CN107793075A - A kind of wall mud and its construction method for decomposing indoor harmful gas - Google Patents
A kind of wall mud and its construction method for decomposing indoor harmful gas Download PDFInfo
- Publication number
- CN107793075A CN107793075A CN201710878646.3A CN201710878646A CN107793075A CN 107793075 A CN107793075 A CN 107793075A CN 201710878646 A CN201710878646 A CN 201710878646A CN 107793075 A CN107793075 A CN 107793075A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- wall
- wall mud
- harmful gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wall mud for decomposing indoor harmful gas, and in particular to environmentally friendly finishing field, in terms of parts by weight, including following component:10~20 parts of nano-disinfection material, 5~10 parts of absorbing and deodorizing agent, 40~50 parts of cement, 10~20 parts of lime, 20~30 parts of fine sand, 3~5 parts of adhesive, 5~10 parts of tourmaline, 3~5 parts of rare earth compound, 20~30 parts of pure water.First inventive point of the present invention:Above-mentioned wall mud will not discharge pernicious gas in itself, while can also decompose the pernicious gas that indoor furniture or other finishing materials are discharged, and play purification except useless effect;Second inventive point of the present invention:Any pollution will not be not only produced in the work progress of above-mentioned wall mud, and the effect that wall mud decomposes indoor harmful gas can be greatly promoted.
Description
Technical field
The present invention relates to environmentally friendly finishing field, specially a kind of wall mud and its construction method for decomposing indoor harmful gas.
Background technology
Indoor decoration pollution refers to that oxygen, formaldehyde, benzene, ammonia and volatility that harmful health is mixed into room air are organic
The phenomenon of the gases such as thing.It is well known that being fitted up to indoor particulate matter, a variety of environmental problems can be brought, such as:Use
Building materials containing poisonous and harmful substances can have an impact to IAQ;Various dust can be produced in fitment process, are discarded
Thing and noise pollution, these can all seriously affect the life of people.The source of indoor decoration pollution is a lot, wherein having suitable one
Partially due to caused by material used in fitment process is improper, including the volatile organic matter gas such as formaldehyde, benzene, dimethylbenzene
Body.But the pernicious gas volatilized in finishing material then can cause one as removed not in time to the health for the personnel of moving in
Fixed harm.
Obviously, in conventional art, being used in room ventilation, not only time-consuming in a manner of pernicious gas to be discharged, waste discharge effect
Fruit is also not fully up to expectations;And the special service for providing and administering indoor harmful gaseous pollution is also provided on the market, and enjoying except useless clothes
While business, also decoration cost is added to owner.Therefore, solves pernicious gas caused by interior decoration from material source
It is urgent problem to be solved.
The content of the invention
It is an object of the invention to solve finishing material to discharge volatile harmful gase and influence resident family's health
A kind of problem, there is provided wall mud and its construction method for decomposing indoor harmful gas.First inventive point of the present invention:Above-mentioned wall
Mud will not discharge pernicious gas in itself, while can also decompose harmful gas that indoor furniture or other finishing materials are discharged
Body, purification is played except useless effect;Second inventive point of the present invention:It will not only produce and appoint in the work progress of above-mentioned wall mud
What pollutes, and can greatly promote the effect that wall mud decomposes indoor harmful gas.
To achieve the above object, the present invention provides following technical scheme:
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, including following component:Nano-disinfection material 10~
20 parts, 5~10 parts of absorbing and deodorizing agent, 40~50 parts of cement, 10~20 parts of lime, 20~30 parts of fine sand, 3~5 parts of adhesive, electricity
5~10 parts of gas stone, 3~5 parts of rare earth compound, 20~30 parts of pure water.
Wherein, nano-disinfection material can not only kill the germ being mingled with room air, can also decompose in room air
Pernicious gas;Caused peculiar smell in the adsorbable fitment process of absorbing and deodorizing agent so that air is more pure and fresh;Tourmaline and micro
Rare earth compound can kill pathogenic bacteria in resident family's living environment, reduce resident family's P.Therefore, by above-mentioned each component
Wall mud is mixed and made into according to default proportioning, is had and is purified the air of a room, kills indoor malignant bacteria and adsorb peculiar smell deodorization
Function.It is especially suitable for, using in the kitchen of easy breed bacteria or toilet, greatly improving the living environment of resident family.
Preferably, the nano-disinfection material is selected from nano titanium oxide, nano zine oxide, nano zirconium dioxide, received
One kind in rice silver powder, copper nanoparticle and copper nanoparticle, or their mixture.
Preferably, the one kind of the absorbing and deodorizing agent in activated carbon, diatomite and bentonite, or theirs are mixed
Compound.
Preferably, the one kind of rare earth compound in lanthanide series sulfate, lanthanide series carbonate, or they
Mixture.
Preferably, the adhesive is polyvinyl alcohol glue.
Preferably, described wall mud, in terms of parts by weight, including following component:5~10 parts of nano titanium oxide, receives
3~5 parts of zinc oxide of rice, 3~5 parts of nano-silver powder, 1~2 part of nano zirconium dioxide, 1~2 part of copper nanoparticle, 5~7 parts of activated carbon,
1~2 part of diatomite, 1~2 part of bentonite, 40~50 parts of cement, 10~20 parts of lime, 20~30 parts of fine sand, polyvinyl alcohol glue 3
~5 parts, 5~10 parts of tourmaline, 1~2 part of lanthanide series sulfate, 2~3 parts of lanthanide series carbonate, 20~30 parts of pure water.
Preferably, the lanthanide series sulfate is selected from least one of lanthanum sulfate, cerous sulfate;Lanthanide series carbonic acid
Salt is selected from least one of lanthanum carbonate, cerous carbonate.
The present invention also provides the construction method of above-mentioned wall mud, and the construction method comprises the following steps:
(1) by nano titanium oxide, nano zine oxide, nano-silver powder, nano zirconium dioxide, copper nanoparticle, activated carbon, silicon
Diatomaceous earth, bentonite, cement, lime, fine sand, polyvinyl alcohol glue, tourmaline, lanthanide series sulfate and lanthanide series carbonate are pressed
Default proportioning is well mixed, grinding, obtains mixed-powder;
(2) in described mixed-powder, pure water is added by default proportioning, stirring obtains mixture slurry;
(3) after wall embryo drenches, mixture slurry is uniformly applied to wall embryo surface, that is, obtains interior wall;
(4) before the unseasoned solidification of mixture slurry, by inner wall surface polish it is coarse after smear diatomite, produce rendering
The shaping interior wall finished.
Preferably, in step (1), the particle diameter of the mixed-powder is 10~20mm.
Preferably, in step (3), the thickness for being applied to the mixture slurry of wall embryo surface is 0.3~0.6cm.
Beneficial effects of the present invention are:
In scheme provided by the present invention, nano-disinfection material can not only kill the germ being mingled with room air,
Also the pernicious gas in room air can be decomposed;Caused peculiar smell in the adsorbable fitment process of absorbing and deodorizing agent so that air is more
Add pure and fresh;Tourmaline and micro rare earth compound can kill the pathogenic bacteria in resident family's living environment, and it is ill general to reduce resident family
Rate.Therefore, above-mentioned each component is mixed and made into wall mud according to default proportioning, has and purify the air of a room, kill indoor cause a disease carefully
Bacterium and the function of adsorbing peculiar smell deodorization.It is especially suitable for, using in the kitchen of easy breed bacteria or toilet, greatly improving
The living environment of resident family.
Embodiment
Embodiment 1
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
5 parts of titanium, 3 parts of nano zine oxide, 3 parts of nano-silver powder, 1 part of nano zirconium dioxide, 1 part of copper nanoparticle, 5 parts of activated carbon, diatomite 1
Part, 1 part of bentonite, 40 parts of cement, 10 parts of lime, 20 parts of fine sand, 3 parts of polyvinyl alcohol glue, 5 parts of tourmaline, lanthanide series sulfuric acid
1 part of salt, 2 parts of lanthanide series carbonate, 20 parts of pure water.
The construction method of above-mentioned wall mud comprises the following steps:
(1) by nano titanium oxide, nano zine oxide, nano-silver powder, nano zirconium dioxide, copper nanoparticle, activated carbon, silicon
Diatomaceous earth, bentonite, cement, lime, fine sand, polyvinyl alcohol glue, tourmaline, lanthanide series sulfate and lanthanide series carbonate are pressed
Above-mentioned default proportioning is well mixed, is ground into mixed-powder, and cross the sieve of 10~20mm screen-apertures.
(2) in described mixed-powder, pure water is added by default proportioning, stirring obtains mixture slurry;
(3) after wall embryo drenches, mixture slurry is uniformly applied to wall embryo surface, thickness between 0.3~0.6mm most
It is good, that is, obtain interior wall;
(4) before the unseasoned solidification of mixture slurry, when inner wall surface is polished into coarse rear smearing diatomite to prevent
Between long diatomite come off, be with sterilization, the functional wall except useless and deodorization functions after drying.
Embodiment 2
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
8 parts of titanium, 4 parts of nano zine oxide, 4 parts of nano-silver powder, 1 part of nano zirconium dioxide, 1 part of copper nanoparticle, 6 parts of activated carbon, diatomite 1
Part, 1 part of bentonite, 45 parts of cement, 15 parts of lime, 25 parts of fine sand, 4 parts of polyvinyl alcohol glue, 7 parts of tourmaline, lanthanide series sulfuric acid
1 part of salt, 2 parts of lanthanide series carbonate, 25 parts of pure water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Embodiment 3
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
7 parts of titanium, 4 parts of nano zine oxide, 4 parts of nano-silver powder, 2 parts of nano zirconium dioxide, 2 parts of copper nanoparticle, 7 parts of activated carbon, diatomite 1
Part, 2 parts of bentonite, 46 parts of cement, 17 parts of lime, 26 parts of fine sand, 4 parts of polyvinyl alcohol glue, 7 parts of tourmaline, lanthanide series sulfuric acid
2 parts of salt, 3 parts of lanthanide series carbonate, 27 parts of pure water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Embodiment 4
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
6 parts of titanium, 5 parts of nano zine oxide, 5 parts of nano-silver powder, 2 parts of nano zirconium dioxide, 1 part of copper nanoparticle, 5 parts of activated carbon, diatomite 1
Part, 1 part of bentonite, 48 parts of cement, 14 parts of lime, 24 parts of fine sand, 4 parts of polyvinyl alcohol glue, 6 parts of tourmaline, lanthanide series sulfuric acid
1 part of salt, 3 parts of lanthanide series carbonate, 22 parts of pure water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Embodiment 5
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
10 parts of titanium, 5 parts of nano zine oxide, 5 parts of nano-silver powder, 2 parts of nano zirconium dioxide, 2 parts of copper nanoparticle, 7 parts of activated carbon, diatomite
2 parts, 2 parts of bentonite, 50 parts of cement, 20 parts of lime, 30 parts of fine sand, 5 parts of polyvinyl alcohol glue, 10 parts of tourmaline, lanthanide series sulphur
2 parts of hydrochlorate, 3 parts of lanthanide series carbonate, 30 parts of pure water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Comparative example 1
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:7 parts of activated carbon,
1 part of diatomite, 2 parts of bentonite, 46 parts of cement, 17 parts of lime, 26 parts of fine sand, 4 parts of polyvinyl alcohol glue, 7 parts of tourmaline, group of the lanthanides member
Plain 2 parts of sulfate, 3 parts of lanthanide series carbonate, 27 parts of pure water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Comparative example 2
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
7 parts of titanium, 4 parts of nano zine oxide, 4 parts of nano-silver powder, 2 parts of nano zirconium dioxide, 2 parts of copper nanoparticle, 46 parts of cement, lime 17
Part, 26 parts of fine sand, 4 parts of polyvinyl alcohol glue, 7 parts of tourmaline, 2 parts of lanthanide series sulfate, 3 parts of lanthanide series carbonate are pure
27 parts of water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Comparative example 3
A kind of wall mud for decomposing indoor harmful gas, in terms of parts by weight, the wall mud drum includes following component:Nanometer titanium dioxide
7 parts of titanium, 4 parts of nano zine oxide, 4 parts of nano-silver powder, 2 parts of nano zirconium dioxide, 2 parts of copper nanoparticle, 7 parts of activated carbon, diatomite 1
Part, 2 parts of bentonite, 46 parts of cement, 17 parts of lime, 26 parts of fine sand, 4 parts of polyvinyl alcohol glue, 27 parts of pure water.
The construction method of above-mentioned wall mud is the same as embodiment 1.
Test case 1
Decoration company holds consultation with cell, and choose same cell with building building 27 sets treat decorating house, are randomly divided into 9 groups,
Numbering is A~I.A~E groups select finishing of the wall mud that embodiment 1~5 is provided as metope respectively when decorating house is fitted up
Material, G~H groups select finishing material of the wall mud that comparative example 1~3 is provided as metope, I respectively when decorating house is fitted up
From common wall mud, (cement is 1 with fine sand mass ratio to group respectively when decorating house is fitted up:2) material as wall surfacing,
Air conditions statistics such as table 1 below in measuring chamber after the completion of finishing:
The room air situation statistical form of table 1
To sum up state:The effect of the removing and harmful gas for the wall mud component that the corresponding embodiment 3 of C groups is provided is best, and by F
~H data result understands that nano-disinfection material has the effect of Synergistic with absorbing and deodorizing agent, while in use, except useless
Effect is optimal.
Claims (10)
- A kind of 1. wall mud for decomposing indoor harmful gas, it is characterised in that in terms of parts by weight, including following component:Nanometer is killed It is 10~20 parts of bacterium material, 5~10 parts of absorbing and deodorizing agent, 40~50 parts of cement, 10~20 parts of lime, 20~30 parts of fine sand, gluing 3~5 parts of agent, 5~10 parts of tourmaline, 3~5 parts of rare earth compound, 20~30 parts of pure water.
- A kind of 2. wall mud for decomposing indoor harmful gas according to claim 1, it is characterised in that the nano-disinfection material Expect one in nano titanium oxide, nano zine oxide, nano zirconium dioxide, nano-silver powder, copper nanoparticle and copper nanoparticle Kind, or their mixture.
- A kind of 3. wall mud for decomposing indoor harmful gas according to claim 1, it is characterised in that the absorbing and deodorizing agent One kind in activated carbon, diatomite and bentonite, or their mixture.
- 4. a kind of wall mud for decomposing indoor harmful gas according to claim 1, it is characterised in that rare earth compound is selected from One kind in lanthanide series sulfate, lanthanide series carbonate, or their mixture.
- 5. a kind of wall mud for decomposing indoor harmful gas according to claim 1, it is characterised in that the adhesive is poly- Vinyl alcohol glue.
- 6. according to a kind of wall mud of any described decomposition indoor harmful gas of Claims 1 to 5, it is characterised in that with weight Number meter, including following component:5~10 parts of nano titanium oxide, 3~5 parts of nano zine oxide, 3~5 parts of nano-silver powder, nanometer 1~2 part of zirconium dioxide, 1~2 part of copper nanoparticle, 5~7 parts of activated carbon, 1~2 part of diatomite, 1~2 part of bentonite, cement 40~ 50 parts, 10~20 parts of lime, 20~30 parts of fine sand, 3~5 parts of polyvinyl alcohol glue, 5~10 parts of tourmaline, lanthanide series sulfate 1 ~2 parts, 2~3 parts of lanthanide series carbonate, 20~30 parts of pure water.
- A kind of 7. wall mud for decomposing indoor harmful gas according to claim 6, it is characterised in that the lanthanide series sulphur Hydrochlorate is selected from least one of lanthanum sulfate, cerous sulfate;Lanthanide series carbonate in lanthanum carbonate, cerous carbonate at least one Kind.
- 8. a kind of construction method of wall mud as claimed in claim 6, it is characterised in that comprise the following steps:(1) by nano titanium oxide, nano zine oxide, nano-silver powder, nano zirconium dioxide, copper nanoparticle, activated carbon, diatom Soil, bentonite, cement, lime, fine sand, polyvinyl alcohol glue, tourmaline, lanthanide series sulfate and lanthanide series carbonate are by pre- Establishing grinding, obtains mixed-powder than well mixed;(2) in described mixed-powder, pure water is added by default proportioning, stirring obtains mixture slurry;(3) after wall embryo drenches, mixture slurry is uniformly applied to wall embryo surface, that is, obtains interior wall;(4) before the unseasoned solidification of mixture slurry, by inner wall surface polish it is coarse after smear diatomite, produce rendering and finish Shaping interior wall.
- 9. construction method according to claim 8, it is characterised in that in step (1), the particle diameter of the mixed-powder is 10 ~20mm.
- 10. construction method according to claim 8, it is characterised in that in step (3), be applied to the mixing of wall embryo surface The thickness of thing slurry is 0.3~0.6cm.