CN107715921A - A kind of indoor formaldehyde removes catalyst and preparation method thereof - Google Patents
A kind of indoor formaldehyde removes catalyst and preparation method thereof Download PDFInfo
- Publication number
- CN107715921A CN107715921A CN201710966904.3A CN201710966904A CN107715921A CN 107715921 A CN107715921 A CN 107715921A CN 201710966904 A CN201710966904 A CN 201710966904A CN 107715921 A CN107715921 A CN 107715921A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- catalyst
- silicon
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of indoor formaldehyde to remove catalyst and preparation method thereof, catalyst component includes 10 20 parts of nano titanium oxide, 4 12 parts of diammonium hydrogen phosphate, 5 10 parts of silicon powder, 28 parts of nano whisker silicon, 4 12 parts of polyvinyl alcohol, 3 10 parts of diatomite, 16 parts of nanometer anion powder, 28 parts of nano zine oxide, 4 12 parts of active carbon nanoparticles in parts by weight, the catalyst of the present invention can effectively remove the formaldehyde of interior, keep room air pure and fresh.
Description
Technical field
The present invention relates to catalyst preparing technical field, specially a kind of indoor formaldehyde removes catalyst and preparation method thereof.
Background technology
The housing industry in China is interior over the next several years will persistently to keep high speed development situation, every year the newly-increased area of residence 5
Hundred million square metres, the old room for having 600,000,000 square metres every year in addition carries out decoration renovation.With the development of Chinese architecture adnornment industry, 2010
Year building decorating industry China have become You18Wan Jia enterprises, more than 1,400 ten thousand practitioners, 1.85 trillion yuan annual value of production it is big
Industry;Since nearly 20 years, Chinese architecture adnornment industry is quickly grown, annual growth will about 20%, this data is significantly larger than the same period
GDP growth rate.
At the same time, a large amount of synthetic materials are widely used in interior decoration and finished product furniture, and they are discharged
The volatility toxic compounds such as formaldehyde serious pollution is caused to indoor environment, be cancer, breathing problem, leukaemia,
The main inducing of immunity reduction, fetus teratogenesis etc., thus caused various diseases and indoor environment case, have had a strong impact on people
The physical and mental health of the people masses and normal life.Room air pollution turns into the another killer of infringement human health.At present, interior is adopted
Removing catalyst can eliminate formaldehyde to a certain extent, but removing is not thorough, and effect is poor.
The content of the invention
It is an object of the invention to provide a kind of indoor formaldehyde to remove catalyst and preparation method thereof, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical scheme:A kind of indoor formaldehyde removes catalyst, and catalyst component is pressed
Parts by weight include nano titanium oxide 10-20 parts, diammonium hydrogen phosphate 4-12 parts, silicon powder 5-10 parts, nano whisker silicon 2-8
Part, polyvinyl alcohol 4-12 parts, diatomite 3-10 parts, nanometer anion powder 1-6 parts, nano zine oxide 2-8 parts, active carbon nanoparticles 4-
12 parts.
Preferably, it is micro- to include 15 parts of nano titanium oxide, 8 parts of diammonium hydrogen phosphate, silicon for the preferable composition proportion of catalyst component
8 parts of powder, 5 parts of nano whisker silicon, 8 parts of polyvinyl alcohol, 7 parts of diatomite, 3 parts of nanometer anion powder, nano zine oxide 5 part, nanometer
8 parts of activated carbon.
Preferably, its preparation method comprises the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.
Compared with prior art, the beneficial effects of the invention are as follows:The catalyst of the present invention can effectively remove interior
Formaldehyde, keep room air it is pure and fresh;Wherein, nanometer anion powder, nano zine oxide, the nano active added in the present invention
Charcoal, the peculiar smell of interior while formaldehyde is eliminated, can be removed, anion is discharged, further purifies air, the present invention can be with
The biological pollutants such as elimination virus bacterium, product have no irritating odor, without secondary pollution;Obtained through overtesting, using this hair
After bright obtained catalyst uses 1 month indoors, content of formaldehyde reduces by 95%;, being capable of fully erased formaldehyde after 2 months.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
The present invention provides following technical scheme:A kind of indoor formaldehyde removes catalyst, and catalyst component includes receiving in parts by weight
Rice titanium dioxide 10-20 parts, diammonium hydrogen phosphate 4-12 parts, silicon powder 5-10 parts, nano whisker silicon 2-8 parts, polyvinyl alcohol 4-12
Part, diatomite 3-10 parts, nanometer anion powder 1-6 parts, nano zine oxide 2-8 parts, active carbon nanoparticles 4-12 parts.
Embodiment one:
Catalyst component includes 10 parts of nano titanium oxide, 4 parts of diammonium hydrogen phosphate, 5 parts of silicon powder, nano whisker silicon in parts by weight
2 parts, 4 parts of polyvinyl alcohol, 3 parts of diatomite, 1 part of nanometer anion powder, 2 parts of nano zine oxide, 4 parts of active carbon nanoparticles.
The preparation method of the present embodiment comprises the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.
Embodiment two:
Catalyst component includes 20 parts of nano titanium oxide, 12 parts of diammonium hydrogen phosphate, 10 parts of silicon powder, nano whisker in parts by weight
8 parts of silicon, 12 parts of polyvinyl alcohol, 10 parts of diatomite, 6 parts of nanometer anion powder, 8 parts of nano zine oxide, 12 parts of active carbon nanoparticles.
The preparation method of the present embodiment comprises the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.
Embodiment three:
Catalyst component includes 12 parts of nano titanium oxide, 5 parts of diammonium hydrogen phosphate, 6 parts of silicon powder, nano whisker silicon in parts by weight
3 parts, 6 parts of polyvinyl alcohol, 5 parts of diatomite, 2 parts of nanometer anion powder, 3 parts of nano zine oxide, 6 parts of active carbon nanoparticles.
The preparation method of the present embodiment comprises the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.
Example IV:
Catalyst component includes 18 parts of nano titanium oxide, 10 parts of diammonium hydrogen phosphate, 9 parts of silicon powder, nano whisker in parts by weight
7 parts of silicon, 10 parts of polyvinyl alcohol, 9 parts of diatomite, 5 parts of nanometer anion powder, 7 parts of nano zine oxide, 10 parts of active carbon nanoparticles.
The preparation method of the present embodiment comprises the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.
Embodiment five:
Catalyst component includes 15 parts of nano titanium oxide, 8 parts of diammonium hydrogen phosphate, 8 parts of silicon powder, nano whisker silicon in parts by weight
5 parts, 8 parts of polyvinyl alcohol, 7 parts of diatomite, 3 parts of nanometer anion powder, 5 parts of nano zine oxide, 8 parts of active carbon nanoparticles.
The preparation method of the present embodiment comprises the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.
The catalyst of the present invention can effectively remove the formaldehyde of interior, keep room air pure and fresh;Wherein, it is of the invention
Nanometer anion powder, nano zine oxide, the active carbon nanoparticles of middle addition, the different of interior can be removed while formaldehyde is eliminated
Taste, anion is discharged, further purifies air, the present invention can be non-stimulated with the biological pollutants such as elimination virus bacterium, product
Property smell, without secondary pollution;Obtained through overtesting, after being used 1 month indoors using catalyst produced by the present invention, formaldehyde contains
Amount reduces by 95%;, being capable of fully erased formaldehyde after 2 months.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of indoor formaldehyde removes catalyst, it is characterised in that:Catalyst component includes nano titanium oxide 10-20 in parts by weight
Part, diammonium hydrogen phosphate 4-12 parts, silicon powder 5-10 parts, nano whisker silicon 2-8 parts, polyvinyl alcohol 4-12 parts, diatomite 3-10 parts,
Nanometer anion powder 1-6 parts, nano zine oxide 2-8 parts, active carbon nanoparticles 4-12 parts.
2. a kind of indoor formaldehyde according to claim 1 removes catalyst, it is characterised in that:The preferable composition of catalyst component is matched somebody with somebody
Than including 15 parts of nano titanium oxide, 8 parts of diammonium hydrogen phosphate, 8 parts of silicon powder, 5 parts of nano whisker silicon, 8 parts of polyvinyl alcohol, diatom
7 parts of soil, 3 parts of nanometer anion powder, 5 parts of nano zine oxide, 8 parts of active carbon nanoparticles.
3. realize that a kind of indoor formaldehyde described in claim 1 removes the preparation method of catalyst, it is characterised in that:Its preparation method
Comprise the following steps:
A, added after mixing silicon powder, nano whisker silicon, diatomite, nanometer anion powder, nano zine oxide, active carbon nanoparticles
Ground in grinder, cross 100 mesh sieves afterwards, obtain mixture A;
B, nano titanium oxide, diammonium hydrogen phosphate are added in mixture A, stirring at low speed in stirred tank, stirring are added after mixing
Speed is 300 revs/min, mixing time 10min, obtains mixture B;
C, polyvinyl alcohol is added in mixture B, after being sufficiently stirred at normal temperatures, 2h is stood at normal temperatures, that is, obtains catalyst.