano photo-catalytic 30~50, formaldehyde catching agent 15~250, active nano silver ion
70~120, deionized water is several.
Optionally, the wall material protective film is composed of the following raw materials in parts by weight: lotion 280~330, nano photo-catalytic 35
~45, formaldehyde catching agent 25~200, active nano silver ion 90~110, deionized water are several.
Optionally, the wall material protective film is composed of the following raw materials in parts by weight: lotion 300, nano photo-catalytic 40, formaldehyde
Agent for capturing 130, active nano silver ion 100, deionized water are several.
Optionally, the lotion is acrylate styrene emulsion polymer.
Optionally, the nano photo-catalytic is titanium dioxide.
Optionally, the formaldehyde catching agent is imidazolidinone.
The application also provides a kind of preparation method of wall material protective film, and the preparation method includes the following steps:
Step 1: lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water
Afterwards, it is added sequentially in reactor tank according to the proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.
3. beneficial effect
Compared with prior art, a kind of beneficial effect of wall material protective film provided by the present application and preparation method thereof is:
Wall material protective film provided by the present application, by by lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver from
Son is dissolved in deionized water, and manufactured product is sprayed at family, public place, surface of wall, can form one layer after dry
Protective film has anti-shedding, light, good hand touch, scrubbing resistance, eliminates the unusual smell, sterilizes, removes formaldehyde, ammonia, benzene,toluene,xylene, VOC
Deng purifying the air of a room, beautify the environment.
Specific embodiment
Hereinafter, the specific embodiment of the application will be described in detail, it is affiliated according to these detailed descriptions
Field technical staff can implement the application it can be clearly understood that the application.Without prejudice to the application principle,
Feature in each different embodiment can be combined to obtain in new embodiment, or substitution some embodiments
Certain features obtain other preferred embodiments.
Nano photo-catalytic refers under light illumination, and chemical change itself does not occur, and can but promote the substance of chemical reaction,
Function is as the chlorophyll in photosynthesis.Dichloride in anatase type TiO2It is most important photocatalyst material, when it absorbs sunlight
Or after the energy in other light sources, the electronics of particle surface is activated, and escapes from original track, while Surface Creation is positively charged
Hole.The electronics of evolution has strong reducing property, and hole can generate after then there is strong oxidizing property, the two to react with the aqueous vapor in air
Active oxygen and hydroxyl free radical.Active oxygen, hydroxyl free radical can be by the oxidations such as most of organic matter, pollutant, foul smell, bacterium point
Solution is at harmless carbon dioxide and water.
Nano photo-catalytic technology is a kind of nano bionic technology, be used for the depollution of environment, self-cleaning material, advanced new energy,
Treatment of cancer, multiple Disciplinary Frontiers such as high efficiency antibacterial.
Embodiment 1
The application provides a kind of wall material protective film, and the wall material protective film is composed of the following raw materials in parts by weight: lotion
250, nano photo-catalytic 30, formaldehyde catching agent 15, active nano silver ion 70, deionized water are several.
Optionally, the lotion is acrylate styrene emulsion polymer.
Optionally, the nano photo-catalytic is titanium dioxide.
Optionally, the formaldehyde catching agent is imidazolidinone.
A kind of preparation method of wall material protective film, the preparation method include the following steps:
Step 1: lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water
Afterwards, it is added sequentially in reactor tank according to the proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.
Embodiment 2
The application provides a kind of wall material protective film, and the wall material protective film is composed of the following raw materials in parts by weight: lotion
280, nano photo-catalytic 35, formaldehyde catching agent 25, active nano silver ion 90, deionized water are several.
Optionally, the lotion is acrylate styrene emulsion polymer.
Optionally, the nano photo-catalytic is titanium dioxide.
Optionally, the formaldehyde catching agent is imidazolidinone.
A kind of preparation method of wall material protective film, the preparation method include the following steps:
Step 1: lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water
Afterwards, it is added sequentially in reactor tank according to the proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.
Embodiment 3
The application provides a kind of wall material protective film, and the wall material protective film is composed of the following raw materials in parts by weight: lotion
300, nano photo-catalytic 40, formaldehyde catching agent 130, active nano silver ion 100, deionized water are several.
Optionally, the lotion is acrylate styrene emulsion polymer.
Optionally, the nano photo-catalytic is titanium dioxide.
Optionally, the formaldehyde catching agent is imidazolidinone.
A kind of preparation method of wall material protective film, the preparation method include the following steps:
Step 1: lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water
Afterwards, it is added sequentially in reactor tank according to the proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.
Embodiment 4
The application provides a kind of wall material protective film, and the wall material protective film is composed of the following raw materials in parts by weight: lotion
330, nano photo-catalytic 45, formaldehyde catching agent 200, active nano silver ion 110, deionized water are several.
Optionally, the lotion is acrylate styrene emulsion polymer.
Optionally, the nano photo-catalytic is titanium dioxide.
Optionally, the formaldehyde catching agent is imidazolidinone.
A kind of preparation method of wall material protective film, the preparation method include the following steps:
Step 1: lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water
Afterwards, it is added sequentially in reactor tank according to the proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.
Embodiment 5
Itself a kind of wall material protective film please be provide, the wall material protective film is composed of the following raw materials in parts by weight: lotion
350, nano photo-catalytic 50, formaldehyde catching agent 250, active nano silver ion 120, deionized water are several.
Optionally, the lotion is acrylate styrene emulsion polymer.
Optionally, the nano photo-catalytic is titanium dioxide.
Optionally, the formaldehyde catching agent is imidazolidinone.
A kind of preparation method of wall material protective film, the preparation method include the following steps:
Step 1: lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water
Afterwards, it is added sequentially in reactor tank according to the proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.
It is wherein most preferred embodiment with embodiment 3.
This application involves a kind of wall material protective film physicochemical property result:
Wall material protective film provided by the present application, by by lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver from
Son is dissolved in deionized water, and manufactured product is sprayed at family, public place, surface of wall, can form one layer after dry
Protective film has anti-shedding, light, good hand touch, scrubbing resistance, eliminates the unusual smell, sterilizes, removes formaldehyde, ammonia, benzene,toluene,xylene, VOC
Deng purifying the air of a room, beautify the environment.
Although the application is described above by referring to specific embodiment, one of ordinary skill in the art are answered
Work as understanding, in principle disclosed in the present application and range, many modifications can be made for configuration disclosed in the present application and details.
The protection scope of the application is determined by the attached claims, and claim is intended to technical characteristic in claim
Equivalent literal meaning or range whole modifications for being included.
Claims (7)
1. a kind of wall material protective film, it is characterised in that: the wall material protective film is composed of the following raw materials in parts by weight: lotion 250
~350, nano photo-catalytic 30~50, formaldehyde catching agent 15~250, active nano silver ion 70~120, deionized water are several.
2. wall material protective film as described in claim 1, it is characterised in that: the wall material protective film by following parts by weight raw material
Composition: lotion 280~330, formaldehyde catching agent 25~200, active nano silver ion 90~110, is gone nano photo-catalytic 35~45
Ionized water is several.
3. wall material protective film as described in claim 1, it is characterised in that: the wall material protective film by following parts by weight raw material
Composition: lotion 300, nano photo-catalytic 40, formaldehyde catching agent 130, active nano silver ion 100, deionized water are several.
4. wall material protective film according to any one of claims 1 to 3, it is characterised in that: the lotion is acrylate benzene
Ethylene emulsion polymerization object.
5. wall material protective film as claimed in claim 4, it is characterised in that: the nano photo-catalytic is titanium dioxide.
6. wall material protective film as claimed in claim 4, it is characterised in that: the formaldehyde catching agent is imidazolidinone.
7. a kind of preparation method of wall material protective film, it is characterised in that: the preparation method includes the following steps:
Step 1: after lotion, nano photo-catalytic, formaldehyde catching agent, active nano silver ion are completely dissolved with deionized water, pressing
It is added sequentially in reactor tank according to proportion；
Step 2: starting reactor tank stirs 30~45 minutes at normal temperature with 300~500 revs/min.