CN106747195B - High adsorption rate kieselguhr wall material and its preparation and construction method - Google Patents
High adsorption rate kieselguhr wall material and its preparation and construction method Download PDFInfo
- Publication number
- CN106747195B CN106747195B CN201611260840.7A CN201611260840A CN106747195B CN 106747195 B CN106747195 B CN 106747195B CN 201611260840 A CN201611260840 A CN 201611260840A CN 106747195 B CN106747195 B CN 106747195B
- Authority
- CN
- China
- Prior art keywords
- weight
- adsorption rate
- wall material
- high adsorption
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of high adsorption rate kieselguhr wall material and its preparation and construction methods, belong to the field of building materials.High adsorption rate kieselguhr wall material of the invention contains the component of following parts by weight: powdered whiting 5--25 parts by weight, calcium hydroxide 10--35 parts by weight, conch meal 5--35 parts by weight, diatomite 20--45 parts by weight, blanc fixe 3--20 parts by weight, adhesive 1--8 parts by weight, moisturizer 0.5--3 parts by weight, land plaster 3--10 parts by weight, thixotroping wetting agent 0.2--2 parts by weight, pre-gelatinized starch 0.3--2 parts by weight, anti-crack fiber 0.2--1.5 parts by weight, functional material 1--8 parts by weight, inorganic color 0.1--15 parts by weight.After being constructed on wall body using kieselguhr wall material provided by the invention, purifies air efficiency and scrub resistance is higher than common diatom ooze coating.
Description
Technical field
The present invention relates to the field of building materials, a kind of high adsorption rate kieselguhr wall material and its preparation and construction party are particularly related to
Method.
Background technique
Diatomite is a kind of biogenic siliceous sedimentary rock, it is mainly made of the remains of ancient times diatom, is had thin
The characteristics such as greasy, loose, light, porous, water imbibition and permeability are strong.Requirement with people to the living environment feature of environmental protection is increasingly
Height, diatom ooze are increasingly becoming a kind of very popular new indoor decoration material, and the wall material for being added to diatomite has
It adjusts room temperature, eliminate the advantages that peculiar smell, absorption and decomposing harmful substances.Currently, can be on wall body surface using kieselguhr wall material
On produce certain texture, with increase its dicoration.The disadvantage is that finished product skin texture surface smoothness is not high, scrub resistance is general,
The problems such as easy accumulation of salt in the surface soil, cleaning harmful gas low efficiency.
Conch meal is conch meal pulverized powder, and the main component of 95 parts by weight is calcium carbonate, there are also a small amount of amino acid and
Polysaccharide material.The high-grade material that food, cosmetics and interior decoration can be done, is widely applicable to animal and fowl fodder and food calcium
Source additive, ornaments processing, desiccant etc..Oyster shell whiting biology coating is house ornamentation interior wall coating emerging in recent years, is conch meal
One of new application, natural environmental protection is its most important advantage, while having the bright and clean exquisiteness of skin texture, and feel is significantly better than traditional silicon
The characteristics of algal gel product, the disadvantage is that soundproof effect is unobvious, cost is higher with respect to diatom ooze.
If it is possible to provide a kind of combination shell powder paint and the respective mutual supplement with each other's advantages of diatom ooze coating, two are overcome
The kieselguhr wall material of the kind respective defect of material then can necessarily meet people to kieselguhr wall material dicoration to a certain extent
Requirement.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high adsorption rate kieselguhr wall material and its preparation and construction method,
Reach shell powder paint and diatom ooze coating has complementary advantages, any surface finish high to the purification adsorption rate of pernicious gas, scrub resistance
Strong effect.
In order to solve the above technical problems, present invention offer technical solution is as follows:
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Preferably, the high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Further, the high adsorption rate kieselguhr wall material, the component containing following parts by weight:
The adhesive is one of polyvinyl alcohol, polyacrylate, ethylene-vinyl acetate copolymer etc. or more
Kind；The moisturizer is one of starch ether, cellulose ether etc. or a variety of.The anti-crack fiber is polypropylene fibre
One of dimension, wood fibre are a variety of；The thixotroping wetting agent is smectites thixotroping wetting agent and aluminium-magnesium silicate thixotroping
One of wetting agent is a variety of；The pre-gelatinized starch is one kind of corn pre-gelatinized starch, potato pre-gelatinized starch
Or it is a variety of；The inorganic color is iron oxide series, bores that purple, brill is green, bismuth is yellow, zinc-iron is yellow, titanium yellow, one of titanium chromium palm fibre
Or it is a variety of；The functional material is one of nano phase ag_2 o, nano-titanium dioxide, zinc oxide, negative ion powder, zeolite
Or it is a variety of.
The present invention also provides a kind of preparation method of high adsorption rate kieselguhr wall material, the high adsorption rate kieselguhr wall material is
It is obtained after pre-mixed additive preparation, pigment preparation, finished product material preparation step.
Preferably, pre-mixed additive preparation is by the bonding in the formula of the high adsorption rate kieselguhr wall material
Agent, moisturizer, anti-crack fiber, thixotroping wetting agent, pre-gelatinized starch and functional material are put into after weighing according to standard proportional
It stirs and is made in high-speed mixer；The pigment preparation is put into after pigment needed for producing proportionally weighs well with dicalcium powder
It stirs and is made in high speed machine；Finished product material preparation be by the raw material in high adsorption rate kieselguhr wall material formula according to than
The size of weight, material surface porosity and mesh number successively puts into agitator tank and stirs with the pre-mixed additive, pigment.
Further, in the pre-mixed additive preparation and pigment preparation process, the mixing time in high-speed mixer is
2-3 minutes；The mixing time of agitator tank is 30-40 minutes in the finished product material preparation process；The weight of the pigment and dicalcium powder
Amount is than being 1: 2-4.
On the other hand, the present invention also provides a kind of construction methods of high adsorption rate kieselguhr wall material, comprising the following steps:
Step 1: substrate inspection processing being carried out to wall body before construction；
Step 2: trowelling, coating layer thickness 0.15-0.2mm, it is desirable that surface being carried out to substrate using the finished product material being stirred
Trace, no shedding are smeared without obvious；
Step 3: carrying out skin texture processing again after the trowelling of step 2 is completely dried.
Further, in the step 1, base treatment is carried out to wall body are as follows: wall is the feelings of big white background or water proof putty
Under condition, if the smooth flawless in surface, without dust, diatom ooze construction can be directly carried out；If there is obvious shedding, need first to brush one
It constructs again all over priming paint or after doing other processing；If big white background has cracking, hollowing, need to pre-process, in case construction finishes
After there is problem after sale.
Preferably, amount of water when finished product material is constructed in the step 2, powder: water=1: 1.2-1.5；Every square metre of wall
Face dosage: 0.3-0.5 kilograms of powder.
Wherein, the skin texture processing in the step 3 to do a flower skin texture with seaweed cotton or does bullet painting, spraying flesh with spray gun
Reason.
The invention has the following advantages:
It is remarkably improved coating itself environmental-protecting performance using the present invention, adsorbs free formaldehyde, benzene, toluene, diformazan in air
The ability of the harmful substances such as benzene, ammonia, TVOC, radon is stronger；Clarification time is obviously shortened than traditional kieselguhr wall material；Scrub resistance is bright
It is aobvious to improve, when wet environment or too low temperature be less prone to traditional kieselguhr wall material such as pattern or accumulation of salt in the surface soil whiting easily occur it is bad
Drawback；Finished product skin texture surface smoothness can be equally matched with emulsion paint, shell powder paint, while there is no than traditional diatom for cost
Native wall material is risen.
Specific embodiment
The present invention provides a kind of high adsorption rate kieselguhr wall material and its preparation and construction methods, to make mesh of the invention
, technical solution and effect it is clearer, clear, the present invention is described in more detail below.It should be appreciated that described herein
Specific embodiment be only used to explain the present invention, be not intended to limit the present invention.The person that is not specified actual conditions in embodiment, presses
The condition that more solito condition or manufacturer suggest carries out.Reagents or instruments used without specified manufacturer is that can pass through
The conventional products that commercially available purchase obtains.
Embodiment 1
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Embodiment 2
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Embodiment 3
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Embodiment 4
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Embodiment 5
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Embodiment 6
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Embodiment 7
A kind of high adsorption rate kieselguhr wall material, the component containing following parts by weight:
Comparative example 1
A kind of tradition kieselguhr wall material, the component containing following parts by weight:
Comparative example 2
A kind of tradition kieselguhr wall material, the component containing following parts by weight:
Embodiment 8
A kind of preparation process of high adsorption rate kieselguhr wall material provided by the invention, it is specific as follows: high adsorption rate diatomite
Wall material is obtained after pre-mixed additive preparation, pigment preparation, finished product material preparation step.
Wherein, pre-mixed additive preparation is by the adhesive in the formula of high adsorption rate kieselguhr wall material, moisturizer, cracking resistance
Fiber, thixotroping wetting agent, pre-gelatinized starch and functional material put into high-speed mixer after weighing according to standard proportional and stir
Mixing obtains；Pigment preparation is to put into stirring in high speed machine after pigment and dicalcium powder needed for producing proportionally weigh well to be made；
Finished product material preparation is by the raw material in high adsorption rate kieselguhr wall material formula according to specific gravity, material surface porosity and mesh
Several sizes successively puts into agitator tank and stirs with the pre-mixed additive, pigment.
Further, in pre-mixed additive preparation and pigment preparation process, the mixing time in high-speed mixer is 2-3 points
Clock；The mixing time of agitator tank is 30-40 minutes in finished product material preparation process；The weight ratio of pigment and dicalcium powder is 1: 2-4.
Embodiment 9
A kind of construction technology of high adsorption rate kieselguhr wall material provided by the invention, specific steps are as follows:
Step 1: substrate inspection processing is carried out to wall body before construction, in the case that wall is big white background or water proof putty, if
The smooth flawless in surface, without dust, can directly carry out diatom ooze construction；If there is obvious shedding, need first to brush one times priming paint
Or it constructs again after doing other processing；If big white background has cracking, hollowing, need to pre-process, in order to avoid occur after construction
Problem after sale；
Step 2: trowelling, coating layer thickness 0.15-0.2mm, it is desirable that surface being carried out to substrate using the finished product material being stirred
Trace, no shedding are smeared without obvious, wherein amount of water when finished product material is constructed, powder: water=1: 1.2-1.5；Every square metre of metope is used
Amount: 0.3-0.5 kilograms of powder；
Step 3: carry out skin texture processing again after the trowelling of step 2 is completely dried, can be made of seaweed cotton flower skin texture or
Bullet painting, spraying skin texture are done with spray gun.
It should be noted that the preferred polyvinyl alcohol commonly used in the art of the adhesive used in embodiment 1-7, poly- third
One of olefin(e) acid ester, ethylene-vinyl acetate copolymer etc. are a variety of；Used moisturizer starch preferably commonly used in the art
One of ether, cellulose ether etc. are a variety of；In anti-crack fiber used polypropylene fibre preferably commonly used in the art, wood fibre
It is one or more；The thixotroping wetting agent is one of smectites thixotroping wetting agent and aluminium-magnesium silicate thixotroping wetting agent
Or it is a variety of；The pre-gelatinized starch be corn pre-gelatinized starch, potato pre-gelatinized starch it is one or more；It is used inorganic
Colorant iron oxide series preferably commonly used in the art, bore purple, brill is green, bismuth is yellow, zinc-iron is yellow, titanium yellow, one of titanium chromium palm fibre or
It is a variety of；Functional material used nano phase ag_2 o preferably commonly used in the art, nano-titanium dioxide, zinc oxide, negative ion powder, boiling
One of stone is a variety of.
Embodiment 1-7 and comparative example 1-2 in conjunction with the embodiments 8 and embodiment 9 construct, in interior wall coating harmful substance limit
Measure execution standard GB 18582, air-cleaning function coating material purifying property JC/T1074-2008, the survey of coating alkali resistance
Determine GB/T9265, Multi wall architectural coatings GB/T9779-2005, the detection of moisture adsorption and releasing characteristic according to JC/T2002-2009, paint film,
Putty membrane drying time measuring method GB/T1728-1979 (1989).As a result as shown in table 1.
1 performance detection data of table
2 scrub resistance detection data of table
As can be seen that the present invention is remarkably improved coating itself environmental-protecting performance, adsorb free formaldehyde in air, benzene, toluene,
The ability of the harmful substances such as dimethylbenzene, ammonia, TVOC, radon is stronger, and the clarification time is obviously shortened than traditional kieselguhr wall material, such as
Table 1, scrub resistance can be significantly improved than traditional kieselguhr wall material, and such as table 2, when wet environment or too low temperature is less prone to pattern
Or the bad drawback that traditional kieselguhr wall material such as accumulation of salt in the surface soil whiting easily occurs；Finished product skin texture surface smoothness can be with emulsion paint, shell
Powder coating is equally matched, while there is no risen cost than traditional kieselguhr wall material.
The above is a preferred embodiment of the present invention, it is noted that for those skilled in the art
For, without departing from the principles of the present invention, it can also make several improvements and retouch, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (10)
1. a kind of high adsorption rate kieselguhr wall material, which is characterized in that the component containing following parts by weight:
Wherein, described adhesive is one of polyvinyl alcohol, polyacrylate, ethylene-vinyl acetate copolymer or a variety of；And
The anti-crack fiber is one of polypropylene fibre, wood fibre or a variety of；
The functional material be one of nano phase ag_2 o, nano-titanium dioxide, zinc oxide, negative ion powder, zeolite or
It is a variety of.
2. high adsorption rate kieselguhr wall material according to claim 1, which is characterized in that the component containing following parts by weight:
3. high adsorption rate kieselguhr wall material according to claim 2, which is characterized in that the component containing following parts by weight:
4. high adsorption rate kieselguhr wall material according to claim 3, which is characterized in that the moisturizer be starch ether,
One of cellulose ether is a variety of；The thixotroping wetting agent is that smectites thixotroping wetting agent and aluminium-magnesium silicate thixotroping soak
One of agent is a variety of；The pre-gelatinized starch be one of corn pre-gelatinized starch, potato pre-gelatinized starch or
It is a variety of；The inorganic color be one of iron oxide series, cobalt violet, cobalt green, bismuth Huang, zinc-iron Huang, titanium yellow, titanium chromium palm fibre or
It is a variety of.
5. the preparation method of high adsorption rate kieselguhr wall material according to claim 4, which is characterized in that the high adsorption rate
Kieselguhr wall material is obtained after pre-mixed additive preparation, pigment preparation, finished product material preparation step；The premix addition
Agent preparation be by the formula of the high adsorption rate kieselguhr wall material adhesive, moisturizer, anti-crack fiber, thixotroping wetting agent,
Pre-gelatinized starch and functional material put into stirring in high-speed mixer and are made after weighing according to standard proportional；The pigment system
Standby is to put into stirring in high speed machine after pigment and dicalcium powder needed for producing proportionally weigh well to be made；The finished product material preparation
Be by the high adsorption rate kieselguhr wall material formula in raw material according to specific gravity, material surface porosity and mesh number size with
The pre-mixed additive, pigment successively put into agitator tank and stir.
6. the preparation method of high adsorption rate kieselguhr wall material according to claim 5, which is characterized in that the premix addition
In agent preparation and pigment preparation process, the mixing time in high-speed mixer is 2-3 minutes；It is stirred in the finished product material preparation process
The mixing time for mixing tank is 30-40 minutes；The weight ratio of the pigment and dicalcium powder is 1:2-4.
7. the construction method of any high adsorption rate kieselguhr wall material of claim 1-4, which is characterized in that including following step
It is rapid:
Step 1: substrate inspection processing being carried out to wall body before construction；
Step 2: trowelling, coating layer thickness 0.15-0.2mm being carried out to substrate using the finished product material being stirred, it is desirable that surface is without smearing
Trace, no shedding；
Step 3: carrying out skin texture processing again after the trowelling of step 2 is completely dried.
8. the construction method of high adsorption rate kieselguhr wall material according to claim 7, which is characterized in that in the step 1,
Substrate inspection processing is carried out to wall body are as follows: in the case that wall is big white background or water proof putty, if the smooth flawless in surface,
Without dust, then diatom ooze construction is directly carried out；If there is shedding, need to construct again after first brushing one times priming paint；If big white background has
Cracking, hollowing, need to pre-process.
9. the construction method of high adsorption rate kieselguhr wall material according to claim 7, which is characterized in that in the step 2
Amount of water when finished product material is constructed, powder: water=1:1.2-1.5；Every square metre of metope dosage: 0.3-0.5 kilograms of powder.
10. the construction method of high adsorption rate kieselguhr wall material according to claim 7, which is characterized in that in the step 3
Skin texture processing for seaweed cotton do flower skin texture or with spray gun do bullet apply, spraying skin texture.