CN105859457A - Flower nutrient soil and preparation method thereof - Google Patents
Flower nutrient soil and preparation method thereof Download PDFInfo
- Publication number
- CN105859457A CN105859457A CN201610468958.2A CN201610468958A CN105859457A CN 105859457 A CN105859457 A CN 105859457A CN 201610468958 A CN201610468958 A CN 201610468958A CN 105859457 A CN105859457 A CN 105859457A
- Authority
- CN
- China
- Prior art keywords
- parts
- sawdust
- water
- soil
- peat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses flower nutrient soil and a preparation method thereof and relates to the technical field of flower culture. The flower nutrient soil comprises, by mass, 5-10 parts of leaf mould, 20-30 parts of field soil, 3-5 parts of chicken manure, 2-3 parts of saw dust, 4-8 parts of plant nutrients, 9-12 parts of zeolite, 7-15 parts of medical stone, 10-20 parts of turf, 3-5 parts of sapropel, 2-5 parts of ferrous sulfate, 7-11 parts of urea water and 5-6 parts of monopotassium phosphate water. The flower nutrient soil and the preparation method thereof have the advantages of reasonable preparation steps, convenience in operation, scientific and reasonable nutrition combination, low cost, capability of increasing planting survival rate effectively, environmental protection, sanitation, dryness, permeability, less proneness to caking, no toxicity and odorlessness and anti-bacterial effect.
Description
Technical field
The present invention relates to technical field of flower cultivation, be specifically related to a kind of Flower nutrient soil and preparation method thereof.
Background technology
What the more conventional use of raw materials of China did soilless culture substrate material has river sand, perlite, Vermiculitum, peat etc., but all there is a lot of problem, independent perlite, Vermiculitum, peat plant flowers as Nutrition Soil, survival rate is the highest, nutrition is single, resource-constrained, high cost, the problem such as plantation that can not adapt to all kinds of plant.Developed into people later be made by absorption nutritional labeling again after a series of calcinings with zeolite powder.Although this manufacture method has improved, but cost of manufacture is higher, and the original abundant nutritional labeling of zeolite powder after calcining is the most destroyed, unfavorable to plant growing, complicated loaded down with trivial details by absorption nutritional labeling operation again, this technical method does not the most obtain fine application.
Patent No. CN 104016787 A discloses a kind of Flower nutrient soil, relates to technical field of biological fertilizer, is made up of the component of following mass percent: leaf mould 20%, mountain mud 20%, field soil 30%, chicken manure 2%, sawdust 18%, raising agent 9%, preservative 0.5%, plant nutrient agent 0.5%.
Although technique scheme cost of manufacture is low, step is succinct, but its nutrition coordinates not science, and plant growing survival rate is the highest, accordingly, it would be desirable to design a kind of Flower nutrient soil that can solve the problem that problem above and preparation method thereof.
Summary of the invention
Problem to be solved by this invention is to provide a kind of Flower nutrient soil and preparation method thereof.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of Flower nutrient soil, in parts by mass, described Flower nutrient soil includes leaf mould 5-10 part, field soil 20-30 part, chicken manure 3-5 part, sawdust 2-3 part, plant nutrient agent 4-8 part, zeolite 9-12 part, Maifanitum 7-15 part, peat 10-12 part, sapropel 3-5 part, ferrous sulfate 2-5 part, urea water 7-11 part, potassium dihydrogen phosphate water 5-6 part.
Preferably, in parts by mass, described Flower nutrient soil includes leaf mould 8 parts, 25 parts of field soil, chicken manure 4 parts, 2 parts of sawdust, plant nutrient agent 6 parts, 11 parts of zeolite, Maifanitum 10 parts, 11 parts of peat, sapropel 4 parts, 3 parts of ferrous sulfate, urea water 9 parts, 6 parts of potassium dihydrogen phosphate water.
A kind of preparation method of Flower nutrient soil, described preparation method specifically includes following steps:
Step one: prepare raw material:
(1) preparing leaf mould: collect tree deciduous leaf, residual grass, dish skin etc. in autumn and winter season, puddle with soil, water-water reactor amasss, compresses a little, and after half a year, turning is once, rewaters or thin human urine, and next year can become thoroughly decomposed, and after drying and sieving, preserves standby；
(2) chicken manure is prepared: collect chicken manure, drying or be exposed to the sun, twist with the fingers and carefully sieve, preserve standby；
(3) sawdust is prepared: installed by sawdust with plastic bag, add the pure water of sawdust weight 60%, tighten bag mouth, be placed under the temperature environment of 28-38 DEG C, can ferment rotten through 1-3 month, then dry in the air to half-dried, measuring the water content of sawdust, be held by hand one after the water content of sawdust to be fermented is transferred to 65-70%, it is standard that webs do not fall water, moisture content is the highest or the lowest is all unfavorable for fermentation, preserves standby；
(4) prepare zeolite powder: select tiltedly fermentation material celadon zeolite, size-reduced to 0.5-1.2mm particle diameter, pH value be 5.5-7.0；
(5) prepare medical stone powder: select the Maifanitum that is made up of silicon dioxide, aluminium sesquioxide, potassium oxide, sodium oxide, magnesium oxide, size-reduced to 0.5-1.0mm particle diameter, pH value be 6.0-7.5；
(6) peat is prepared: being air-dried by standby peat to water content weight ratio is 25%-55%, pulverizes, is the standard screen of 6mm by aperture；
(7) sapropel is prepared: air-dried by sapropel to water content ratio as 10%-30%, pulverize, be the standard screen of 6mm by aperture；
Step 2: sterilization, after being mixed by above-mentioned material, adds field soil and plant nutrient agent according to percentage by weight after preparing above-mentioned material, and then mix homogeneously carries out routine disinfection；
Step 3: with the pH of ferrous sulfate regulation mixture between 4-8；
Step 4: windrow, is spread among sawdust windrow after putting into urea water, potassium dihydrogen phosphate water in the above-mentioned raw material prepared, then sawdust is piled raft, breathability covering on the complete bonnet of heap；
Step 5: overturning, the good sawdust of heap was through 8-12 days, fermentation temperature reaches about 50 DEG C, can stir once through 28-34 hour under about 50 DEG C hot conditionss, the most again until temperature reaches 50 DEG C, second time is stirred, and second time is placed 4-6 days after stirring naturally, fermentation temperature is stable just completes fermentation below 35 DEG C, obtains this flower culturing soil.
Preferably, in parts by mass, described plant nutrient agent includes garlic powder 2-5 part, tealeaf residue 20-35 part, Sorghum vulgare Pers. powder 4-7 part, Shell of Water Chestnut powder 8-10 part, Fructus Lycopersici esculenti skin 5-10 part.
Preferably, described standby peat is the one in meadow peat, woody peat, moss peat.
Using technical scheme, preparation process is reasonable, it is simple to operation, and nutrition coordinates scientific and reasonable, low cost, it is possible to be effectively improved plant growing survival rate, environmentally-friendly sanitary, dry and comfortable ventilative, is difficult to knot hard, nonpoisonous and tasteless, sterilizes antibacterial.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with detailed description of the invention, the present invention is expanded on further.
Embodiment
1
A kind of Flower nutrient soil, in parts by mass, described Flower nutrient soil includes leaf mould 5 parts, 20 parts of field soil, chicken manure 3 parts, 2 parts of sawdust, plant nutrient agent 4 parts, 9 parts of zeolite, Maifanitum 7 parts, 10 parts of peat, sapropel 3 parts, 2 parts of ferrous sulfate, urea water 7 parts, 5 parts of potassium dihydrogen phosphate water.
A kind of preparation method of Flower nutrient soil, described preparation method specifically includes following steps:
Step one: prepare raw material:
(1) preparing leaf mould: collect tree deciduous leaf, residual grass, dish skin etc. in autumn and winter season, puddle with soil, water-water reactor amasss, compresses a little, and after half a year, turning is once, rewaters or thin human urine, and next year can become thoroughly decomposed, and after drying and sieving, preserves standby；
(2) chicken manure is prepared: collect chicken manure, drying or be exposed to the sun, twist with the fingers and carefully sieve, preserve standby；
(3) sawdust is prepared: installed by sawdust with plastic bag, add the pure water of sawdust weight 60%, tighten bag mouth, be placed under the temperature environment of 28 DEG C, can ferment rotten through 1 month, then dry in the air to half-dried, measuring the water content of sawdust, be held by hand one after the water content of sawdust to be fermented is transferred to 65%, it is standard that webs do not fall water, moisture content is the highest or the lowest is all unfavorable for fermentation, preserves standby；
(4) prepare zeolite powder: select tiltedly fermentation material celadon zeolite, size-reduced to 0.5mm particle diameter, pH value be 5.5；
(5) prepare medical stone powder: select the Maifanitum that is made up of silicon dioxide, aluminium sesquioxide, potassium oxide, sodium oxide, magnesium oxide, size-reduced to 0.5mm particle diameter, pH value be 6.0；
(6) peat is prepared: being air-dried by standby peat to water content weight ratio is 25%, pulverizes, is the standard screen of 6mm by aperture；
(7) sapropel is prepared: being air-dried by sapropel to water content ratio is 10%, pulverizes, is the standard screen of 6mm by aperture；
Step 2: sterilization, after being mixed by above-mentioned material, adds field soil and plant nutrient agent according to percentage by weight after preparing above-mentioned material, and then mix homogeneously carries out routine disinfection；
Step 3: with the pH of ferrous sulfate regulation mixture between 4；
Step 4: windrow, is spread among sawdust windrow after putting into urea water, potassium dihydrogen phosphate water in the above-mentioned raw material prepared, then sawdust is piled raft, breathability covering on the complete bonnet of heap；
Step 5: overturning, the good sawdust of heap was through 8 days, fermentation temperature reaches about 50 DEG C, can stir once through 28 hours under about 50 DEG C hot conditionss, the most again until temperature reaches 50 DEG C, second time is stirred, and second time is placed 4 days after stirring naturally, fermentation temperature is stable just completes fermentation at 35 DEG C, obtains this flower culturing soil.
Wherein, in parts by mass, described plant nutrient agent includes garlic powder 2 parts, tealeaf residue 20 parts, Sorghum vulgare Pers. powder 4 parts, 8 parts of Shell of Water Chestnut powder, Fructus Lycopersici esculenti skin 5 parts.
Wherein, described standby peat is meadow peat.
Embodiment
2
A kind of Flower nutrient soil, in parts by mass, described Flower nutrient soil includes leaf mould 10 parts, 30 parts of field soil, chicken manure 5 parts, 3 parts of sawdust, plant nutrient agent 8 parts, 12 parts of zeolite, Maifanitum 15 parts, 12 parts of peat, sapropel 5 parts, 5 parts of ferrous sulfate, urea water 11 parts, 6 parts of potassium dihydrogen phosphate water.
A kind of preparation method of Flower nutrient soil, described preparation method specifically includes following steps:
Step one: prepare raw material:
(1) preparing leaf mould: collect tree deciduous leaf, residual grass, dish skin etc. in autumn and winter season, puddle with soil, water-water reactor amasss, compresses a little, and after half a year, turning is once, rewaters or thin human urine, and next year can become thoroughly decomposed, and after drying and sieving, preserves standby；
(2) chicken manure is prepared: collect chicken manure, drying or be exposed to the sun, twist with the fingers and carefully sieve, preserve standby；
(3) sawdust is prepared: installed by sawdust with plastic bag, add the pure water of sawdust weight 60%, tighten bag mouth, be placed under the temperature environment of 38 DEG C, can ferment rotten through 3 months, then dry in the air to half-dried, measuring the water content of sawdust, the water content of sawdust to be fermented is transferred to 70% to grab one by defensive position, it is standard that webs do not fall water, moisture content is the highest or the lowest is all unfavorable for fermentation, preserves standby；
(4) prepare zeolite powder: select tiltedly fermentation material celadon zeolite, size-reduced to 1.2mm particle diameter, pH value be 7.0；
(5) prepare medical stone powder: select the Maifanitum that is made up of silicon dioxide, aluminium sesquioxide, potassium oxide, sodium oxide, magnesium oxide, size-reduced to 1.0mm particle diameter, pH value be 7.5；
(6) peat is prepared: being air-dried by standby peat to water content weight ratio is 55%, pulverizes, is the standard screen of 6mm by aperture；
(7) sapropel is prepared: being air-dried by sapropel to water content ratio is 30%, pulverizes, is the standard screen of 6mm by aperture；
Step 2: sterilization, after being mixed by above-mentioned material, adds field soil and plant nutrient agent according to percentage by weight after preparing above-mentioned material, and then mix homogeneously carries out routine disinfection；
Step 3: with the pH of ferrous sulfate regulation mixture between 8；
Step 4: windrow, is spread among sawdust windrow after putting into urea water, potassium dihydrogen phosphate water in the above-mentioned raw material prepared, then sawdust is piled raft, breathability covering on the complete bonnet of heap；
Step 5: overturning, the good sawdust of heap was through 12 days, fermentation temperature reaches about 50 DEG C, can stir once through 34 hours under about 50 DEG C hot conditionss, the most again until temperature reaches 50 DEG C, second time is stirred, and second time is placed 6 days after stirring naturally, fermentation temperature is stable just completes fermentation at 35 DEG C, obtains this flower culturing soil.
Wherein, in parts by mass, described plant nutrient agent includes garlic powder 5 parts, tealeaf residue 35 parts, Sorghum vulgare Pers. powder 7 parts, 10 parts of Shell of Water Chestnut powder, Fructus Lycopersici esculenti skin 10 parts.
Wherein, described standby peat is woody peat.
Embodiment
3
A kind of Flower nutrient soil, in parts by mass, described Flower nutrient soil includes leaf mould 8 parts, 25 parts of field soil, chicken manure 4 parts, 2 parts of sawdust, plant nutrient agent 6 parts, 11 parts of zeolite, Maifanitum 10 parts, 11 parts of peat, sapropel 4 parts, 3 parts of ferrous sulfate, urea water 9 parts, 6 parts of potassium dihydrogen phosphate water.
A kind of preparation method of Flower nutrient soil, described preparation method specifically includes following steps:
Step one: prepare raw material:
(1) preparing leaf mould: collect tree deciduous leaf, residual grass, dish skin etc. in autumn and winter season, puddle with soil, water-water reactor amasss, compresses a little, and after half a year, turning is once, rewaters or thin human urine, and next year can become thoroughly decomposed, and after drying and sieving, preserves standby；
(2) chicken manure is prepared: collect chicken manure, drying or be exposed to the sun, twist with the fingers and carefully sieve, preserve standby；
(3) sawdust is prepared: installed by sawdust with plastic bag, add the pure water of sawdust weight 60%, tighten bag mouth, be placed under the temperature environment of 33 DEG C, can ferment rotten through 2 months, then dry in the air to half-dried, measuring the water content of sawdust, the water content of sawdust to be fermented is transferred to 68% to grab one by defensive position, it is standard that webs do not fall water, moisture content is the highest or the lowest is all unfavorable for fermentation, preserves standby；
(4) prepare zeolite powder: select tiltedly fermentation material celadon zeolite, size-reduced to 0.8mm particle diameter, pH value be 6.5；
(5) prepare medical stone powder: select the Maifanitum that is made up of silicon dioxide, aluminium sesquioxide, potassium oxide, sodium oxide, magnesium oxide, size-reduced to 0.8mm particle diameter, pH value be 6.5；
(6) peat is prepared: being air-dried by standby peat to water content weight ratio is 40%, pulverizes, is the standard screen of 6mm by aperture；
(7) sapropel is prepared: being air-dried by sapropel to water content ratio is 20%, pulverizes, is the standard screen of 6mm by aperture；
Step 2: sterilization, after being mixed by above-mentioned material, adds field soil and plant nutrient agent according to percentage by weight after preparing above-mentioned material, and then mix homogeneously carries out routine disinfection；
Step 3: with the pH of ferrous sulfate regulation mixture between 6；
Step 4: windrow, is spread among sawdust windrow after putting into urea water, potassium dihydrogen phosphate water in the above-mentioned raw material prepared, then sawdust is piled raft, breathability covering on the complete bonnet of heap；
Step 5: overturning, the good sawdust of heap was through 10 days, fermentation temperature reaches about 50 DEG C, can stir once through 30 hours under about 50 DEG C hot conditionss, the most again until temperature reaches 50 DEG C, second time is stirred, and second time is placed 5 days after stirring naturally, fermentation temperature is stable just completes fermentation at 35 DEG C, obtains this flower culturing soil.
Wherein, in parts by mass, described plant nutrient agent includes garlic powder 3 parts, tealeaf residue 30 parts, Sorghum vulgare Pers. powder 5 parts, 9 parts of Shell of Water Chestnut powder, Fructus Lycopersici esculenti skin 8 parts.
Wherein, described standby peat is moss peat.
Based on above-mentioned, using technical scheme, preparation process is reasonable, it is simple to operation, and nutrition coordinates scientific and reasonable, low cost, it is possible to be effectively improved plant growing survival rate, environmentally-friendly sanitary, dry and comfortable ventilative, is difficult to knot hard, nonpoisonous and tasteless, sterilizes antibacterial.
Obviously the present invention implements and is not subject to the restrictions described above; if the improvement of the various unsubstantialities that the method design that have employed the present invention is carried out with technical scheme; or the most improved design by the present invention and technical scheme directly apply to other occasion, all within protection scope of the present invention.
Claims (5)
1. a Flower nutrient soil, it is characterized in that, in parts by mass, described Flower nutrient soil includes leaf mould 5-10 part, field soil 20-30 part, chicken manure 3-5 part, sawdust 2-3 part, plant nutrient agent 4-8 part, zeolite 9-12 part, Maifanitum 7-15 part, peat 10-12 part, sapropel 3-5 part, ferrous sulfate 2-5 part, urea water 7-11 part, potassium dihydrogen phosphate water 5-6 part.
A kind of Flower nutrient soil the most according to claim 1, it is characterized in that: in parts by mass, described Flower nutrient soil includes leaf mould 8 parts, 25 parts of field soil, chicken manure 4 parts, 2 parts of sawdust, plant nutrient agent 6 parts, 11 parts of zeolite, Maifanitum 10 parts, 11 parts of peat, sapropel 4 parts, 3 parts of ferrous sulfate, urea water 9 parts, 6 parts of potassium dihydrogen phosphate water.
3. the method for the Flower nutrient soil prepared described in claim 1-2 any one, it is characterised in that described preparation method specifically includes following steps:
Step one: prepare raw material:
(1) preparing leaf mould: collect tree deciduous leaf, residual grass, dish skin etc. in autumn and winter season, puddle with soil, water-water reactor amasss, compresses a little, and after half a year, turning is once, rewaters or thin human urine, and next year can become thoroughly decomposed, and after drying and sieving, preserves standby；
(2) chicken manure is prepared: collect chicken manure, drying or be exposed to the sun, twist with the fingers and carefully sieve, preserve standby
；
(3) sawdust is prepared: installed by sawdust with plastic bag, add the pure water of sawdust weight 60%, tighten bag mouth, be placed under the temperature environment of 28-38 DEG C, can ferment rotten through 1-3 month, then dry in the air to half-dried, measuring the water content of sawdust, be held by hand one after the water content of sawdust to be fermented is transferred to 65-70%, it is standard that webs do not fall water, moisture content is the highest or the lowest is all unfavorable for fermentation, preserves standby；
(4) prepare zeolite powder: select tiltedly fermentation material celadon zeolite, size-reduced to 0.5-1.2mm particle diameter, pH value be 5.5-7.0；
(5) prepare medical stone powder: select the Maifanitum that is made up of silicon dioxide, aluminium sesquioxide, potassium oxide, sodium oxide, magnesium oxide, size-reduced to 0.5-1.0mm particle diameter, pH value be 6.0-7.5；
(6) peat is prepared: being air-dried by standby peat to water content weight ratio is 25%-55%, pulverizes, is the standard screen of 6mm by aperture；
(7) sapropel is prepared: air-dried by sapropel to water content ratio as 10%-30%, pulverize, be the standard screen of 6mm by aperture；
Step 2: sterilization, after being mixed by above-mentioned material, adds field soil and plant nutrient agent according to percentage by weight after preparing above-mentioned material, and then mix homogeneously carries out routine disinfection；
Step 3: with the pH of ferrous sulfate regulation mixture between 4-8；
Step 4: windrow, is spread among sawdust windrow after putting into urea water, potassium dihydrogen phosphate water in the above-mentioned raw material prepared, then sawdust is piled raft, breathability covering on the complete bonnet of heap；
Step 5: overturning, the good sawdust of heap was through 8-12 days, fermentation temperature reaches about 50 DEG C, can stir once through 28-34 hour under about 50 DEG C hot conditionss, the most again until temperature reaches 50 DEG C, second time is stirred, and second time is placed 4-6 days after stirring naturally, fermentation temperature is stable just completes fermentation below 35 DEG C, obtains this flower culturing soil.
A kind of Flower nutrient soil the most according to claim 1, it is characterised in that: in parts by mass, described plant nutrient agent includes garlic powder 2-5 part, tealeaf residue 20-35 part, Sorghum vulgare Pers. powder 4-7 part, Shell of Water Chestnut powder 8-10 part, Fructus Lycopersici esculenti skin 5-10 part.
The preparation method of a kind of Flower nutrient soil the most according to claim 3, it is characterised in that: described standby peat is the one in meadow peat, woody peat, moss peat.