CN1585041A - Non-burned damp-proof insulative material and preparing method thereof - Google Patents
Non-burned damp-proof insulative material and preparing method thereof Download PDFInfo
- Publication number
- CN1585041A CN1585041A CN 200410027565 CN200410027565A CN1585041A CN 1585041 A CN1585041 A CN 1585041A CN 200410027565 CN200410027565 CN 200410027565 CN 200410027565 A CN200410027565 A CN 200410027565A CN 1585041 A CN1585041 A CN 1585041A
- Authority
- CN
- China
- Prior art keywords
- powder
- mixed
- damp
- unburned
- mixer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The insulated material applied in this invention is mixed by the mineral earth and a little bit cheap industrial material with the inorganic adhesive. The producing method is to mix the fin material uniformly and add appropriate volume inorganic adhesive to produce the material.
Description
Technical field
The present invention relates to a kind of unburned damp proof insulation material, specifically is a kind of unburned high withstand voltage, unburned damp proof insulation material of low current leakage that is used for electric product and power equipment or device.
The invention still further relates to the preparation method of above-mentioned insulating material.
Background technology
Insulating material is the very crucial electrical material of making in electric product and power equipment or the device of a class, especially solid inorganic insulation material, it comprises the hard section bar or the fibrous type material products of pottery, glass and inorganic mineral and silicate mine preparation widely.This class material and goods also are widely used in electric heating environment, equipment or device.
At present, be very ripe as the strong insulation of conducting heat or being incubated of the many solids that are used for electric heating environment, equipment or device, the insulating material of protection against the tide and the technology of section bar.The goods of this class material are except that needs are sought high-quality raw material and prescription, and the manufacturing of product often must realize by the ceramic preparation technology of high temperature sintering.Therefore, high energy consumption and manufacturing cost are essential.Along with the progress of the technology and the market demand, the making of a class electric heating products, device and electric heating environment, the carrier of its live part disapproves and adopts above-mentioned material and manufacture craft to realize.In the manufacture process of product or system, these carriers itself are as the making of powder participation product or system, and for example very popular in recent years new-type sealed type electric furnace of a class, this class electric furnace only just are tens million of in some national annual turnovers of Europe.The manufacturing of the stone or metal plate for standing a stove on as a precaution against fire of this electric furnace and considering a problem of relating to: the formula materials and the metal stone or metal plate for standing a stove on as a precaution against fire of the insulating material powder of determining are compressed to the one with groove as following, in as the powder groove of heating wire carrier, embed heating wire or electroheat member, suppress coated with powder again.Like this, metal stone or metal plate for standing a stove on as a precaution against fire, powder carrier, heating wire or heat generating components are combined together securely.These powders through pressure compression moulding have had certain intensity.In order to protect other external objects of gumming (disapproving the electroheat member that maybe wouldn't permit heat and heat transfer plate etc.), do not allow to take high-sintering process through moulding with powder that other objects are bonded together as the metal of heating wire, electroheat member and other high temperature rapid wear destructible parts, bonding powder or other.Yet, prior art to adapt to above-mentioned requirements and manufacture have high withstand voltage, low current leakage and the good material of damp proof insulation performance have certain difficulty, the keeping of high insulation characterisitic after the moisture absorption especially.
Summary of the invention
The objective of the invention is to shortcoming, a kind of unburned high withstand voltage, low current leakage damp proof insulation material are provided at the prior art existence.Insulating material of the present invention adopts a series of natural materials cheaply to fill a prescription, and adopt the utmost point low temperature that is different from ceramic fabrication technique to cure " unburned " technology, make have high withstand voltage, the electric heating insulated product of low current leakage, material of the present invention still has very good damp proof insulation performance, and has overcome because of " unburned " makes goods must have the back that makes moist that makes that unsurmountable open structure causes and reduce the shortcoming of goods insulation property.
Another object of the present invention is to provide the preparation method of this insulating material.。
For achieving the above object, the present invention has taked following technical scheme:
A kind of unburned damp proof insulation material is mixed by two kinds of materials of A and B and to form, and by weight percentage, A accounts for 82～93%, and B accounts for 7～18%;
By weight percentage, the A material is grouped into by following one-tenth:
Kaolin 45～62
Quartz sand 15～25
Emergy 12～20
Magnesium oxide 1～4
Mullite 10～16;
The B material is an inorganic adhesive, fills a prescription to be sulfuric acid magnalium inorganic glue powder 15～40g/1000ml H
2O;
The preparation process of above-mentioned insulating material is as follows:
(1) preparation A material; Proportioning by above-mentioned A material weighs up raw material, and places and mixed in the mixer for 30～60 seconds;
(2) weight proportion of pressing A material and B material then adds the B material, stirs 5～8 minutes in mixer, makes powder and adhesive evenly mix also granulation.
Compared with the prior art, the present invention has following beneficial effect:
1, the product that makes of the present invention can obtain higher electrical insulation properties, especially material and height insulation, the high voltage endurance of goods when damp attitude;
2, the present invention adopts cheap natural raw ore powder, and simple manufacture method and " unburned " technology that energy consumption is reduced greatly greatly reduce the cost of product.
Embodiment
The invention will be further described below in conjunction with specific embodiment.
Embodiment 1
The A material is formed:
Raw material ratio (parts by weight)
Kaolin 48
Quartz sand 22
Emergy 12
Magnesium oxide 4
Mullite 14
The prescription of B material is: 30g sulfuric acid magnalium inorganic glue powder/1000ml water
In the insulating material, by weight, the A material accounts for 92%, and the B material accounts for 8%.Preparation process:
(1) preparation A material; Proportioning by above-mentioned A material weighs up raw material, and places and mixed in the mixer for 40 seconds;
(2) weight proportion of pressing A material and B material then adds the B material, stirs 8 minutes in mixer, makes powder and adhesive evenly mix also granulation.
Embodiment 2
The A material is formed:
Raw material ratio (parts by weight)
Kaolin 52
Quartz sand 18
Emergy 13
Magnesium oxide 2
Mullite 15
The B material is that the prescription of inorganic adhesive is: 25g sulfuric acid magnalium inorganic glue powder/1000ml water
In the insulating material, the A material accounts for 88%, and the B material accounts for 12%.
Preparation process:
(1) preparation A material; Proportioning by above-mentioned A material weighs up raw material, and places and mixed in the mixer for 60 seconds;
(2) weight proportion of pressing A material and B material then adds the B material, stirs 6 minutes in mixer, makes powder and adhesive evenly mix also granulation.
Embodiment 3
The A material is formed:
Raw material ratio (parts by weight)
Kaolin 57
Quartz sand 16
Emergy 12
Magnesium oxide 3
Mullite 12
The B material is that the prescription of inorganic adhesive is: 18g sulfuric acid magnalium inorganic glue powder/1000ml water
In the insulating material, by weight percentage, the A material accounts for 82%, and the B material accounts for 18%.Preparation process:
(1) preparation A material; Proportioning by above-mentioned A material weighs up raw material, and places and mixed in the mixer for 45 seconds;
(2) weight proportion of pressing A material and B material then adds the B material, stirs 7 minutes in mixer, makes powder and adhesive evenly mix also granulation.
The concrete application method of insulating material of the present invention is as follows:
For example on the pig iron electric furnace dish, make the bottom carrier of the pressed by powder electric furnace heating wire of grain with the present invention, elder generation is by specification requirement heating wire on arranging on the carrier of electric furnace, the invention described above is made the powder of grain on arranging on heating wire again, go up at last the surface layer that press is suppressed into the heating wire carrier, and put into baker and cure, final stoving temperature, time are 400～550 ℃/10～20min, and so far, the invention process finishes.
Electric furnace carrier example of making is formulated procedural application and is adopted the application of material of the present invention in other.
Adopt prescription provided by the present invention and manufacture method, the product that makes can reach following technical-economic index:
1, electric strength E
b〉=3500V.AC./mm., 0.5mA was through 1 fen kind;
2, hot leakage current I
j≤ 0.1mA.260V.AC., 650 ℃;
3, insulation resistance Rj
1〉=500M Ω .500V.DC.;
4, damp attitude insulation resistance Rj
2〉=40M Ω .500V.DC., under the relative humidity 95%, 25 ℃ of ambient temperatures through 20 hours;
5, make product powder carrier and do not shrink, do not ftracture, 1 meter high fall do not ftracture, not broken.
6, the material cost that provided of the present invention prescription is 500～800 yuan/ton.
Claims (2)
1, a kind of unburned damp proof insulation material is characterized in that being mixed by two kinds of materials of A and B and forms, and in parts by weight, the A material is grouped into by following one-tenth:
Kaolin 45～62
Quartz sand 15～25
Emergy 12～20
Magnesium oxide 1～4
Mullite 10～16;
The B material is an inorganic adhesive, fills a prescription to be sulfuric acid magnalium inorganic glue powder 15～40g/1000ml H
2O; In the insulating material, by weight percentage, A accounts for 82～93%, and B accounts for 7～18%.
2, the described unburned damp proof insulation preparation methods of claim 1 comprises the steps:
(1) preparation of A material: the A material was mixed for 30～60 seconds in each mixer that becomes to be placed in;
(2) add the B material, stirred 5～8 minutes, powder and adhesive are evenly mixed and granulation in mixer.