CN105662121B - 一种电炒锅的加工工艺 - Google Patents
一种电炒锅的加工工艺 Download PDFInfo
- Publication number
- CN105662121B CN105662121B CN201610264782.9A CN201610264782A CN105662121B CN 105662121 B CN105662121 B CN 105662121B CN 201610264782 A CN201610264782 A CN 201610264782A CN 105662121 B CN105662121 B CN 105662121B
- Authority
- CN
- China
- Prior art keywords
- pot body
- bottom plate
- plate
- welded
- frying pan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种电炒锅及加工工艺，用于解决将设置有加热管的底板焊接在纯铁锅体底部时焊接不上的问题。一种电炒锅，包括锅体、底板和加热管，所述底板固定在锅体的底部，在所述底板上设有加热管，其特征是，除与底板相对的锅体表面上设有氮化层。一种电炒锅的加工工艺，包括以下步骤：(1)、将铁板进行拉伸得到锅体；(2)、在锅体底部焊接保护板；(3)、对步骤(2)的锅体进行氮化处理；(4)、打磨掉经过步骤(3)处理的锅体底部的保护板，然后在锅体底部焊接底板，焊接底板时保证锅体底部温度在410℃‑430℃之间；(5)、对经过步骤(4)处理的锅体内部进行抛丸处理，直至锅体内部出现高低不平的麻点。通过本发明可方便的将底板及加热管焊接在电炒锅底部。
Description
技术领域
本发明涉及电炒锅制作技术领域，具体地说是一种电炒锅及加工工艺。
背景技术
对于普通的电炒锅锅体，如201、304、410、430不锈钢材质的锅体或铸铁锅体都可以采用常规的焊接方式在锅体底部焊接加热管。对于纯铁锅体，锅体氮化后其物理变化很大，此时再将铝制的底板焊接在锅体底部时，存在焊不上的问题，在底板上设有加热管。若采用打磨锅体底部将氮化层去除后，再焊接底板，则锅体的底部变薄，将底板焊接在锅体底部后锅体内侧会出现变色。
发明内容
本发明的目的在于提供一种电炒锅及加工工艺，用于解决将设置有加热管的底板焊接在纯铁锅体底部时焊接不上的问题。
本发明解决其技术问题所采取的技术方案是：一种电炒锅，包括锅体、底板和加热管，所述底板固定在锅体的底部，在所述底板上设有加热管，其特征是，除与底板相对的锅体表面上设有氮化层。
一种电炒锅的加工工艺，其特征是，包括以下步骤：
(1)、将铁板进行拉伸得到锅体；
(2)、在锅体底部焊接保护板；
(3)、对步骤(2)的锅体进行氮化处理；
(4)、打磨掉经过步骤(3)处理的锅体底部的保护板，然后在锅体底部焊接底板，焊接底板时保证锅体底部温度在410℃-430℃之间；
(5)、对经过步骤(4)处理的锅体内部进行抛丸处理，直至锅体内部出现高低不平的麻点。
进一步地，采用钎焊的方式在锅体底部焊接底板。
进一步地，所述保护板为圆形结构。
进一步地，采用机加工的方式去除锅体底部的焊缝，使得保护板与锅体分离。
本发明的有益效果是：本发明提供的电炒锅的加工工艺，首先通过铁板拉伸得到锅体，然后在锅体底部焊接保护板并拿去氮化处理，氮化处理后的电炒锅可以避免生锈现象。将保护板去除后由于锅体底部无氮化层，故可以成功的将底板焊接在锅体底部。对锅体进行抛丸处理，可以去除锅体内部的变色，增强美观的同时，还能避免粘锅现象的发生。
附图说明
图1为电炒锅锅体的示意图；
图中：1锅体，2底板，3加热管，4焊缝。
具体实施方式
下面结合附图对本发明的具体实施方式进行描述。
如图1所示，一种电炒锅，包括锅体1、底板2和加热管3，锅体为纯铁材质，采用焊接的方式将底板焊接固定在锅体的底部，底板为铝板且通常为圆形结构，在底板上设置有加热管，锅体上除与底板相对的锅体底部外均设置有氮化层，即除锅体底部焊缝所围区域之外均设置有氮化层，氮化层的设置可以避免锅体的生锈，氮化层的获得可通过对锅体进行氮化处理得到。在与底板相对应的锅体的底部没有氮化层，此处不设置氮化层的目的是为了方便底板的焊接。锅体底部无氮化层，可以将整个锅体进行氮化，然后对锅体底部进行机加工，以去除锅体底部的氮化层。
上述电炒锅的加工工艺，包括以下步骤：
(1)、将铁板进行拉伸得到锅体；
(2)、采用钎焊的方式在锅体底部焊接圆形的保护板，保护板的设置可以在锅体的氮化过程中保护锅体的底部，避免锅体底部氮化层的生成；
(3)、对步骤(2)的锅体进行氮化处理；
(4)、打磨掉经过步骤(3)处理的锅体底部的保护板，可以采用机加工的方式去除锅体底部的焊缝，使得保护板与锅体分离；然后采用钎焊的方式在锅体底部焊接底板，焊接底板时保证锅体底部温度在410℃-430℃之间，底板上设置有加热管，此时由于焊接的原因锅体内壁会产生变色现象；
(5)、对经过步骤(4)处理的锅体内部进行抛丸处理，直至锅体内部出现高低不平的麻点。
对锅体内部进行抛丸处理，可以打磨掉锅体内部的变色层，同时，锅体内部麻点的出现，使得锅体内部高低不平，这样在炒菜时，不会出现粘锅的现象。同时，锅体底部强度高耐冲击不易破损。
Claims (2)
1.一种电炒锅的加工工艺，其特征是，包括以下步骤：
(1)、将铁板进行拉伸得到锅体；
(2)、在锅体底部焊接圆形的保护板；
(3)、对步骤(2)的锅体进行氮化处理；
(4)、打磨掉经过步骤(3)处理的锅体底部的保护板，然后采用钎焊的方式在锅体底部焊接底板，在所述底板上设有加热管，焊接底板时保证锅体底部温度在410℃-430℃之间；
(5)、对经过步骤(4)处理的锅体内部进行抛丸处理，直至锅体内部出现高低不平的麻点。
2.根据权利要求1所述的电炒锅加工工艺，其特征是，采用机加工的方式去除锅体底部的焊缝，使得保护板与锅体分离。