CN105839122A - 一种陶瓷器皿釉料配制罐清洗剂 - Google Patents

一种陶瓷器皿釉料配制罐清洗剂 Download PDF

Info

Publication number
CN105839122A
CN105839122A CN201610196403.7A CN201610196403A CN105839122A CN 105839122 A CN105839122 A CN 105839122A CN 201610196403 A CN201610196403 A CN 201610196403A CN 105839122 A CN105839122 A CN 105839122A
Authority
CN
China
Prior art keywords
parts
sodium
preparation tank
cleaning agent
glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610196403.7A
Other languages
English (en)
Inventor
许纯荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Blue And White Fang Ci Industry Limited-Liability Co
Original Assignee
Anhui Blue And White Fang Ci Industry Limited-Liability Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Blue And White Fang Ci Industry Limited-Liability Co filed Critical Anhui Blue And White Fang Ci Industry Limited-Liability Co
Priority to CN201610196403.7A priority Critical patent/CN105839122A/zh
Publication of CN105839122A publication Critical patent/CN105839122A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种陶瓷器皿釉料配制罐清洗剂,涉及陶瓷制造技术领域,由如下重量份数的原料制成:钠基膨润土15‑20份、火山灰10‑15份、卡波树脂10‑15份、鲸蜡醇8‑12份、羧甲基纤维素钠8‑12份、分子筛原粉6‑10份、海泡石粉5‑8份、聚乙烯醇5‑8份、十二烷基苯磺酸钠4‑6份、聚丙烯酸钠3‑5份、水杨酸钠2‑3份、烟酰胺2‑3份、丙酮15‑20份、乙醇50‑60份、水200‑250份。本发明使用方便,使用时只需用该清洗剂对配制罐搅拌浸泡10min,即可有效溶解配制罐内壁粘附的釉料,清洗效果好,并且对配制罐具有防锈作用,充分保护配制罐,从而延长其使用寿命和保证釉料的纯度。

Description

一种陶瓷器皿釉料配制罐清洗剂
技术领域:
本发明涉及陶瓷制造技术领域,具体涉及一种陶瓷器皿釉料配制罐清洗剂。
背景技术:
陶瓷釉料是生产陶瓷的半成品,统称基础釉,它是利用多种陶瓷用原料按照一定比例配制而成。陶瓷釉料的固体成分包括长石、石英、碱土金属氧化物和辅助原料,经水混合配成釉浆。釉料配制罐一般选用不锈钢金属罐,在釉料配制完成后在配制罐的内壁上会粘附一层釉料,不能直接用水冲洗掉,如需彻底清除需要借助工具,这样一来就容易破坏配制罐内壁结构,导致在以后使用时内壁出现生锈腐蚀现象,降低釉料的纯度,从而影响施釉效果。
发明内容:
本发明所要解决的技术问题在于提供一种使用方便、清洗效果好且清洗效率高的陶瓷器皿釉料配制罐清洗剂。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种陶瓷器皿釉料配制罐清洗剂,由如下重量份数的原料制成:
钠基膨润土15-20份、火山灰10-15份、卡波树脂10-15份、鲸蜡醇8-12份、羧甲基纤维素钠8-12份、分子筛原粉6-10份、海泡石粉5-8份、聚乙烯醇5-8份、十二烷基苯磺酸钠4-6份、聚丙烯酸钠3-5份、水杨酸钠2-3份、烟酰胺2-3份、丙酮15-20份、乙醇50-60份、水200-250份。
其制备方法包括如下步骤:
(1)将卡波树脂和聚乙烯醇加入乙醇中,充分混合后浸泡15min,再于微波频率2450MHz、功率800W下微波处理5min,然后加入鲸蜡醇和聚丙烯酸钠,继续微波处理10min,即得物料I;
(2)向水中加入钠基膨润土、火山灰、分子筛原粉和海泡石粉,充分混合后浸泡30min,然后加入球磨机中,球磨至细度小于50μm,即得物料II;
(3)向物料I中加入物料II、羧甲基纤维素钠、十二烷基苯磺酸钠、水杨酸钠、烟酰胺和丙酮,充分混合均匀后于0-5℃下静置8-12h,即得清洗剂。
本发明的有益效果是:本发明以钠基膨润土、火山灰和卡波树脂为主要原料,辅以鲸蜡醇等助剂制得陶瓷器皿釉料配制罐清洗剂,该清洗剂澄清透明,使用方便,使用时只需用该清洗剂对配制罐搅拌浸泡10min,即可有效溶解配制罐内壁粘附的釉料,清洗效果好,并且对配制罐具有防锈作用,充分保护配制罐,从而延长其使用寿命和保证釉料的纯度。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1
(1)将10份卡波树脂和8份聚乙烯醇加入50份乙醇中,充分混合后浸泡15min,再于微波频率2450MHz、功率800W下微波处理5min,然后加入8份鲸蜡醇和4份聚丙烯酸钠,继续微波处理10min,即得物料I;
(2)向200份水中加入15份钠基膨润土、10份火山灰、8份分子筛原粉和5份海泡石粉,充分混合后浸泡30min,然后加入球磨机中,球磨至细度小于50μm,即得物料II;
(3)向物料I中加入物料II、8份羧甲基纤维素钠、4份十二烷基苯磺酸钠、3份水杨酸钠、2份烟酰胺和2份丙酮,充分混合均匀后于0-5℃下静置12h,即得清洗剂。
实施例2
(1)将12份卡波树脂和6份聚乙烯醇加入60份乙醇中,充分混合后浸泡15min,再于微波频率2450MHz、功率800W下微波处理5min,然后加入10份鲸蜡醇和3份聚丙烯酸钠,继续微波处理10min,即得物料I;
(2)向250份水中加入20份钠基膨润土、12份火山灰、6份分子筛原粉和5份海泡石粉,充分混合后浸泡30min,然后加入球磨机中,球磨至细度小于50μm,即得物料II;
(3)向物料I中加入物料II、10份羧甲基纤维素钠、5份十二烷基苯磺酸钠、2份水杨酸钠、2份烟酰胺和15份丙酮,充分混合均匀后于0-5℃下静置12h,即得清洗剂。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种陶瓷器皿釉料配制罐清洗剂,其特征在于,由如下重量份数的原料制成:
钠基膨润土15-20份、火山灰10-15份、卡波树脂10-15份、鲸蜡醇8-12份、羧甲基纤维素钠8-12份、分子筛原粉6-10份、海泡石粉5-8份、聚乙烯醇5-8份、十二烷基苯磺酸钠4-6份、聚丙烯酸钠3-5份、水杨酸钠2-3份、烟酰胺2-3份、丙酮15-20份、乙醇50-60份、水200-250份。
2.根据权利要求1所述的陶瓷器皿釉料配制罐清洗剂,其特征在于,其制备方法包括如下步骤:
(1)将卡波树脂和聚乙烯醇加入乙醇中,充分混合后浸泡15min,再于微波频率2450MHz、功率800W下微波处理5min,然后加入鲸蜡醇和聚丙烯酸钠,继续微波处理10min,即得物料I;
(2)向水中加入钠基膨润土、火山灰、分子筛原粉和海泡石粉,充分混合后浸泡30min,然后加入球磨机中,球磨至细度小于50μm,即得物料II;
(3)向物料I中加入物料II、羧甲基纤维素钠、十二烷基苯磺酸钠、水杨酸钠、烟酰胺和丙酮,充分混合均匀后于0-5℃下静置8-12h,即得清洗剂。
CN201610196403.7A 2016-03-30 2016-03-30 一种陶瓷器皿釉料配制罐清洗剂 Pending CN105839122A (zh)